RU99103931A - METHOD FOR INCREASING THE THERMAL STABILITY OF ALPHA-SUBSTITUTED ACRYLATE GRAFT-COPOLYMERS, PRODUCT OBTAINED BY THIS METHOD AND COMPOSITION CONTAINING THIS PRODUCT - Google Patents

METHOD FOR INCREASING THE THERMAL STABILITY OF ALPHA-SUBSTITUTED ACRYLATE GRAFT-COPOLYMERS, PRODUCT OBTAINED BY THIS METHOD AND COMPOSITION CONTAINING THIS PRODUCT

Info

Publication number
RU99103931A
RU99103931A RU99103931/04A RU99103931A RU99103931A RU 99103931 A RU99103931 A RU 99103931A RU 99103931/04 A RU99103931/04 A RU 99103931/04A RU 99103931 A RU99103931 A RU 99103931A RU 99103931 A RU99103931 A RU 99103931A
Authority
RU
Russia
Prior art keywords
propylene
ethylene
olefin
alpha
copolymer
Prior art date
Application number
RU99103931/04A
Other languages
Russian (ru)
Inventor
Абузар САЙЕД
Original Assignee
Монтелл Норт Америка Инк
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Монтелл Норт Америка Инк filed Critical Монтелл Норт Америка Инк
Publication of RU99103931A publication Critical patent/RU99103931A/en

Links

Claims (13)

1. Способ повышения термостабильности альфа-замещенных акрилатных графт-сополимеров, включающий следующие стадии:
(а) получение графт-сополимера, имеющего основную полимерную цепь из материала на основе пропиленового полимера, содержащего привитые к нему в процессе полимеризации мономеры, которые включают (i) 1-3 С алкил-замещенную акриловую кислоту и (ii) сложный эфир 1-3 С алкил-замещенной акриловой кислоты, и общее количество полимеризованных мономеров составляет 20 - 240 ч на сто частей материала на основе полимера пропилена и количество (i) составляет 1 - 20%, в расчете на общую массу мономеров, и
(б) удаление любого непрореагировавшего мономера графт-полимеризации из образующегося привитого материала на основе полимера пропилена, разложение любого непрореагировавшего инициатора полимеризации и дезактивация любых оставшихся в этом материале свободных радикалов.1. The method of increasing the thermal stability of alpha-substituted acrylate graft copolymers, comprising the following stages:
(a) obtaining a graft copolymer having a main polymer chain from a material based on a propylene polymer, containing monomers grafted to it during the polymerization process, which include (i) 1-3 C alkyl-substituted acrylic acid and (ii) ester 1- 3 C alkyl-substituted acrylic acid, and the total amount of polymerized monomers is 20 - 240 hours per hundred parts of the material based on propylene polymer and the amount (i) is 1 - 20%, calculated on the total weight of monomers, and
(b) removing any unreacted graft polymerization monomer from the resulting grafted material based on propylene polymer, decomposing any unreacted polymerization initiator and deactivating any free radicals remaining in the material. 2. Способ по п. 1, отличающийся тем, что материал на основе полимера пропилена выбирают из группы, включающей
(а) кристаллический гомополимер пропилена, имеющий показатель изотактичности больше 80;
(б) кристаллический сополимер пропилена и олефина, выбранного из группы, включающей этилен и 4-10 С альфа- олефины, при условии, что когда олефином является этилен, максимальное количество полимеризованного этилена составляет 10 мас.%, и когда олефином является 4-10 С альфа-олефин, максимальное содержание этого полимеризованного олефина составляет 20 мас.%, причем сополимер имеет показатель изотактичности больше 85;
(в) кристаллический тройной сополимер пропилена и двух олефинов, выбранных из группы, включающей этилен и 4-8 С альфа-олефины, при условии, что максимальное содержание полимеризованного 4-8 С альфа-олефина составляет 2 мас. % и когда одним из олефинов является этилен, максимальное количество полимеризованного этилена составляет 5 мас.%, тройной сополимер имеет показатель изотактичности больше 85;
(г) полимерную композицию на основе олефина, включающую:
(i) 10 - 60 мас.% кристаллического гомополимера пропилена, имеющего показатель изотактичности больше 80, или кристаллический сополимер выбирают из группы, включающей (а) пропилен и этилен, (б) пропилен, этилен и 4-8 С альфа-олефин, и (в) пропилен и 4-8 С альфа-олефин, содержание пропилена в сополимере составляет более 85 мас.% и показатель изотактичности больше 85;
(ii) 5 - 25% сополимера этилена и пропилена или 4-8 С альфа-олефина, который не растворим в ксилоле при комнатной температуре,
(iii) 30 - 70% эластомерного сополимера, выбранного из группы, включающей (а) этилен и пропилен, (б) этилен, пропилен и 4 - 8 С альфа-олефин, и (в) этилен и 4 - 8 С альфа-олефин, причем сополимер необязательно содержит 0,5 - 10% диена, содержит менее 70% по массе этилена и расторим в ксилоле при температуре окружающей среды, имеет характеристическую вязкость 1,5 - 4,0 дл/г,
и общее количество (ii) и (iii), в расчете на общую массу полимерной композиции на основе олефина, составляет 50 - 90%, массовое отношение (ii) / (iii), составляет менее 0,4, предпочтительно, от 0,1 до 0,3, и эту композицию получают полимеризацией, по крайней мере, двухстадийной, и она имеет модуль при изгибе менее 150 МПа;
или (д) термопластичный олефин, включающий:
(i) 10 - 60% кристаллического гомополимера пропилена, имеющего показатель изотактичности больше 80, или кристаллический сополимер, выбранный из группы, включающей (а) этилен и пропилен, (б) этилен, пропилен и 4 - 8 С альфа-олефин, и (в) этилен и 4 - 6 С альфа-олефин, содержание пропилена в сополимере больше 85% и показатель изотактичности больше 85;
(ii) 20 - 60% аморфного сополимера, выбранного из группы, включающей (а) этилен и пропилен, (б) этилен, пропилен и 4-8 С альфа-олефин, и (в) этилен и 4-6 С альфа-олефин, причем сополимер необязательно содержит 0,5 - 10% диена и содержит менее 70% этилена, и растворяется в ксилоле при температуре окружающей среды; и
(iii) 3 - 40% сополимера этилена и пропилена или 4-8 С альфа-олефина, который не растворяется в ксилоле при температуре окружающей среды,
причем композиция имеет модуль при изгибе больше 150, но менее 1200 МПа.2. The method according to p. 1, characterized in that the material based on propylene polymer is selected from the group including
(a) crystalline propylene homopolymer having an isotacticity index greater than 80;
(b) a crystalline copolymer of propylene and an olefin selected from the group consisting of ethylene and 4-10 C alpha olefins, provided that when the olefin is ethylene, the maximum amount of polymerized ethylene is 10% by weight, and when the olefin is 4-10 With alpha-olefin, the maximum content of this polymerized olefin is 20 wt.%, And the copolymer has an isotacticity index greater than 85;
(c) a crystalline terpolymer of propylene and two olefins selected from the group comprising ethylene and 4-8 C alpha-olefins, provided that the maximum content of polymerized 4-8 C alpha olefin is 2 wt. % and when ethylene is one of the olefins, the maximum amount of polymerized ethylene is 5% by weight, the terpolymer has an isotacticity index greater than 85;
(g) an olefin-based polymer composition comprising:
(i) 10 to 60% by weight of a crystalline propylene homopolymer having an isotacticity index greater than 80, or the crystalline copolymer is selected from the group including (a) propylene and ethylene, (b) propylene, ethylene and 4-8 C alpha olefin, and (c) propylene and 4-8 C alpha-olefin, the content of propylene in the copolymer is more than 85 wt.% and the isotacticity index is more than 85;
(ii) 5 to 25% copolymer of ethylene and propylene, or 4-8 C alpha olefin, which is not soluble in xylene at room temperature,
(iii) 30 - 70% elastomeric copolymer selected from the group comprising (a) ethylene and propylene, (b) ethylene, propylene and 4 - 8 C alpha-olefin, and (c) ethylene and 4 - 8 C alpha-olefin the copolymer optionally contains 0.5-10% of a diene, contains less than 70% by weight of ethylene and dissolves in xylene at ambient temperature, has a characteristic viscosity of 1.5-4.0 dl / g,
and the total amount of (ii) and (iii), calculated on the total weight of the olefin-based polymer composition, is 50–90%, the mass ratio (ii) / (iii) is less than 0.4, preferably from 0.1 to 0.3, and this composition is obtained by polymerization of at least a two-stage process, and it has a flexural modulus of less than 150 MPa;
or (e) a thermoplastic olefin comprising:
(i) 10 to 60% crystalline propylene homopolymer having an isotacticity index greater than 80, or a crystalline copolymer selected from the group comprising (a) ethylene and propylene, (b) ethylene, propylene, and 4-8 ° C alpha-olefin, and ( c) ethylene and 4 - 6 C alpha-olefin, the content of propylene in the copolymer is more than 85% and the isotacticity index is more than 85;
(ii) 20 to 60% of an amorphous copolymer selected from the group comprising (a) ethylene and propylene, (b) ethylene, propylene, and 4-8 C alpha olefin, and (c) ethylene and 4-6 C alpha olefin , and the copolymer optionally contains 0.5 to 10% of the diene and contains less than 70% of ethylene, and is soluble in xylene at ambient temperature; and
(iii) 3 to 40% copolymer of ethylene and propylene, or 4-8 C alpha olefin, which does not dissolve in xylene at ambient temperature,
moreover, the composition has a bending modulus greater than 150, but less than 1200 MPa. 3. Способ по п.1, отличающийся тем, что полимерный материал на основе пропилена представляет собой гомополимер пропилена. 3. The method according to claim 1, characterized in that the polymeric material based on propylene is a homopolymer of propylene. 4. Способ по п.1, отличающийся тем, что замещенной акриловой кислотой является метакриловая кислота. 4. The method according to claim 1, characterized in that the substituted acrylic acid is methacrylic acid. 5. Способ по п.4, отличающийся тем, что сложный эфир замещенной акриловой кислоты представляет собой сложный эфир 1-4 С алканола. 5. The method according to p. 4, characterized in that the ester of the substituted acrylic acid is an ester of 1-4 C alkanol. 6. Способ по п.5, отличающийся тем, что сложным эфиром является метилметакрилат. 6. The method according to claim 5, characterized in that the ester is methyl methacrylate. 7. Способ по п.1, отличающийся тем, что количество (а) (i) составляет 1 - 5%. 7. The method according to claim 1, characterized in that the amount of (a) (i) is 1 to 5%. 8. Продукт, полученный способом по п.1. 8. The product obtained by the method according to claim 1. 9. Композиция, содержащая продукт по п.8 и 2 - 30%, в расчете на общую массу композиции, одного или нескольких каучуковых компонент, выбранных из группы, включающей (а) каучук на основе олефиного сополимера, (б) блок-сополимер на основе моноалкенилароматического углеводорода и сопряженного диена и (в) каучук типа "ядро-оболочка". 9. A composition containing the product according to claim 8 and 2 - 30%, calculated on the total weight of the composition, one or more rubber components selected from the group comprising (a) an olefin copolymer-based rubber, (b) a block copolymer on based on monoalkenyl aromatic hydrocarbon and conjugated diene and (c) core-shell rubber. 10. Композиция по п.9, отличающаяся тем, что также содержит 5 - 90%, в расчете на общую массу композиции, материала на основе полимера пропилена с широким молекулярно-массовым распределнием, имеющим Мw/Mn от 5 до 60 и скорость течения расплава 0,5 - 50 г/10 мин.10. The composition according to claim 9, characterized in that it also contains 5 - 90%, calculated on the total weight of the composition, of a material based on propylene polymer with a wide molecular weight distribution, having a M w / M n from 5 to 60 and a speed melt flow 0.5 - 50 g / 10 min. 11. Продукт, полученный по способу п.6. 11. The product obtained according to method 6. 12. Композиция, содержащая продукт по п.11 и 2 - 30%, в расчете на общую массу композиции, одного или нескольких каучуковых компонентов, выбранных из группы, включающей (а) каучук на основе олефинового сополимера, (б) блок-сополимер на основе моноалкенил-ароматического углеводорода и сопряженного диена, и (в) каучук типа "ядро-оболочка". 12. A composition containing the product according to claim 11 and 2 - 30%, calculated on the total weight of the composition, of one or more rubber components selected from the group comprising (a) an olefin copolymer-based rubber, (b) a block copolymer on a monoalkenyl-aromatic hydrocarbon and a conjugated diene, and (c) core-shell rubber. 13. Композиция по п.12, отличающаяся тем, что дополнительно содержит 5 - 90%, в расчете на общую массу композиции, материала на основе полимера пропилена, имеющего Mw/Mn от 5 до 60 и скорость течения расплава 0,5 - 50 г/10 мин.13. The composition according to p. 12, characterized in that it additionally contains 5 to 90%, calculated on the total weight of the composition, of a material based on propylene polymer having M w / M n from 5 to 60 and the melt flow rate 0.5 - 50 g / 10 min.
RU99103931/04A 1998-02-27 1999-02-26 METHOD FOR INCREASING THE THERMAL STABILITY OF ALPHA-SUBSTITUTED ACRYLATE GRAFT-COPOLYMERS, PRODUCT OBTAINED BY THIS METHOD AND COMPOSITION CONTAINING THIS PRODUCT RU99103931A (en)