SU1027187A1

SU1027187A1 - Lubricating composition

Info

Publication number: SU1027187A1
Application number: SU813366903A
Authority: SU
Inventors: Григорий Григорьевич Чигаренко; Виктор Александрович Коган; Виктор Сергеевич Болотников; Анатолий Сергеевич Бурлов; Геннадий Павлович Барчан
Original assignee: Ростовский Ордена Трудового Красного Знамени Государственный Университет
Priority date: 1981-12-25
Filing date: 1981-12-25
Publication date: 1983-07-07

Abstract

СМАЗОЧНАЯ КОМПОЗИЦИЯ, содержаща базовое масло, сложный эфир фталевой кислоты и присадки, отличающа с тем, что, с целью улучшени нагрузочных, антифрикционных и-противоизносньк свойств композиций , в качестве присадок она содержит 2-тиазолилазо-р1 афтол и бис-LUBRICANT COMPOSITION, containing base oil, phthalic acid ester and additives, characterized in that, in order to improve the load, antifriction and anti-wear properties of the compositions, it contains 2-thiazolylazo-p1 aphthol and bis as additives

Description

Изобретение относитс к смазочным маслам и смазкам на их основе и может быть испбпьзовано в машин - и приборостроении дл смазки узлов трени , сталь-сталь и сталь-сплав меаи за счет реализации избирательного переноса. Известны смазочные композиции на основе нефт ных в синтетических масел с аобавлением сложных эфиров азелаиновой кислоты и 1-(2-окси-1-«афтилазо)2-41афтол-4-сульфокислоты С } г сложных эфвров ааип новсД кислоты и 2-тиаз лилазо -р-нафтола 23. Известна также смазочна композици сооержаша базовое .масло, сложный эфир фталевой кислоты присаакн бис(2 - ксибензаль )-,4-ч1иам1Шофецоп Сз 3 . Указанные композиции имеют высокие смазочные характеристики за счет реа лизации режима избирательного переноса в парецс трени сталь сплав меа . Неаостатком известных композиций вл етс узка область п{Я менени . Они облацают хорсоиими смазочными свойствами в парах трени сталь - сплав меаи. В парах сталь-сталь они обладают недостаточно высокими смазочными свойствами. Целью изобретени вл етс улучшение антифрикционных, нагрузочных и противоизносных свойств масел и смазок на их основе Поставленна цель.достигаетс тем, что смазочна композици , сооержаша базовое масло, сложный эфир фталевой кислоты и присадки в качестве последних содержит 2-ФиaзoлшIaзoif -нaфтoл и бис-(2-1Тиазолилазо)- $-нафтопат) ко бальта при следующем соотнсмпении компонентов , вес.%: 2-тиазолшшзо 41афтоп 0,,ЗО Био-(2.гиазолилазо)нафтолат ) кобальтаО,О5Д),30 Сложный эфир фталевсЛ кислоты20-30 Базовое маслоДо 10О ЭФИ1&1 фталевой кислоты ввод т как ОЛЯ улучшени смазочных свойств, так и дл улучшени растворимости пртсааок. Добавка эфира ниже 20 вес.% недоста точна дл растворени добавок, выше 30 не намного улучшает смазочные свойства но приводит к удорожанию композиций. Тиазр илазор| г«афтап (лиганд) имеет формулуНи и введен дл улучшени смазочных свойств композиции. Бис-(тиазолилаао-/ №|фтопат) кобальта (комплекс) имеет формулу г- |Г,1 И усиливает действие лиганда. Дл приготовлени композиций используют нефт ные масла различного химического строени , имеющие неодинаковые физико-химические свойства: основаАСВ-, индуст{И1альные, вакуумное ВМ-4, прибо{ ное МВП, (эфиры пентаэритрита и жирных кислот фракции С,-С.) Масла 1 смешивают с эфирами и раствор ют лиганд и комплекс при нагревании и интенсивном перемешивании. После охлаждени получают масло, готовое к употреблению. Смазочные свойства исследуют на машине TOfKiOBoro трени . Подвижные образцы диаметром 6 мм и неподвижные планки Изготавливают из стали 45. Объем масшнюй ванны 35-40 см , средн скорость 0,8 м/с. Нагружение ступенчатое. Длительность испытаний 5 ч. Образцы обрабатывают до З-го класса чистоты и обезжиривают диэтиловым эфиром и ацетоном. Фиксируют максимальную нап- рузку выше которой не реализуетс устойчивый режим трени или режим избирательного переноса и коэффициент трени , Износ (тредел ют весовым методом по разнице веса образцов до и после испытаний. Весовую интенсивность износа определ ют по формуле где q, - потер веса образцов; Sn плошадь контгиста; L - путь трени . Дл сравнени приведены данные испь таний смазоч1в 1х композиций состава, вес.%; 1ш.(2-окси-1наафтш1азо)-2 афто} -4-«ульфокислота 0,2; сложный эфир азелаиновой кислоты 2О; индустриальное - 5О до 1ОО (состав 1), а также состава, вес.% бис 2-оксибензаль-2,4-диаминофенол 0,2; динонилфталат 20; индустриальное-50 до 1ОО, и состав вес.%: 2-тиазолилазо- нафтол 0,2; динониладипинат 20; инду стриальное-50 до 10О. Результать : испытаний привеаены в таблице.The invention relates to lubricating oils and lubricants based on them and can be used in machinery - and instrumentation for lubricating friction units, steel-steel and steel-alloy mei through the implementation of selective transfer. Oil based lubricating compositions are known in synthetic oils with the addition of esters of azelaic acid and 1- (2-hydroxy-1- "aftilazo) 2-41 naphthol-4-sulfonic acid C} g of complex acid aypavensD acid and 2-thiaz lilazo - p-naphthol 23. Also known is a lubricant composition containing a basic oil, ester of phthalic acid, psaacn bis (2 - xibenzal) -, 4-h1iam1 Shoftocop Cz 3. These compositions have high lubricating characteristics due to the implementation of the regime of selective transfer to steel alloy steel me- thary fatigue. The non-residual composition of known compositions is the narrow region of the n {i change. They are characterized by high lubricating properties in pairs of friction steel - an alloy of mei. In steel-steel pairs, they do not have high enough lubricating properties. The aim of the invention is to improve the antifriction, load and anti-wear properties of oils and lubricants based on them. The goal is achieved by the fact that the lubricant composition, containing the base oil, phthalic acid ester and the additives, as the latter, contains 2-Phazole Iazoif-naphthol and bis- ( 2-1Tiazolylazo) - $ -naptopat) cobalt with the following ratio of components, wt.%: 2-thiazolshzo 41 naptop 0, ZO Bio- (2.giazolylazo) naphtholate-cobaltO, O5D), 30 Phthalate ester of acid 20-30 Base oil up to 10 o ephi1 &ph; 1 phthalic acid is added to OLYA to improve lubricating properties and to improve the solubility prtsaaok. The addition of ether below 20% by weight is not enough to dissolve the additives, above 30 does not much improve the lubricity, but increases the cost of the compositions. Tiazr and Alazor | The aftap (ligand) has the formula &num; and is introduced to improve the lubricating properties of the composition. Bis- (thiazolyl-ao- / No. | phtopath) cobalt (complex) has the formula g- | G, 1 And enhances the action of the ligand. For the preparation of compositions, petroleum oils of various chemical structures with different physicochemical properties are used: base ACB-, industrial {Ialnye, vacuum VM-4, equip- ment {MVP, (esters of pentaerythritol and fatty acids of fraction C, -C.) Oils 1 mixed with ethers and the ligand and complex are dissolved with heating and vigorous stirring. After cooling, a ready-to-eat oil is obtained. Lubricating properties are examined on a TOfKiOBoro friction machine. Movable samples with a diameter of 6 mm and fixed strips Made of steel 45. The volume of a large-scale bath is 35-40 cm, average speed is 0.8 m / s. Step loading. The test duration is 5 hours. Samples are processed to the 3rd class of purity and degreased with diethyl ether and acetone. The maximum load above which the steady mode of friction or selective transfer mode and the coefficient of friction are not recorded are recorded. Wear (determined by the weight method for the difference in weight of the samples before and after testing. The weighting intensity of wear is determined by the formula where q, is the weight loss of the samples; Sn area of contigist; L - way of friction. For comparison, data on lubrication of 1x compositions of composition, wt.%; 1 point (2-hydroxy-1aaftsh1azo) -2 afto} -4- "ulfacid 0,2; azelaic acid ester 2O; industrial - 5O to 1OO (composition 1), and t kzhe composition, wt.% bis 2-hydroxybenzal-2,4-diaminophenol 0.2, dinonyl phthalate 20; industrial-50 to 1OO, and composition wt.%: 2-thiazolylazo-naphthol 0.2; dinonyl adipate 20; industrial- 50 to 10 O. Result: the tests are shown in the table.

Смазочна композици Lubricating composition

состав 1composition 1

состав 2 состав 3 Масл на composition 2 composition 3 Oil on

. основа . the foundation

Инцустриаль- Дигексипфталат нов-5ОIncustrial-Digeksipftalat new-5O

Инаустриал Inaustrial

Двнонилфталат ное-бОDvonylphthalate noe-bo

О,О91 19,54O, O91 19.54

«"

О,О98 2О.43 0,097 2О,12O, O98 2O.43 0.097 2O, 12

О,09в 18,31 ОДОЗ 17,25 0,053 9,22 0,067 9,81 0,048 5,34 О,О45 4,21 . 0,О45 4,18 0,О47 4,32 0,О46 4,28 О,О 44 4,О8 O,Q43 4,О8O, 09c 18.31 ODOZ 17.25 0.053 9.22 0.067 9.81 0.048 5.34 O, O45 4.21. 0, O45 4.18 0, O47 4.32 0, O46 4.28 O, O 44 4, O8 O, Q43 4, O8

80 0,137 31,4780 0.137 31.47

О,09119,98Oh, 09119.98

0,0526,980.0526.98

0,0476,610.0476.61

О,0486,620486.62

О,О466,34Oh, O466,34

9О 0,098 18,349O 0.098 18.34

Claims

LUBRICANT COMPOSITION containing base oil, phthalic acid ester and additives, characterized in that, in order to improve the load, antifriction and antiwear properties of the compositions, it contains as additives

2-thiazolylazo-r-naphthol and bis— (2 — thiazole-ilazo-p-naphtholate) cobalt in the following ratio of components ^ wt.%: ~

0.05-0.3

20-30

2-thiazolylazo-r-naphthol Bis- (2-thiazole ilazo-β-naphtholate) cobalt Phthalic acid ester

Base oil

Up to 100 •>

\ ··.

2 and introduced to improve the lubricating properties of the composition.

Bis (thiazolylazo- / £ -naphtholate) cobalt (complex) has the formula

1 1027187