SG189806A1

SG189806A1 - An apparatus and method for size reduction

Info

Publication number: SG189806A1
Application number: SG2013030275A
Authority: SG
Inventors: Hitchcock Paul; Pearce Wayne; Pilgrim Mark
Original assignee: Musse Inc
Priority date: 2009-10-20
Filing date: 2009-10-20
Publication date: 2013-05-31

Abstract

55AbstractAn apparatus and method for size reductionThe present invention provides a method for size reduction of a material comprising the steps of: feeding material through a feed assembly into a5 cyclone chamber, the cyclone chamber having an elongate cylindrical conduit having a frusto-conical section; adding at least one viscosity modifying agent into the cyclone chamber; and providing a cyclonic fluid stream within the cyclone chamber. The present invention also provides an apparatus for size reduction of a material. The apparatus comprises: a cyclone chamber (4) having10 an elongate cylindrical conduit having a frusto-conical section (4a); a device (5) for creating a cyclonic fluid stream within the cyclone chamber (4), such that the frusto-conical section (4a) of the cyclone chamber (4) terminates in an opening forming the inlet to the device; an air inlet tube (3) in fluid connection with the cyclone chamber (4) at the opposite end of the frusto-conical section (4a); and a15 feed assembly for feeding material into the cyclone chamber (4). (Figure 1)

Description

An apparatus and method for size reduction

Field of the invention

The present invention provides an apparatus and method for reducing the size of a material. The apparatus and method may also reduce moisture content of a material.

Background of the invention

There are several apparatus described for processing a material without mechanical action in order to reduce the particle size of the material. Most of these apparatus consist of an inlet tube, a cyclone chamber with an impelier fan for pulling air and the material to be processed through the system. The high pressure air stream is used to create a vortex in the cyclone chamber which entraps the material and holds it in a cyclonic suspension in which the material is fractionated.

An example of such an apparatus is described in WO 98/35756. WO 98/35756 describes a machine with a cyclonic chamber of adjustable length to tune the apparatus to achieve a standing wave at a particular harmonic frequency generated by a fan. It is stated at WO 00/24518 that the process of WO 98/35756 has a number of difficulties, the main one being that the physical processing which occurs in the cyclone chamber does not degrade all the material into the required size and as a result, undegraded material exits the chamber and hits the impeller. The force with which this occurs causes the fan to last no more than a few hours, even when constructed from the strongest of materials known to man.

Summary of the invention

The present invention seeks to address the problems above, and in particular provides improved methods and apparatus for reducing the size of a material.

The present invention also provides a method and apparatus for removing moisture from a material.

According to one aspect, the present invention provides a method for size reduction of a material, the method comprising the steps of: - feeding material through a feed assembly into a cyclone chamber, the cyclone chamber having an elongate cylindrical conduit having a frusto- conical section; - adding at least one viscosity modifying agent into the cyclone chamber; and - providing a cyclonic fluid stream within the cyclone chamber.

According to a particular aspect, the cyclonic fluid stream within the cyclone chamber may have a kinematic viscosity (v) of 1x10° m%s <v < 1x10™ ms.

According to a particular aspect, the viscosity modifying agent may be a kinematic viscosity modifying agent.

The step of adding at least one viscosity modifying agent into the cyclone chamber may be carried out before or after the step of feeding material into the cyclone chamber. Any suitable viscosity modifying agent may be added. For example, the viscosity modifying agent may be selected from the group consisting of: moist air; water, warm air; cold air; oxygen; nitrogen; argon; carbon dioxide; water-based surfactants; calcium sulphate; glass; boric oxide; calcium fluoride; aluminium oxide; and a combination thereof.

Any suitable amount of viscosity modifying agent may be added into the cyclone chamber. In particular, the viscosity modifying agent is added into the cyclone chamber such that the kinematic viscosity (v) of the cyclonic fluid stream within the cyclone chamber is 1x10° m%s <v < 1x10" m%s.

According to a particular aspect, the cyclonic fluid stream is provided by a device, the device being located in an opening formed at the termination of the frusto-conical section of the cyclone chamber.

The method may further comprise the step of collecting material whose size has been reduced. In particular, the average particle size of the material whose size has been reduced may be 5 nm —- 150 um.

According to a second aspect, the present invention provides an apparatus for size reduction of material according to a method of a first aspect of the present invention. The apparatus may comprise: - a cyclone chamber having an elongate cylindrical conduit having a frusto-conical section; - a device for creating a cyclonic fluid stream within the cyclone chamber, such that the frusto-conical section of the cyclone chamber terminates in an opening forming the inlet to the device; - an air inlet tube in fluid connection with the cyclone chamber at the opposite end of the frusto-conical section; and - afeed assembly for feeding material into the cyclone chamber.

The feed assembly may also be for feeding at least one viscosity modifying agent.

The apparatus may further comprise a computer control system for controlling the amount of material, air, and/or viscosity modifying agent fed through the feed assembly into the cyclone chamber. The viscosity modifying agent may be a kinematic viscosity modifying agent. In particular, the computer control system is capable of monitoring the kinematic viscosity (v) of the cyclonic fluid stream within the cyclone chamber and accordingly, adjusts the amount of material, air and/or viscosity modifying agent fed through the feed assembly into the cyclone chamber.

A third aspect of the present invention is a method for size reduction of a material, the method comprising the steps of: — feeding material through a feed assembly into a cyclone chamber, the cyclone chamber having an elongate cylindrical conduit having a frusto- conical section; and — providing a cyclonic fluid stream within the cyclone chamber, wherein the cyclonic fluid stream has a kinematic viscosity (v) of 1x10° m%s < v<1x10" m?s.

The method may further comprise the step of adding at least one viscosity modifying agent into the cyclone chamber. The at least one viscosity modifying agent may be a kinematic viscosity modifying agent. In particular, the step of adding at least one viscosity modifying agent into the cyclone chamber may be carried out before or after the step of feeding material into the cyclone chamber.

Any suitable viscosity modifying agent may be added. For example, the viscosity modifying agent may be selected from the group consisting of: moist air; water; warm air; cold air; oxygen; nitrogen; argon; carbon dioxide; water- based surfactants; calcium sulphate; glass; boric oxide; calcium fluoride; aluminium oxide; and a combination thereof. Other examples of viscosity modifying agents include, but are not limited to, helium, sulphur dioxide, castor oil, corn starch solution, glycerine and tar. The corn starch solution may be 22

Baume corn starch solution, 24 Baume corn starch solution or 26 Baume corn starch solution.

Any suitable amount of viscosity modifying agent may be added into the cyclone chamber. According to a particular aspect, the viscosity modifying agent may be added into the cyclone chamber such that the kinematic viscosity (v) of the cyclonic fluid stream within the cyclone chamber is 1x10° m%s < v < 1x10” m?/s. In particular, the step of adding at least one viscosity modifying agent is carried out when the kinematic viscosity (v) of the cyclonic fluid stream within 5 the cyclone chamber is outside the range of 1x10° m%s <v < 1x10" ms.

The method may further comprise the step of collecting material whose size has been reduced. In particular, the average particle size of the material whose size has been reduced may be 5 nm — 150 um. Even more in particular, the average particle size of the material whose size has been reduced may be 8 nm —~ 100 um, 15 nm — 50 pm, 25 nm — 25 um, 50 nm — 10 um, 75 nm — 5 um, 100 nm — 800 nm, 150 nm = 700 nm, 200 nm — 600 nm, 300 nm — 500 nm, 400 nm — 450 nm.

Another aspect of the present invention is an apparatus for size reduction of a material according to a method of a third aspect of the present invention, the apparatus comprising: - a cyclone chamber having an elongate cylindrical conduit having a frusto-conical section; - a device for creating a cyclonic fluid stream within the cyclone chamber, such that the frusto-conical section of the cyclone chamber terminates in an opening forming the inlet to the device; - an air inlet tube in fluid connection with the cyclone chamber at the opposite end of the frusto-conical section; - a feed assembly for feeding material into the cyclone chamber; and

- a computer control system for monitoring the kinematic viscosity (v) of the cyclonic fluid stream in the cyclone chamber.

According to a particular aspect, the feed assembly may also be for feeding at least one viscosity modifying agent into the cyclone chamber. The at least one viscosity modifying agent may be a kinematic viscosity modifying agent. In particular, the computer control system is capable of monitoring the kinematic viscosity (v) of the cyclonic fluid stream within the cyclone chamber and accordingly, adjusts the amount of material, air and/or viscosity modifying agent fed through the feed assembly into the cyclone chamber.

Another aspect of the present invention is an apparatus for size reduction of a material comprising: - a cyclone chamber having an elongate cylindrical conduit having a frusto-conical section; - a device for creating a cyclonic fluid stream within the cyclone chamber, such that the frusto-conical section of the cyclone chamber terminates in an opening forming the inlet to the device; - an air inlet tube in fluid connection with the cyclone chamber at the opposite end of the frusto-conical section; and - afeed assembly for feeding material into the cyclone chamber, wherein the ratio of diameter of the feed assembly to diameter of the air inlet tube is 0.3-0.5.

The apparatus may further comprise a computer control system for controlling feeding material and fluid stream within the cyclone chamber.

According to another aspect, the present invention provides a method for size reduction of a material, the method comprising the steps of:

- feeding material through a feed assembly into a cyclone chamber, the cyclone chamber having an elongate cylindrical conduit having a frusto- conical section; - providing a cyclonic fluid stream within the cyclone chamber; and - controlling the ratio of the volume of material fed into the feed assembly to the volume of air within the cyclone chamber, wherein the ratio is < 40%.

Brief description of the figures

Figure 1 shows a perspective view of an apparatus according to one embodiment of the present invention;

Figure 2 shows a plot of kinematic viscosity against Reynolds number for a head loss of 87 m.

Figure 3 shows a plot of head loss against kinematic viscosity for different values of pipe roughness (& ).

Figure 4 shows the Malvern particle size distribution of a sample of brown coal whose size is reduced according to the apparatus of one aspect of the present invention (sample A);

Figure 5 shows the Malvern particle size distribution of a sample of brown coal whose size is reduced according to milling (sample B); and

Figure 6 shows the rate of weight loss against temperature for each of samples

A and B.

Detailed description of the invention

Bibliographic references mentioned in the present specification are for convenience listed in the form of a list of references and added at the end of the examples. The whole content of such bibliographic references is herein incorporated by reference.

A number of equipment designs and operating mechanisms are reported in the prior art, examples of which are provided above. In general, such equipment consists of a conical cyclone chamber with an impeller fan for pulling air and the material to be processed through the system. The air stream is used to create a vortex in a cyclone chamber which entraps the material, holding it in a cyclonic suspension in which it is processed to some degree. During processing, the particle size of the material may be reduced.

The fluid dynamics of a vortex-based material processing system is very cemplex and varies continuously throughout the process cycle. Complications may arise due to the fact that the particles of the material fed into the processing system have inertia and behave differently to the rest of the fluid within the processing system, predominantly air and water vapour, under turbulent flow conditions.

The continuous change in size and concentration of the particles of the material whose size is to be reduced and which are suspended within the fluid, along with concomitant changes in the water content within the processing system, result in a dynamic situation in which particles are forced in and out of the effective processing zone. In particular, when the material to be processed within the processing system is added to the airstream within the processing system, the fluid dynamics of the system changes dramatically and the

Reynolds number changes. In order for the material to be effectively processed within the processing system, the flow conditions need to be optimised to ensure that particles are subjected to the shear forces of the vortex for as long as possible.

The Reynolds number for a fluid flow in a pipe or tube is a dimensionless number which provides the ratio of inertia forces to viscous forces. Generally, a flow with a large Reynolds number indicates turbulent flow, while a small

Reynolds number is indicative of a flow in which the inertia forces are small compared to the viscous forces and are characteristically laminar flows. For the purposes of the present invention, the Reynolds number may be generally defined as:

Re=YL_pVD vA u where

V is the mean fluid velocity of the fluid flow through the pipe (m/s);

D is the diameter of the pipe (m); u is the dynamic viscosity of the fluid (Pa.s or N.s/m?);

Vv is the kinematic viscosity of the fluid (i.e. v = 2 (m?/s); 0 p is the density of the fluid (kg/m®);

Q is the volumetric flow rate of the fluid within the pipe (m*/s); and

A is the cross-sectional area of the pipe (m?).

It would be known to a person skilled in the art that a Reynolds number of less than 2300 is indicative of laminar flow, a Reynolds number of between 2300 and 4000 is indicative of transient flow and a Reynolds number of greater than 4000 is indicative of turbulent flow.

Therefore, better control over the Reynolds number of the flow is desired during the processing of the material in the processing system. According to a first aspect of the present invention, there is provided a method for size reduction of a material, the method comprising the steps of: - feeding material through a feed assembly into a cyclone chamber, the cyclone chamber having an elongate cylindrical conduit having a frusto- conical section; - adding at least one viscosity modifying agent into the cyclone chamber; and - providing a cyclonic fluid stream within the cyclone chamber.

Viscosity is a fluid’s internal resistance to flow. The higher the viscosity of a fluid, the more resistant the fluid is to flow. Conversely, the lower the viscosity of a fluid, the lower resistant the fluid is to flow. For the purposes of the present invention, a viscosity modifying agent is defined as an agent which when added into a system, is capable of changing the viscosity of the fluid flow within the system. In particular, the viscosity modifying agent may be capable of changing the kinematic viscosity of the fluid flow within the system. The kinematic viscosity of the fluid flow is the ratio of dynamic viscosity of the fluid flow and density of the fluid.

The viscosity modifying agent may be in the solid, liquid or gaseous state. The viscosity modifying agent may be a kinematic viscosity modifying agent. The term “viscosity modifying agent” encompasses flow promoters. Examples of viscosity modifying agents and flow promoters include, but are not limited to, moist air; water; warm air; cold air; oxygen; nitrogen; argon; carbon dioxide; water-based surfactants; calcium sulphate; glass; boric oxide; calcium fluoride; aluminium oxide; or a combination thereof. Other examples of viscosity modifying agents include, but are not limited to, helium, sulphur dioxide, castor oil, corn starch solution, glycerine and tar. The corn starch solution may be 22

Baume corn starch solution, 24 Baume corn starch solution or 26 Baume corn starch solution. For the purposes of the present invention, moist air is defined as air with a higher moisture content compared to ambient air. For the purposes of the present invention, warm air is defined as air having a temperature higher than the temperature of ambient air. For the purposes of the present invention, cold air is defined as air having a temperature lower than the temperature of ambient air.

The step of adding at least one viscosity modifying agent into the cyclone chamber may be carried out before or after the step of feeding material through a feed assembly into the cyclone chamber. The step of adding at least one viscosity modifying agent into the cyclone chamber may be carried out after the step of providing a cyclonic fluid stream within the cyclone chamber. The step of adding at least one viscosity modifying agent into the cyclone chamber may be repeated more than once. In particular, the step of adding at least one viscosity modifying agent may be repeated during the method for size reduction of the material fed through the feed assembly into the cyclone chamber.

According to a particular aspect, the cyclonic fluid stream within the cyclone chamber may have a kinematic viscosity (v) of 1x10® m%s <v < 1x10" m?s.

The cyclonic fluid stream may comprise the material fed into the cyclone chamber through the feed assembly. Accordingly, reference fo the cyclonic fluid stream having a particular kinematic viscosity may be a measure of the kinematic viscosity of the air stream comprising the material within the cyclone chamber. When the cyclonic fluid stream within the cyclone chamber has a kinematic viscosity (v) of 1x10° m¥s < v < 1x10" m?%s, flow conditions are optimised and the size of the material may be reduced efficiently. However, when the material whose size is to be reduced is added into the cyclone chamber, the fluid dynamics may change and consequently, the kinematic viscosity (v) of the cyclonic fluid stream may change.

Accordingly, the kinematic viscosity (v) of the cyclonic fluid stream may be modified by addition of at least one viscosity modifying agent. For example, when at least one viscosity modifying agent is added, the kinematic viscosity (v) of the cyclonic fluid stream within the cyclone chamber may change such that the kinematic viscosity (v) is 1x10° m%s <v < 1x10" m%s.

According to a particular aspect, the cyclonic fluid stream within the cyclone chamber may have a Reynolds number of 4x10° — 1x10°.

The addition of the at least one viscosity modifying agent may be a controlled addition of the at least one viscosity modifying agent. The addition of the at least one viscosity modifying agent may result in better control over the kinematic viscosity (v) of the cyclonic fluid stream within the cyclone chamber, thus improving the flow properties, stability and sustainability of the cyclonic fluid stream within the cyclone chamber. Any suitable amount of viscosity modifying agent may be added. In particular, the amount of viscosity modifying agent added may be dependent on the kinematic viscosity (v). Even more in particular, the amount of the at least one viscosity modifying agent added may be dependent on the amount required to bring the kinematic viscosity (v) of the cyclonic fluid stream to be 1x10° m%s <v < 1x10" m%s. The amount of the at least one viscosity modifying agent added may be dependent on the amount required to bring the Reynolds number of the cyclonic fluid stream to be 4x10° — 1x10°,

According to a particular aspect, the amount of viscosity modifying agent added may be dependent on the material whose size is to be reduced. For example, if the material is very large and/or very moist, the amount of viscosity modifying agent added into the cyclone chamber is increased. The addition of the viscosity modifying agent may enhance the processing of the material.

Any suitable viscosity modifying agent may be used for the purposes of the present invention. For example, the viscosity modifying agent may be selected from the group consisting of: moist air; water; warm air; cold air; oxygen; nitrogen; argon; carbon dioxide; water-based surfactants; calcium sulphate; glass; boric oxide; caicium fluoride; aluminium oxide; and a combination thereof.

In particular, the viscosity modifying agent is water and/or moist air. Other examples of viscosity modifying agents include, but are not limited to, helium, sulphur dioxide, castor oil, corn starch solution, glycerine and tar. The corn starch solution may be 22 Baume corn starch solution, 24 Baume corn starch solution or 26 Baume corn starch solution.

According to a particular aspect, the material whose size is to be reduced may also be used after processing as a co-additive with at least one viscosity modifying agent. In particular, material whose size has already been reduced may be added together with the at least one viscosity modifying agent. For example, if brown coal has been processed and reduced to a size of 5 nm — 100 um, then some of this material may be added when raw coal is being processed to alter the viscosity.

The cyclonic fluid stream within the cyclone chamber is provided by a device.

Cyclonic fluid stream according to the present invention refers to a cyclone created in a stream of fluid passing through a conduit, preferably of circular cross-section. In a cyclonic fluid stream, the centripetal forces created by the motion of the fluid. stream pull any particulate material entrained in the fluid stream away from the walls of the conduit and towards its central region. If a wide range of sonic frequencies are created within the conduit, a pattern of powerful vortices are created in the fluid stream. Energies are released by conversion of the potential energy to kinetic energy due to the stresses created within the cyclone which causes a minute explosion. The vortices of the cyclone take the form of implosions which are capable of breaking the material up further into smaller particles.

The vortices created in the cyclonic fluid stream carry further harmonic frequencies generated by the specially designed apparatus. This sets up a pulse from the standing wave configuration within the system, and this causes pockets of fluid within the standing wave to achieve a velocity beyond the sonic range. This can be tuned for a particular type of material which enhances the ability of the vortices created to break up very hard and soft materials such as stone and to reduce the moisture content of the materials.

The device used in the step of providing a cyclonic fluid stream within the cyclone chamber may be any suitable device which is capable of providing a cyclonic fluid stream. According to a particular aspect, the device may be located in an opening formed at the termination of the frusto-conical section of the cyclone chamber. An example of a device capable of providing a cyclonic fluid stream includes a fan. it would be obvious to a person skilled in the art that other devices which are capable of providing a cyclonic fluid stream are also within the scope of the present invention.

According to a particular aspect, the device may be an impellor fan. in particular, the impellor fan may comprise a plurality of radially extending vanes and a hub such that each of the plurality of vanes is equispaced about the hub. The impellor fan may further comprise an interrupter located within the hub for deflecting the fluid stream in front of the hub.

According to a particular aspect, the ratio of the volume of material fed into the feed assembly to the volume of air within the cyclone chamber may be < 40%. If the volume of the material fed into the feed assembly exceeds 40% of the volume of air within the cyclone chamber, the vortex created within the cyclonic fluid stream may collapse and lose its processing capacity.

The method may further comprise the step of collecting material whose size has been reduced. The average particle size of the material whose size has been reduced may be 5 nm — 150 um. In particular, the average particle size of the material whose size has been reduced may be 8 nm — 100 um, 15 nm — 50 um, 25 nm — 25 um, 30 nm — 20 um, 50 nm — 10 um, 75 nm — 5 um, 100 nm — 800 nm, 150 nm — 700 nm, 200 nm — 600 nm, 300 nm — 500 nm, 400 nm — 450 nm.

Even more in particular, the average particle size of the material whose size has been reduced is 20-100 um. A skilled person would understand that the average particle size is dependent on the application in which the material whose size has been reduced is going to be used and the end use of the material whose size has been reduced. For example, for coal, the average particle size of coal after the method for size reduction of the present invention may be 50 — 100 um. For zinc oxide for use in the preparation of cosmetics, the average particle size of zinc oxide after the method for size reduction of the present invention may be 20 — 40 nm.

For the purposes of the present invention, average particle size of a material refers to the average particie size of a material on a mass basis. The particle size of a material may be defined by its largest dimension. Any standard method suitable for determining the particle size may be used. For example, the

Mastersizer 2000 particle size analyzer (Malvern Instruments Limited) may be used for determining the particle size. The particle size distribution may be determined by any suitable method. For example, the method as described in

ASTM C136 or ASTM C117 may be used to determine the particle size distribution of fine and coarse aggregates by sieving. For example, a bulk sample comprising material whose size has been reduced is sieved through a set of sieves, each sieve ranging in size. The sieves may be standard sieves.

The bulk sampie is sieved through the stack of sieves to determine the particle size distribution by measuring the weight of the material remaining on each sieve.

A second aspect of the present invention is an apparatus for size reduction of a material according to the method described above. The apparatus comprises:

- a cyclone chamber having an elongate cylindrical conduit having a frusto-conical section; - a device for creating a cyclonic fluid stream within the cyclone chamber, such that the frusto-conical section of the cyclone chamber terminates in an opening forming the inlet to the device; - an air inlet tube in fluid connection with the cyclone chamber at the opposite end of the frusto-conical section; and - a feed assembly for feeding material into the cyclone chamber.

The device for creating a cyclonic fluid stream within the cyclone chamber may be any suitable device. An example of a device for creating a cyclonic fluid stream includes a fan.

According to a particular aspect, the device may be an impellor fan. In particular, the impellor fan may comprise a plurality of radially extending vanes and a hub such that each of the plurality of vanes is equispaced about the hub. The impellor fan may further comprise an interrupter located within the hub for deflecting the cyclonic fluid stream in front of the hub.

The apparatus may further comprise a computer control system for controlling the amount of feeding material fed through the feed assembly into the cyclone chamber. The computer control system may also control the amount of fluid within the cyclone chamber. The computer control system may also control the amount of the at least one viscosity modifying agent added into the cyclone chamber. In particular, the computer control system is capable of monitoring the head loss and cyclonic air (fluid) velocity which are a direct measure of the kinematic viscosity of the material being fed into the cyclone chamber through the feed assembly for any particular system geometry.

As mentioned above, the addition of the at least one viscosity modifying agent may be a controlled addition of the at least one viscosity modifying agent. The addition of the at least one viscosity modifying agent may be controlled by a computer control system. For example, the computer control system may detect a change in the kinematic viscosity (v) of the cyclonic fluid stream within the cyclone chamber such that the kinematic viscosity (v) is outside a pre- determined range. The computer control system may detect a change in the

Reynolds number of the cyclonic fluid stream within the cyclone chamber such that the Reynolds number is outside a pre-determined range. The computer control system will therefore prompt the controlled addition of at least one viscosity modifying agent in order to return the kinematic viscosity (v) to within its pre-determined range. Therefore, the computer control system may aid in improving the flow properties, stability and sustainability of the cyclonic fluid stream within the cyclone chamber.

The different parts of the apparatus are described in more detail below.

According to third aspect, the present invention provides a method for size reduction of a material, the method comprising the steps of: - feeding material through a feed assembly into a cyclone chamber, the cyclone chamber having an elongate cylindrical conduit having a frusto- conical section; and - providing a cyclonic fluid stream within the cyclone chamber, wherein the cyclonic fluid stream has a kinematic viscosity (v) of 1x107® ms < v < 1x10" m%s.

According to a particular aspect, the Reynolds number of the cyclonic fluid stream may be 4x10° — 1x10%.

The method may further comprise the step of adding at least one viscosity modifying agent into the cyclone chamber. Any suitable viscosity modifying agent may be used for the purposes of the present invention, as described above. The step of adding the at least one viscosity modifying agent may be carried out before or after the step of feeding material through a feed assembly into the cyclone chamber. The step of adding at least one viscosity modifying agent into the cyclone chamber may be carried out after the step of providing a cyclonic fluid stream within the cyclone chamber. The step of adding at least one viscosity modifying agent into the cyclone chamber may be repeated more than once. In particular, the step of adding at least one viscosity modifying agent may be repeated during the method for size reduction of the material fed through the feed assembly into the cyclone chamber.

According to a particular aspect, when the cyclonic fluid stream within the cyclone chamber has a kinematic viscosity (v) of 1x10% m%s <v < 1x10" m?s, flow conditions are optimised and the size of the material may be reduced efficiently. However, when the material whose size to be reduced is added into the cyclone chamber, the fluid dynamics may change and consequently, the kinematic viscosity (v) of the cyclonic fluid stream may change.

Accordingly, the kinematic viscosity (v) of the cyclonic fluid stream may be modified by addition of at least one viscosity modifying agent. For example, when at least one viscosity modifying agent is added, the kinematic viscosity (v) of the cyclonic fluid stream within the cyclone chamber may change such that the kinematic viscosity (v) is 1x10% ms <v < 1x10” ms.

The addition of the at least one viscosity modifying agent may be a controlled addition of the at least one viscosity modifying agent. The addition of the at least one viscosity modifying agent may result in better control of the kinematic viscosity (v) of the cyclonic fluid stream within the cyclone chamber, thus improving the flow properties, stability and sustainability of the cyclonic fluid stream within the cyclone chamber. Any suitable amount of viscosity modifying agent may be added. In particular, the amount of viscosity modifying agent added may be dependent on the kinematic viscosity (v). Even more in particular, the amount of the at least one viscosity modifying agent added may be dependent on the amount required to bring the kinematic viscosity (v) of the cyclonic fluid stream to be 1x10® m%s < v < 1x10" m?%s. According to a particular aspect, the amount of viscosity modifying agent added may be dependent on the material whose size is to be reduced. For example, if the material is very large and/or very moist, the amount of viscosity modifying agent added into the cyclone chamber is increased. The addition of the viscosity modifying agent may enhance the processing of the material.

According to a particular aspect, the amount of the at least one viscosity modifying agent added may be dependent on the amount required to bring the

Reynolds number of the cyclonic fluid stream to be 4x10° — 1x108.

The device used in the step of providing a cyclonic fluid stream within the cyclone chamber may be any suitable device which is capable of providing a cyclonic fluid stream. According to a particular aspect, the device may be located in an opening formed at the termination of the frusto-conical section of the cyclone chamber. Examples of devices capable of providing a cyclonic fluid stream are provided above.

According to a particular aspect, the ratio of the volume of material fed into the feed assembly to the volume of air within the cyclone chamber may be < 40%. If the volume of the material fed into the feed assembly exceeds 40% of the volume of air within the cyclone chamber, the vortex created within the cyclonic air stream may collapse and lose its processing capacity.

The method may further comprise the step of collecting material whose size has been reduced. The average particle size of the material whose size has been reduced may be 5 nm — 150 um. In particular, the average particle size of the material whose size has been reduced may be 8 nm — 100 um, 15 nm — 50 um, 25 nm ~ 25 um, 30 nm —= 20 um, 50 nm — 10 um, 75 nm — 5 um, 100 nm —- 800 nm, 150 nm - 700 nm, 200 nm — 600 nm, 300 nm — 500 nm, 400 nm — 450 nm.

Even more in particular, the average particle size of the material after the material has undergone size reduction is 20 — 100 um. A skilled person would understand that the average particle size is dependent on the application in which the material whose size has been reduced is going to be used and the end use of the material whose size has been reduced. For example, for coal, the average particle size of coal after the method for size reduction of the present invention may be 50 — 100 um. For zinc oxide for use in the preparation of cosmetics, the average particle size of zinc oxide after the method for size reduction of the present invention may be 20 - 40 nm.

The present invention aiso provides an apparatus for size reduction of a material according to the method of the third aspect of the present invention described above. The apparatus comprises:

- a cyclone chamber having an elongate cylindrical conduit having a frusto-conical section; - a device for creating a cyclonic fluid stream within the cyclone chamber, such that the frusto-conical section of the cyclone chamber terminates in an opening forming the inlet to the device; - an air inlet tube in fluid connection with the cyclone chamber at the opposite end of the frusto-conical section; - a feed assembly for feeding material into the cyclone chamber; and - a computer control system for monitoring the kinematic viscosity (v) of the cyclonic fluid stream in the cyclone chamber.

According to a particular aspect, the computer control system for monitoring the kinematic viscosity (v) of the cyclonic fluid stream in the cyclone chamber is such that the computer control system may detect if the kinematic viscosity (v) of the cyclonic fluid stream is outside a pre-determined range. The pre- determined range may be 1x10° m%s <v < 1x10” m%s. The computer control system may detect if the Reynolds number of the cyclonic fluid stream is outside a pre-determined range.

The computer control system may be capable of monitoring the head loss and cyclonic air (fluid) velocity which are a direct measure of the kinematic viscosity of the material being fed into the cyclone chamber through the feed assembly for any particular system geometry. In particular, when the kinematic viscosity (v) of the cyclonic fluid stream is outside the pre-determined range, the computer control system may prompt the alteration of flow conditions within the cyclone chamber. In particular, the computer control system may cause the addition of at least one viscosity modifying agent in order to return the kinematic viscosity (v) and/or Reynolds number of the cyclonic fluid stream to be within a pre-determined range. Therefore, the computer control system may aid in improving the flow properties, stability and sustainability of the cyclonic fluid stream within the cyclone chamber. The addition of at least one viscosity modifying agent may be as described above.

The different parts of the apparatus are described in more detail below.

A further aspect of the present invention is an apparatus for size reduction of a material comprising: - a cyclone chamber having an elongate cylindrical conduit having a frusto-conical section; - a device for creating a cyclonic fluid stream within the cyclone chamber, such that the frusto-conical section of the cyclone chamber terminates in an opening forming the inlet to the device; - an air inlet tube in fluid connection with the cyclone chamber at the opposite end of the frusto-conical section; and - a feed assembiy for feeding material into the cyclone chamber, wherein the ratio of diameter of the feed assembly to diameter of the air inlet tube is 0.3-0.5.

In particular, the ratio of the diameter of the feed assembly to the diameter of the air inlet tube is 0.5. Such a ratio may provide for a maximum volume of air to volume of material ratio of 60:40. When the material whose size to be reduced is a slurry, the ratio of the diameter of the feed assembly to the diameter of the airinlet tube is 0.35.

The apparatus may further comprise a computer control system for controlling the amount of material fed through the feed assembly into the cyclone chamber and the amount of fluid within the cyclone chamber.

The different parts of the apparatus are described in more detail below.

There is also provided a method for size reduction of a material in the apparatus as described above, the method comprising the step of controlling ratio of the volume of material fed into the feed assembly to the volume of air within the cyclone chamber is < 40%. In particular, the ratio of the volume of material fed into the feed assembly to the volume of air within the cyclone chamber is < 35%, < 30%, <25%, <20%.

According to a particular aspect, the step of controlling the ratio of the volume of material fed into the feed assembly to the volume of air within the cyclone chamber may be carried out by a computer control system. Any suitable computer control system may be used. For example, the computer control system may control the ratio by controlling the amount of material fed through the feed assembly into the cyclone chamber and the amount of air within the cyclone chamber.

The method may further comprise the step of collecting material whose size has been reduced. The average particle size of the material whose size has been reduced may be 5 nm - 150 um. In particular, the average particle size of the material whose size has been reduced may be 8 nm — 100 um, 15 nm - 50 um, 25 nm —- 25 pum, 30 nm — 20 um, 50 nm — 10 um, 75 nm — 5 um, 100 nm — 800 nm, 150 nm — 700 nm, 200 nm — 600 nm, 300 nm ~ 500 nm, 400 nm — 450 nm.

Even more in particular, the average particle size of the material after the material has undergone size reduction is 20 — 100 um. A skilled person would understand that the average particle size is dependent on the application in which the material whose size has been reduced is going to be used and the end use of the material whose size has been reduced. For example, for coal, the average particle size of coal after the method for size reduction of the present invention may be 50 — 100 um. For zinc oxide for use in the preparation of cosmetics, the average particle size of zinc oxide after the method for size reduction of the present invention may be 20 ~ 40 nm.

Another aspect of the present invention is a method for size reduction of a material, the method comprising the steps of: - feeding material through a feed assembly into a cyclone chamber, the cyclone chamber having an elongate cylindrical conduit having a frusto- conical section; - providing a cyclonic fluid stream within the cyclone chamber; and - controlling the ratio of the volume of material fed into the feed assembly to the volume of air within the cyclone chamber, wherein the ratio is < 40%.

In particular, the ratio of the volume of material fed into the feed assembly to the volume of air within the cyclone chamber is < 35%, < 30%, < 25%, < 20%.

The device used in the step of providing a cyclonic fluid stream within the cyclone chamber may be any suitable device which is capable of providing a cyclonic fluid stream. According to a particular aspect, the device may be located in an opening formed at the termination of the frusto-conical section of the cyclone chamber. Examples of devices capable of providing a cyclonic fuid stream are provided above.

Even more in particular, the average particle size of the material after the material has undergone size reduction is 20 — 100 um. A skilled person would understand that the average particle size is dependent on the application in which the material whose size has been reduced is going to be used and the end use of the material whose size has been reduced. For example, for coal, the average particle size of coal after the method for size reduction of the present invention may be 50 — 100 um. For zinc oxide for use in the preparation of cosmetics, the average particle size of zinc oxide after the method for size reduction of the present invention may be 20 — 40 nm.

When the fluid dynamic conditions of the cyclonic fluid stream within the cyclone chamber are optimised in view of the methods according to any aspect of the present invention, a reverse vortex may be created inside the outer vortex within the cyclonic fluid stream such that a sustainable cyclonic fluid stream is produced. The intersection of the outer and inner vortices creates a turbulent boundary layer. The intense disruption caused by the interaction between particles of material within the cyclone chamber in the boundary layer breaks the material into particles of varying sizes. The main vortex spirals in one direction and carries most of the coarser particles and the inner vortex spirals in the opposite direction and carries finer particles.

Further, any water which may be contained in the particles of the material may evaporate rapidly as the particies move to a lower pressure zone. This evaporation may be sufficiently rapid to further break down the particles. As the particles break down, more of the surface of the particle is exposed and this facilitates further evaporation.

The suspended particles of the material do not move in a smooth spiral around the cyclonic fluid stream. In particular, the large and small particles collide with each other and develop opposite electrical charges due to triboelectric processes. The larger particles become positively charged and the smaller particles become negatively charged.

At some point, particularly in areas of low pressure within the cyclone chamber, the oppositely charged particles will come into sufficiently close proximity for the electrostatic field to be of sufficient influence to ionise the air between them.

Depending on the pressure, this may result in either corona or glow discharge plasmas being formed.

At atmospheric pressure, the breakdown voltage in dry air is 30KV/ecm. This is significantly reduced at lower pressures and at higher humidity levels. In addition, because electric field strength is inversely proportional to the radius of particle, the breakdown voltage is lower for smaller particles. Therefore, as the particles continue to reduce in size, the ionisation process becomes more likely and more frequent.

Electrostatic discharges are therefore produced and transmit high frequency radio waves which could be used for monitoring the method of size reduction and for the purposes of feedback control.

An embodiment of the apparatus according to the present invention is shown in

Figure 1. The apparatus 100 comprises an impeller suction fan 5 and a cyclone chamber 4. The cycione chamber 4 is generally cylindrical and is arranged such that its longitudinal axis lies along the axis of rotation of the impeller suction fan 5. The impeller suction fan 5 is rotatably supported within a housing 6. The impeller suction fan 5 creates the rotation and suction of air.

The impeller suction fan 5 is keyed to one end of a drive shaft (not shown) which is supported by a tunnel bearing 9 mounted on the rear of the housing 6.

A drive train 10 is fastened to the other end of the shaft. The drive train 10 provides power to apparatus 100. In operation, the drive train 10 is driven by a variable speed motor, internal combustion engine or any mechanical driver 12.

The impeller suction fan is driven at typical speeds of 90-250 m/s. However, a skilled person would realise that any suitable speed may be used for the purposes of the present invention. In particular, the speed of the impeller suction fan may depend on the kinematic viscosity of the material being processed. The speed of the impeller suction fan may change in response to the degree of comminution of the material. The drive train 10 is secured to a bench 11. Bench 11 may be cushioned.

One end of the cyclone chamber 4 is fitted with an air inlet tube 3 in engagement therewith. The other end of the cyclone chamber 4 terminates in a frusto-conical section 4a which has an opening (not shown).

The cyclone chamber 4 is secured, for example by welding, so that the opening of the housing 6 and the mouth of the frusto-conical section 4a are coincident.

Thus the inlet of the impeller suction fan 5 extends partly into the frusto-conical section 4a of the cyclone chamber 4. In particular, the internal width of the housing 6 would be approximately 5 cm wider than the width of the impeller suction fan 5. :

A feed assembly 2 for receiving the material whose size is to be reduced is mounted on the air inlet tube 3 adjacent an open end 3a thereof and partly extending into the air inlet tube 3. Any suitable feed assembly can be used for the purposes of the present invention. The material to be reduced is fed through the feed assembly 2 subsequently enters the air inlet tube 3. Air and material pass through the air inlet tube 3 before entering the cyclone chamber 4. The air inlet tube 3 is also connected to a stator 1 at the open end 3a of the air inlet tube 3. The stator 1 is an egg-shaped focal point which focuses the tail of the vortex created in the cyclonic fluid stream within the cyclone chamber 4.

The feed assembly 2 regulates the ratio of the volume of material fed through the feed assembly 2 to the volume of fluid within the cycione chamber 4 during the operation of the apparatus 100. This may be controlled by the diameter of the feed assembly 2 in relation to the diameter of the air inlet tube 3.

Apparatus 100 also comprises an exhaust duct 8. Air and material go through the exhaust duct 8 after the air and material have passed through the cyclone chamber 4. The air and material which go through the exhaust duct 8 may be directed to a collection and disbursement area.

The impeller suction fan 5 comprises a plurality of radially extending vanes 5a.

Preferably, the number of vanes 5a is from eight to twelve, depending on the type of material to be granulated. Greater average particle size reduction of the material exiting exhaust duct 8 may be achieved with a higher number of vanes 5a, while drier material exits the exhaust duct with lesser number of vanes 5a.

The vanes 5a may be formed of and further may be coated with a layer of high - abrasion resistant material to protect the vanes 5a against metal contamination as well as to provide a cushion to protect brittle particles such as diamonds which are released from ore such as kimberlite to allow large diamonds which would otherwise be crushed to emerge intact.

Each of the vanes 5a is offset from the radius of the impeller by an angle within 3-10°. The higher the angle, the better suited is apparatus 100 for applications requiring greater moisture reduction of the material fed through the feed assembly 2. A lower angle is better suited for applications requiring greater size reduction of the material fed through the feed assembly 2. The vanes 5a are equispaced about a hub (not shown). The hub receives the vanes 5a and is secured to the drive shaft. Each vane 5a is generally concave, the concavity of each vane 5a facing the direction of rotation of the impeller suction fan 5.

An interrupter 13 may be fitted into a central bore at the front side of the hub facing the inlet of the impeller suction fan 5. The interrupter 13 is a discordant shaped object lock nut which locks the impeller suction fan 5 onto the drive shaft. The interrupter 13 may comprise a disc mounted on a central spine. The spine may be screw-threaded so that the interrupter 13 can be screw-fitted into the central bore of the hub. The interrupter 13 disturbs the stationary fluid directly in front of the hub. The interrupter 13 has a diameter approximately equal to the diameter of the hub. In particular, the centre diameter of the interrupter 13 may be approximately equal to the diameter of the hub.

The orientation and design of the impeller vanes 5a can be further optimised by computer-aided design and can be further adjusted dynamically to compensate for any wear of the vanes. In particular, the degree of curvature of the vanes can be adjusted by computational fluid dynamics analysing wear patterns created by a given product and redesigning the vane to give optimum freedom from abrasion.

The apparatus 100 also comprises a scroll 7 which is a multiple-angled spiral- shaped volute inside the housing which determines the air volume contained and exhausted by apparatus 100 in combination with the air inlet tube 3.

According to a particular embodiment, the housing 6 contains a scroll 7 with a total volume in proportion to the diameter of the impeller suction fan 5, such that for every 300 mm in the diameter of the impeller suction fan 5, the volume of the scroll 7 should be 0.120-0.177 m®. In particular, the volume of the scroll 7 may be 0.150 m® for every 300 mm diameter of the impeller suction fan 5.

The scroll 7 may extend from the inside wall of the exhaust duct 8 to the outside wall of the exhaust duct 8 in a spiral shape to create the total air volume capacity of the apparatus 100.

According to a particular embodiment, the discharge area of the exhaust duct 8 may be approximately 35% of the volume of the scroll 7. The exhaust duct 8 is attached to the housing 6 where the scroll 7 terminates.

The granulation and drying of a material may be further improved by introducing an externally generated frequency to the cyclonic fluid stream by means of a speaker or electrical feed, for example. Typical frequencies may be 25 to 28 Hz, 57.6 Hz, 576 Hz for a fan running at 5760 rpm. Disassociation of water can be enhanced by introduction of a frequency of approximately 42.7 Hz.

Apparatus 100 may also comprise a computer control system (not shown). The computer control system may maintain and/or monitor the operation of the apparatus 100. In particular, the computer control system may maintain and/or monitor the operational constancy when material whose size is to be reduced is fed into the apparatus 100. Even more in particular, the computer control system may monitor the kinematic viscosity (v) and/or the Reynolds number of the cyclonic fluid stream within the cyclone chamber 4 and/or the ratio of the volume of the material fed into the feed assembly to the volume of the fluid within the cyclone chamber 4.

According to a particular embodiment, the length of the air inlet tube 3 is within 200-240% of the diameter of the impeller suction fan 5. Even more in particular,

the length of the air inlet tube 3 is approximately 220% of the diameter of the impeller suction fan 5.

According to another particular embodiment, the width of the air inlet tube 3 is approximately 33% of the diameter of the impeller suction fan 5.

Another particular embodiment provides that the size of the stator 1 may be varied to produce differing processing results of the same input material fed through the feed assembly 2. For example, when a smaller stator 1 is used, the final average particle size of the material passing through the exhaust duct 8 will be larger compared to when a larger stator 1 is used. In particular, the diameter of the stator should not exceed 50% of the diameter of the air inlet tube.

According to a particular embodiment, the length of the cyclone chamber 4 is within 65-85%, 70-80%, 75-78% of the length of the air inlet tube 3. Even more in particular, the length of the cyclone chamber 4 is 70% of the length of the air inlet tube 3.

According to another particular embodiment, the width of the cyclone chamber 4 reduces over its length from the width of the impeller suction fan 5 to the width of the air inlet tube 3.

According to a particular embodiment, the diameter of the impeller suction fan 5 may be three times the width of the air inlet tube 3a. The vanes 5a of the impeller suction fan 5 may be positioned from the hub of the impeller suction fan 5 to a fixing ring at an angle of 45° to the axis of rotation of the impeller suction fan 5. Further, the width of the impeller suction fan 5 may be one third the diameter of the impeller suction fan 5.

The apparatus 100 may be scaled to any size provided the ratio of all components is kept to scale and sufficient power is provided during operation of the apparatus 100.

In operation, the motor 12 is run-up to speed until the optimum conditions are achieved for granulating a particular material by tuning the apparatus to the natural resonance frequency of the material. The drive train 10 and its control are of significant importance. It must provide sufficient power for a cyclonic fluid stream to be formed within the cyclone chamber 4. Motor 12 may also have to increase its power once the material whose size is to be reduced is fed through the feed assembly 2 into the cyclone chamber 4 so that the vortices formed within the cyclonic fluid stream in the cyclone chamber 4 do not collapse.

The types of materials which may granulated by the apparatus according to any aspect of the present invention ranges from metal ores, glass, plastic, coal, lignite (brown coal), petroleum coke, mezotrace, oil shale, drywall, ash, manure, sewage sludge, salt crystal, mineral and ore bearing sand, fertilizers, cement raw materials, black sand, grains such as soybeans, corn, oats, barley, milo and rice.

The apparatus according to any aspect of the present invention can be utilised to reduce the moisture content of numerous materials such as wet clay, paper pulp, brown coal, phosphates, sulphates, fish and bones to produce a fine dry powder. It is aiso useful for drying pigmentation cake which contains up to 50% water. Mining slurries can be dried either in powder form or dewatered sufficiently for chemical treatment for extraction of metals.

The material to be reduced in size is fed into the feed assembly 2 and enters the air inlet tube 3. The material then passes through the air inlet tube 3 and enters the path of the cyclonic fluid stream created by the impeller suction fan 5 within the cyclone chamber 4. The material is fragmented within the cyclone chamber 4 before entering the impeller suction fan 5 due to the tuned harmonics carried by the vortices within the cyclonic fluid stream and is drawn by the cyclonic fluid stream into the inlet of the impeller suction fan 5.

The material then enters the exhaust duct 8 and exits the apparatus 100 to a collection and disbursement area. The size of the exhaust duct 8 can be varied to adjust the fluid flow through the apparatus 100.

Materials which have exited the apparatus 100 through the exhaust duct 8 are sorted according to the average particle size by any suitable method known in the art. Materials having a larger average particle size than desired may be fed back into the apparatus 100 through the feed assembly 2 into cyclone chamber 4 for re-processing.

As described above, a computer control system may be installed. During normal operation, there is virtually no load, particularly if a DC constant torque motor is utilised to drive the impeller suction fan 5. Therefore, sensors can be provided to detect any increase in load, for example due to a large particle hitting the impeller suction fan 5, to activate a cut-off switch and brake.

The sensors may alternatively, detect particularly large particles in transit such as diamonds and perform the same function. Sensors may also be utilised to detect large particles in the exhaust duct 8 and increase the speed of the impeller suction fan 5 to ensure that the material is finely granulated.

The computer control system may also detect changes in kinematic viscosity (v) of the cyclonic fluid stream within the cyclone chamber 4. According to a particular embodiment, if the kinematic viscosity (v) of the cyclonic fluid stream within the cyclone chamber 4 falls outside a pre-determined range, the computer control system may prompt the alteration of flow conditions within the cyclone chamber 4. In particular, the computer control system may cause the addition of at least one viscosity modifying agent into the cyclone chamber 4 in order to return the kinematic viscosity (v) of the cyclonic fluid stream in the cyclone chamber 4 within the pre-determined range. Any suitable viscosity modifying agent may be used for the purposes of the present invention as described above.

The computer control system may also detect changes in the ratio of the volume of material fed through the feed assembly 2 to the volume of the fluid within the cyclone chamber 4. If the ratio exceeds a pre-determined value, the computer control system adjusts the amount of fluid present in the cyclone chamber 4 by altering the speed of the impeller suction fan 5 and/or the amount of material being fed through the feed assembly 2 into the cyclone chamber 4.

In particular, if the volume of material fed through the feed assembly 2 into the cyclone chamber exceeds 40% of the volume of air within the cyclone chamber 4, the vortices within the cyclonic fluid stream in the cyclone chamber 4 may collapse. According to a particular embodiment, the ratio of the volume of material fed through the feed assembly 2 into the cyclone chamber 4 to the volume of air in the cyclone chamber 4 is < 40%.

In the light of this disclosure, modifications of the described embodiment, as well as other embodiments, all within the scope of the appended claims will now become apparent to persons skilled in the art. Arrangement of the different parts of the apparatus according to any aspect of the present invention are similar to the apparatus described in prior art such as in WO 98/35756, US 7,500,830, WO 03/006166, herein incorporated by reference, and the like.

Having now generally described the invention, the same will be more readily understood through reference to the following examples which are provided by way of illustration, and are not intended to be limiting of the present invention.

EXAMPLES

Example 1

The following example exemplifies the determination of a suitable range of kinematic viscosity (v) within which to carry out the method according to any aspect of the present invention.

The Moody Diagram can be represented by the Colebrook White equation: y 126/72

I 12 oe . 2 = Alog[(———) + (——— Equation (1

J slg Z a )] q (1) where: f is the friction factor (often referred to as A in the Moody Diagram where J = 4f); - represents the relative pipe roughness; and

Re represents the Reynolds number.

Equation 1 can be solved iteratively for f for known values of Re and.

Re = ud Equation (2)

Vv where: u is the airflow (fluid) velocity through the pipe; d is the diameter of the pipe v is the kinematic viscosity of the material being processed. v= “ Equation (3) pO where: wis the dynamic viscosity p is the density.

The pressure drop in the pipe is represented by Equation (4) as follows:

AP =h, pg Equation (4) where: ht is the head loss in the pipe and gis the acceleration due to gravity.

The Darcy - Weisbach equation for turbulent flow in a pipe with circular cross- section represents hy as follows: n, = 2 Equation (5) where,

Lis the length of the pipe.

Typical experimental vaiues for some parameters have been used in this analysis. In particular, d = 0.305 m, L = 1.610 m, and u = 166 m/s.

In fluid dynamic analysis of fluid flow through pipes, by is taken as a measure of the roughness of the inside of the pipe. For the purposes of the present analysis, however, it is taken to be a measure of any parameter which alters the level of turbulence during processing such as particle size, shape efc..

A Moody diagram shows two distinct regions of turbulence which can be used for materials processing — transitional turbulence and complete turbulence regions. It can be shown that these two regions have completely different processing characteristics.

Control is exercised over the process of the present invention by changing the airflow (fluid) velocity (i.e. by changing the speed of the impellor) to maintain the optimum pressure drop and therefore, head loss for the properties of the material being processed. These material properties are characterised by the kinematic viscosity, v, of the material which determines its flow characteristics.

It can be seen from Figure 2 that within the transitional turbulence region, i.e. be 1 x 10° which represents a pipe with smooth sides, a material with high v is processed at low Reynolds Numbers and material with low v is processed at high Reynolds Numbers. Figure 2 was obtained by mathematically manipulating equations 1 to 5. Figure 2 shows how the system handles material of different (or changing) kinematic viscosity in the transitional turbulence region.

Controlling the head loss to a particular value, for example, 87m, by changing the airflow (fluid) velocity allows material with a kinematic viscosity range over three orders of magnitude to be processed. Materials of different kinematic viscosities are processed at different values of Reynolds number, depending on the velocity required to maintain the head loss.

In particular, the materials in this example are processed at a head loss of approximately 87 m and the airflow (fluid) velocity, u, is varied between 100 and 200 m/s to maintain this hf value over the kinematic viscosity range of the materials (three orders of magnitude).

For any given material it is possible to change its kinematic viscosity to allow better processing under system operating conditions which may be restricted in terms of fluid flow velocity or pressure drop. Changes in v can be brought about in many ways, such as by adding a viscosity modifying agent as this will aiter the dynamic viscosity, yu, of the material. The density, p, depends on the density of the material being processed, the density of the gas/liquid and also on the size and shape of the material being processed. In particular, the density of the material being processed can be changed by changing the size of the particles/granules and their tendency to agglomerate through the addition of surfactants. Changes in the dynamic viscosity, nu, and the density, p, of the materials being processed will change its kinematic viscosity, v, and its flow characteristics in the regions of turbulence.

Figure 3 represents a processing system operating at an fluid-flow velocity of approximately 163 m/s. Figure 3 shows a plot of head loss against kinematic viscosity for different values of pipe roughness. The pipe roughness takes into account the solids content in the fluid stream and the frictional and turbulence effects caused by their motions. Figure 3 was obtained by mathematically manipulating equations 1 to §. The line determining the boundary between transitional turbulence and complete turbulence is the locus of the points at which the head loss no longer varies with kinematic viscosity.

It can be seen that changing the kinematic viscosity of the material being processed as described above only has an effect in the transitional turbulence region. In the complete turbulence region, changes in kinematic viscosity provide no control over the level of system head loss. For optimum processability, regardless of the degree of communition (i.e. the friction factor), the kinematic viscosity has to be within a certain range to ensure that processing takes place within the transitional turbulence regime, as seen in

Figure 3. In this regime, the method for size reduction of the material being processed can be controlled by controlling the head loss by changing the velocity of the cyclonic fluid stream. For example, this can be achieved by changing the impellor fan speed. In the complete turbulence region, this control

Is not possible. Therefore, the use of viscosity modifying agents helps to ensure that the method is controllable.

Example 2

A sample of brown coal sourced from Victoria, Australia, is split into two. One batch was prepared using the apparatus described above (batch is hereinafter referred to as “Sample A”). The second batch (hereinafter referred to as “Sample B") was dried and milled using industry standard coal preparation milling method as described in ASTM D2013-07 (Standard practice for preparing coal samples for analysis).

Both the coal samples were both subjected to the foilowing analysis: a) Proximate and Ultimate analyses - measuring moisture, ash, volatile matter, sulphur, chlorine, Gross Calorific value, Net Calorific Value; b) Size analysis; c) Intrinsic reactivity; and d) Scanning Electron microscopy — Energy Dispersive Spectrometry (SEM-

EDX).

Each of the above analyses and their results will be described in detail below. a) Proximate and Ultimate analyses

The proximate analysis was carried out using the standard ASTM (American

Society for Testing and Materials) D3172 methodology and the Ultimate analysis was carried out using ASTM D3176. The results of the proximate analysis and ultimate analysis of Samples A and B are as shown in Table 1 below. The results are typical of a low rank (brown) coal with the raw sample containing a high moisture content and low calorific value. Sample A was significantly drier than Sample B. The ash content was significantly lower for

Sample A and demonstrated a higher percentage of volatile matter which is beneficial. Sample A demonstrated a significantly higher gross and net calorific value which leads to more efficient combustion, better efficiencies and also less greenhouse gas emissions from brown coal combustion.

The results of the proximate analysis and ultimate analysis are provided in

Table 1.

Sample A Sample B

Total moisture (%) | 16.9 | 44.9

Ash content (%) 7 9.3

Volatile matter {%) 40.4 26.0

Suiphur content (%) 0.46 0.31

Chlorine content (%) 0.05 0.030

Gross calorific value (kJ/kg) 21220 13560

Net calorific value (kJ/kg) 20802 12007

Table 1: Results of the proximate and ultimate analysis b) Particle Size Analysis

The particle size analysis was carried out using a Mastersizer 2000 particle size analyser (Malvern instruments Limited). The method used for the analysis was the General Purpose analysis model as described in the Malvern Instruments

Operator's Guide.

The particle size distribution for the two samples is markedly different. Sample

A was significantly finer with few particies greater than 50 ym. Both samples contained similar particle morphologies, with some elongated particles, but most particles had an aspect ratio lower than 2. Particle sizing for sample A and sample B was obtained using Malvern Laser Diffraction particle size analyzer (Maivern Instruments GmbH), the results from which are shown in Figures 4 and 5, respectively.

The difference in particle sizing is immediately apparent from the different profiles, with sample A showing a single and even distribution about a mean particle diameter of about 10 ym as seen by line “A” in Figure 4. Sample B showed a bi-modal size distribution with peaks at about 10 um and 70 ym as seen by line “A” in Figure 5. Line “B” in each of Figures 4 and 5 refer fo the cumulative percentage of material so that it can be seen how much of the material is at a particular size.

The dsp, dig and dg values are shown in Table 2 below. dso is defined as the median average particle size, whilst the dqg particle size is the diameter where 10% of the particles have a smaller diameter (and hence the remaining 90% is coarser). The definition of dgo is therefore the particle size where 90% of the particles have a smaller diameter and the remaining 10% is coarser.

Sample A Sample B dsp | 9 29 dyo | 5 8 (deo | 16 110

Table 2: The dsp, dio and dgo values of samples A and B.

From the results obtained in Table 2, it can be seen that sample A resulted in a much smaller particle size distribution compared to sample B. Further, the average particle size of sample A was also smaller than that of sample B, indicating better processing of the sample. ¢) Intrinsic Reactivity

The intrinsic reactivity is a measure of how easily coal burns by reaction with oxygen to form carbon dioxide, CO,. For the purposes of the present example, this has been measured by Thermal Gravimetric Analysis (TGA). In this test, a weighed sample of coal was heated in air at a fixed rate (10°C per minute) and the rate of weight loss was determined, yielding a curve. The TGA profiles for

Samples A and B are shown in Figure 6.

Sample A appeared to burn out faster than Sample B and yielded an unusual spike in the profile at approximately 400°C. The peak temperature and burnout : temperature of sample B is notably higher than that of the sample A. The peak temperature is the temperature at which the maximum rate of weight loss occurs. The burnout temperature is the temperature at which burnout is considered virtuaily complete and is defined by a rate of weight loss < 0.1%/min. Both peak temperature and burnout temperature will increase as reactivity decreases.

Based on Figure 6, it can be seen that sample A yields better results than sample B. It is preferable to have lower peak temperatures and burnout temperatures as it demonstrates that the coal is more reactive. Additionally, lower peak temperatures result in lower NO, emissions from coal combustion and also reduction in carbon in the ash content. d) SEM-EDX analysis

The ratio of carbon to oxygen was determined using the SEM-EDX analysis.

SEM/EDX provides a pictorial representation of the surface with the eiemental composition of the selected area. The technique is sensitive for elements to approximately 0.1 wt % and can probe depths from 0.2 to 8 mm depending on the energy of the electron beam used and the average atomic number of the sample. For the purposes of the present example, the protocol followed for the

SEM-EDX analysis was as described in MJ Walzak et al, The Use of XPS,

FTIR, SEM/EDX, Contact Angle, and AFM in the Characterization of Coatings,

Journal of Materials Engineering and Performance, 7(3):317-323, 1998.

The results obtained are shown in Table 3 below.

Weight% | Atomic Weight %

Sample A average 2.29 | 3.05

Sample B average 3.15

Table 3: Results of SEM-EDX analysis

The weight % is on a mass basis and the atomic weight % is based on the atomic weight.

From the SEM-EDX analysis, it appears that there is a difference in carbon to oxygen ratios between the two samples which will lead to more complete combustion due to the increased ratio of oxygen.

Example 3

A sample of Bauxite material from Queensland, Australia with a moisture content of 16% was obtained. The effect of the addition of viscosity modifying agent on the sample was tested. The viscosity modifying agents chosen were heated air with a temperature of approximately 50°C and a mist spray of water.

Ambient temperature and humidity were 26°C and 30%, respectively.

Tests were then conducted by adding heat and then repeated by adding moisture. 1. Baseline Test, no water or heat added: Moisture of the sample was reduced to 7%. 2, Heated air added to air intake: Moisture of the sample was reduced to 9%. 3. Mist spray added to air intake: Moisture of the sample was reduced to 4%.

Conclusion

It has been demonstrated that the addition of a viscosity modifying agent resuits in the material to be reduced much better and with a much narrower particle size distribution. It has also been demonstrated that adding water as a viscosity modifying agent to the material whose size is to be reduced during the process of size reduction results unexpectedly and counter-intuitively, in a dryer product.

These effects may be explained in terms of improved flow conditions within the cyclone chamber as a result of the addition of viscosity modifying agents that are capable of modifying the kinematic viscosity of the fluid within the cyclone chamber. The consequent optimisation of the Reynolds number allows an increase in the residence time of the material whose size is to be reduced in the cyclone vortex and subsequently allows more exposure to the shear forces which fracture the material and thereby reducing their size and releasing more trapped moisture.

Further, ionisation of the main components of humid air is known to produce a range of free radicals and reactive gaseous species including ozone and hydrogen peroxide. Large electric fields produced in wind-blown sand and dust : storms produce energetic electrons that catalyze the production of hydrogen peroxide and ozone, both strong oxidants, from moist air.

There is no previous mention of the triboelectric charging of particles in the prior art associated with vortex-based processing systems. Furthermore, there is no mention of harnessing and controlling this effect to improve the properties of the material being processed in the cyclone chamber.

Plasmas are highly reactive chemical environments and both the hydrogen peroxide and ozone formed as a result of friboelectric charging and the subsequent ionisation of air and water vapour can be used to chemically modify the surface of the particles being processed in the cyclone chamber.

Furthermore, optimising the Reynolds number can also be used in controlling the ionisation of the air and water vapour. Reactive or nonreactive gases may also be introduced into the cyclone chamber.

For example, the properties of lignite coal are beneficially altered when processed using the apparatus and/or method as described in any embodiment above. Lignite is normally very hydrophilic but when it is subjected to the size reduction according to the method and/or apparatus according to any aspect of the present invention, the end product of the lignite becomes very hydrophobic, which is the desired state for facilitating further processing in the energy industry.

Also, the same material, normally prone to spontaneous combustion is rendered inert and requires an ignition source to ignite after being processed by the apparatus of any aspect of the present invention.

Claims

1. A method for size reduction of a material, the method comprising the steps of: - feeding material through a feed assembly into a cyclone chamber, the cyclone chamber having an elongate cylindrical conduit having a frusto-conical section; - adding at least one viscosity modifying agent into the cyclone chamber; and - providing a cyclonic fluid stream within the cyclone chamber.

2. The method according to claim 1, wherein the cyclonic fluid stream has a kinematic viscosity (v) of 1x10® m%s <v < 1x10” ms.

3. The method according to claim 1 or claim 2, wherein the viscosity modifying agent is a kinematic viscosity modifying agent.

4. The method according to any one of the preceding claims, wherein the viscosity modifying agent is selected from the group consisting of: moist air, water; warm air; cold air; oxygen; nitrogen; argon; carbon dioxide; water-based surfactants; calcium sulphate; glass; boric oxide; calcium fluoride; aluminium oxide; and a combination thereof.

5. The method according to any one of the preceding claims, wherein the ratio of the volume of material fed into the feed assembly to the volume of air within the cyclone chamber is < 40%.

6. The method according to any one of the preceding claims, wherein the step of adding at least one viscosity modifying agent into the cyclone chamber is carried out before or after the step of feeding material through a feed assembly into the cyclone chamber.

7. The method according to any one of the preceding claims, wherein the cyclonic fluid stream is provided by a device, the device being located in an opening formed at the termination of the frusto-conical section of the cyclone chamber.

8. The method according to claim 7, wherein the device is an impelior fan comprising a plurality of radially extending vanes and a hub such that each of the plurality of vanes is equispaced about the hub, and wherein the impelior fan further comprises an interrupter located within the hub for deflecting the cyclonic fluid stream in front of the hub.

9. The method according to any one of the preceding claims, wherein the material fed through the feed assembly is selected from the group consisting of: metal ores, glass, plastic, coal, lignite, petroleum coke, mezotrace, oil shale, drywall, ash, manure, sewage sludge, salt crystal, mineral and ore bearing sand, fertilizers, cement raw materials, black sand, grains , and a combination thereof.

10. The method according to any one of the preceding claims, wherein the method further comprises the step of collecting material whose size has been reduced.

11. The method according to claim 10, wherein the material whose size has been reduced has an average particle size of 5 nm — 150 um.

12. An apparatus for size reduction of a material according to the method of any one of the preceding claims, the apparatus comprising: - a cyclone chamber having an elongate cylindrical conduit having a frusto-conical section;

- a device for creating a cyclonic fluid stream within the cyclone chamber, such that the frusto-conical section of the cyclone chamber terminates in an opening forming the inlet to the device; - an air inlet tube in fluid connection with the cyclone chamber at the opposite end of the frusto-conical section; and - a feed assembly for feeding material into the cyclone chamber.

13. The apparatus according to claim 12, wherein the device for creating a cyclonic fluid stream is an impellor fan comprising a plurality of radially extending vanes and a hub such that each of the plurality of vanes is equispaced about the hub, and wherein the impellor fan further comprises an interrupter located within the hub for defiecting the cyclonic fluid stream in front of the hub.

14. The apparatus according to claim 13, wherein the diameter of the interrupter is approximately equal to the diameter of the hub.

15. The apparatus according to any one of claims 12 to 14, wherein the - length of the air inlet tube is 200-240% of the diameter of the device.

16. The apparatus according to any one of claims 12 to 15, wherein the width of the air inlet tube is approximately 33% of the diameter of the device.

17. The apparatus according to any one of claims 12 to 16, wherein the length of the cyclone chamber is 65-85% of the length of the air inlet tube.

18. The apparatus according to any one of claims 12 to 17, wherein the width of the device is one third the diameter of the device.

19. The apparatus according to any one of claims 13 to 18, wherein each of the plurality of vanes extends radially at an angle 3-10° to the radius of the impellor fan.

20. The apparatus according to any one of claims 13 to 18, wherein each of the plurality of vanes is concave in profile such that the concavity faces in the defection of rotation of the impellor fan.

21. The apparatus according to any one of claims 12 to 20, further comprising a computer control system for controlling amount of material, air, and viscosity modifying agent within the cyclone chamber.

22. A method for size reduction of a material, the method comprising the steps of: - feeding material through a feed assembly into a cyclone chamber, the cyclone chamber having an elongate cylindrical conduit having a frusto-conical section; and - providing a cyclonic fluid stream within the cyclone chamber, wherein the cyclonic fluid stream has a kinematic viscosity (v) of 1x10 m%s <v< 1x10" m¥s.

23. The method according to claim 22, further comprising the step of adding at least one viscosity modifying agent into the cyclone chamber.

24. The method according to claim 23, wherein the at least one viscosity modifying agent is a kinematic viscosity modifying agent.

25. The method according to claim 23 or claim 24, wherein the step of adding at least one viscosity modifying agent into the cyclone chamber is carried out when the kinematic viscosity (v) of the cyclonic fluid stream within the cyclone chamber is outside the range of 1x10° m%s <v < 1x10™" ms.

26. The method according to any one of claims 23 to 25, wherein the viscosity modifying agent is selected from the group consisting of: moist air, water; warm air; cold air; oxygen; nitrogen; argon; carbon dioxide; water-based surfactants; calcium sulphate; glass; boric oxide; calcium fluoride; aluminium oxide; and a combination thereof.

27. The method according to any one of claims 22 to 26, wherein the ratio of the volume of material fed into the feed assembly to the volume of air within the cyclone chamber is <40%.

28. The method according to any one of claims 23 to 27, wherein the step of adding at least one viscosity modifying agent into the cyclone chamber is carried out before or after the step of feeding material through a feed assembly into the cyclone chamber.

29. The method according to any one of claims 22 to 29, wherein the cyclonic fluid stream is provided by a device, the device being located in an opening formed at the termination of the frusto-conical section of the’ cyclone chamber.

30. The method according to claim 29, wherein the device is an impellor fan comprising a plurality of radially extending vanes and a hub such that each of the plurality of vanes is equispaced about the hub, and wherein the impelior fan further comprises an interrupter located within the hub for deflecting the cyclonic fluid stream in front of the hub.

31. The method according to any one of claims 22 to 30, wherein the material fed through the feed assembly is selected from the group consisting of: metal ores, glass, plastic, coal, lignite, petroleum coke,

mezotrace, oil shale, drywall, ash, manure, sewage sludge, salt crystal, mineral and ore bearing sand, fertilizers, cement raw materials, black sand, grains, and a combination thereof.

32. The method according to any one of claims 22 to 31, wherein the method further comprises the step of collecting material whose size has been reduced.

33. The method according to claim 32, wherein the material whose size has been reduced has an average diameter of 5 nm — 150 um.

34. An apparatus for size reduction of a material according to the method of any one of claims 22 to 33, the apparatus comprising: - a cyclone chamber having an elongate cylindrical conduit having a frusto-conical section; - a device for creating a cyclonic fluid stream within the cyclone chamber, such that the frusto-conical section of the cyclone chamber terminates in an opening forming the inlet to the device; - an air inlet tube in fluid connection with the cyclone chamber at the opposite end of the frusto-conical section; - a feed assembly for feeding material into the cyclone chamber; and - a computer control system for monitoring the kinematic viscosity (v) of the cyclonic fuid stream in the cyclone chamber.

35. The apparatus according to claim 34, wherein the device for creating a cyclonic fluid stream is an impellor fan comprising a plurality of radially extending vanes and a hub such that each of the plurality of vanes is equispaced about the hub, and wherein the impellor fan further comprises an interrupter located within the hub for deflecting the cyclonic fluid stream in front of the hub.

36. The apparatus according to claim 35, wherein the diameter of the interrupter is approximately equal to the diameter of the hub.

37. The apparatus according to any one of claims 34 to 36, wherein the length of the air inlet tube is 200-240% of the diameter of the device.

38. The apparatus according to any one of claims 34 to 37, wherein the width of the air inlet tube is approximately 33% of the diameter of the device.

39. The apparatus according to any one of claims 34 to 38, wherein the length of the cyclone chamber is 65-85% of the length of the air inlet tube.

40. The apparatus according to any one of claims 34 to 39, wherein the width of the device is one third the diameter of the device. :

41. The apparatus according to any one of claims 35 to 40, wherein each of the plurality of vanes extends radially at an angle within the range 3-10° to the radius of the impellor fan.

42. The apparatus according to any cne of claims 35 to 41, wherein each of the plurality of vanes is concave in profile such that the concavity faces in the defection of rotation of the impellor fan.

43. An apparatus for size reduction of a material comprising: - a cyclone chamber having an elongate cylindrical conduit having a frusto-conical section;

- a device for creating a cyclonic fluid stream within the cyclone chamber, such that the frusto-conical section of the cyclone chamber terminates in an opening forming the inlet to the device, - an air inlet tube in fluid connection with the cyclone chamber at the opposite end of the frusto-conical section; and - a feed assembly for feeding material into the cyclone chamber, wherein the ratio of diameter of the feed assembly to diameter of the air inlet tube is 0.3-0.5.

44. The apparatus according to claim 43, the device for creating a cyclonic fluid stream is an impellor fan comprising a plurality of radially extending vanes and a hub such that each of the plurality of vanes is equispaced about the hub, and wherein the impellor fan further comprises an interrupter located within the hub for deflecting the cyclonic fluid stream in front of the hub.

45. The apparatus according to claim 44, wherein the diameter of the interrupter is approximately equal to the diameter of the hub.

46. The apparatus according to any one of claims 43 to 45, wherein the length of the air inlet tube is 200-240% of the diameter of the device.

47. The apparatus according to any one of claims 43 to 46, wherein the width of the air inlet tube is approximately 33% of the diameter of the device.

48. The apparatus according to any one of claims 43 to 47, wherein the length of the cyclone chamber is 65-85% of the length of the air inlet tube.

49. The apparatus according to any one of claims 43 to 48, wherein the width of the device is one third the diameter of the device.

50. The apparatus according to any one of claims 44 to 49, wherein each of the plurality of vanes extends radially at an angle within the range 3-10° to the radius of the impellor fan.

51. The apparatus according to any one of the claims 44 to 50, wherein each of the plurality of vanes is concave in profile such that the concavity faces in the defection of rotation of the impelior fan.

52. The apparatus according to any one of claims 43 to 51, further comprising a computer control system for controlling feeding material and cyclonic fluid stream within the cyclone chamber.

53. A method for size reduction of a material in the apparatus of any one of the claims 43 to 52 comprising the step of controlling the ratio of the volume of material fed into the feed assembly to the volume of air within the cyclone chamber, wherein the ratio is < 40%.

54. A method for size reduction of a material, the method comprising the steps of: - feeding material through a feed assembly into a cyclone chamber, the cyclone chamber having an elongate cylindrical conduit having a frusto-conical section; - providing a cyclonic fluid stream within the cyclone chamber; and - controlling the ratio of the volume of material fed into the feed assembly to the volume of air within the cyclone chamber, wherein the ratio is < 40%.