RU2772859C2 - Double salt as powerful primary tenside for calcium sulfate mixtures containing recycled gypsum - Google Patents
Double salt as powerful primary tenside for calcium sulfate mixtures containing recycled gypsum Download PDFInfo
- Publication number
- RU2772859C2 RU2772859C2 RU2020115734A RU2020115734A RU2772859C2 RU 2772859 C2 RU2772859 C2 RU 2772859C2 RU 2020115734 A RU2020115734 A RU 2020115734A RU 2020115734 A RU2020115734 A RU 2020115734A RU 2772859 C2 RU2772859 C2 RU 2772859C2
- Authority
- RU
- Russia
- Prior art keywords
- gypsum
- composition
- alpha
- double salt
- fatty acid
- Prior art date
Abstract
Description
Настоящее изобретение относится к гипсовой композиции, которая содержит переработанный гипс и пенообразователь, который включает в себя по меньшей мере одну двойную соль альфа-сульфоновой жирной кислоты, к способу ее получения, а также к изделию, содержащему гипсовую композицию в соответствии с изобретением. Кроме того, настоящее изобретение относится к применению пенообразователя, который содержит по меньшей мере одну двойную соль альфа-сульфоновой жирной кислоты, для снижения плотности во влажном состоянии водной гипсовой композиции, которая имеет долю переработанного гипса по меньшей мере 0,5 мас.%.The present invention relates to a gypsum composition that contains recycled gypsum and a blowing agent that includes at least one double salt of an alpha-sulfonic fatty acid, to a process for its preparation, as well as to an article containing a gypsum composition in accordance with the invention. In addition, the present invention relates to the use of a blowing agent which contains at least one alpha-sulfonic fatty acid double salt for reducing the wet density of an aqueous gypsum composition which has a recycled gypsum content of at least 0.5 wt%.
В строительной промышленности применяют различные строительные материалы, содержащие гипс. К содержащим гипс строительным материалам относят гипсы, такие как отделочные гипсы, гипсовые штукатурные растворы, машинные гипсовые штукатурки, штукатурные гипсы, адгезионные гипсы, гипсы для заделки швов, шпаклевочные гипсы, изолирующие гипсы, высокопрочные гипсы, готовые гипсовые штукатурные смеси и мраморные гипсы. Помимо этого, содержащие гипс строительные материалы охватывают гипсосодержащие готовые строительные элементы, такие как гипсокартонные плиты, гипсоволокнистые плиты, гипсосодержащие стеновые панели, гипсовые панели с флисовым покрытием и гипсосодержащие формованные изделия.In the construction industry, various building materials containing gypsum are used. Gypsum-containing building materials include gypsums such as finishing gypsum, gypsum plasters, machine gypsum plasters, stucco plasters, adhesive gypsums, grout gypsums, putty gypsums, insulating gypsums, high-strength gypsums, ready-made gypsum plasters, and marble gypsums. In addition, gypsum-containing building materials include gypsum-containing prefabricated building elements such as gypsum boards, gypsum fiber boards, gypsum-containing wall panels, fleece-coated gypsum boards, and gypsum-containing molded products.
В гипсовой промышленности производители обязаны возвращать переработанный гипсовый материал обратно в производственный процесс. Под которым следует понимать гипсосодержащий строительный мусор и отходы от сноса зданий и сооружений, при этом, в частности, к ним относят гипсовые плиты (гипсокартонные плиты, гипсоволокнистые плиты, цельные гипсовые панели). Отходы от гипсовых плит возникают, например, в виде обрезков при производстве гипсокартонных плиты или при строительстве новых зданий, а также при проведении ремонтных работ и по демонтажу.In the gypsum industry, manufacturers are required to recycle recycled gypsum material back into the production process. Which should be understood as gypsum-containing construction waste and waste from the demolition of buildings and structures, while, in particular, they include gypsum boards (gypsum boards, gypsum fiber boards, solid gypsum panels). Waste from gypsum boards occurs, for example, in the form of scraps during the production of gypsum boards or during the construction of new buildings, as well as during repair work and demolition.
Однако проблема утилизации переработанного гипса заключается в том, что качество материала очень отличается из-за добавок, содержащихся в отходах от гипсовых плит. Например, гидрофобизированные гипсокартонные плиты, которые применяют для отделки помещений с повышенной влажностью, содержат доли силоксанов, которые обладают очень сильным антивспенивающим действием. При производстве гипсокартонных плит к гипсовой массе добавляют предварительно созданную пену для снижения плотности продукта. Поэтому присутствие содержащего силоксан переработанного гипса при производстве гипсокартонных плит часто является основным недостатком из-за антивспенивающего эффекта.However, the problem of recycling recycled gypsum is that the quality of the material is very different due to the additives contained in the gypsum board waste. For example, hydrophobized gypsum boards, which are used for finishing rooms with high humidity, contain proportions of siloxanes, which have a very strong anti-foaming effect. In the production of gypsum boards, pre-created foam is added to the gypsum mass to reduce the density of the product. Therefore, the presence of siloxane-containing recycled gypsum in the production of gypsum boards is often a major disadvantage due to the anti-foaming effect.
Следовательно, существует потребность в гипсовых композициях, которые можно эффективно вспенивать независимо от содержащегося количества и качества переработанного гипсового материала.Therefore, there is a need for gypsum compositions that can be effectively foamed regardless of the quantity and quality of the processed gypsum material contained.
Поэтому задача настоящего изобретения состояла в том, чтобы обеспечить гипсовую композицию, к которой можно добавлять переработанный гипс, не оказывая отрицательного влияния на эффективность пены.Therefore, the object of the present invention was to provide a gypsum composition to which recycled gypsum can be added without adversely affecting foam performance.
Эта задача была решена с помощью водной гипсовой композиции, содержащей:This problem was solved with the help of an aqueous gypsum composition containing:
i) по меньшей мере 40,0 мас.% гипса иi) at least 40.0 wt.% gypsum and
ii) по меньшей мере 0,002 мас.%, преимущественно по меньшей мере 0,005 мас.% пенообразователя, который содержит по меньшей мере одну двойную соль альфа-сульфоновой жирной кислоты,ii) at least 0.002% by weight, preferably at least 0.005% by weight of a blowing agent which contains at least one alpha-sulfonic fatty acid double salt,
в пересчете на общую массу гипсовой композиции,in terms of the total weight of the gypsum composition,
при этом гипс имеет долю переработанного гипса по меньшей мере 0,5 мас.%, в пересчете на общую долю гипса в гипсовой композиции.wherein the gypsum has a recycled gypsum content of at least 0.5% by weight, based on the total gypsum content of the gypsum composition.
При этом оказалось неожиданным, что прежде всего, тензидные структуры двойных солей, в особенности двойные соли альфа-сульфоновой жирной кислоты, действуют мощно в отношении содержащих силоксан материалов, вследствие чего значительно снижается пеноразрушающее действие силоксанов. Независимо от доли переработанного гипса при применении пен, основывающихся на двойной соли альфа-сульфоновой жирной кислоты, при изготовлении гипсовых плит, выход пены остается почти постоянным.Surprisingly, in particular, double salt tenside structures, in particular alpha-sulfonic fatty acid double salts, have a strong effect on materials containing siloxane, whereby the defoaming action of siloxanes is significantly reduced. Regardless of the proportion of recycled gypsum, when using foams based on the double salt of alpha-sulfonic fatty acid in the manufacture of gypsum boards, the foam yield remains almost constant.
Таким образом, в соответствии с предпочтительным вариантом осуществления настоящего изобретения доля переработанного гипса представляет собой содержащий силоксан переработанный гипс.Thus, according to a preferred embodiment of the present invention, the proportion of recycled gypsum is siloxane-containing recycled gypsum.
В соответствии с другим предпочтительным вариантом осуществления настоящего изобретения по меньшей мере одна двойная соль альфа-сульфоновой жирной кислоты представляет собой соединение формулы (I)According to another preferred embodiment of the present invention, the at least one alpha-sulfonic fatty acid double salt is a compound of formula (I)
при этом R1 представляет собой линейный или разветвленный алкильный или алкиленовый остаток с 6-16 С-атомами, а М1 и М2 независимо друг от друга представляют собой Н, Li, Na, K, Са/2, Mg/2, аммоний или алканоламин.while R 1 is a linear or branched alkyl or alkylene residue with 6-16 C atoms, and M 1 and M 2 independently of each other are H, Li, Na, K, Ca / 2, Mg / 2, ammonium or alkanolamine.
Предпочтительно R1 представляет собой линейный алкильный остаток с 8-6 С-атомами.Preferably R 1 is a linear alkyl residue with 8-6 carbon atoms.
Особенно предпочтительно М1 и М2 представляют собой Na.Particularly preferably M 1 and M 2 are Na.
В соответствии с другим вариантом осуществления настоящего изобретения композиция, кроме того, содержит по меньшей мере 0,005 мас.%, предпочтительно по меньшей мере 0,002 мас.% по меньшей мере одного котензида, отличающегося от двойных солей альфа-сульфоновой жирной кислоты.In accordance with another embodiment of the present invention, the composition further comprises at least 0.005% by weight, preferably at least 0.002% by weight of at least one cotenside other than alpha-sulfonic fatty acid double salts.
Особенно предпочтительно по меньшей мере один котензид выбирают из группы, состоящей из алкилполигликозидов, алкиламидобетаинов, глутаматов, сульфокетонов, сульфатов, (в том числе алкилсульфатов, алкилэфирсульфатов) изеционатов, соединений N-ацил-аминокислоты, сульфоацетатов, сульфонатов, сульфосукцинатов, тауратов, бетаинов, амфотензидов, алканоламидов, аминоксидов, карбоксилатов, алкилэтоксилатов, катионных тензидов, катионных полимеров, гидролизатов белков, силиконов, жирных спиртов, производных белков, отбеливающих веществ двойных солей, неионогенных тензидов, а также их смесей.Particularly preferably, at least one cotenside is selected from the group consisting of alkyl polyglycosides, alkylamido betaines, glutamates, sulfoketones, sulfates, (including alkyl sulfates, alkyl ether sulfates) isecyanates, N-acyl-amino acid compounds, sulfoacetates, sulfonates, sulfosuccinates, taurates, betaines, amphotensides, alkanolamides, amine oxides, carboxylates, alkyl ethoxylates, cationic surfactants, cationic polymers, protein hydrolysates, silicones, fatty alcohols, protein derivatives, double salt bleaching agents, nonionic surfactants, and mixtures thereof.
В соответствии с другим вариантом осуществления настоящего изобретения композиция, кроме того, содержит по меньшей мере один растворитель.In accordance with another embodiment of the present invention, the composition further comprises at least one solvent.
В соответствии с другим предпочтительным вариантом осуществления настоящего изобретения композиция содержит одну или несколько добавок, выбранных из группы, включающей в себя простые эфиры целлюлозы, гашеную известь, крахмалы, модифицированные крахмалы, гидрофобизирующие вещества, минеральные добавки, агрегаты низкой плотности, волокна, ускорители, загустители, замедлители, порообразующие добавки, вспенивающие вещества, агенты набухания, наполнители, полиакрилаты, диспергирующие средства, пластификаторы, суперабсорбенты и стабилизаторы.In accordance with another preferred embodiment of the present invention, the composition contains one or more additives selected from the group consisting of cellulose ethers, slaked lime, starches, modified starches, water repellents, mineral additives, low density aggregates, fibers, accelerators, thickeners. , retarders, blowing agents, blowing agents, swelling agents, fillers, polyacrylates, dispersants, plasticizers, superabsorbents and stabilizers.
Помимо этого, в соответствии с предпочтительным вариантом осуществления настоящего изобретения гипсовая композиция включает в себя от 0,0001 до 1,0 мас.% замедлителя и/или от 0,01 до 2,0 мас.% пластификатора.In addition, in accordance with a preferred embodiment of the present invention, the gypsum composition includes from 0.0001 to 1.0 wt.% retarder and/or from 0.01 to 2.0 wt.% plasticizer.
Кроме того, настоящее изобретение относится к изделию, содержащему описанную выше гипсовую композицию.In addition, the present invention relates to a product containing the above-described gypsum composition.
В частности, предпочтительно изделие представляет собой отделочные гипсы, гипсовые штукатурные растворы, машинная гипсовая штукатурка, штукатурные гипсы, адгезионные гипсы, гипсы для заделки швов, шпаклевочные гипсы, изолирующие гипсы, высокопрочные гипсы, готовые гипсовые штукатурные смеси, мраморные гипсы или гипсосодержащие готовые строительные элементы, такие как гипсокартонные плиты, гипсоволокнистые плиты, гипсосодержащие стеновые панели, гипсовые панели с флисовым покрытием и гипсосодержащие формованные изделия.Particularly preferably, the article is a finishing gypsum, gypsum stucco, machine gypsum plaster, stucco gypsum, adhesive gypsum, grouting gypsum, filler gypsum, insulating gypsum, high-strength gypsum, ready-made gypsum plaster, marble gypsum or gypsum-containing prefabricated building elements. such as gypsum board, gypsum fiber board, gypsum wallboard, fleece-coated gypsum board, and gypsum molded products.
Кроме того, настоящее изобретение относится к способу получения водной гипсовой композиции, включающему в себя:In addition, the present invention relates to a method for producing an aqueous gypsum composition, including:
а) создание пены из пенообразователя, который содержит по меньшей мере одну двойную соль альфа-сульфоновой жирной кислоты,a) creating foam from a blowing agent that contains at least one double salt of an alpha-sulfonic fatty acid,
б) приготовление композиции, содержащей воду, гипс и при необходимости вспомогательные средства,b) preparation of a composition containing water, gypsum and, if necessary, auxiliary agents,
в) воздействие срезывающих сил на полученную в стадии б) композицию с добавлением пены из стадии а),c) the effect of shear forces on the composition obtained in stage b) with the addition of foam from stage a),
при этом гипс имеет долю переработанного гипса по меньшей мере 0,5 мас.%, в пересчете на общую долю гипса в композиции.wherein the gypsum has a recycled gypsum content of at least 0.5% by weight, based on the total gypsum content of the composition.
Кроме того, настоящее изобретение относится к применению пенообразователя, который содержит по меньшей мере одну двойную соль альфа-сульфоновой жирной кислоты, для снижения плотности во влажном состоянии водной гипсовой композиции, которая имеет долю переработанного гипса по меньшей мере 0,5 мас.%, в пересчете на общую долю гипса в композиции.In addition, the present invention relates to the use of a blowing agent which contains at least one alpha-sulfonic fatty acid double salt for reducing the wet density of an aqueous gypsum composition which has a recycled gypsum content of at least 0.5% by weight, in in terms of the total proportion of gypsum in the composition.
В особенности предпочтительно, что по меньшей мере одна двойная соль альфа-сульфоновой жирной кислоты представляет собой одно из приведенных выше соединений.It is particularly preferred that at least one alpha-sulfonic fatty acid double salt is one of the above compounds.
В дальнейшем настоящее изобретение описано более подробно.Hereinafter, the present invention is described in more detail.
Как уже было пояснено выше, предлагаемая в изобретении композиция содержит гипс, имеющий долю переработанного гипса по меньшей мере 0,5 мас.%.As already explained above, the composition according to the invention contains a gypsum having a recycled gypsum content of at least 0.5% by weight.
В контексте настоящего изобретения понятие «гипс» относится к соединению сульфата кальция в его безводной или гидратированной форме, такому как, например, гипсовая порода, состоящая из этого соединения в кристаллической форме, а также к соответствующему строительному материалу, такому как полугидрат, дигидрат или ангидрит сульфата кальция формулы CaSO4 ⋅ x Н2О, при этом х равен 0, 
Гипсовая композиция в соответствии с изобретением содержит по меньшей мере 40,0 мас.%, более предпочтительно от 45,0 до 70,0 мас.%, особенно предпочтительно от 50,0 до 65,0 мас.% гипса, в пересчете на общую массу гипсовой композиции.The gypsum composition according to the invention contains at least 40.0% by weight, more preferably from 45.0 to 70.0% by weight, particularly preferably from 50.0 to 65.0% by weight of gypsum, based on the total mass of gypsum composition.
Доля переработанного гипса в применяемом в соответствии с изобретением гипсе составляет по меньшей мере 0,5 мас.%, более предпочтительно по меньшей мере 2,0 мас.%, особенно предпочтительно по меньшей мере 5,0 мас-%, в пересчете на общую долю гипса в композиции.The proportion of recycled gypsum in the gypsum used according to the invention is at least 0.5% by weight, more preferably at least 2.0% by weight, particularly preferably at least 5.0% by weight, based on the total plaster in the composition.
В контексте настоящего изобретения понятие «переработанный гипс» относится к гипсу, который уже был использован при производстве гипсосодержащих изделий и извлечен из указанных изделий. Примеры гипсосодержащих изделий, из которых извлекают переработанный гипс, представляют собой отделочные гипсы, гипсовые штукатурные растворы, машинную гипсовую штукатурку, штукатурные гипсы, адгезионные гипсы, гипсы для заделки швов, шпаклевочные гипсы, изолирующие гипсы, высокопрочные гипсы, готовые гипсовые штукатурные смеси, мраморные гипсы, а также гипсосодержащие готовые строительные элементы, такие как гипсокартонные плиты, гипсоволокнистые плиты, гипсосодержащие стеновые панели, гипсовые панели с флисовым покрытием и гипсосодержащие формованные изделия.In the context of the present invention, the term "recycled gypsum" refers to gypsum that has already been used in the manufacture of gypsum-containing products and extracted from these products. Examples of gypsum-containing products from which recycled gypsum is recovered are finishing gypsum, gypsum plasters, machine gypsum plasters, stucco plasters, adhesive gypsums, grouting gypsums, putty gypsums, insulating gypsums, high-strength gypsums, ready-made gypsum plasters, marble gypsums , as well as gypsum-containing prefabricated building elements such as gypsum boards, gypsum fiber boards, gypsum-containing wall panels, fleece-coated gypsum boards, and gypsum-containing molded products.
Как правило, переработанный гипс содержит добавки, содержащиеся в изделиях, включающих в себя гипс, которые возвращают в производственный процесс. Например, в гидрофобизированных гипсокартонных плитах, используемых для отделки помещений с повышенной влажностью, содержатся силоксаны или восковые эмульсии.Typically, recycled gypsum contains additives found in articles containing gypsum that are recycled back into the manufacturing process. For example, hydrophobized gypsum boards used for finishing rooms with high humidity contain siloxanes or wax emulsions.
Переработанный гипс в соответствии с настоящим изобретением предпочтительно содержит силоксаны. Силоксаны представляют собой линейные или циклические соединения формулыThe processed gypsum according to the present invention preferably contains siloxanes. Siloxanes are linear or cyclic compounds of the formula
при этом R1 означает водород или алкильный остаток, a R2, при наличии, означает группу -О-, которая образует замыкание кольца между концевыми группами 
В частности, переработанный гипс содержит по меньшей мере 0,01 мас.% силоксанов, более предпочтительно от 0,02 до 5,0 мас.% силоксанов, особенно предпочтительно от 0,05 до 2,0 мас.%, в пересчете на общую массу переработанного гипса.In particular, the processed gypsum contains at least 0.01% by weight of siloxanes, more preferably from 0.02 to 5.0% by weight of siloxanes, particularly preferably from 0.05 to 2.0% by weight, based on the total mass of processed gypsum.
Соответственно этому гипсовая композиция в соответствии с изобретением содержит по меньшей мере 0,01 мас.% силоксанов, более предпочтительно от 0,01 до 2,0 мас.% силоксанов, особенно предпочтительно от 0,02 до 1,0 мас.%, в пересчете на общую массу гипсовой композиции.Accordingly, the gypsum composition according to the invention contains at least 0.01% by weight of siloxanes, more preferably from 0.01 to 2.0% by weight of siloxanes, particularly preferably from 0.02 to 1.0% by weight, in in terms of the total weight of the gypsum composition.
Кроме того, гипсовая композиция в соответствии с изобретением содержит по меньшей мере 0,005 мас.% пенообразователя, который содержит по меньшей мере одну двойную соль альфа-сульфоновой жирной кислоты, или по меньшей мере 0,007 мас.%, или по меньшей мере 0,01 мас.%, в пересчете на общую массу гипсовой композиции.In addition, the gypsum composition in accordance with the invention contains at least 0.005 wt.% foaming agent, which contains at least one double salt of alpha-sulfonic fatty acids, or at least 0.007 wt.%, or at least 0.01 wt. .%, based on the total weight of the gypsum composition.
В другом варианте осуществления гипсовая композиция в соответствии с изобретением содержит по меньшей мере 0,002 мас.% пенообразователя, который содержит по меньшей мере одну двойную соль альфа-сульфоновой жирной кислоты, более предпочтительно по меньшей мере 0,003 мас.%, особенно предпочтительно по меньшей мере 0,005 мас.%, в пересчете на общую массу гипсовой композиции.In another embodiment, the gypsum composition according to the invention contains at least 0.002% by weight of a blowing agent which contains at least one alpha-sulfonic fatty acid double salt, more preferably at least 0.003% by weight, particularly preferably at least 0.005 wt.%, in terms of the total weight of the gypsum composition.
В одном варианте осуществления пенообразователь содержит по меньшей мере 30 мас.%, по меньшей мере 45 мас.%, или по меньшей мере 60 мас.% по меньшей мере одной двойной соли альфа-сульфоновой жирной кислоты, в пересчете на общую массу пенообразователя. Особенно предпочтительно пенообразователь состоит из по меньшей мере одной двойной соли альфа-сульфоновой жирной кислоты.In one embodiment, the blowing agent contains at least 30 wt.%, at least 45 wt.%, or at least 60 wt.% of at least one alpha-sulfonic fatty acid double salt, based on the total weight of the blowing agent. Particularly preferably, the blowing agent consists of at least one alpha-sulfonic fatty acid double salt.
Предпочтительно пенообразователь содержит по меньшей мере 15 мас.%, более предпочтительно по меньшей мере 25 мас.%, особенно предпочтительно по меньшей мере 30 мас.% по меньшей мере одной двойной соли альфа-сульфоновой жирной кислоты, в пересчете на общую массу пенообразователя. Особенно предпочтительно пенообразователь состоит из по меньшей мере одной двойной соли альфа-сульфоновой жирной кислоты.Preferably the blowing agent contains at least 15 wt.%, more preferably at least 25 wt.%, particularly preferably at least 30 wt.% of at least one alpha-sulfonic fatty acid double salt, based on the total weight of the blowing agent. Particularly preferably, the blowing agent consists of at least one alpha-sulfonic fatty acid double salt.
В контексте настоящего изобретения понятие «пенообразователь» относится к поверхностно-активным веществам, обладающим определенной пленкообразующей способностью и которые таким образом способствуют образованию пены в жидкостях.In the context of the present invention, the term "foaming agent" refers to surfactants having a certain film-forming ability and which thus contribute to the formation of foam in liquids.
Предпочтительно по меньшей мере одна двойная соль альфа-сульфоновой жирной кислоты представляет собой соединение формулы (I)Preferably the at least one alpha-sulfonic fatty acid double salt is a compound of formula (I)
при этом R1 представляет собой линейный или разветвленный алкильный или алкиленовый остаток с 6-16 С-атомами, а М1 и М2 независимо друг от друга означают Н, Li, Na, K, Са/2, Mg/2, аммоний или алканоламин. При этом особенно предпочтительными алканоламинами являются моноэтаноламин, диэтаноламин, триэтаноламин и моно-изопропаноламин.wherein R 1 represents a linear or branched alkyl or alkylene residue with 6-16 carbon atoms, and M 1 and M 2 independently of each other mean H, Li, Na, K, Ca/2, Mg/2, ammonium or alkanolamine. While particularly preferred alkanolamines are monoethanolamine, diethanolamine, triethanolamine and mono-isopropanolamine.
Кроме того, применяется условие, чтобы доля соединений формулы (I) в по меньшей мере одной двойной соли альфа-сульфоновой жирной кислоты, в которой остаток R1 представляет собой алкиленовый остаток, составляла 3 мас-% или менее, в пересчете на общую массу по меньшей мере одной двойной соли альфа-сульфоновой жирной кислоты.In addition, the condition is applied that the proportion of compounds of formula (I) in at least one double salt of alpha-sulfonic fatty acid, in which the residue R 1 represents an alkylene residue, is 3 wt% or less, based on the total weight by weight. at least one alpha-sulfonic fatty acid double salt.
Предпочтительно R1 представляет собой насыщенный, линейный алкильный остаток с 8-16 С-атомами, более предпочтительно 9-16 С-атомами, особенно предпочтительно 10-12 С-атомами.Preferably R 1 is a saturated, linear alkyl radical with 8-16 carbon atoms, more preferably 9-16 carbon atoms, particularly preferably 10-12 carbon atoms.
Особенно предпочтительно применяется условие, чтобы доля соединений формулы (I) в по меньшей мере одной двойной соли альфа-сульфоновой жирной кислоты, в которой остаток R1 представляет собой децильный и/или додецильный остаток, составляла 90 мас.% или более, в пересчете на общую массу по меньшей мере одной двойной соли альфа-сульфоновой жирной кислоты.Particularly preferably, the condition is applied that the proportion of compounds of formula (I) in at least one double salt of alpha-sulfonic fatty acid, in which the residue R 1 represents a decyl and/or dodecyl residue, is 90 wt.% or more, calculated on the total weight of at least one alpha-sulfonic fatty acid double salt.
Особенно предпочтительно М1 и М2 означают Na.Particularly preferably M 1 and M 2 are Na.
Соответственно, по меньшей мере одна двойная соль альфа-сульфоновой жирной кислоты в соответствии с настоящим изобретением особенно предпочтительно представляет собой динатриевую соль 2-сульфододекановой кислоты, динатриевую соль 2-сульфотетрадекановой кислоты или их смеси. Особенно предпочтительно по меньшей мере одна двойная соль альфа-сульфоновой жирной кислоты представляет собой смесь динатриевой соли 2-сульфододекановой кислоты и динатриевой соли 2-сульфотетрадекановой кислоты.Accordingly, the at least one alpha-sulfonic fatty acid double salt according to the present invention is particularly preferably 2-sulfododecanoic acid disodium, 2-sulfotetradecanoic acid disodium or mixtures thereof. Particularly preferably, the at least one alpha-sulfonic fatty acid double salt is a mixture of 2-sulfododecanoic acid disodium salt and 2-sulfotetradecanoic acid disodium salt.
Соединения формулы (I) могут быть получены всеми способами, известными специалистам в данной области. При этом особенно предпочтительным способом получения является сульфирование соответствующих карбоновых кислот. В этом случае соответствующую карбоновую кислоту, в особенности соответствующую жирную кислоту, подвергают взаимодействию с газообразным триоксидом серы, причем триоксид серы преимущественно используют в таком количестве, чтобы молярное соотношение SO3 к жирной кислоте находилось в диапазоне от 1,0 : 1 до 1,1 : 1. Полученные таким образом неочищенные продукты, которые представляют собой кислые продукты сульфонирования, затем частично или полностью нейтрализуют, при этом предпочтительной является полная нейтрализация водным NaOH. При желании также можно осуществить стадии очистки.Compounds of formula (I) can be obtained by all methods known to experts in this field. In this case, a particularly preferred preparation method is the sulfonation of the corresponding carboxylic acids. In this case, the corresponding carboxylic acid, in particular the corresponding fatty acid, is reacted with gaseous sulfur trioxide, the sulfur trioxide being preferably used in such an amount that the molar ratio of SO 3 to fatty acid is in the range from 1.0:1 to 1.1 : 1. The crude products thus obtained, which are acidic sulphonation products, are then partially or completely neutralized, complete neutralization with aqueous NaOH being preferred. Purification steps can also be carried out if desired.
В соответствии с другим предпочтительным вариантом осуществления гипсовая композиция в соответствии с изобретением содержит по меньшей мере 0,002 мас.% по меньшей мере одного котензида, более предпочтительно по меньшей мере 0,003 мас.%, особенно предпочтительно по меньшей мере 0,005 мас.%, в пересчете на общую массу гипсовой композиции.According to another preferred embodiment, the gypsum composition according to the invention contains at least 0.002% by weight of at least one cotenside, more preferably at least 0.003% by weight, particularly preferably at least 0.005% by weight, based on the total weight of the gypsum composition.
По меньшей мере один котензид представляет собой по меньшей мере один пенообразователь, отличающийся от двойных солей альфа-сульфоновой жирной кислоты.At least one cotenside is at least one blowing agent other than alpha-sulfonic fatty acid double salts.
Предпочтительно по меньшей мере один котензид представляет собой пенообразователь, выбранный из группы, состоящей из алкилполигликозидов, алкиламидобетаинов, глутаматов, сульфокетонов, сульфатов, (в том числе алкилсульфатов, алкилэфирсульфатов) изеционаты, соединений N-ацил-аминокислоты, сульфоацетатов, сульфонатов, сульфосукцинатов, тауратов, бетаинов, амфотензидов, алканоламидов, аминоксидов, карбоксилатов, алкилэтоксилатов, катионных тензидов, катионных полимеров, гидролизатов белков, силиконов, жирных спиртов, производных белков, отбеливающих веществ двойных солей, неионогенных тензидов, а также их смесей.Preferably, at least one cotenside is a blowing agent selected from the group consisting of alkyl polyglycosides, alkylamido betaines, glutamates, sulfoketones, sulfates, (including alkyl sulfates, alkyl ether sulfates) isocyanates, N-acyl-amino acid compounds, sulfoacetates, sulfonates, sulfosuccinates, taurates , betaines, amphotensides, alkanolamides, amine oxides, carboxylates, alkyl ethoxylates, cationic surfactants, cationic polymers, protein hydrolysates, silicones, fatty alcohols, protein derivatives, double salt bleaching agents, nonionic surfactants, and mixtures thereof.
Предпочтительными алкилполигликозидами являются соединения формулы (II)Preferred alkyl polyglycosides are compounds of formula (II)
при этом R2 означает линейный или разветвленный алкильный и/или алкиленовый остаток с 8-18 С-атомами, G означает остаток сахара с 5 или 6 С-атомами и р равняется числам от 1 до 10.while R 2 means a linear or branched alkyl and/or alkylene residue with 8-18 carbon atoms, G means a sugar residue with 5 or 6 carbon atoms and p is equal to numbers from 1 to 10.
Предпочтительными алкиламидобетаинами являются соединения формулы (III)Preferred alkylamido betaines are compounds of formula (III)
при этом R3 означает линейный или разветвленный алкильный или алкиленовый остаток с 7-19 С-атомами, а у означает целое число в пределах от 2 до 4.while R 3 means a linear or branched alkyl or alkylene residue with 7-19 carbon atoms, and y means an integer in the range from 2 to 4.
Предпочтительные соединения N-ацил-аминокислоты предпочтительно представляют собой соединения N-ацил-глутаминовой кислоты формулы (IV)Preferred N-acyl-amino acid compounds are preferably N-acyl-glutamic acid compounds of formula (IV)
при этом R4 означает линейный или разветвленный алкильный или алкиленовый остаток с 7-19 С-атомами, а остатки М3 и М4 независимо друг от друга выбраны из группы, включающей в себя Н, Li, Na, K, Са/2, Mg/2, аммоний и алканоламины.while R 4 means a linear or branched alkyl or alkylene residue with 7-19 C atoms, and the residues M 3 and M 4 are independently selected from the group including H, Li, Na, K, Ca / 2, Mg/2, ammonium and alkanolamines.
В соответствии с другим вариантом осуществления настоящего изобретения композиция дополнительно содержит по меньшей мере один растворитель. Предпочтительно композиция содержит от 0,0001 мас.% до 0,2 мас.% по меньшей мере одного растворителя, в пересчете на общую массу гипсовой композиции.In accordance with another embodiment of the present invention, the composition further comprises at least one solvent. Preferably, the composition contains from 0.0001 wt.% to 0.2 wt.% at least one solvent, based on the total weight of the gypsum composition.
Растворитель предпочтительно выбирают из группы, включающей в себя гексиленгликоль, (2-метил-2,4-пентандиол), этанол, пропаналь, н-пропиловый спирт, 1-пентанол, 2-пентанол, 3-пентанол, 2-метил-1-бутанол, 2-метил-2-бутанол, 3-метил-1-бутанол, 3-метил-2-бутанол, 2,2-диметил-1-пропанол, н-пропиловый эфир уксусной кислоты, н-бутиловый эфир уксусной кислоты, 1-пентилацетат, 2-пентилацетат, 3-пентилацетат, изопентилацетат, 1,1-диметилпропилацетат, 2-метилбутилацетат, 2-этилгексилацетат, 2-бутооксиэтанол, 2-(2-бутооксиэтокси)-этанол, простой монобутиловый эфир триэтиленгликоля, 3,6,9,12-тетраоксагексадекан-1-ол, 2-гексокси-1-этанол, 2-(2-гексилоксиэтокси)этанол, 1-метокси-2-пропанол, метоксипропоксипропанол, 1-бутоокси-2-пропанол, простой бутиловый эфир ди(пропиленгликоля), простой бутиловый эфир три(пропиленгликоля), 2-бутооксиэтилацетат, 2-(2-бутооксиэтокси)этилацетат, 1-метокси-2-пропилацетат и их смеси.The solvent is preferably selected from the group consisting of hexylene glycol, (2-methyl-2,4-pentanediol), ethanol, propanal, n-propyl alcohol, 1-pentanol, 2-pentanol, 3-pentanol, 2-methyl-1- butanol, 2-methyl-2-butanol, 3-methyl-1-butanol, 3-methyl-2-butanol, 2,2-dimethyl-1-propanol, acetic acid n-propyl ester, acetic acid n-butyl ester, 1-pentyl acetate, 2-pentyl acetate, 3-pentyl acetate, isopentyl acetate, 1,1-dimethylpropyl acetate, 2-methylbutyl acetate, 2-ethylhexyl acetate, 2-butoxyethanol, 2-(2-butoxyethoxy)ethanol, triethylene glycol monobutyl ether, 3.6 ,9,12-tetraoxahexadecan-1-ol, 2-hexoxy-1-ethanol, 2-(2-hexyloxyethoxy)ethanol, 1-methoxy-2-propanol, methoxypropoxypropanol, 1-butooxy-2-propanol, butyl ether di (propylene glycol), tri(propylene glycol) butyl ether, 2-butoxyethyl acetate, 2-(2-butoxyethoxy)ethyl acetate, 1-methoxy-2-propyl acetate, and mixtures thereof.
Гипсовая композиция в соответствии с изобретением может содержать пенообразователь в невспененном виде или в виде заранее подготовленной пены. Способ получения заранее подготовленной пены известен специалисту в данной области техники.The gypsum composition according to the invention may contain a blowing agent in non-foamed form or in the form of preformed foam. The method of obtaining a pre-prepared foam is known to a person skilled in the art.
Заранее подготовленная пен предпочтительно имеет плотность пены от 50 до 180 г/л, более предпочтительно от 60 до 140 г/л, особенно предпочтительно от 70 до 120 г/л.The preformed foam preferably has a foam density of 50 to 180 g/l, more preferably 60 to 140 g/l, particularly preferably 70 to 120 g/l.
Гипсовая композиция в соответствии с изобретением предпочтительно содержит по меньшей мере 40,0 мас.%, более предпочтительно от 45,0 до 75,0 мас.%, особенно предпочтительно от 50,0 до 65,0 мас.% гипса, по меньшей мере 0,005 мас.%, более предпочтительно по меньшей мере 0,007 мас.%, особенно предпочтительно по меньшей мере 0,01 мас.% пенообразователя, который содержит по меньшей мере одну двойную соль альфа-сульфоновой жирной кислоты, по выбору, по меньшей мере 0,002 мас.%, более предпочтительно по меньшей мере 0,003 мас.%, особенно предпочтительно по меньшей мере 0,005 мас.% по меньшей мере одного котензида, по выбору по меньшей мере 0,0001 мас.%, преимущественно от 0,0005 мас.% до 0,2 мас.% по меньшей мере одного растворителя и от 20,0 до 65,0 мас.%, более предпочтительно от 30,0 до 55,0 мас.%, особенно предпочтительно от 35,0 до 50,0 мас.% воды, в пересчете на общую массу гипсовой композиции.The gypsum composition according to the invention preferably contains at least 40.0% by weight, more preferably from 45.0 to 75.0% by weight, particularly preferably from 50.0 to 65.0% by weight of gypsum, at least 0.005% by weight, more preferably at least 0.007% by weight, particularly preferably at least 0.01% by weight of a blowing agent which contains at least one alpha-sulfonic fatty acid double salt, optionally at least 0.002% by weight .%, more preferably at least 0.003 wt.%, particularly preferably at least 0.005 wt.% of at least one cotenside, optionally at least 0.0001 wt.%, preferably from 0.0005 wt.% to 0 20.0 to 65.0 wt.% of at least one solvent, more preferably 30.0 to 55.0 wt.%, particularly preferably 35.0 to 50.0 wt.% water, in terms of the total weight of the gypsum composition.
В другом варианте осуществления гипсовая композиция в соответствии с изобретением предпочтительно содержит по меньшей мере 40,0 мас.%, более предпочтительно от 45,0 до 75,0 мас.%, особенно предпочтительно от 50,0 до 65,0 мас.% гипса, по меньшей мере 0,002 мас.%, более предпочтительно по меньшей мере 0,003 мас.%, особенно предпочтительно по меньшей мере 0,005 мас.% пенообразователя, который содержит по меньшей мере одну двойную соль альфа-сульфоновой жирной кислоты, по выбору, по меньшей мере 0,001 мас.%, более предпочтительно по меньшей мере 0,002 мас.%, особенно предпочтительно по меньшей мере 0,003 мас.% по меньшей мере одного котензида, по выбору по меньшей мере 0,0001 мас.%, преимущественно от 0,0005 мас.% до 0,2 мас.% по меньшей мере одного растворителя и от 20,0 до 65,0 мас.%, более предпочтительно от 30,0 до 55,0 мас.%, особенно предпочтительно от 35,0 до 50,0 мас.% воды, в пересчете на общую массу гипсовой композиции.In another embodiment, the gypsum composition according to the invention preferably contains at least 40.0 wt.%, more preferably from 45.0 to 75.0 wt.%, particularly preferably from 50.0 to 65.0 wt.% gypsum , at least 0.002 wt.%, more preferably at least 0.003 wt.%, particularly preferably at least 0.005 wt.% of a blowing agent which contains at least one alpha-sulfonic fatty acid double salt, optionally at least 0.001 wt.%, more preferably at least 0.002 wt.%, particularly preferably at least 0.003 wt.% of at least one cotenside, optionally at least 0.0001 wt.%, preferably from 0.0005 wt.% up to 0.2 wt.% of at least one solvent and from 20.0 to 65.0 wt.%, more preferably from 30.0 to 55.0 wt.%, particularly preferably from 35.0 to 50.0 wt. .% water, based on the total weight of the gypsum composition.
Соответственно этому гипсовая композиция в соответствии с изобретением предпочтительно имеет водогипсовое соотношение от 0,3 до 1,5, более предпочтительно от 0,5 до 1,0, особенно предпочтительно от 0,7 до 0,8.Accordingly, the gypsum composition according to the invention preferably has a gypsum-to-water ratio of 0.3 to 1.5, more preferably 0.5 to 1.0, particularly preferably 0.7 to 0.8.
Кроме того, гипсовая композиция в соответствии с изобретением может быть модифицирована посредством добавления добавок. Обычно гипсовая композиция содержит добавки, которые влияют на свойства текучести или на процесс отверждения. Например, гипсовая композиция в соответствии с изобретением может содержать одну или несколько добавок, выбранных из группы, включающей в себя простые эфиры целлюлозы, гашеную известь, минеральные добавки, агрегаты низкой плотности, волокна, ускорители, загустители, замедлители, порообразующие добавки, вспенивающие вещества, агенты набухания, наполнители, полиакрилаты, диспергирующие средства, пластификаторы, суперабсорбенты и стабилизаторы.In addition, the gypsum composition according to the invention can be modified by adding additives. Typically, the gypsum composition contains additives that affect the flow properties or the curing process. For example, the gypsum composition according to the invention may contain one or more additives selected from the group consisting of cellulose ethers, slaked lime, mineral additives, low density aggregates, fibers, accelerators, thickeners, retarders, blowing agents, blowing agents, swelling agents, fillers, polyacrylates, dispersants, plasticizers, superabsorbents and stabilizers.
Таким образом, гипсовая композиция в соответствии с изобретением содержит, более предпочтительно состоит из, по меньшей мере 40,0 мас.%, более предпочтительно от 45,0 до 70,0 мас.%, особенно предпочтительно от 50,0 до 65,0 мас.% гипса, по меньшей мере 0,005 мас.%, более предпочтительно по меньшей мере 0,007 мас.%, особенно предпочтительно по меньшей мере 0,01 мас.% пенообразователя, который содержит по меньшей мере одну двойную соль альфа-сульфоновой жирной кислоты, по выбору, по меньшей мере 0,002 мас.%, более предпочтительно по меньшей мере 0,003 мас.%, особенно предпочтительно по меньшей мере 0,005 мас.% по меньшей мере одного котензида, по выбору по меньшей мере 0,0001 мас.%, преимущественно от 0,0005 мас.% до 0,2 мас.% по меньшей мере одного растворителя, от 20,0 до 65,0 мас.%, более предпочтительно от 30,0 до 55,0 мас.%, особенно предпочтительно от 35,0 до 50,0 мас.% воды и от 0,0 до 5,0 мас.%, более предпочтительно от 0,0001 до 3,0 мас.%, особенно предпочтительно от 0,001 до 1,0 мас.% добавок, в пересчете на общую массу гипсовой композиции.Thus, the gypsum composition according to the invention contains, more preferably consists of at least 40.0 wt.%, more preferably from 45.0 to 70.0 wt.%, particularly preferably from 50.0 to 65.0 wt.% gypsum, at least 0.005 wt.%, more preferably at least 0.007 wt.%, particularly preferably at least 0.01 wt.% foaming agent, which contains at least one double salt of alpha-sulfonic fatty acid, optionally at least 0.002% by weight, more preferably at least 0.003% by weight, particularly preferably at least 0.005% by weight of at least one cotenside, optionally at least 0.0001% by weight, preferably from 0.0005 wt.% to 0.2 wt.% of at least one solvent, from 20.0 to 65.0 wt.%, more preferably from 30.0 to 55.0 wt.%, especially preferably from 35, 0 to 50.0 wt% water and 0.0 to 5.0 wt%, more preferably 0.0001 to 3.0 wt%, particularly preferably 0.001 to 1.0 wt.% additives, in terms of the total weight of the gypsum composition.
В предпочтительном вариант осуществления гипсовая композиция в соответствии с изобретением содержит, более предпочтительно состоит из, по меньшей мере 40,0 мас.%, более предпочтительно от 45,0 до 70,0 мас.%, особенно предпочтительно от 50,0 до 65,0 мас.% гипса, по меньшей мере 0,002 мас.%, более предпочтительно по меньшей мере 0,003 мас.%, особенно предпочтительно по меньшей мере 0,005 мас.% пенообразователя, который содержит по меньшей мере одну двойную соль альфа-сульфоновой жирной кислоты, по выбору, по меньшей мере 0,001 мас.%, более предпочтительно по меньшей мере 0,002 мас.%, особенно предпочтительно по меньшей мере 0,003 мас.% по меньшей мере одного котензида, по выбору по меньшей мере 0,0001 мас.%, преимущественно от 0,0005 мас.% до 0,2 мас.% по меньшей мере одного растворителя от 20,0 до 65,0 мас.%, более предпочтительно от 30,0 до 55,0 мас.%, особенно предпочтительно от 35,0 до 50,0 мас.% воды и от 0,0 до 5,0 мас.%, более предпочтительно от 0,0001 до 3,0 мас.%, особенно предпочтительно от 0,001 до 1,0 мас.% добавок, в пересчете на общую массу гипсовой композиции.In a preferred embodiment, the gypsum composition according to the invention contains, more preferably consists of at least 40.0 wt.%, more preferably from 45.0 to 70.0 wt.%, particularly preferably from 50.0 to 65, 0 wt.% gypsum, at least 0.002 wt.%, more preferably at least 0.003 wt.%, particularly preferably at least 0.005 wt.% of a blowing agent that contains at least one double salt of alpha-sulfonic fatty acid, according to the choice of at least 0.001 wt.%, more preferably at least 0.002 wt.%, particularly preferably at least 0.003 wt.% of at least one cotenside, optionally at least 0.0001 wt.%, preferably from 0 .0005 wt.% to 0.2 wt.% of at least one solvent from 20.0 to 65.0 wt.%, more preferably from 30.0 to 55.0 wt.%, especially preferably from 35.0 to 50.0 wt.% water and from 0.0 to 5.0 wt.%, more preferably from 0.0001 to 3.0 wt.%, especially Pretty much 0.001 to 1.0% by weight of additives, based on the total weight of the gypsum composition.
Предпочтительно гипсовая композиция в соответствии с изобретением может содержать замедлители, ускорители и/или пластификаторы.Preferably, the gypsum composition according to the invention may contain retarders, accelerators and/or plasticizers.
В контексте настоящего изобретения понятие «замедлитель» относится к добавке, которая замедляет процесс отверждения гипсовой композиции. Неограничивающими примерами замедлителей являются винная кислота, лимонная кислота, а также их соли, глюконаты, гидролизат белка, поликонденсированная аминокислота, фосфаты, комплексообразующие агенты, гидроксикарбоновые кислоты, сахар иды, органофосфаты, а также их смеси.In the context of the present invention, the term "retarder" refers to an additive that slows down the curing process of the gypsum composition. Non-limiting examples of moderators are tartaric acid, citric acid, and their salts, gluconates, protein hydrolyzate, polycondensed amino acid, phosphates, complexing agents, hydroxycarboxylic acids, saccharides, organophosphates, and mixtures thereof.
В контексте настоящего изобретения понятие «ускоритель» относится к добавке, которая ускоряет процесс отверждения гипсовой композиции. Неограничивающими примерами ускорителей являются K2SO4, а также тонко измельченный дигидрат.In the context of the present invention, the term "accelerator" refers to an additive that accelerates the curing process of the gypsum composition. Non-limiting examples of accelerators are K 2 SO 4 and finely divided dihydrate.
В контексте настоящего изобретения понятие «пластификатор» относится к добавке, которая влияет на свойства текучести гипсовой композиции. Пригодными пластификаторами для гипсовой композиции в соответствии с изобретением являются пластификаторы на основе нафталинсульфоната, меламинсульфоната, лигнинсульфоната, кетоновой смолы, полиарилового эфира и поликарбоксилатного эфира.In the context of the present invention, the term "plasticizer" refers to an additive that affects the flow properties of the gypsum composition. Suitable plasticizers for the gypsum composition according to the invention are those based on naphthalene sulfonate, melamine sulfonate, lignin sulfonate, ketone gum, polyaryl ether and polycarboxylate ether.
Особенно предпочтительно гипсовая композиция в соответствии с изобретением содержит от 0,0001 до 1,0 мас.% замедлителя и/или от 0,01 до 2,0 мас.% пластификатора.Particularly preferably, the gypsum composition according to the invention contains from 0.0001 to 1.0% by weight of a retarder and/or from 0.01 to 2.0% by weight of a plasticizer.
Кроме того, гипсовая композиция в соответствии с изобретением содержит, более предпочтительно состоит из, по меньшей мере 40,0 мас.%, более предпочтительно от 45,0 до 70,0 мас.%, особенно предпочтительно от 50,0 до 65,0 мас.% гипса, по меньшей мере 0,005 мас.%, более предпочтительно по меньшей мере 0,007 мас.%, особенно предпочтительно по меньшей мере 0,01 мас.% пенообразователя, который содержит по меньшей мере одну двойную соль альфа-сульфоновой жирной кислоты, по выбору, по меньшей мере 0,002 мас.%, более предпочтительно по меньшей мере 0,003 мас.%, особенно предпочтительно по меньшей мере 0,005 мас.% по меньшей мере одного котензида, по выбору по меньшей мере 0,0001 мас.%, преимущественно от 0,0005 мас.% до 0,2 мас.% по меньшей мере одного растворителя и от 20,0 до 65,0 мас.%, более предпочтительно от 30,0 до 55,0 мас.%, особенно предпочтительно от 35,0 до 50,0 мас.% воды, от 0,0001 до 1,0 мас.% замедлителя и от 0,01 до 2,0 мас.% пластификатора и от 0,0 до 5,0 мас.%, более предпочтительно 0,0001 до 3,0 мас.%, особенно предпочтительно от 0,001 до 1,0 мас.% добавок, в пересчете на общую массу гипсовой композиции.In addition, the gypsum composition according to the invention contains, more preferably consists of at least 40.0 wt.%, more preferably from 45.0 to 70.0 wt.%, particularly preferably from 50.0 to 65.0 wt.% gypsum, at least 0.005 wt.%, more preferably at least 0.007 wt.%, particularly preferably at least 0.01 wt.% foaming agent, which contains at least one double salt of alpha-sulfonic fatty acid, optionally at least 0.002% by weight, more preferably at least 0.003% by weight, particularly preferably at least 0.005% by weight of at least one cotenside, optionally at least 0.0001% by weight, preferably from 0.0005 wt.% to 0.2 wt.% of at least one solvent and from 20.0 to 65.0 wt.%, more preferably from 30.0 to 55.0 wt.%, particularly preferably from 35, 0 to 50.0 wt.% water, 0.0001 to 1.0 wt.% retarder and 0.01 to 2.0 wt.% plasticizer and 0.0 to 5.0 wt.%, more preferred 0.0001 to 3.0% by weight, particularly preferably 0.001 to 1.0% by weight of additives, based on the total weight of the gypsum composition.
В предпочтительном варианте осуществления гипсовая композиция в соответствии с изобретением содержит, более предпочтительно состоит из по меньшей мере 40,0 мас.%, более предпочтительно от 45,0 до 70,0 мас.%, особенно предпочтительно от 50,0 до 65,0 мас.% гипса, по меньшей мере 0,002 мас.%, более предпочтительно по меньшей мере 0,003 мас.%, особенно предпочтительно по меньшей мере 0,005 мас.% пенообразователя, который содержит по меньшей мере одну двойную соль альфа-сульфоновой жирной кислоты, по выбору по меньшей мере 0,001 мас.%, более предпочтительно по меньшей мере 0,002 мас.%, особенно предпочтительно по меньшей мере 0,003 мас.% по меньшей мере одного котензида, по выбору по меньшей мере 0,0001 мас.%, преимущественно от 0,0005 мас.% до 0,2 мас.% по меньшей мере одного растворителя и от 20,0 до 65,0 мас.%, более предпочтительно от 30,0 до 55,0 мас.%, особенно предпочтительно 35,0 до 50,0 мас.% воды, от 0,0001 до 1,0 мас.% замедлителя и от 0,01 до 2,0 мас.% пластификатора и 0,0 до 5,0 мас.%, более предпочтительно от 0,0001 до 3,0 мас.%, особенно предпочтительно от 0,001 до 1,0 мас.% добавок, в пересчете на общую массу гипсовой композиции.In a preferred embodiment, the gypsum composition according to the invention contains, more preferably consists of at least 40.0 wt.%, more preferably from 45.0 to 70.0 wt.%, particularly preferably from 50.0 to 65.0 wt.% gypsum, at least 0.002 wt.%, more preferably at least 0.003 wt.%, particularly preferably at least 0.005 wt.% of a blowing agent which contains at least one alpha-sulfonic fatty acid double salt, optionally at least 0.001 wt.%, more preferably at least 0.002 wt.%, particularly preferably at least 0.003 wt.% of at least one cotenside, optionally at least 0.0001 wt.%, preferably from 0.0005 wt.% to 0.2 wt.% of at least one solvent and from 20.0 to 65.0 wt.%, more preferably from 30.0 to 55.0 wt.%, particularly preferably 35.0 to 50, 0 wt.% water, from 0.0001 to 1.0 wt.% retarder and from 0.01 to 2.0 wt.% plasticizer and 0.0 to 5, 0 wt.%, more preferably 0.0001 to 3.0 wt.%, particularly preferably 0.001 to 1.0 wt.% additives, based on the total weight of the gypsum composition.
Плотность во влажном состоянии предлагаемой в изобретении гипсовой композиции предпочтительно составляет менее чем 1400 кг/м3, более предпочтительно менее чем 1250 кг/м3, особенно предпочтительно менее чем 1100 кг/м3.The wet density of the gypsum composition according to the invention is preferably less than 1400 kg/m 3 , more preferably less than 1250 kg/m 3 , particularly preferably less than 1100 kg/m 3 .
Кроме того, настоящее изобретение относится к изделию, содержащему гипсовую композицию в соответствии с изобретением.In addition, the present invention relates to a product containing a gypsum composition in accordance with the invention.
Предпочтительно изделие содержит по меньшей мере 80 мас.%, более предпочтительно по меньшей мере 90 мас.%, особенно предпочтительно по меньшей мере 95 мас.% предлагаемой в изобретении гипсовой композиции.Preferably, the product contains at least 80% by weight, more preferably at least 90% by weight, particularly preferably at least 95% by weight of the gypsum composition according to the invention.
В предпочтительном варианте осуществления настоящего изобретения изделие состоит из предлагаемой в изобретении гипсовой композиции.In a preferred embodiment of the present invention, the article consists of the gypsum composition according to the invention.
Указанное выше изделие предпочтительно представляет собой отделочные гипсы, гипсовые штукатурные растворы, машинную гипсовую штукатурку, штукатурные гипсы, адгезионные гипсы, гипсы для заделки швов, шпаклевочные гипсы, изолирующие гипсы, высокопрочные гипсы, готовые гипсовые штукатурные смеси и мраморные гипсы, а также гипсосодержащие готовые строительные элементы, такие как гипсокартонные плиты, гипсоволокнистые плиты, гипсосодержащие стеновые панели, гипсовые панели с флисовым покрытием и гипсосодержащие формованные изделия.The above product is preferably a finishing gypsum, gypsum stucco, machine gypsum plaster, stucco gypsum, adhesive gypsum, grouting gypsum, filler gypsum, insulating gypsum, high-strength gypsum, ready-made gypsum plaster and marble gypsum, as well as gypsum-containing ready-made building materials. elements such as gypsum boards, gypsum fiber boards, gypsum-containing wall panels, fleece-coated gypsum boards, and gypsum-containing molded products.
Особенно предпочтительно изделие представляет собой гипсокартонную плиту.Particularly preferably, the product is a gypsum board.
Помимо этого, настоящее изобретение относится к способу получения водной гипсовой композиции, включающему в себя:In addition, the present invention relates to a method for producing an aqueous gypsum composition, including:
а) создание пены из пенообразователя, который содержит по меньшей мере одну двойную соль альфа-сульфоновой жирной кислоты,a) creating foam from a blowing agent that contains at least one double salt of an alpha-sulfonic fatty acid,
б) приготовление композиции, содержащей воду, гипс и при необходимости добавки,b) preparation of a composition containing water, gypsum and, if necessary, additives,
в) воздействие срезывающих сил на полученную в стадии б) композицию с добавлением пены из стадии а),c) the effect of shear forces on the composition obtained in stage b) with the addition of foam from stage a),
при этом гипс имеет долю переработанного гипса по меньшей мере 0,5 мас.%, в пересчете на общую долю гипса в композиции.wherein the gypsum has a recycled gypsum content of at least 0.5% by weight, based on the total gypsum content of the composition.
Согласно стадии а) предлагаемого в изобретении способа изготовленную заранее пену получают из пенообразователя, который содержит по меньшей мере одну двойную соль альфа-сульфоновой жирной кислоты, чтобы уменьшить вес изделия из гипса. Пену изготавливают из смеси, содержащей пенообразователь, воздух и воду с использованием подходящего генератора пены. Способы изготовления пены для гипсовой композиции известны специалистам в данной области.According to step a) of the process according to the invention, a prefabricated foam is obtained from a blowing agent which contains at least one alpha-sulfonic fatty acid double salt in order to reduce the weight of the gypsum product. Foam is made from a mixture containing a blowing agent, air and water using a suitable foam generator. Methods for making foam for a gypsum composition are known to those skilled in the art.
Смесь, из которой изготовлена пена, предпочтительно также содержит по меньшей мере один растворитель. Предпочтительно, содержит смесь, из которой изготовлена пена содержит от 0,5 мас.% до 30,0 мас.% по меньшей мере одного растворителя, в пересчете на общую массу пены.The mixture from which the foam is made preferably also contains at least one solvent. Preferably, it contains a mixture from which the foam is made contains from 0.5 wt.% to 30.0 wt.% of at least one solvent, based on the total weight of the foam.
Растворитель предпочтительно выбирают из группы, включающей в себя гексиленгликоль, (2-метил-2,4-пентандиол), этанол, пропаналь, н-пропиловый спирт, 1-пентанол, 2-пентанол, 3-пентанол, 2-метил-1-бутанол, 2-метил-2-бутанол, 3-метил-1-бутанол, 3-метил-2-бутанол, 2,2-диметил-1-пропанол, н-пропиловый эфир уксусной кислоты, н-бутиловый эфир уксусной кислоты, 1-пентилацетат, 2-пентилацетат, 3-пентилацетат, изопентилацетат, 1,1-диметилпропилацетат, 2-метилбутилацетат, 2-этилгексилацетат, 2-бутооксиэтанол, 2-(2-бутооксиэтокси)-этанол, монобутиловый эфир триэтиленгликоля, 3,6,9,12-тетраоксагексадекан-1-ол, 2-гексокси-1-этанол, 2-(2-гексилоксиэтокси)этанол, 1-метокси-2-пропанол, метоксипропоксипропанол, 1-бутоокси-2-пропанол, бутиловый эфир ди(пропиленгликоля), бутиловый эфир три(пропиленгликоля), 2-бутооксиэтилацетат, 2-(2-бутооксиэтокси)этилацетат, 1-метокси-2-пропилацетат и их смеси.The solvent is preferably selected from the group consisting of hexylene glycol, (2-methyl-2,4-pentanediol), ethanol, propanal, n-propyl alcohol, 1-pentanol, 2-pentanol, 3-pentanol, 2-methyl-1- butanol, 2-methyl-2-butanol, 3-methyl-1-butanol, 3-methyl-2-butanol, 2,2-dimethyl-1-propanol, acetic acid n-propyl ester, acetic acid n-butyl ester, 1-pentyl acetate, 2-pentyl acetate, 3-pentyl acetate, isopentyl acetate, 1,1-dimethylpropyl acetate, 2-methylbutyl acetate, 2-ethylhexyl acetate, 2-butoxyethanol, 2-(2-butoxyethoxy)-ethanol, triethylene glycol monobutyl ether, 3.6, 9,12-tetraoxahexadecan-1-ol, 2-hexoxy-1-ethanol, 2-(2-hexyloxyethoxy)ethanol, 1-methoxy-2-propanol, methoxypropoxypropanol, 1-butooxy-2-propanol, di(propylene glycol) butyl ether ), tri(propylene glycol) butyl ether, 2-butoxyethyl acetate, 2-(2-butoxyethoxy)ethyl acetate, 1-methoxy-2-propyl acetate, and mixtures thereof.
Пенообразователь, который содержит по меньшей мере одну двойную соль альфа-сульфоновой жирной кислоты, предпочтительно представляет собой по меньшей мере одно из вышеупомянутых соединений.The blowing agent which contains at least one alpha-sulfonic fatty acid double salt is preferably at least one of the above compounds.
В соответствии со стадией б) изготавливают композицию, содержащую воду, гипс и по выбору одну или несколько из приведенных выше добавок. Гипс содержит долю переработанного гипса по меньшей мере 0,5 мас.%, более предпочтительно по меньшей мере 2,0 мас.%, особенно предпочтительно по меньшей мере 5,0 мас.%, в пересчете на общую долю гипса в композиции.According to step b), a composition is prepared containing water, gypsum and, optionally, one or more of the above additives. The gypsum contains a recycled gypsum content of at least 0.5% by weight, more preferably at least 2.0% by weight, particularly preferably at least 5.0% by weight, based on the total gypsum content of the composition.
Указанный переработанный гипс предпочтительно представляет собой содержащий силоксан переработанный гипс, как описано выше.Said processed gypsum is preferably a siloxane-containing processed gypsum as described above.
Вследствие воздействия срезывающих сил на полученную в стадии б) композицию с добавлением пены из стадии а) получают гипсовую композицию в соответствии с изобретением.Due to the effect of shear forces on the composition obtained in step b), with the addition of foam from step a), a gypsum composition is obtained in accordance with the invention.
Кроме того, настоящее изобретение относится к применению пенообразователя, который содержит по меньшей мере одну двойную соль альфа-сульфоновой жирной кислоты, для снижения плотности во влажном состоянии водной гипсовой композиции, которая имеет долю переработанного гипса по меньшей мере 0,5 мас.%, в пересчете на общую долю гипса в композиции.In addition, the present invention relates to the use of a blowing agent which contains at least one alpha-sulfonic fatty acid double salt for reducing the wet density of an aqueous gypsum composition which has a recycled gypsum content of at least 0.5% by weight, in in terms of the total proportion of gypsum in the composition.
В особенности предпочтительно, чтобы по меньшей мере одна двойная соль альфа-сульфоновой жирной кислоты представляла собой одно из приведенных выше соединений.It is particularly preferred that at least one alpha-sulfonic fatty acid double salt is one of the above compounds.
Нижеследующие примеры предназначены для более подробного пояснения изобретения.The following examples are intended to explain the invention in more detail.
ПримерыExamples
1) Способы1) Ways
Плотность во влажном состоянииWet Density
Чтобы определить плотность во влажном состоянии гипсовых композиций определяли соотношение массы и объема, выливая соответствующую композицию в химический стакан с известным объемом, а затем взвешивая его.To determine the wet density of gypsum compositions, the mass to volume ratio was determined by pouring the appropriate composition into a known volume beaker and then weighing it.
Плотность пеныFoam Density
Чтобы определить плотность пены определяли соотношение массы и объема, выливая соответствующую пену в химический стакан с известным объемом, а затем взвешивая его.To determine the density of a foam, the mass to volume ratio was determined by pouring the appropriate foam into a beaker of known volume and then weighing it.
2) Получение переработанного гипса2) Obtaining recycled gypsum
Для приготовления гипсового теста 300 г бета-полугидрата (полученного в результате удаления серы из дымовых газов) помещали в 201,0 г воды, которая содержала 3,0 г силоксана (Silres BS 94, от фирмы Wacker Chemie) и оставляли для замачивания на 15 секунд. Затем смесь сдвигали в течение 30 секунд при 285 об./мин. и выливали в форму. Через 15 минут образец для испытаний извлекали из формы и подвергали термической обработке в течение одного часа при 150°С в атмосфере насыщенного пара. После этого испытуемые образцы хранили при 40°С до тех пор, пока масса не стала постоянной.For the preparation of gypsum dough, 300 g of beta-hemihydrate (obtained from the removal of sulfur from flue gases) was placed in 201.0 g of water, which contained 3.0 g of siloxane (Silres BS 94, from Wacker Chemie) and allowed to soak for 15 seconds. The mixture was then sheared for 30 seconds at 285 rpm. and poured into a mold. After 15 minutes, the test piece was removed from the mold and subjected to heat treatment for one hour at 150° C. in a saturated steam atmosphere. Thereafter, the test specimens were stored at 40° C. until the weight became constant.
Для дальнейшей обработки образцы измельчали с помощью шаровой мельницы до d50 приблизительно 10 мкм и затем прокаливали в течение 5 часов при 150°С. После охлаждения до комнатной температуры переработанный гипс можно было использовать для испытаний.For further processing, the samples were ground using a ball mill to d 50 approximately 10 μm and then calcined for 5 hours at 150°C. After cooling to room temperature, the recycled gypsum could be used for testing.
3) Композиции на основе тензидов сульфатов простых жирных алкиловых эфиров3) Compositions based on tensides sulfates of simple fatty alkyl ethers
Сначала изготавливали пену на основе сульфата простых жирных алкиловых эфиров.First, a fatty alkyl ether sulfate foam was produced.
Для этой цели 0,40%-ый раствор тензидов (Vinapor GYP 2680, BASF) был преобразован в пену с использованием генератора пены на основе системы ротор/статор путем добавления сжатого воздуха. Установленная плотность пены составляла 75 г/л.For this purpose, a 0.40% surfactant solution (Vinapor GYP 2680, BASF) was converted to foam using a rotor/stator based foam generator by adding compressed air. The determined density of the foam was 75 g/l.
Эталонная смесь R1Reference mixture R1
Для приготовления гипсового теста 350 г бета-полугидрата (полученного в результате удаления серы из дымовых газов) гомогенизировали с 0,035 г замедлителя (Plastretard) и 3,3 г тонкоизмельченного дигидрата и затем помещали в 234,2 г воды, которая содержала 1,05 г бетанафталинового пластификатора, и оставляли для замачивания на 15 секунд. Затем смесь сдвигали в течение 30 секунд при 1600 об./мин. В течение этого времени добавляли пену на основе сульфата простого жирного алкилового эфира (18,2 г с плотностью 75 г/л). Полученная из этого плотность в свежем виде эталонной смеси 1 составляла 1050 кг/м3.To prepare a gypsum paste, 350 g of beta-hemihydrate (obtained from the removal of sulfur from flue gases) was homogenized with 0.035 g of moderator (Plastretard) and 3.3 g of finely divided dihydrate and then placed in 234.2 g of water, which contained 1.05 g betanapthalene plasticizer, and left to soak for 15 seconds. The mixture was then sheared for 30 seconds at 1600 rpm. During this time, an alkyl fatty ether sulfate foam (18.2 g with a density of 75 g/l) was added. The resulting fresh density of reference mixture 1 was 1050 kg/m 3 .
Эталонная смесь R2Reference mixture R2
Получение эталонной смеси R2 осуществляли аналогично эталонной смеси R1 с той разницей, что 5% бета-полугидрат заменяли на содержащий силоксан переработанный гипс. Плотность во влажном состоянии эталонной смеси R2 увеличилась до 1380 кг/м3.The preparation of the reference mixture R2 was carried out similarly to the reference mixture R1, with the difference that the 5% beta-hemihydrate was replaced with siloxane-containing recycled gypsum. The wet density of the reference mixture R2 increased to 1380 kg/m 3 .
4) Композиции на основе тензидов двойной соли альфа-сульфоновой жирной кислоты4) Compositions based on tensides of double salt of alpha-sulfonic fatty acid
Сначала изготавливали пену на основе двойной соли альфа-сульфоновой жирной кислоты.First, an alpha-sulfonic fatty acid double salt foam was made.
Для этой цели 0,40%-ый раствор тензидов на основе Na двойной соли С12/14-альфа-сульфоновой жирной кислоты был преобразован в пену с использованием генератора пены на основе системы ротор/статор путем добавления сжатого воздуха. Установленная плотность пены составляла 75 г/л.For this purpose, a 0.40% Na surfactant solution of C12/14-alpha-sulfonic fatty acid double salt Na was converted to foam using a rotor/stator foam generator by the addition of compressed air. The determined density of the foam was 75 g/l.
Эталонная смесь R3Reference mixture R3
Для приготовления гипсового теста 350 г бета-полугидрата (полученного в результате удаления серы из дымовых газов) гомогенизировали с 0,035 г замедлителя (Plastretard) и 3,3 г тонкоизмельченного дигидрата и затем помещали в 234,2 г воды, которая содержала 1,05 г бетанафталинового пластификатора, и оставляли для замачивания на 15 секунд. Затем смесь сдвигали в течение 30 секунд при 1600 об./мин. В течение этого времени добавляли пену на основе двойной соли альфа-сульфоновой жирной кислоты (18,2 г с плотностью 75 г/л). Полученная из этого плотность в свежем виде эталонной смеси 1 составляла 1110 кг/м3.To prepare a gypsum paste, 350 g of beta-hemihydrate (obtained from the removal of sulfur from flue gases) was homogenized with 0.035 g of moderator (Plastretard) and 3.3 g of finely divided dihydrate and then placed in 234.2 g of water, which contained 1.05 g betanapthalene plasticizer, and left to soak for 15 seconds. The mixture was then sheared for 30 seconds at 1600 rpm. During this time, an alpha-sulfonic fatty acid double salt foam (18.2 g with a density of 75 g/l) was added. The resulting fresh density of reference mixture 1 was 1110 kg/m 3 .
Пример Е1 (в соответствии с изобретением)Example E1 (according to the invention)
Получение Примера Е1 осуществляли аналогично эталонной смеси R3 с той разницей, что 5% бета-полугидрат заменяли на содержащий силоксан переработанный гипс. Плотность во влажном состоянии Примера в соответствии с изобретением увеличилась только до 1170 кг/м3.The preparation of Example E1 was carried out similarly to the reference mixture R3, with the difference that the 5% beta-hemihydrate was replaced with siloxane-containing recycled gypsum. The wet density of the Example according to the invention only increased to 1170 kg/m 3 .
Композиции и свойства эталонных смесей и Примера в соответствии с изобретением представлены в Таблице 1.The compositions and properties of the reference mixtures and Example according to the invention are presented in Table 1.
Результаты показывают, что содержащие переработанный гипс композиции при применении пен на основе двойной соли альфа-сульфоновой жирной кислоты имеют лишь немного более высокую плотность во влажном состоянии, чем эталонные смеси, которые не содержат переработанный гипс, в то время как в случае содержащих переработанный гипс композиций с пенами на основе сульфатов простых жирных алкиловых эфиров наблюдают отчетливое увеличение плотности во влажном состоянии.The results show that recycled gypsum-containing compositions using alpha-sulfonic fatty acid double salt foams have only slightly higher wet densities than reference mixtures that do not contain recycled gypsum, while recycled gypsum-containing compositions with foams based on fatty alkyl ether sulfates, a distinct increase in wet density is observed.
Claims (24)