SG11201806148XA - Kaolin for the mechanical reinforcement of polymeric laser sinter powder - Google Patents

Kaolin for the mechanical reinforcement of polymeric laser sinter powder

Info

Publication number
SG11201806148XA
SG11201806148XA SG11201806148XA SG11201806148XA SG11201806148XA SG 11201806148X A SG11201806148X A SG 11201806148XA SG 11201806148X A SG11201806148X A SG 11201806148XA SG 11201806148X A SG11201806148X A SG 11201806148XA SG 11201806148X A SG11201806148X A SG 11201806148XA
Authority
SG
Singapore
Prior art keywords
sinter powder
kaolin
mechanical reinforcement
polymeric
laser sinter
Prior art date
Application number
SG11201806148XA
Inventor
Claus Gabriel
Ruth Lohwasser
Philipp Kloke
Simon Gramlich
Rainer Ostermann
Original Assignee
Basf Se
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Basf Se filed Critical Basf Se
Publication of SG11201806148XA publication Critical patent/SG11201806148XA/en

Abstract

BASFSE INV/WOW PF0000077314 SE/WOW 33 EB14-7314PC “as originally filed” Kaolin for mechanical reinforcement of polymeric laser sinter powder The present invention relates to a process for producing a shaped body by selective 5 laser sintering of a sinter powder (SP). The sinter powder (SP) comprises at least one polyamide (P) and in the range from 10% to 50% by weight of at least one aluminosilicate. The at least one aluminosilicate has a D50 in the range from 2.5 to 4.5 µm. The present invention further relates to shaped bodies obtainable by the process of the invention. 10
SG11201806148XA 2016-02-19 2017-02-16 Kaolin for the mechanical reinforcement of polymeric laser sinter powder SG11201806148XA (en)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
EP16156543 2016-02-19
PCT/EP2017/053481 WO2017140764A1 (en) 2016-02-19 2017-02-16 Kaolin for the mechanical reinforcement of polymeric laser sinter powder

Publications (1)

Publication Number Publication Date
SG11201806148XA true SG11201806148XA (en) 2018-09-27

Family

ID=55409756

Family Applications (1)

Application Number Title Priority Date Filing Date
SG11201806148XA SG11201806148XA (en) 2016-02-19 2017-02-16 Kaolin for the mechanical reinforcement of polymeric laser sinter powder

Country Status (12)

Country Link
US (1) US11802191B2 (en)
EP (1) EP3416809A1 (en)
JP (1) JP7013379B2 (en)
KR (1) KR20180115689A (en)
CN (1) CN108698315A (en)
AU (1) AU2017221105A1 (en)
CA (1) CA3014262A1 (en)
IL (1) IL261074A (en)
MX (1) MX2018010013A (en)
SG (1) SG11201806148XA (en)
TW (1) TW201805143A (en)
WO (1) WO2017140764A1 (en)

Families Citing this family (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CA3012792A1 (en) 2016-02-19 2017-08-24 Basf Se Polyamide composition comprising a polyamide and an additive
TW201817812A (en) * 2016-07-29 2018-05-16 巴斯夫歐洲公司 Polyamide blends for laser sinter powder
JP7118075B2 (en) 2017-02-01 2022-08-15 ビーエーエスエフ ソシエタス・ヨーロピア Method for producing polyamide powder by precipitation
KR20200056455A (en) * 2017-10-04 2020-05-22 바스프 에스이 Sintered powder containing inorganic flame retardants for manufacturing molded products
ES2934932T3 (en) * 2018-09-26 2023-02-28 Basf Se Sinter powder (PS) comprising a first polyamide component (PA1) and a second polyamide component (PA2), wherein the melting point of the second polyamide component (PA2) is higher than the melting point of the first polyamide component (PA1)
DE102021111495A1 (en) * 2021-05-04 2022-11-10 Fraunhofer-Gesellschaft zur Förderung der angewandten Forschung eingetragener Verein Method for producing 3D printing material and components made from it, and 3D printing material and component produced using the method
FR3124112A1 (en) * 2021-06-17 2022-12-23 Fabulous ADDITIVE MANUFACTURING METHOD, POLYMER POWDER COMPOSITION COMPRISING A DETECTION ADDITIVE, AND OBJECT OBTAINED BY SAID METHOD
WO2023135143A1 (en) * 2022-01-11 2023-07-20 Basf Se Sinter powder (sp) comprising at least one polyamide mxd6 and at least one semicrystalline polyamide

Family Cites Families (45)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
BE562610A (en) 1957-11-22
CH372423A (en) 1958-08-12 1963-10-15 Ciba Geigy Process for the production of solid preparations
US3446782A (en) 1965-04-14 1969-05-27 Toray Industries Method of manufacture of powdery synthetic linear polyamides
CH519000A (en) 1970-02-24 1972-02-15 Inventa Ag Process for the production of polyamide 12 sinter powder
CH549622A (en) 1971-06-16 1974-05-31 Ciba Geigy Ag PLASTIC-CONTAINING POWDERS, THEIR USE FOR THE PRODUCTION OF PURE POWDER AND MANUFACTURING METHODS FOR PLASTIC-CONTAINING POWDERS.
DE2458347A1 (en) 1974-12-10 1976-06-16 Hoechst Ag PROCESS FOR THE PREPARATION OF BASIC OXAZINE DYES
DE2906647C2 (en) 1979-02-21 1980-12-11 Chemische Werke Huels Ag, 4370 Marl Process for the production of powdery coating agents !! based on polyamides with at least 10 aliphatically bonded carbon atoms per carbonamide group
US5166237A (en) * 1989-04-20 1992-11-24 Sumitomo Chemical Company, Ltd. Thermoplastic resin composition
US5527877A (en) 1992-11-23 1996-06-18 Dtm Corporation Sinterable semi-crystalline powder and near-fully dense article formed therewith
US5648450A (en) 1992-11-23 1997-07-15 Dtm Corporation Sinterable semi-crystalline powder and near-fully dense article formed therein
JPH08143768A (en) * 1994-11-16 1996-06-04 Kanegafuchi Chem Ind Co Ltd Heat-resistant thermoplastic resin composition
DE19708946A1 (en) 1997-03-05 1998-09-10 Huels Chemische Werke Ag Production of polyamide powder with narrow particle size distribution and low porosity
US6110411A (en) * 1997-03-18 2000-08-29 Clausen; Christian Henning Laser sinterable thermoplastic powder
DE19747309B4 (en) 1997-10-27 2007-11-15 Degussa Gmbh Use of a polyamide 12 for selective laser sintering
JP3757081B2 (en) 1999-06-30 2006-03-22 オリヱント化学工業株式会社 Water-insoluble nigrosine and related technologies
US6773859B2 (en) * 2001-03-06 2004-08-10 E. I. Du Pont De Nemours And Company Process for making a flexographic printing plate and a photosensitive element for use in the process
EP1256595A1 (en) * 2001-05-10 2002-11-13 Sika AG, vorm. Kaspar Winkler & Co. Adhesive filled with surface-treated chalk and carbon black
US20060108567A1 (en) 2002-07-23 2006-05-25 Charati Sanjay G Conductive poly (arylene ether) compositions and methods of making the same
US20110217495A1 (en) * 2002-08-27 2011-09-08 Ems-Chemie Ag Polyamide moulding materials for the production of moulded articles having reduced surface carbonization
JP2004155927A (en) * 2002-11-07 2004-06-03 Asahi Kasei Chemicals Corp Polyamide resin composition giving low discoloration to weathering
DE102004012682A1 (en) * 2004-03-16 2005-10-06 Degussa Ag Process for the production of three-dimensional objects by means of laser technology and application of an absorber by inkjet method
US7579397B2 (en) * 2005-01-27 2009-08-25 Rensselaer Polytechnic Institute Nanostructured dielectric composite materials
KR20090008202A (en) * 2006-03-20 2009-01-21 니혼 이타가라스 가부시키가이샤 Cosmetic preparation containing flaky glass
ES2324734T3 (en) * 2007-02-07 2009-08-13 Ems-Chemie Ag POLYAMIDE MOLDING COMPOUNDS FILLED WITH REDUCED WATER ABSORPTION.
ATE445660T1 (en) * 2007-05-03 2009-10-15 Ems Patent Ag PARTIALLY AROMATIC POLYAMIDE MOLDING COMPOUNDS AND USES THEREOF
US7737091B2 (en) * 2007-08-28 2010-06-15 Imerys Proppants and anti-flowback additives made from sillimanite minerals, methods of manufacture, and methods of use
FR2933706B1 (en) 2008-07-10 2010-08-27 Arkema France PULVERULENT COMPOSITION FOR THE MANUFACTURE OF OBJECTS HAVING A STABLE METAL APPEARANCE DURING TIME AND AN IMPROVED CUT RESISTANCE
WO2010101134A1 (en) 2009-03-05 2010-09-10 宇部興産株式会社 Polyamide particles and process for producing same
FR2955330B1 (en) 2010-01-19 2012-01-20 Arkema France THERMOPLASTIC POWDER COMPOSITION AND THREE-DIMENSIONAL ARTICLES MADE BY SINKING SUCH A COMPOSITION
CN102933299B (en) * 2010-04-01 2015-11-25 巴斯夫欧洲公司 Prepare the method for the material all in one piece through coating
EP2621712B1 (en) 2010-09-28 2018-10-24 DSM IP Assets B.V. Polymer powder composition
US8999483B2 (en) * 2010-11-29 2015-04-07 Corning Incorporated Honeycomb structure comprising an outer cement skin and a cement therefor
US20130253145A1 (en) * 2010-12-02 2013-09-26 Adeka Corporation Polyester resin composition and molded body of same
CN103562316B (en) * 2011-05-27 2015-11-25 旭化成化学株式会社 Reinforced polyamide resin particle
DE102011078722A1 (en) 2011-07-06 2013-01-10 Evonik Degussa Gmbh Powder containing polymer-coated inorganic particles
DE102011078719A1 (en) 2011-07-06 2013-01-10 Evonik Degussa Gmbh Powder containing polymer-coated particles
CN103665746B (en) * 2012-08-30 2015-07-01 上海壬丰复合材料有限公司 Micropore friction material with low abrasion and high stability coefficient and manufacturing method thereof
CN107207767B (en) 2014-12-01 2018-12-07 巴斯夫欧洲公司 Polyamide thermoplastic particle
WO2016116618A1 (en) 2015-01-23 2016-07-28 Basf Se Desalination of polyaryl ethers by means of melt extraction
CN107371367A (en) 2015-01-23 2017-11-21 巴斯夫欧洲公司 The desalination of polyaryl ether from melt polymerization process
RU2718644C2 (en) 2015-07-29 2020-04-10 Басф Се Cleaning particles and use thereof
AU2016376850C1 (en) * 2015-12-21 2021-05-27 Sika Technology Ag Polyaldimine and curable polyurethane composition
CA3012792A1 (en) 2016-02-19 2017-08-24 Basf Se Polyamide composition comprising a polyamide and an additive
MX2018010014A (en) 2016-02-19 2018-11-09 Basf Se Anti-nucleating agent for laser sintering powder.
EP3417003A1 (en) 2016-02-19 2018-12-26 Basf Se Process for preparing polyamide powders by precipitation

Also Published As

Publication number Publication date
JP2019507034A (en) 2019-03-14
KR20180115689A (en) 2018-10-23
WO2017140764A1 (en) 2017-08-24
JP7013379B2 (en) 2022-01-31
CA3014262A1 (en) 2017-08-24
IL261074A (en) 2018-11-04
EP3416809A1 (en) 2018-12-26
AU2017221105A1 (en) 2018-08-23
CN108698315A (en) 2018-10-23
US11802191B2 (en) 2023-10-31
US20210206941A1 (en) 2021-07-08
MX2018010013A (en) 2018-11-09
TW201805143A (en) 2018-02-16

Similar Documents

Publication Publication Date Title
SG11201806148XA (en) Kaolin for the mechanical reinforcement of polymeric laser sinter powder
MX2019001264A (en) Polyamide blends for laser sintered powder.
SG11201806061RA (en) Anti-nucleating agent for laser sintering powder
MX2019001265A (en) Polyamide blends containing a reinforcing agent for laser sintered powder.
SG11201806152XA (en) Process for preparing polyamide powders by precipitation
PH12016502077A1 (en) Method for the production of parts made from metal or metal matrix composite and resulting from additive manufacturing followed by an operation involving the forging of said parts
WO2017103121A3 (en) Production of an opaque silica glass article
MX2019001263A (en) Polyamide blends containing a polyarylether for laser sintered powder.
IT201700041618A1 (en) Method of production of metal powders by gas atomization and metal powder production plant according to this method.
EP2883633A3 (en) Method for production of performance enhanced metallic materials
MY190659A (en) Method for producing biohydrocarbons
SG11201809193RA (en) Bead polymer made of hard phase with domains of a soft phase
WO2015045273A8 (en) Alloy steel powder for powder metallurgy and method of producing iron-based sintered body
MX2018013137A (en) Alloy powder, sintered body, method for producing alloy powder and method for producing sintered body.
IL280072A (en) Semi-synthetic powder material, obtained by modifying the composition of a natural marine biomaterial, method for producing same, and applications thereof
MX2019001774A (en) Method for producing electronic components by means of 3d printing.
PH12020551171A1 (en) Protecting a bioactive and/or precursor thereof
MX2017009985A (en) Powder metal composition for easy machining.
SG11201903358TA (en) Copper Alloy Powder, Method of Producing Additively-Manufactured Article, and Additively-Manufactured Article
EP3829644A4 (en) Method for producing particle, and particle produced by the method and medicament
MY189848A (en) Microsilica slurry and method for producing such slurry
PH12020550950A1 (en) Composite metal component and method of producing same
WO2014121898A8 (en) Method for producing a through-hole in a metallic body
EE201600010A (en) A polymer composite material contains oil shale ash and method for manufacture its
MX2020005493A (en) Dehydrated coating compositions in solid form, production method thereof, and method for rehydrating same.