SU1089069A1 - Batch for making foamed glass

Info

Publication number: SU1089069A1
Application number: SU813365958A
Authority: SU
Inventors: Эмма Рубеновна Саакян
Original assignee: Научно-Исследовательский Институт Камня И Силикатов
Priority date: 1981-12-15
Filing date: 1981-12-15
Publication date: 1984-04-30

Abstract

ШИХТА ДЛЯ ПОЛУЧЕНИЯ nEHOCWEKЛА , включающа перлит, гидрат окиси натри и газообразователь, о т л ичающа с тем, что, с целью повышени прочности, она в качестве газообразовател содержит углерод при следующем соотношении компонентов , мас.%: Гидрат окиси натри 6-12 Углерод0,015-0,09 ПерлитОстальноеThe CHARGE TO GET nEHOCWEKL, including perlite, sodium hydroxide and a blowing agent, is about the fact that, in order to increase its strength, it contains carbon as a blowing agent in the following ratio, wt.%: Sodium hydroxide 6-12 Carbon 0 , 015-0,09 PerliteEverything Else

Description

X)X)

хx

) Изобретение относитс к составам дл получени теплоизол ционных материалов , в частности пеностекла. Известен состав шихты дл изготов лени пеностекла, содержащий, мас.% перлит 91,5-94 и гидрат окиси 6-8,5 вспенивающийс в интервале температур 850-950 С с образованием пеностекла с объемной массой 200-900 кг/ и водЬпоглощением до 5% м . Недостаток данного состава высока температура вспенивани . Наиболее близок к предлагаемому состав шихты дл получени пеностекла 2 , содержащий, мас.%: Перлит 87,0-93,9 Гидрат окиси натри 6,0-12,0 KNO,0,1-1,0 Недостатками известного состава пеностекла вл ютс невысока механи ческа прочность как следствие неоднородности структуры, а также расход газообразовател . Цель изобретени - повышение про ности. Поставленна цель достигаетс тем, что шихта дл получени пеностекла , включающа перлит, гидрат окиси натри и газообразователь. в качестве газообразовател содержит углерод при следующем соотношении компонентов, мас.%: Гидрат окиси натри 6-12 Углерод0,015-0,09 ПерлитОстальное Дл получени пеностекла производ т сухой помол ингредиентов дл получени порошка с удельной поверхностью 3500-5000 . К готовому порошку добавл ют раствор гидрата окиси натри , перемешивают в бегунах и вспучивают при 800-850 С в течение 5-15 мин. Конкретные составы шихты и ее свойства приведены в таблице. Из шихты с небольшим количеством углерода получаетс высокопрочное пеностекло, что объ сн етс правильным формированием его структуры вследствие обеспечени достаточного контакта между частицами стекла и более раннего образовани на поверхности спеков стекловидной газонепроницаемой пленки, преп тствзгющей выходу образующихс газов. Использование предлагаемого состава шихты позволит снизить себестоимость пеностекла.The invention relates to compositions for the preparation of heat insulating materials, in particular foam glass. The known composition of the mixture for the manufacture of foam glass, containing, wt.% Perlite 91.5-94 and oxide hydrate 6-8.5 foaming in the temperature range 850-950 C with the formation of foam glass with a bulk weight of 200-900 kg / and water absorption up to 5 % m The disadvantage of this composition is high foaming temperature. Closest to the proposed composition of the mixture to obtain foam glass 2, containing, wt.%: Perlite 87.0-93.9 Sodium hydroxide 6.0-12.0 KNO, 0.1-1.0. The disadvantages of the known composition of foam glass are low mechanical strength as a result of heterogeneity of the structure, as well as the consumption of the gasifier. The purpose of the invention is to enhance the pro. This goal is achieved in that the charge for the preparation of foam glass, including perlite, sodium hydroxide and a blowing agent. as a blowing agent contains carbon in the following ratio, wt.%: Sodium hydroxide 6-12 Carbon 0,015-0,09 Perlite Other For the production of foam glass a dry grinding of the ingredients is made to obtain a powder with a specific surface of 3500-5000. A solution of sodium hydroxide is added to the finished powder, mixed in runners and expanded at 800-850 ° C for 5-15 minutes. The specific composition of the mixture and its properties are shown in the table. High-strength foamed glass is obtained from a mixture with a small amount of carbon, which is explained by the correct formation of its structure due to the provision of sufficient contact between the glass particles and the earlier formation of a vitreous gas-tight film on the surface of the specimen preventing the formation of gases. The use of the proposed composition of the charge will reduce the cost of foamed glass.

Предлагаемый 88,985 11,0 0,015 420 8,71 38,94 11,0 0,06 270 88,93 11,0 0,07 280 Мелкий, 0,8 равномерный То же 0,9 1,0 Средний, раз- 1,1 номерный Бежевьш СветлыйThe proposed 88.985 11.0 0.015 420 8.71 38.94 11.0 0.06 270 88.93 11.0 0.07 280 Fine, 0.8 uniform The same 0.9 1.0 Medium, size 1, 1 number Beige Light

Продолжение таблицыTable continuation

Claims

MIXTURE FOR PRODUCING FOAM GLASS, including perlite, sodium hydroxide and a blowing agent, characterized in that, in order to increase strength, it contains carbon as a blowing agent in the following ratio, wt.%:

Sodium Oxide Hydrate 6-12

Carbon 0.015-0.09

Perlite rest