SU1454796A1 - Decorative opacified glass - Google Patents
Decorative opacified glass Download PDFInfo
- Publication number
- SU1454796A1 SU1454796A1 SU874254101A SU4254101A SU1454796A1 SU 1454796 A1 SU1454796 A1 SU 1454796A1 SU 874254101 A SU874254101 A SU 874254101A SU 4254101 A SU4254101 A SU 4254101A SU 1454796 A1 SU1454796 A1 SU 1454796A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- glass
- temperature
- blue
- production
- decorative
- Prior art date
Abstract
Изобретение относитс к составам глушеных стекол и может быть использовано как облицовочный декоративный материал, а также при производстве стеклокремнезита и дл .эмалировани стеклоизделий. С целью снижени температуры верхнего преде- л а кристаллизации и получени темно- синего цв ета с голубыми разводами без введени красителей стекло содержит , мас.%: SiO,j 46-53,4; ,5-9,3; BjOj 18,5-28,2, NajO 8,5-10,0; 1,8-4; TiO. ,0. Температура варки 1410-143С С, температура выработки 1070-1080 С, температура верхнего предела кристаллизации 980 С, температура разм гчени 510- 530 С. 1 табл. С SThe invention relates to glassy glass compositions and can be used as a decorative facing material, as well as in the production of glass-silica and for enamelling glass products. In order to reduce the temperature of the upper crystallization limit and obtain a dark blue color with blue spots without the introduction of dyes, the glass contains, in wt.%: SiO, j 46-53.4; 5-9.3; BjOj 18.5-28.2, NajO 8.5-10.0; 1.8-4; Tio. , 0. The cooking temperature is 1410-143 ° C, the production temperature is 1070-1080 ° C, the upper crystallization limit temperature is 980 ° C, and the softening temperature is 510-530 ° C. Table 1. With s
Description
1one
Изобретение относитс к составам глушеных стекол и может быть использовано как облицовочный декоративный материал, а также при производстве стеклокремнезита и дл эмалировани стеклоизделий с КЛТР (75-80) The invention relates to jammed glass compositions and can be used as a facing decorative material, as well as in the production of glass-silica and for enameling glassware with CTE (75-80)
Целью изобретени вл етс сниже-- ние температуры верхнего предела кристаллизации и получение темно си- него цвета с голубыми разводами без введени красителей.The aim of the invention is to reduce the temperature of the upper crystallization limit and to obtain a dark blue color with blue spots without the introduction of dyes.
Конкретные составы стекол и их свойства приведены в таблице.Specific compositions of glasses and their properties are shown in the table.
Как видно из таблицы, предложенное соотношение компонентов.обеспечивает температуру верхнего предела кристаллизации и глушение высокой степени, получение декоративных стекол синего цвета с голубыми разводами без применени красителей, .As can be seen from the table, the proposed ratio of components provides the temperature of the upper limit of crystallization and the killing of a high degree, obtaining decorative blue glasses with blue stains without the use of dyes.
получение плит стеклокремнезита голубого цвета с желтыми разводами, а также создание голубого эмалевого покрова без дополнительного введени пигмента.the production of blue-colored glassfibre plates with yellow stains, as well as the creation of a blue enamel coat without the addition of pigment.
Стекла при отливке глушатс и окрашиваютс , высокий художественный эффект достигаетс при про влении голубых разводов на темно-синем фоне изделий. Количество и характер рас- .пределени голубой окраски полностью зависит от содержани в стекле оксидов титана и фосфора. Независимо от содержани TiO и при термообработке стеклогранул та при 870- 900°С получаютс плиты стеклокремнезита голубого цвета с желтыми разводами , при нанесении стеклопорошка на гор чую поверхность стеклоплиток соз4 СП 4;: ЧGlasses during casting are glittered and painted; high artistic effect is achieved when blue stains appear on a dark blue background of products. The amount and nature of the blue color distribution depends entirely on the content of titanium and phosphorus oxides in the glass. Regardless of the TiO content and the heat treatment of the glass granules at 870 - 900 ° C, blue glass-silicate plates with yellow stains are obtained, and when applying the glass powder on the hot surface of the glass slabs cos4 SP 4 ;: H
СОWITH
00
бого цвета.God color
Предложенные стекла обладают водоустойчивостью . КЛТР составл ет (60-68)-10 . Температура разм гчени 510-530 С.The proposed glass are waterproof. The LTCR is (60-68) -10. The softening temperature is 510-530 C.
Стекла получают и вырабатывают по обычной технологии, дл получени стеклогранул та фриттуют в воде, дл эмалевого покрыти измельчают в фарфоровой мельнице. .Glasses are obtained and produced according to a conventional technology, for the production of glass granules, they are fritted in water, for an enamel coating they are ground in a porcelain mill. .
: Использование данного глушеного стекла при производстве облицовочных стеклоплиток и плит стеклокрем- незита позвол ет снизить температуру выработки стекол на 100° при сохранении высокого съема стекломассы с 1 м варочной части ванной печи (700- 800 кГ). Кроме того, упрощение состатериальных затрат.: The use of this jammed glass in the production of cladding glazed tiles and glass wedges makes it possible to reduce the temperature of glass production by 100 ° while maintaining a high removal of glass mass from 1 m of the cooking part of the bath (700-800 kg). In addition, the simplification of core costs.
Claims (1)