SU1320393A1 - Lightweight plugging composition - Google Patents
Lightweight plugging composition Download PDFInfo
- Publication number
- SU1320393A1 SU1320393A1 SU853967755A SU3967755A SU1320393A1 SU 1320393 A1 SU1320393 A1 SU 1320393A1 SU 853967755 A SU853967755 A SU 853967755A SU 3967755 A SU3967755 A SU 3967755A SU 1320393 A1 SU1320393 A1 SU 1320393A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- cement
- calcium chloride
- lignin
- water
- solution
- Prior art date
Abstract
Изобретение предназначено дл цементировани нефт ных и газовых скважин при наличии в их разрезах пластов, склонных к ноглощени м и гидроразрыва.м. Цель изобретени - снижение водоотделени . Тампо- нажный раствор содержит портландцемент, хлорид кальци , облегчающую добавку и воду. В качестве облегчающей добавки раствор содержит шлам-лигнин (ШЛ) состава. мас.°/о: лигнин 50-60, активный ил 18--20, окись алюмини 10-15, целлюлозное волокно 8-10 и полиакриламид 2-3. Соотношение компонентов в растворе следующее, мас.%: портландцемент 47,39-54,05; ШЛ 10,81 - 16,59; .хлорид кальци 2,37- 2,70; вода остальное. Введение в раствор ШЛ способствует повышению седиментационной устойчивости и кольматирующей способности тампонажного раствора. Прочность цементного камн значительно больше, чем у других облегченных тамнонажных составов. Это позвол ет сократить врем ожидани затвердевани цементных растворов и повысить качество цементировани скважин. 1 табл. Ф 00 ГчЭ о ОО со О5 i-.The invention is intended for cementing oil and gas wells in the presence of formations in their sections that are prone to absorption and hydraulic fracturing. The purpose of the invention is to reduce water separation. The cement solution contains portland cement, calcium chloride, facilitating the addition and water. As a facilitating additive, the solution contains sludge-lignin (SHL) composition. wt. & o / o: lignin 50-60, activated sludge 18--20, alumina 10-15, cellulose fiber 8-10 and polyacrylamide 2-3. The ratio of components in solution is the following, wt%: Portland cement 47.39-54.05; SL 10.81 - 16.59; Calcium chloride 2.37-2.70; water the rest. The introduction of SL into the solution contributes to the improvement of the sedimentation stability and clogging ability of the cement slurry. The strength of cement stone is much greater than that of other light weight cement compositions. This makes it possible to shorten the waiting time for cement mortars and improve the quality of well cementing. 1 tab. F 00 ГЧЭ о ОО с О5 i-.
Description
Изобретение относитс к тампонажным растворам, предназначенным дл цементировани нефт ных и газовых скважин при наличии в их разрезах пластов, склонных к поглош,ени м и гидроразрывам.The invention relates to cement slurries intended for cementing oil and gas wells in the presence of formations in their sections that are prone to extrusion, hydraulic fracturing and fracturing.
Целью изобретени вл етс снижение водоотделени .The aim of the invention is to reduce water separation.
Тампонажный раствор содержит в качестве облегчающей добавки шлам-лигнин (ШЛ), СОСТОЯН1ИЙ, мае.°/о: лигнин 50-60; активный ил 18-20; окись алюмини 10-15; целлюлозное волокно 8-10 и полиакрил- амид 2-3, вл ющийс отходом биохимической очистки сточных вод производства целлюлозы нри следующем соотноп1ении компонентов , .мас.°/о:The cement slurry contains as a lightening additive a slurry-lignin (SL), CONDITION, May. ° / o: lignin 50-60; activated sludge 18-20; alumina 10-15; cellulose fiber 8-10 and polyacrylamide 2-3, which is a waste of biochemical wastewater treatment of cellulose production at the following ratio of components, mas.% / o:
Портландцемент 47,39-54,05Portland cement 47.39-54.05
Шлам-лигнин10,81 - 16,59Slime lignin10.81 - 16.59
Хлорид кальци 2,37-2,70Calcium Chloride 2.37-2.70
ВодаОстальноеWaterEverything
В таблице приведены составы тамнонаж- ных растворов и их технологические параметры .The table shows the composition of the cement solutions and their technological parameters.
Пример. Д.т приготовлени тампонаж- ного раствора были вз ты пробы тампонаж- ного портландцемента, шлам-лигнина - отхода производства целлюлозно-бумажного комбината (ВЦБК) и хлорида кальци .Example. D.t of the preparation of the cement slurry were taken samples of cementing Portland cement, sludge-lignin - waste production of a pulp and paper mill (VTsBK) and calcium chloride.
Дл придани однородности составу осуществл ли пере.мешивание компонентов в пропеллерной мешалке при частоте вращени ее вала 1400 об/мин в течение 15 мин. У полученных растворов измер ли плотность , растекаемость, водоотделение, сроки схватывани , прочность на изгиб и сжатие.To ensure uniformity of the composition, the components were mixed in a propeller mixer at a rotational speed of its shaft of 1400 rpm for 15 minutes. The resulting solutions were measured for density, flow, water separation, setting time, bending strength and compression.
Как видно из таблицы, с увеличением количества вводимого ШЛ плотность тампо- нажного раствора снижаетс . При этом водоотделение уменьшаетс и достигает нулевого значени , в услови х испытаний спижа- етс проницаемость камн . Плотность там- понажного раствора снижаетс за счет более легкого, чем цемент, ШЛ (плотностьAs can be seen from the table, with an increase in the number of administered SL, the density of the cement solution decreases. At the same time, water separation decreases and reaches zero, in conditions of testing the stone permeability decreases. The density of the cement slurry is reduced due to a lighter than cement, SL (density
00
5five
00
5five
110°-1150 кг/м- ), а также возрастающего В/Ц. Снижение водоотделени достигаетс за счет компонентов, содержащихс в ШЛ активного ила, окиси алюмини , целлюлозного волокна и полиакриламида. Прочность цементного камн на высоком уровне, а также требуемые сроки схватывани получают в результате ввода хлорида кальци .110 ° -1150 kg / m-), as well as increasing W / C. The reduction in water separation is achieved by the components contained in the SL of activated sludge, alumina, cellulose fiber and polyacrylamide. The strength of the cement stone at a high level, as well as the required setting time, are obtained as a result of the input of calcium chloride.
Граничные значени вводимого шлам- лигнина. Мини.мальное количество шлам- лигнина вз то по плотности при ее значении 1650 кг/м и менее, тампонажный раствор считаетс облегченным. Максимальное количество вводимого ШЛ определ лось по наименьшей допустимой прочности цементного камн на изгиб, котора составл ет 0,7 МПа.Boundary values of the injected sludge lignin. The minimum amount of sludge lignin is taken up in density with a value of 1,650 kg / m or less, the cement slurry is considered lightened. The maximum amount of injected SL was determined by the lowest permissible bending strength of the cement stone, which is 0.7 MPa.
Технологи применени в промышленных услови х данного раствора следующа . Портландцемент и шлам-лигнин в заданной пропорции загружают в бункеры цементо- смесительных машин.The industrial application technology for this solution is as follows. Portland cement and lignin slurry are loaded into cement and mixing machines in a given proportion.
Хлорид кальци смешивают с водой. Затем включают в работу насосы цементировочных агрегатов и цементосмесительные машины и полученным водным раствором затвор ют смесь портландцемента и пглам- лигнииа и подают в скважину.Calcium chloride is mixed with water. Then, cementing units pumps and cementing machines are put into operation and the mixture of portland cement and plumlinium is obtained with the resulting aqueous solution and fed into the well.
Claims (1)