SU1520045A1 - Polymer cement mixture for colouring fronts of buildings - Google Patents
Polymer cement mixture for colouring fronts of buildings Download PDFInfo
- Publication number
- SU1520045A1 SU1520045A1 SU864149637A SU4149637A SU1520045A1 SU 1520045 A1 SU1520045 A1 SU 1520045A1 SU 864149637 A SU864149637 A SU 864149637A SU 4149637 A SU4149637 A SU 4149637A SU 1520045 A1 SU1520045 A1 SU 1520045A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- buildings
- mixture
- cement mixture
- sulfur
- fronts
- Prior art date
Abstract
Изобретение предназначено дл окраски фасадных поверхностей. Цель изобретени - упрощение процесса приготовлени при снижении объемной массы и водопоглощени . Полимерцементна смесь дл окраски фасадов зданий содержит, мас.%: поливинилацетатную дисперсию или бутадиенстирольный латекс 5-30, портландцемент 10-25, серу 50-70. Адгези полимерцементной смеси к бетону 1,21-2,03 МПа, водопоглощение 1,9-3,6. 1 табл.The invention is intended for painting facade surfaces. The purpose of the invention is to simplify the cooking process while reducing the bulk density and water absorption. Polymer-cement mixture for painting facades of buildings contains, wt%: polyvinyl acetate dispersion or styrene-butadiene latex 5-30, portland cement 10-25, sulfur 50-70. Adhesion of polymer cement mixture to concrete 1.21-2.03 MPa, water absorption 1.9-3.6. 1 tab.
Description
Изобретение относитс к строительству , в частности к составам дл отделки фасадных поверхностей стен и конструкций зданий промьшшенного, жилищного и культурно-бытового назначени .The invention relates to the construction, in particular, to compositions for the finishing of the facade surfaces of walls and structures of industrial buildings, housing and cultural facilities.
Цель изобретени - упрощение процесса приготовлени при снижении объемной массы и водопоглощени .The purpose of the invention is to simplify the cooking process while reducing the bulk density and water absorption.
В качестве наполнител в смеси примен ют тонкодисперсный материал - техническую серу, котора вл етс основным структурообразующим элементом покрыти , регулирующим плотность, в зкость, укрывистость и другие свойства смеси. Количество серы в смеси определ ют, исход из условий придани всей смеси светлого тона дл получени хороших декоративных свойств покрыти , обеспечени легкости ее, при этом необходимо было не ухудшить физико-механические характеристикиFine material is used as a filler in the mixture - technical sulfur, which is the main structure-forming element of the coating that controls the density, viscosity, opacity, and other properties of the mixture. The amount of sulfur in the mixture is determined on the basis of the conditions for giving the entire mixture a bright tone in order to obtain good decorative properties of the coating, to ensure its lightness, while it was necessary not to impair the physical and mechanical characteristics
смеси. Поэтому при введении менее 50% серы увеличиваетс количество других компонентов, а именно дорогосто щих портландцемента и полимерного в жущего, что повышает стоимость смеси и может ухудшить цвет.mixes. Therefore, the introduction of less than 50% sulfur increases the amount of other components, namely, expensive portland cement and polymer cement, which increases the cost of the mixture and may deteriorate the color.
Увеличение количества серы в смеси (более 70%) нецелесообразно, так как при этом снижаетс количество полимерного в жущего - портландцемента , что приводит к ухудшению физико- механических свойств - снижению прочности , морозостойкости, атмосферр- стойкости, ухудшению адгезии.An increase in the amount of sulfur in the mixture (more than 70%) is impractical, since it reduces the amount of polymer vista - portland cement, which leads to a deterioration of the physicomechanical properties, such as a decrease in strength, frost resistance, resistance to weather, and adhesion.
Предлагаема отделочна смесь представл ет собой суспензию сухой части (цемент + сера) в водной дисперсии полимера, дисперси поли- винилацетата (ПВА), которую приготавливают путем смешивани . Состав готов т в смесителе СО-П или БС-43 при непрерывном перемешивании рецептурО1The proposed blend is a suspension of the dry part (cement + sulfur) in an aqueous polymer dispersion, polyvinyl acetate (PVA) dispersion, which is prepared by mixing. The composition is prepared in a CO-P or BS-43 mixer with continuous mixing of formulation O1.
юYu
«"
О1O1
него количества дисперсии ПВА,разведеной небольшим количеством воды,затем в смеситель загружают сухую часть, состо щую из цемента и серы. Остальное количество воды добавл ют в смеситель до получени однородной смеси необходимой подвижности (9-12 см по осадке конуса) в течение 5-10 мин.the amount of PVA dispersion diluted with a small amount of water, then a dry part consisting of cement and sulfur is loaded into the mixer. The remaining amount of water is added to the mixer until a homogeneous mixture of the desired mobility is obtained (9-12 cm over the sediment cone) within 5-10 minutes.
Предпагаема смесь состоит из мелкодисперсных материалов (размер частиц порошковой технической серы менее 50 мк) и дает гладку фактуру поверхности. Отделочное покрытие следует наносить на подготовленную фасадную поверхность. Подготовка заключаетс в устранении дефектов (трещин , раковин и др.), очистке поверхности от пьши, масл ных п тен и брызг раствора и не требует той тщательности и трудоемкости, как под окраску фасадными красками.The pre-mix consists of finely dispersed materials (the particle size of powder technical sulfur is less than 50 microns) and gives a smooth surface texture. The finishing coating should be applied on the prepared facade surface. The preparation consists in the elimination of defects (cracks, cavities, etc.), cleaning the surface from piercing, oil stains and spray of the solution and does not require the same care and laboriousness as for painting with facade paints.
Кроме того, влажность поверхности допускаетс до 25% (в случае отделки красками и другими составами влажность не должна превышать 8%).In addition, surface moisture is allowed up to 25% (in the case of paints and other compositions, the humidity should not exceed 8%).
Составы нанос т пневмораспылите- лем установки С-582 А (СО-2 Л) с диаметром сопел до 5 мм с рассто ни 30-40 см от отделываемой поверхности или при помощи шпаклевочного агрегата АШ-80. Возможно нанесение смеси валиком.The compositions are applied with a pneumatic sprayer of the C-582 A installation (CO-2 L) with nozzle diameter up to 5 mm from a distance of 30-40 cm from the surface to be trimmed or with the help of an ASH-80 spackling unit. It is possible to apply the mixture with a roller.
Такие преимущества предлагаемой смеси, как тонкодисперсность (составл ющие частицы размером менее 50 мк), небольшой объемный вес смеси ( f - 1,3 г/см по сравнению - 1,8-2,3 г/см), отсутствие в составе абразивных материалов - кварцевых песков позвол ют реализовать их в более широком выборе оборудовани дл приготовлени и нанесени составов . Указанные свойства смеси соответствуют технологическим параметра лакокрасочных материалов, примен емых дл окраски фасадов. Дл приготовлени смеси можно использовать смесители дл приготовлени масл ных составов: СО-8, СО-137, СО-129, дл J нанесени - мал рные агрегаты СО-154, СО-169 , СО-150.Such advantages of the proposed mixture as fine dispersion (constituting particles less than 50 microns in size), small bulk density of the mixture (f - 1.3 g / cm compared to 1.8-2.3 g / cm), the absence of abrasive materials in the composition - quartz sands allow them to be implemented in a wider choice of equipment for the preparation and application of compositions. These properties of the mixture correspond to the technological parameter of paints and varnishes used for painting facades. Mixers can be used to prepare the mixture for preparing oil compositions: CO-8, CO-137, CO-129, for J deposition - small aggregates CO-154, CO-169, CO-150.
Наиболее перспективным вл етс использование установок высокого давлени дл безвоздушного распылени 0 высоков зких составов /в зкость 200- 300 с) 7000Н, УБРХ-1М, которые за один проход позвол ют получать толстослойное (до 3 мм декоративное покрытие .The most promising is the use of high-pressure installations for airless spraying of highly viscous compositions / viscosity 200-300 s) 7000H, UBRH-1M, which in one pass allows to obtain a thick-layer (up to 3 mm decorative coating).
5 Рекомендуема толщина покрыти 2-5 мм. Расход 0,8-1,5 кг/м.5 Recommended coating thickness 2-5 mm. Consumption 0.8-1.5 kg / m.
Признав& целесообразность максимального переноса отделочных работ со стройки на заводы строительной ин- 0 дустрии можно использовать предлагаемую полимерцементную смесь и способ нанесени дл отделки изделий крупнопанельного домостроени на вертикальных конвейерах отделки в цехах 5 заводов.Recognizing & expediency of maximal transfer of finishing works from construction to construction industry plants, the proposed polymer-cement mixture and application method can be used for finishing large-panel house-building products on vertical finishing conveyors in the workshops of 5 plants.
Составы могут быть применены как дл вновь стро щихс зданий, так и дп обновлени фасадов при реставрации эксплуатируемых зданий. 0Compositions can be applied both for newly constructed buildings and reconstruction of facades during restoration of existing buildings. 0
Claims (1)