SU1188146A1 - Piezoelectric ceramic material - Google Patents
Piezoelectric ceramic material Download PDFInfo
- Publication number
- SU1188146A1 SU1188146A1 SU823498387A SU3498387A SU1188146A1 SU 1188146 A1 SU1188146 A1 SU 1188146A1 SU 823498387 A SU823498387 A SU 823498387A SU 3498387 A SU3498387 A SU 3498387A SU 1188146 A1 SU1188146 A1 SU 1188146A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- ceramic material
- lead glass
- piezoelectric ceramic
- pbtio
- maintaining
- Prior art date
Abstract
1. ПЬЕЗОЭЛЕКТРИЧЕСКИЙ КЕРАМИЧЕСКИЙ МАТЕРИАЛ, включающий ,PbTiO, Nd2Ti,jOy или и свинцовое стекло, отличающийс тем, что, с целью увеличени механической прочности при сохранении электрофизических свойств, он содержит указанные компоненты в следукнцем соотношении, мас.%: FbTiO,84-94 или 5-15 Свинцовое стекло 1 2. Материал по п. 1, отличающийс тем, что свинцовое стекло имеет следующий состав, мас.%: РЬО73,02 ТЮз5,64 SbjO,8,27 ,071. PIEZOELECTRIC CERAMIC MATERIAL, including, PbTiO, Nd2Ti, jOy or and lead glass, characterized in that, in order to increase the mechanical strength while maintaining the electrophysical properties, it contains these components in the following ratio, wt.%: FbTiO, 84-94 or 5-15 Lead glass 1 2. The material according to claim 1, characterized in that the lead glass has the following composition, in wt%: PbO73.02 TUz5.64 SbjO, 8.27, 07
Description
00 0000 00
х Изобретение относитс к электронной технике и может быть использовано дл изготовлени вибропреобразователей , СВЧ-резонаторов, имеющих высокую температурную стабильность резонансной частоты, в качестве электромеханических фильтров и т.д. Целью изобретени вл етс увеличение механической прочности при сохранении электрофизических свойств. Дл изготовлени керамического дл изготовлени керамического чатериала используют оксиды марки ч.д.a., смешивание и помол провод т в шмовом барабане в среде изопропилового спирта в течение 12 ч. После 15 высушивани шликера при 150-200°С осуществл ют синтез PbTiO при 850 С в течение 4 ч. Брикеты после синтеза измельчают указанным способом и во врем измельчени ввод т предвари- 20 тельно синтезированные при в течение 4 ч соединени Nd2Ti20y или La-TijOy и стекло. Последнее плав т в корундовом тигле при 12401280с в течение 0,5 ч и фриттуют. 25 После гомогенизации смесь компонентов высушивают, прессуют диски диаметром 10 мм, использу в качестве св зки трехпроцентный водный раствор поливинилового спирта, спекают диски при 1150-1190 С в течение 1 ч. После шлифовки вакуумным напьшением нанос т алюминиевые электроды и провод т пол ризацию в полисилоксановом масле при в течение 4 ч при посто нном поле напр женностью 30-45 кВ/мм. В табл. 1 представлены составы полученных материалов, в табл. 2 электрофизические свойства. Т а б л и ц а 1 Состав, мас.% 1т PbTiO I Nd-Ti-O Стекло -- -1 Используют стекло, содержащее , мас.%:РЬО 73,02; TiO 5,64; 8,27 иSiOg 13,07. блица2The invention relates to electronic engineering and can be used to manufacture vibration transducers, microwave resonators having a high temperature stability of a resonance frequency, as electromechanical filters, etc. The aim of the invention is to increase the mechanical strength while maintaining the electrical properties. For the manufacture of ceramic for the manufacture of ceramic chaterial, oxides of grade ch.a.a are used, mixing and grinding are carried out in a shock drum in isopropyl alcohol for 12 hours. After 15 drying of the slurry at 150–200 ° C, PbTiO is synthesized at 850 C for 4 hours. The briquettes after synthesis are ground by the above method, and during grinding, Nd2Ti20y or La-TijOy compounds and glass are synthesized in advance for 4 hours. The latter is melted in a corundum crucible at 12401280s for 0.5 h and is fritted. 25 After homogenization, the mixture of components is dried, pressed disks with a diameter of 10 mm, using a three percent aqueous solution of polyvinyl alcohol as a binder, sintering disks at 1150-1190 ° C for 1 hour. After grinding by vacuum coating, aluminum electrodes are applied and polarization is carried out polysiloxane oil for 4 h at a constant field strength of 30-45 kV / mm. In tab. 1 presents the compositions of the obtained materials, in table. 2 electrophysical properties. Table 1 Composition, wt.% 1t PbTiO I Nd-Ti-O Glass - -1 Glass containing, in wt.%, Is used: PHO 73.02; TiO 5.64; 8.27 and SiOg 13.07. blitz2
Claims (2)