SU1180486A1 - Composition for artificial hole-bottom - Google Patents
Composition for artificial hole-bottom Download PDFInfo
- Publication number
- SU1180486A1 SU1180486A1 SU833667467A SU3667467A SU1180486A1 SU 1180486 A1 SU1180486 A1 SU 1180486A1 SU 833667467 A SU833667467 A SU 833667467A SU 3667467 A SU3667467 A SU 3667467A SU 1180486 A1 SU1180486 A1 SU 1180486A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- composition
- epoxy resin
- quartz sand
- hardener
- plasticizer
- Prior art date
Abstract
СОСТАВ ДЛЯ ИСКУССТВЕННОГО ЗАБОЯ СКВАЖИНЫ, включающий эпоксидную с.молу, пластификатор, отвердитель и наполнитель - кварцевый песок, отличающийс тем, что, с целью повышени прочности и долговечности камн на его основе, он содержит в качестве пластификатора полиэфиракрилат, отвердител - дицианэтилдиэтилентриа .мин при следующем соотношении компонентов, мае. Эпоксидна смола 45,0-45,7 Полиэфиракрилат 4,6-6,6 Дицианэтилди этилен-, 4,1-4,9 триамин Кварцевый песок ОстальноеCOMPOSITION FOR ARTIFICIAL WELLING OF A WELL, including epoxy resin, plasticizer, hardener and filler - quartz sand, characterized in that, in order to increase the strength and durability of stone based on it, it contains polyether acrylate as a plasticizer, hardener - dicyanethyl diethylene tether. The following ratio of components, May. Epoxy resin 45.0-45.7 Polyether acrylate 4.6-6.6 Dicyanethyldi ethylene-, 4.1-4.9 triamine Quartz sand Else
Description
0000
о иabout and
ооoo
О5 Изобретение относитс к составам дл создани искусственных забоев при бурении многоствольных скважин, сложенных породами VIII-XI категорий буримости. Цель изобретени - повышение прочности и долговечности камн на основе состава дл искусственного забо скважины, включающего эпоксидную смолу, пластификатор , отвердитель и наполнитель - кварцевый песок. Пример I. Берут 450 г эпоксидной смолы и нагревают до 60-70°С. В подогретую смолу добавл ют пластификатор - полиэфиракрилат (46 г) и смесь тщательно перемешивают . В пластифицированную смолу добавл ют 463 г кварцевого песка, после чего смесь вновь тщательно перемешивают до получени однородной смеси и охлаждают до комнатной температуры (18-20°С). Затем в охлажденную до комнатной температуры смесь добавл ют 41 г отвердител и полученный состав еще раз тщательно перемешивают. Приготовление составов при других соотношени х компонентов осуществл етс в той же последовательности и отличаетс лишь количественным содержанием компо- 25 нентов. В предлагаемом составе были использованы эпоксидна дианова смола ЭД-20, отвердитель УП-0633 и пластификатор - полиэфиракрилат МГФ-9. В промысловых услови х приготовленный состав заливают в специальный контейнер диаметром 57 мм на базе тампонажного снар да СТ-10-59 и опускают в скважиВ табл. 1 приведены предлагаемые составь1 . В табл. 2 приведены прочностные свойства предлагаемого состава в сравнении с известным. Из каждого состава были изготовлены контрольные образцы в количестве 5 шт размером 20х20хЗОмм, которые подвергались статическому сжатию через 24, 72 ч и через мес ц. Сжатие образцов происходило на прессе П-10. Жизнеспособность состава определ лась в лабораторных услови х, максимально приближенных к услови м буровой скважины. Приготовленный по предлагаемой технологии состав (5 вариантов) разливалс в специальные формы размером 20x20x30 мм, которые помещались в ванночку с минерализованной водой. Послед помещалась в термостат, где она выдерживалась при 40°С.O5 The invention relates to compositions for creating artificial faces during the drilling of multilateral wells composed of rocks of VIII-XI categories of drillability. The purpose of the invention is to increase the strength and durability of stone based on the composition for an artificial bottom hole, including epoxy resin, plasticizer, hardener and filler - quartz sand. Example I. Take 450 g of epoxy resin and heated to 60-70 ° C. A plasticizer, polyester acrylate (46 g), is added to the preheated resin and the mixture is thoroughly mixed. 463 g of quartz sand is added to the plasticized resin, after which the mixture is thoroughly mixed again to obtain a homogeneous mixture and cooled to room temperature (18-20 ° C). Then, 41 g of hardener is added to the mixture cooled to room temperature and the resulting composition is thoroughly mixed again. The preparation of the compositions at different ratios of the components is carried out in the same sequence and differs only in the quantitative content of the components. In the proposed composition were used epoxy resin Dianova ED-20, the curing agent UP-0633 and the plasticizer - polyester acrylate MGF-9. In field conditions, the prepared composition is poured into a special container with a diameter of 57 mm on the basis of cementing slurry CT-10-59 and dipped into the well of the table. 1 shows the proposed composition1. In tab. 2 shows the strength properties of the proposed composition in comparison with the known. From each composition, control samples were made in an amount of 5 pieces of size 20x20xOmm, which were subjected to static compression after 24, 72 hours and months. Compression of the samples occurred on the press P-10. The viability of the composition was determined in laboratory conditions as close as possible to the conditions of the borehole. The composition prepared according to the proposed technology (5 variants) was poured into special forms with a size of 20x20x30 mm, which were placed in a bath with saline water. The placenta was placed in a thermostat, where it was kept at 40 ° C.
Эпоксидна смолаEpoxy resin
Полиэфиракрилат пластификаторPolyether acrylate plasticizer
Дицианэтилдиэтилентриаминотвердитель4 ,1Dicyanthylethylamine triamide hardener4, 1
Кварцевый песок - наполнительQuartz sand - filler
Таблица 1Table 1
45,745.7
45,2 45,35 45,545.2 45.35 45.5
5,65.6
6,66,6
6,16.1
5,15.1
4,94.9
4,74.7
4,54.5
,33
Остальное Примечание: Else Note:
Таблица 2 Известный j мас,%: эпоксидна смола ЭД-10 100, дибутилфтапат 20; гексаметилендиамин 12; кварцевый песок 200.Table 2 Known j wt,%: epoxy resin ED-10 100, dibutylphapt 20; hexamethylenediamine 12; quartz sand 200.
Claims (1)