SU1023070A1 - Plugging composition - Google Patents
Plugging composition Download PDFInfo
- Publication number
- SU1023070A1 SU1023070A1 SU813332358A SU3332358A SU1023070A1 SU 1023070 A1 SU1023070 A1 SU 1023070A1 SU 813332358 A SU813332358 A SU 813332358A SU 3332358 A SU3332358 A SU 3332358A SU 1023070 A1 SU1023070 A1 SU 1023070A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- solution
- sodium silicate
- weight
- water
- cement slurry
- Prior art date
Abstract
ТАМПОНАЖНЫЙ РАСТВОР, включающий силикат натри и воду, отличающийс тем, что, с целью увеличени проникак цей способности , он дополнителыю содержит борную кислоту при с |юдуюшем соотношении компонентов , мас.ч.: Силикат натри 42-324 Борна кислота13 25 Вода754-849 (ЛSLOTTED SOLUTION, including sodium silicate and water, characterized in that, in order to increase penetration ability, it additionally contains boric acid at a ratio of components, parts by weight: Sodium silicate 42-324 Boric acid13 25 Water 754-849 ( L
Description
toto
со о Изобретение относитс к строительс-гву и может быть использовано, например, при создании противофильтрационных завес в осиовании гидротехнических сооружений. Известен тампонажный раствор, включающий раствор силиката натри и щавелевую кислоту JL . Недостатком этого раствора вл етс трудность регулировани времени геле- образовани , что требует высокой гочно сти дозировки компонентов. Известен также тампонажный раствор, включающий раствор силиката натри , дополнительно содержащий алюминат нат ри 2 . Недостатком данного раствора вл етс его низка проникающа способнтозть вследствие высокой в зкости, равной 3,5 4 сП. Цель изобретени - увеличение проникающей способности тампсжажного раст вора. Цель достигаетс тем. что тампонаж- ный раствор, включающий силикат натри и воду, дополнительно содержит борную кислоту при следующем соотношении компонентов , вес.ч.: 42-324 Силикат натри 13-25 кислота 754-949 Вода Пример 1 приготовлени тампонажного раствора: /врем гелеобразовани 14 мин, юэ кость раствора 2,6 сП, температура Готов т раствор силиката натри плотч ностью 1,19 г/см. Отдельно гото;ё т 4% ..«ый раствор борной кислоты в силикате натри плотностью 1,01 г/см. Концентраци в 4% прин та как максимум растворимости. При меньшей концентрации не получаетс плавное регулирование времени гелеобразовани , так как приходитс вводить слишком большое количество воаы. Если примен ть раствор борной кислоты в силикате натри не 1,01, а 1,О2 г/см, то сам отвераитель через короткое врем дает гель. Дл получени 1 л тампонажного раствора смещивают 255 вес.ч. сш1икат натрид (в расчете на плотность 1,38 г/см ), , 25,0 вес.ч. борной кислоты, 796 вес.ч.воды . Пример 2 , Услови приготовлени тампонажного раствора: врем гелеобразовани 24О мин, в зкость раствора 2,6 сП, температура 2О°С. Готов т раствор силиката натри плотностью 1,19 г/см. Отдельно готов т 4%ный раствор бориой кислоты в силикате натри плотностью 1,О1 г/см. Дл получени 1 л тампонажного раствора смешивают 324 вес.ч. силиката натри , 21 вес.ч. бо{жой кислоты и 754 вес.ч. воды, П р и м е р 3 . Услови приготовлени тампонажного раствора: врем гелеобразовани 8 мин, в зкость раствора 1,3 сП, температура , Готов т раствор силиката натри плотностью 1,03 г/см % Отдельно готов т 4%-«ый раствор борной кислоты в силикате натри с плотностью 1,01 г/см. Дл получени 1 л тампонажного раствора смешивают 42 с.ч. силиката натри , 20 вес.ч. борной кислоты и 949 вес.ч. воды, Пр и м е р 4 , Услови приготовлени тампонажного раствора: врем гелеобразовани 24О мин, в зкость раствоРа 1.3 сП, температура 20®С. , Дл получени 1 л тампонажного растiiE« pa смешивают 56 вес.ч, силиката нат. ри , 13 вес.ч. бо{щой кислоты и 926 вес.ч. воды. Результаты исследовани составов данного тампонажного раствора приведены в таблице.The invention relates to construction and can be used, for example, when creating impervious curtains in the direction of hydraulic structures. Known cement slurry, including a solution of sodium silicate and oxalic acid JL. The disadvantage of this solution is the difficulty of controlling the time of gelation, which requires high dosage of the components. A cement slurry solution is also known, which includes a solution of sodium silicate, additionally containing sodium aluminate 2. The disadvantage of this solution is its low permeability due to a high viscosity of 3.5 to 4 cP. The purpose of the invention is to increase the penetrating ability of a thumping plant. The goal is achieved by those. that the cement slurry, including sodium silicate and water, additionally contains boric acid in the following ratio of components, parts by weight: 42-324 Sodium silicate 13-25 acid 754-949 Water Example 1 preparation of cement slurry: / gelation time 14 min , bone of a solution of 2.6 cP, temperature Preparing a solution of sodium silicate with a density of 1.19 g / cm. Separately, a 4% .. solution of boric acid in sodium silicate with a density of 1.01 g / cm. Concentration in 4% is taken as maximum solubility. At a lower concentration, smooth regulation of the gelation time is not obtained, since too much voi must be injected. If you use a solution of boric acid in sodium silicate, not 1.01, but 1, O2 g / cm, then the extractor itself will give a gel after a short time. To obtain 1 liter of cement slurry, 255 parts by weight are shifted. nitrate sodium (based on a density of 1.38 g / cm), 25.0 parts by weight boric acid, 796 parts by weight of water. Example 2, Conditions for preparing a cement slurry: gelation time 24 O min., Solution viscosity 2.6 cP, temperature 2 O ° C. A solution of sodium silicate with a density of 1.19 g / cm is prepared. Separately, a 4% solution of boric acid in sodium silicate with a density of 1, O1 g / cm is prepared. To obtain 1 liter of cement slurry, 324 parts by weight are mixed. sodium silicate, 21 weight.h. bo {zhid acid and 754 wt.h. water, EXAMPLE 3. Conditions for preparing the cement slurry: gelation time 8 minutes, solution viscosity 1.3 cP, temperature, Prepare a solution of sodium silicate with a density of 1.03 g / cm% Separately prepare 4% - boron acid solution in sodium silicate with a density of 1 , 01 g / cm. To obtain 1 liter of cement slurry, 42 centimeters are mixed. sodium silicate, 20 weight.h. boric acid and 949 weight.h. water, Ex. 4, Conditions for the preparation of the cement slurry: gelation time 24 O min., solution viscosity 1.3 cP, temperature 20 ° C. , To obtain 1 liter of cementing > pa, they mix 56 parts by weight, silicate of nat. ri, 13 weight.h. more than hydrochloric acid and 926 weight parts. water. The results of the study of the compositions of this cement slurry are given in the table.
2525
796 796
255 255
21 754 324 85421 754 324 854
14 19614 196
1414
77
2,6 2.6
ОABOUT
240240
220 2,6 220 2.6
21 2,121 2.1
99
Из результатов исслесюёани видно, что в зкость данного тампонажнотч) раст вора равна 1,3-2,6 сП что существенно ниже в зкости тампонажноГЬодолжение таблицыFrom the results of the survey, it can be seen that the viscosity of this tamponazhnotch) rastor is equal to 1.3-2.6 cP, which is significantly lower than the viscosity of the plugging table.
го раствора, вз того за прототип (3-4сП), т. е. повышаегс проникающа способность данного тампо нажного раствора.solution, taken as a prototype (3-4cP), i.e., the penetrating power of this tampon solution is increased.
Claims (1)