RU2678316C1 - Composition for electrical insulation of isotropic electrical steel - Google Patents
Composition for electrical insulation of isotropic electrical steel Download PDFInfo
- Publication number
- RU2678316C1 RU2678316C1 RU2018105833A RU2018105833A RU2678316C1 RU 2678316 C1 RU2678316 C1 RU 2678316C1 RU 2018105833 A RU2018105833 A RU 2018105833A RU 2018105833 A RU2018105833 A RU 2018105833A RU 2678316 C1 RU2678316 C1 RU 2678316C1
- Authority
- RU
- Russia
- Prior art keywords
- composition
- electrical
- isotropic
- polyvinyl alcohol
- electrical insulation
- Prior art date
Abstract
Description
Изобретение относится к области электроизоляционных композиций для изотропной электротехнической стали.The invention relates to the field of electrical insulating compositions for isotropic electrical steel.
Известен водорастворимый состав для электроизоляционных покрытий электротехнической стали [1], RU 2121178 С1, включающий 46-47%-ный бутадиен-стирольный латекс, ортофосфорную кислоту, оксиэтилированные алкилфенолы и воду, отличающийся тем, что он содержит дополнительно оксид магния, гидроксид алюминия, борную кислоту и жидкие комплексные удобрения при следующем соотношении компонентов, мас. %:Known water-soluble composition for electrical insulation coatings of electrical steel [1], RU 2121178 C1, including 46-47% styrene-butadiene latex, phosphoric acid, ethoxylated alkyl phenols and water, characterized in that it additionally contains magnesium oxide, aluminum hydroxide, boric acid and liquid complex fertilizers in the following ratio of components, wt. %:
Ортофосфорная кислота - 25,0-27,5Phosphoric acid - 25.0-27.5
Оксиэтилированные алкилфенолы - 2,4-4,0Oxyethylated alkyl phenols - 2.4-4.0
Оксид магния - 2,0-2,4Magnesium Oxide - 2.0-2.4
Гидроксид алюминия - 1,2-1,6Aluminum hydroxide - 1.2-1.6
Борная кислота - 0,14-0,25Boric acid - 0.14-0.25
Жидкие комплексные удобрения - 1,0-3,0Liquid complex fertilizers - 1.0-3.0
Вода - Остальное.Water - The rest.
Недостатком данного состава являются слипаемость обработанных листов стали в рулоне, сложность и высокая себестоимость.The disadvantage of this structure is the stickiness of the processed steel sheets in a roll, complexity and high cost.
Известен состав [2], RU 2225650 С2, мас. %:The known composition [2], RU 2225650 C2, wt. %:
Поливиниловый спирт 50-80Polyvinyl alcohol 50-80
Ортофосфорная кислота 15-22Phosphoric Acid 15-22
Мочевина 3-8Urea 3-8
Этиловый спирт 50-80Ethyl alcohol 50-80
Поверхностно-активное вещество 5-8Surfactant 5-8
Щелочно-алюмо-боро-силикатное стекло 70-90Alkaline-aluminum-boron-silicate glass 70-90
Оксид хрома (III) 5-6.Chromium (III) oxide 5-6.
Недостатком патента является недостаточна водостойкость состава и использование пожароопасного растворителя этилового спирта.The disadvantage of the patent is the lack of water resistance of the composition and the use of a flammable solvent of ethyl alcohol.
Наиболее близким к заявляемому изобретению является композиция [3], RU 2161341 С1.Closest to the claimed invention is a composition [3], RU 2161341 C1.
Композиция для создания термически устойчивого электроизоляционного покрытия на электротехнических сталях, содержащая поливиниловый спирт, ортофосфорную кислоту и воду, отличающаяся тем, что дополнительно содержит мочевину, тиомочевину, этиловый спирт, глицерин, фталевый ангидрид, борную кислоту и поверхностно-активное вещество, полученное реакцией, 1,1,2,2,3,3,4,4,5,5,6,6-додекафтор-1Н-гептан-7-ола с пятиокисью фосфора при следующем содержании компонентов, г/л:Composition for creating a thermally stable insulating coating on electrical steels, containing polyvinyl alcohol, phosphoric acid and water, characterized in that it further comprises urea, thiourea, ethyl alcohol, glycerin, phthalic anhydride, boric acid and a surface-active substance obtained by the reaction, 1 , 1,2,2,3,3,4,4,5,5,6,6-dodecafluoro-1H-heptane-7-ol with phosphorus pentoxide in the following components, g / l:
Поливиниловый спирт - 50,0-80,0Polyvinyl alcohol - 50.0-80.0
Ортофосфорная кислота - 12,0-15,0Phosphoric acid - 12.0-15.0
Мочевина - 3,0-15,0Urea - 3.0-15.0
Тиомочевина - 0-6,0Thiourea - 0-6.0
Глицерин - 0-20,0Glycerin - 0-20.0
Этиловый спирт - 10,0-50,0Ethyl alcohol - 10.0-50.0
Фталевый ангидрид - 0-6,0Phthalic Anhydride - 0-6.0
Борная кислота - 0-5,0Boric acid - 0-5.0
Поверхностно-активное вещество - 3,0-6,0Surfactant - 3.0-6.0
Вода - До общего объема в 1 литр.Water - Up to a total volume of 1 liter.
Состав сложен и сохраняет недостатки связанные с использованием спирта.The composition is complex and retains the disadvantages associated with the use of alcohol.
Задачей данного изобретения является создание электроизоляционного состава с повышенной влагостойкостью, электрическим сопротивлением, с не слеживаемостью в рулонах, пожаростойкостью за счет исключения органических растворителей.The objective of the invention is to provide an insulating composition with increased moisture resistance, electrical resistance, non-caking in rolls, fire resistance by eliminating organic solvents.
Поставленная задача достигается тем, что на листовую электротехническую изотропную сталь наносят состав, содержащий, мас. %The problem is achieved in that on a sheet of electrical isotropic steel is applied a composition containing, by weight. %
Ортофосфорная кислота - 12,4-17,9Phosphoric acid - 12.4-17.9
Оксид магния - 0,33-0,83Magnesium Oxide - 0.33-0.83
Гидроксид алюминия - 0,29-0,87Aluminum hydroxide - 0.29-0.87
ПАВ - С9Н19С6Н4O(С2Н4O)nН - 0,2-1,2Surfactant - С 9 Н 19 С 6 Н 4 O (С 2 Н 4 O) nН - 0.2-1.2
Дипропилен-гликолевый моно n-бутиловый эфир - 0,01-0,3Dipropylene glycol mono n-butyl ether - 0.01-0.3
Поливиниловый спирт - 4-5Polyvinyl alcohol - 4-5
Химочищенная вода - Остальное.Chemically Purified Water - Else.
Состав готовят следующим образом.The composition is prepared as follows.
1 Готовят раствор А:1 Prepare solution A:
Растворяют в водном растворе фосфат алюминия и магния. В качестве сырья используют гидроокись алюминия и каустический магнезит, являющийся отходом производства металлургической окиси магния. В полученную суспензию вв6дятгпрй перемешивании фосфорную кислоту со скоростью 60 л/мин. При приготовлении раствор разогревается до 70-80°С, выдерживается при этой температуре 3-4 часа и фильтруется.Dissolve aluminum and magnesium phosphate in an aqueous solution. As raw materials, aluminum hydroxide and caustic magnesite, which is a waste product of the production of metallurgical magnesium oxide, are used. Phosphoric acid at a speed of 60 l / min is added to the resulting suspension of vv6dyat with stirring. During preparation, the solution is heated to 70-80 ° C, maintained at this temperature for 3-4 hours and filtered.
2 Готовят раствор Б:2 Prepare solution B:
Растворяют в водном растворе поливиниловый спирт, перемешивают в течение 4 часов для набухания, добавляют смесь полиэтиленгликолевых эфиров моноалкилфенолов состава С9Н19С6Н4O(С2Н4O)nН. Раствор нагревают до температуры не менее 92°С, перемешивают до полного растворения поливинилового спирта.Polyvinyl alcohol is dissolved in an aqueous solution, stirred for 4 hours to swell, a mixture of polyethylene glycol ethers of monoalkylphenols of the composition C 9 H 19 C 6 H 4 O (C 2 H 4 O) nH is added. The solution is heated to a temperature of at least 92 ° C, stirred until the polyvinyl alcohol is completely dissolved.
3 Смешивают два раствора в соотношении: раствор А: раствор Б=1:2,3, добавляя в конце Дипропилен-гликолевый моно n-бутиловый эфир в заданном количестве.3 Mix two solutions in the ratio: solution A: solution B = 1: 2.3, adding at the end dipropylene-glycol mono n-butyl ether in a given amount.
Примеры:Examples:
Во всех примерах образцы электротехнической изотропной стали обрабатывались в течение 5 с при температуре 20±5°С. Излишки раствора удалялись отжимом гуммированными валками. Покрытия подвергались термообработке при температуре 450-600°С в течение 30-60 с.In all examples, samples of electrical isotropic steel were processed for 5 s at a temperature of 20 ± 5 ° C. Excess solution was removed by squeezing with gummed rolls. The coatings were heat treated at a temperature of 450-600 ° C for 30-60 s.
Физико-механические свойства покрытий определялись следующими показателями: коэффициент сопротивления при заданной толщине по ГОСТ 12119.8-98.Physico-mechanical properties of the coatings were determined by the following indicators: resistance coefficient at a given thickness according to GOST 12119.8-98.
В таблице приведены характеристики раствора, физико-механические свойства покрытий, полученных в предлагаемых растворах и по прототипу.The table shows the characteristics of the solution, physico-mechanical properties of the coatings obtained in the proposed solutions and the prototype.
При анализе полученных экспериментальных данных видно, что при содержании ПВС, ортофосфорной кислоты, оксида магния, гидроксида алюминия выше и ниже заявленной концентрации состав обладает более низкими физико-механическими характеристиками. Также в заявленном составе добавка дипропилен-гликолевого моно n-бутилового эфира позволяет улучшить смачиваемость при нанесении и стабильность состава в 1,5 раза.An analysis of the obtained experimental data shows that when the content of PVA, phosphoric acid, magnesium oxide, aluminum hydroxide is higher and lower than the declared concentration, the composition has lower physicomechanical characteristics. Also in the claimed composition, the addition of dipropylene-glycol mono n-butyl ether can improve the wettability during application and the stability of the composition by 1.5 times.
ЛИТЕРАТУРАLITERATURE
1. Патент RU 2121178 по заявке №9696123510, 16.12.1996.1. Patent RU 2121178 by application No. 9696123510, 16.16.1996.
2. Патент RU 2225650 по заявке №2002104650/09, 20.02.2002.2. Patent RU 2225650 according to the application No. 2002104650/09, 02.20.2002.
3. Патент RU 2161341 по заявке №99113084/09, 16.06.1999.3. Patent RU 2161341 by application No. 99113084/09, 06.16.1999.
4. ГОСТ 12119.8-98 «Сталь электротехническая. Методы определения магнитных и электрических свойств. Метод измерения коэффициента сопротивления изоляционного покрытия».4. GOST 12119.8-98 "Electrical steel. Methods for determining magnetic and electrical properties. Method for measuring the resistance coefficient of an insulating coating.
Claims (8)