RU2674428C2 - Mold-resistant paper and gypsum panel, antimicrobial paper coating and related methods - Google Patents
Mold-resistant paper and gypsum panel, antimicrobial paper coating and related methods Download PDFInfo
- Publication number
- RU2674428C2 RU2674428C2 RU2016104073A RU2016104073A RU2674428C2 RU 2674428 C2 RU2674428 C2 RU 2674428C2 RU 2016104073 A RU2016104073 A RU 2016104073A RU 2016104073 A RU2016104073 A RU 2016104073A RU 2674428 C2 RU2674428 C2 RU 2674428C2
- Authority
- RU
- Russia
- Prior art keywords
- paper
- fungicide
- antimicrobial coating
- weight
- group
- Prior art date
Abstract
Description
ПЕРЕКРЕСТНЫЕ ССЫЛКИ НА РОДСТВЕННЫЕ ЗАЯВКИCROSS RELATIONS TO RELATED APPLICATIONS
Настоящая заявка на патент испрашивает приоритет на основании заявки на патент США №14/095499, поданной 3 декабря 2013 года, и предварительной заявки на патент США №61/858698, поданной 26 июля 2013 года, которые в полном объеме включены в настоящий документ посредством ссылки.This patent application claims priority based on US patent application No. 14/095499, filed December 3, 2013, and provisional patent application US No. 61/858698, filed July 26, 2013, which are fully incorporated herein by reference .
ОБЛАСТЬ ТЕХНИКИFIELD OF TECHNOLOGY
Настоящее изобретение относится к бумаге, стойкой к микробному росту. Также предложена композиция для нанесения противомикробного покрытия. Кроме того, изобретение относится к способам изготовления неплесневеющей бумаги и гипсовых панелей.The present invention relates to paper resistant to microbial growth. Also provided is a composition for applying an antimicrobial coating. In addition, the invention relates to methods for the manufacture of non-moldy paper and gypsum panels.
УРОВЕНЬ ТЕХНИКИBACKGROUND
Гипсовые плиты, также известные как гипсовые панели, гипсокартон и обшивочные листы, являются популярными строительными материалами со свойствами, необходимыми для применения в закрытых помещениях. Изготовление гипсовых плит включает получение гипсового сердечника из строительного раствора, содержащего полугидрат сульфата кальция, воду и добавки. Указанный строительный раствор непрерывно подают на конвейер и зажимают между двух обшивочных листов бумаги. Один лист бумаги называют облицовочным листом и другой лист бумаги называют задним листом. Каждый из двух листов бумаги имеет две стороны или поверхности. Одна сторона представляет собой обратную сторону или сторону соединения, находящуюся в контакте с гипсовым строительным раствором, и известна как «нижняя или обратная сторона бумаги». Другая сторона каждого бумажного листа, которая не находится в контакте с гипсовым строительным раствором, известна как «верхняя или лицевая сторона». Полученную в результате сборную конструкцию формуют в виде панели. Полугидрат сульфата кальция реагирует с водой с превращением полугидрата в матрицу взаимосвязанных кристаллов дигидрата сульфата кальция, что приводит к схватыванию и отверждению строительного раствора. В результате получают непрерывную ленту затвердевшего материала. Такая непрерывная лента движется на конвейере до тех пор, пока обожженный гипс не схватится в достаточной степени, чтобы выдержать обработку и удаление с конвейера. Далее непрерывную гипсовую ленту нарезают на куски подходящей длины и затем излишек воды, который не является необходимым для гидратации обожженного гипса, испаряют из гипсовой панели в обжиговой печи, в которой панель подвергают воздействию высокой температуры.Gypsum boards, also known as gypsum panels, drywall and cladding sheets, are popular building materials with the properties needed for indoor use. The manufacture of gypsum boards includes the production of a gypsum core from a mortar containing calcium sulfate hemihydrate, water and additives. The specified mortar is continuously fed to the conveyor and clamped between two paper sheets. One sheet of paper is called a facing sheet and another sheet of paper is called a back sheet. Each of the two sheets of paper has two sides or surfaces. One side is the back or joint side in contact with the gypsum mortar, and is known as the “bottom or back side of the paper”. The other side of each paper sheet that is not in contact with the gypsum mortar is known as the “top or front side”. The resulting prefabricated structure is molded in the form of a panel. Calcium sulfate hemihydrate reacts with water to convert the hemihydrate into a matrix of interconnected crystals of calcium sulfate dihydrate, which leads to the setting and curing of the mortar. The result is a continuous tape of hardened material. Such a continuous belt moves on the conveyor until the calcined gypsum has grasped enough to withstand processing and removal from the conveyor. Next, a continuous gypsum tape is cut into pieces of suitable length and then excess water, which is not necessary for hydration of the calcined gypsum, is evaporated from the gypsum panel in a kiln in which the panel is exposed to high temperature.
Микробный рост предпочитает среды, в которых споры находят влагу и питательные вещества, необходимые для метаболизма. Водяной пар и споры являются неизбежными компонентами в окружающих средах, в которых применяют гипсовые панели. Помимо влаги, которая присутствует в окружающей среде, продукты, применяемые при строительстве внутренних помещений, иногда соприкасаются с водой вследствие просачивания, протекающих крыш или труб, затопления, конденсации и т.п. Такие воздействия происходят при отсутствии каких-либо нарушений при изготовлении или применении гипсовых плит.Microbial growth prefers environments in which spores find moisture and nutrients needed for metabolism. Water vapor and spores are unavoidable components in environments in which gypsum panels are used. In addition to the moisture that is present in the environment, products used in the construction of interior spaces sometimes come in contact with water due to seepage, leaking roofs or pipes, flooding, condensation, etc. Such effects occur in the absence of any violations in the manufacture or use of gypsum boards.
Обшивочные бумажные листы для гипсовых панелей, также известные как облицовочные материалы, обшивочный материал, бумажные облицовочные материалы и т.п., получают с применением технологии бумажного производства, которая начинается с получения жидкой массы волокон, состоящей из бумажных отходов, химических добавок и воды. Бумажные отходы отделяют от загрязняющих веществ, превращают в волокнистую массу, загущают, очищают и затем дренируют через сито с получением мата из волокон произвольной ориентации. Дополнительное количество воды удаляют путем прессования мата или применения отсасывания. Неформально, «мокрая часть» относится к процессу изготовления бумаги перед удалением воды из жидкой массы с последующим формованием бумаги и прессованием. Стадию указанного процесса после прессования с получением рулона называют «сухой частью». После дренирования и прессования указанный мат перемещают через секцию сушильного устройства, где испаряют оставшуюся воду. Затем лист бумаги подвергают обработке в каландре, в котором происходит увеличение содержание влаги (4-9%) и полировка поверхности волокнистого листа.Cladding paper sheets for gypsum panels, also known as cladding materials, cladding material, paper cladding materials and the like, are obtained using papermaking technology, which begins with a liquid mass of fibers consisting of paper waste, chemical additives and water. Paper waste is separated from contaminants, converted into pulp, thickened, cleaned and then drained through a sieve to obtain a mat of fibers of arbitrary orientation. Additional water is removed by pressing the mat or applying suction. Informally, the “wet part” refers to the process of making paper before removing water from the liquid mass, followed by paper shaping and pressing. The step of the process after pressing to form a roll is called the “dry portion”. After drainage and pressing, said mat is moved through a section of the drying device where the remaining water is evaporated. Then the sheet of paper is subjected to processing in a calender, in which there is an increase in the moisture content (4-9%) and polishing the surface of the fibrous sheet.
Были предприняты попытки изготовить гипсовые плиты, стойкие к микробному росту, путем введения биоцида, такого как соль пиритиона, в гипсовый сердечник, облицовочные материалы или и туда и сюда, как описано в патенте США №6893752, озаглавленном «Mold Resistant Gypsum Panel and Method of Making Same», включенном в настоящий документ посредством ссылки. Однако было доказано, что получение неплесневеющей бумаги, подходящей для применения в гипсовой панели, является трудным и дорогостоящим процессом. В способах, известных ранее в данной области техники, водорастворимый или диспергируемый биоцид добавляют во время мокрой части процесса изготовления бумаги. В этом случае основная масса биоцида терялась во время стадии формования, при которой воду дренируют и выдавливают из бумажного мата. Оставшийся биоцид дополнительно разлагается на стадии в сушильном устройстве на бумажной фабрике и в печи для обжига плит. Таким образом, остается постоянная потребность в получении бумаги, которая удерживает фунгицид в количестве, достаточном для подавления микробного роста.Attempts have been made to make microbial growth resistant gypsum boards by introducing a biocide, such as a pyrithione salt, into a gypsum core, cladding materials, or both, as described in US Pat. No. 6,893,752, entitled “Mold Resistant Gypsum Panel and Method of Making Same ”, incorporated herein by reference. However, it has been proven that obtaining non-moldy paper suitable for use in gypsum panels is a difficult and expensive process. In methods previously known in the art, a water-soluble or dispersible biocide is added during the wet part of the papermaking process. In this case, the bulk of the biocide was lost during the molding step, in which water was drained and squeezed out of the paper mat. The remaining biocide is further decomposed in a stage in a drying device in a paper mill and in a stove for burning plates. Thus, there remains a constant need for paper that retains the fungicide in an amount sufficient to inhibit microbial growth.
КРАТКОЕ ОПИСАНИЕ ИЗОБРЕТЕНИЯSUMMARY OF THE INVENTION
Предложена неплесневеющая бумага, которая удерживает активный фунгицид в количестве, достаточном для подавления роста микробов, таких как, например, плесень и милдью. Предложен способ получения неплесневеющей бумаги с противомикробным покрытием, а также способ нанесения покрытия на лист бумаги. Кроме того, описана гипсовая панель с улучшенными противомикробными свойствами и способ изготовления такой панели.A non-moldable paper is proposed which retains an active fungicide in an amount sufficient to inhibit the growth of microbes, such as, for example, mold and mildew. A method for producing non-moldable paper with an antimicrobial coating is proposed, as well as a method for coating a sheet of paper. In addition, a gypsum panel with improved antimicrobial properties and a method for manufacturing such a panel are described.
В одном из вариантов реализации изобретения предложена неплесневеющая бумага, по меньшей мере одна поверхность которой покрыта противомикробным покрытием, содержащим полимеризованный силоксан и фунгицид. Согласно некоторым вариантам реализации изобретения, фунгицид может содержать по меньшей мере одно из следующих соединений: 3-йод-2-пропинилбутилкарбамат, пиритион цинка, оксид цинка, азоксистробин, тиабендазол, октилизотиазолин, дихлороктилизотиазолин, диметилдитиокарбамат цинка, бензимидазол, 3-(3,4-дихлорфенил)-1,1-диметилмочевину.In one embodiment of the invention, non-moldy paper is provided, at least one surface of which is coated with an antimicrobial coating containing polymerized siloxane and a fungicide. According to some embodiments of the invention, the fungicide may contain at least one of the following compounds: 3-iodine-2-propynylbutylcarbamate, zinc pyrithione, zinc oxide, azoxystrobin, thiabendazole, octylisothiazoline, dichloroctylisothiazoline, zinc dimethyldithiocarbamate 3, benzene -dichlorophenyl) -1,1-dimethylurea.
Различные сорта бумаги, в том числе манильскую бумагу и бумагу Newslined, можно сделать неплесневеющими путем каландрования с применением противомикробной композиции, содержащей полимеризованный силоксан и по меньшей мере один фунгицид, такой как 3-йод-2-пропинилбутилкарбамат, пиритион цинка, оксид цинка, азоксистробин, тиабендазол, октилизотиазолин, дихлороктилизотиазолин, диметилдитиокарбамат цинка, бензимидазол, 3-(3,4-дихлорфенил)-1,1-диметилмочевина. Подходящие противомикробные композиции включают композиции, в которых частицы фунгицида больше 1 микрона, но меньше 30 микрона. По меньшей мере согласно некоторым вариантам реализации изобретения композиция для нанесения противомикробного покрытия дополнительно содержит связующее вещество, в том числе такие связующие вещества, как карбоксиметилцеллюлоза, поливиниловый спирт, стирольные акриловые латексы, стирол-бутадиеновый полимер, казеин и крахмалы.Various grades of paper, including manila paper and Newslined paper, can be made non-moldy by calendering using an antimicrobial composition containing a polymerized siloxane and at least one fungicide such as 3-iodine-2-propynylbutylcarbamate, zinc pyrithione, zinc oxide, azoxystrobin , thiabendazole, octylisothiazoline, dichloroctylisothiazoline, zinc dimethyldithiocarbamate, benzimidazole, 3- (3,4-dichlorophenyl) -1,1-dimethylurea. Suitable antimicrobial compositions include compositions in which the fungicide particles are greater than 1 micron but less than 30 micron. In at least some embodiments, the antimicrobial coating composition further comprises a binder, including binders such as carboxymethyl cellulose, polyvinyl alcohol, styrene acrylic latexes, styrene-butadiene polymer, casein and starches.
Согласно дополнительным вариантам реализации изобретения также описана гипсовая панель, стойкая к образованию плесени и милдью. Указанную панель изготавливают путем размещения гипсового сердечника между двух неплесневеющих листов бумаги, полученной путем нанесения на по меньшей мере одну сторону листов бумаги композиции противомикробного покрытия, содержащей полимеризованный силоксан и фунгицид. Гипсовая панель содержит гипсовый сердечник, расположенный между двух листов бумаги, передним листом бумаги и задним листом бумаги, при этом каждый из двух листов бумаги имеет лицевую сторону и нижнюю сторону, причем гипсовый строительный раствор находится вблизи нижних сторон, а лицевые стороны покрыты композицией для нанесения противомикробного покрытия.According to further embodiments of the invention, a gypsum board resistant to mold and mildew is also described. The specified panel is made by placing a gypsum core between two non-moldy sheets of paper, obtained by applying to at least one side of the paper sheets an antimicrobial coating composition containing polymerized siloxane and a fungicide. The gypsum panel comprises a gypsum core located between two sheets of paper, a front sheet of paper and a back sheet of paper, each of the two sheets of paper having a front side and a lower side, the gypsum mortar being close to the lower sides and the front sides are coated with a coating composition antimicrobial coating.
Согласно дополнительным вариантам реализации изобретения также описан способ изготовления неплесневеющей многослойной бумаги, включающий: подачу бумаги в каландр; подачу в каландр композиции для нанесения противомикробного покрытия, содержащей от 1% до 10% неионного полимеризованного силоксана и от 1% до 10% водонерастворимого фунгицида, выбранного из группы, состоящей из 3-йод-2-пропинилбутилкарбамата, пиритиона цинка, оксида цинка, азоксистробина, тиабендазола, октилизотиазолина, дихлороктилизотиазолина, диметилдитиокарбамата цинка, бензимидазола, 3-(3,4-дихлорфенил)-1,1-диметилмочевины и их комбинации; и нанесение композиции противомикробного покрытия на по меньшей мере одну поверхность бумаги с помощью каландра.According to additional embodiments of the invention, a method for manufacturing non-moldy multilayer paper is also described, including: feeding paper into a calender; feeding into the calender a composition for applying an antimicrobial coating containing from 1% to 10% non-ionic polymerized siloxane and from 1% to 10% water-insoluble fungicide selected from the group consisting of 3-iodo-2-propynylbutylcarbamate, zinc pyrithione, zinc oxide, azoxystrobin , thiabendazole, octyl isothiazoline, dichloroctyl isothiazoline, zinc dimethyldithiocarbamate, benzimidazole, 3- (3,4-dichlorophenyl) -1,1-dimethylurea, and combinations thereof; and applying the antimicrobial coating composition to at least one surface of the paper using a calender.
КРАТКОЕ ОПИСАНИЕ ЧЕРТЕЖЕЙBRIEF DESCRIPTION OF THE DRAWINGS
На фиг. 1 показано, что стойкость гипсовой панели к образованию плесени улучшается при применении водонерастворимого фунгицида; иIn FIG. 1 shows that the resistance of the gypsum panel to mold is improved by using a water-insoluble fungicide; and
На фиг. 2 показано, что стойкость гипсовой панели к образованию плесени улучшается при изменении размера частиц водонерастворимого фунгицида.In FIG. 2 shows that the resistance of the gypsum panel to mold is improved by changing the particle size of the water-insoluble fungicide.
ПОДРОБНОЕ ОПИСАНИЕ ЧЕРТЕЖЕЙDETAILED DESCRIPTION OF THE DRAWINGS
В неплесневеющих гипсовых панелях можно использовать различные сорта бумаги, в том числе сорта, описанные в публикации заявки на патент США 2012/0088114 «Mold-resistant gypsum panel», идеи которой включены в настоящий документ посредством ссылки.Various types of paper can be used in non-moldable gypsum panels, including those described in US Patent Application Publication 2012/0088114, Mold-resistant gypsum panel, the ideas of which are incorporated herein by reference.
Подходящая бумага также включает манильскую бумагу или обклеечную бумагу с гладким каландрированным покрытием и бумагу Newslined или бумагу обратной стороны листа (back paper) с более грубым покрытием. Оба сорта бумаги являются многослойными и содержат по меньшей мере один слой лайнера и несколько слоев наполнителя. Для манильской бумаги в слоях лайнера обычно используют вторичную бумагу из лиственной целлюлозы с более короткими волокнами по сравнению со слоями наполнителя, в которых применяют более длинные волокна. Более короткая длина волокна из лиственной целлюлозы обеспечивает более гладкую поверхность для окрашивания и декорирования. Бумага Newslined обычно содержит тот же тип волокна в слое лайнера, который применяют в слоях наполнителя.Suitable paper also includes manila or smooth calendered paper and Newslined or rougher back paper. Both grades of paper are multilayer and contain at least one layer of liner and several layers of filler. For manila paper, liner layers typically use recycled hardwood pulp paper with shorter fibers compared to filler layers that use longer fibers. The shorter fiber length of hardwood pulp provides a smoother surface for dyeing and decoration. Newslined paper usually contains the same type of fiber in the liner layer that is used in the filler layers.
Неожиданно было установлено, что различные виды бумаги можно сделать неплесневеющими. Такие виды бумаги включают, но не ограничиваются ими, многослойную бумагу, содержащую по меньшей мере один слой лайнера и по меньшей мере один слой наполнителя. Кроме того, такие виды бумаги включают, но не ограничиваются ими, манильскую бумагу и бумагу сорта Newslined.It has been unexpectedly found that various types of paper can be made non-moldy. Such types of paper include, but are not limited to, multilayer paper containing at least one layer of liner and at least one layer of filler. In addition, these types of paper include, but are not limited to, manila paper and Newslined paper.
В описании настоящего изобретения термин «неплесневеющая» бумага применяется в его широком значении и включает любую бумагу, которая удерживает фунгицид в количестве, достаточном для полного или частичного подавления, замедления или предотвращения микробного роста. Термин «микробный рост» также используется широко и включает рост бактерий, грибов, дрожжей, плесени, милдью, водорослей и т.п. Термин «противомикробный» применяется широко и означает противомикробный, противогрибковый, противодрожжевой и т.п. Кроме того, все процентные содержания, приведенные в описании настоящего изобретения, рассчитаны по массе. Стойкость бумаги к образованию плесени можно определить с помощью стандартного испытания на стойкость к росту плесени на поверхности внутренних покрытий в климатической камере, известного как стандартное испытание на стойкость к образованию плесени ASTM D3273-12. Согласно данному стандарту бумагу относят к неплесневеющей, если она получает оценку 8 (от 11 до 20% поверхности повреждено и покрыто плесенью, в дальнейшем просто порча), 9 (от 1 до 10% порчи) или 10 (0% порчи) в испытаниях ASTM D3273-12, при которых бумагу подвергают воздействию почвы, инокулированной плесенью. Это же стандартное испытание ASTM D3273-12 можно использовать для определения стойкости к образованию плесени гипсовой панели. Согласно такому стандарту гипсовую панель относят к неплесневеющей, если она получает оценку 8 (от 11 до 20% порчи), 9 (от 1 до 10% порчи) или 10 (0% порчи).In the description of the present invention, the term "non-moldable" paper is used in its broad sense and includes any paper that holds the fungicide in an amount sufficient to completely or partially suppress, slow down or prevent microbial growth. The term "microbial growth" is also used widely and includes the growth of bacteria, fungi, yeast, mold, mildew, algae, etc. The term "antimicrobial" is used broadly and means antimicrobial, antifungal, antifungal, etc. In addition, all percentages described in the description of the present invention are calculated by weight. Mold resistance of paper can be determined using the standard mold resistance test on the surface of internal coatings in a climate chamber, known as the ASTM D3273-12 standard mold resistance test. According to this standard, paper is classified as non-moldable if it receives a rating of 8 (11 to 20% of the surface is damaged and moldy, then simply spoilage), 9 (1 to 10% spoilage), or 10 (0% spoilage) in ASTM tests D3273-12, in which the paper is exposed to mold inoculated soil. The same ASTM D3273-12 standard test can be used to determine the mold resistance of gypsum panels. According to such a standard, a gypsum panel is classified as non-moldable if it receives a rating of 8 (11 to 20% damage), 9 (1 to 10% damage) or 10 (0% damage).
По меньшей мере согласно некоторым вариантам реализации изобретения неплесневеющую бумагу изготавливают с применением вторичных материалов, в том числе вторичной газетной бумаги. В дальнейшем такие вторичные материалы называют газетной бумагой (News). Указанная бумага может содержать вплоть до 100% газетной бумаги. По меньшей мере согласно некоторым вариантам реализации изобретения указанная бумага состоит из 70% волокон газетной бумаги и 30% волокон форзацной бумаги, которые представляют собой короткие волокна с длиной в диапазоне от 0,8 до 1,5 мм, и с содержанием минеральных веществ обычно от 20 до 25%. По меньшей мере согласно некоторым вариантам реализации изобретения неплесневеющая бумага может содержать до 80% волокон газетной бумаги и 20% волокон форзацной бумаги. Согласно некоторым другим вариантам реализации изобретения неплесневеющая бумага может содержать до 90% волокон газетной бумаги и 10% волокон форзацной бумаги. Лайнер для бумаги обратной стороны листа может представлять собой старые гофрированные контейнеры (ОСС) или отходы двухслойной крафт-бумаги (DLK). Волокна таких бумажных отходов обычно содержат 2/3 волокон с длиной в диапазоне от 2,5 до 3,6 мм в случае крафт-лайнеров из хвойной древесины, и 1/3 волокон с длиной в диапазоне от 0,8 до 1,5 мм для для среднего слоя из твердой древесины между лайнерами.According to at least some embodiments of the invention, non-moldy paper is made using recycled materials, including recycled newsprint. These secondary materials are hereinafter referred to as Newsprint. Said paper may contain up to 100% newsprint. At least in some embodiments of the invention, said paper consists of 70% newsprint fibers and 30% fly-paper fibers, which are short fibers with a length in the range of 0.8 to 1.5 mm, and with a mineral content typically of 20 to 25%. At least in some embodiments, the moldless paper may contain up to 80% newsprint fibers and 20% fly-paper fibers. In some other embodiments, the moldless paper may contain up to 90% newsprint fibers and 10% fly-paper fibers. The paper liner on the back of the sheet can be old corrugated containers (OSS) or waste from two-layer kraft paper (DLK). The fibers of such paper waste typically contain 2/3 of fibers with a length in the range of 2.5 to 3.6 mm in the case of softwood craft liners, and 1/3 of fibers with a length in the range of 0.8 to 1.5 mm for for the middle layer of solid wood between the liners.
Неплесневеющую бумагу получают путем нанесения противомикробного покрытия на по меньшей мере одну или обе из двух сторон бумаги (лицевую и нижнюю) во время стадии в каландре. Согласно некоторым вариантам реализации изобретения неплесневеющую бумагу изготавливают таким образом, что покрытие наносят на обе стороны. Согласно другим вариантам реализации изобретения покрытие наносят только на одну сторону. Согласно дополнительным вариантам реализации изобретения покрытие наносят только на лицевую сторону бумаги. Согласно дополнительным вариантам реализации изобретения покрытие наносят только на нижнюю сторону бумаги. Согласно другим вариантам реализации изобретения противомикробное покрытие наносят на обе стороны бумаги: лицевую и нижнюю стороны.Moldless paper is obtained by applying an antimicrobial coating to at least one or both of the two sides of the paper (front and bottom) during the calendaring stage. According to some embodiments of the invention, non-moldy paper is made in such a way that the coating is applied on both sides. According to other embodiments of the invention, the coating is applied on only one side. According to additional embodiments of the invention, the coating is applied only to the front side of the paper. According to additional embodiments of the invention, the coating is applied only to the underside of the paper. According to other embodiments of the invention, an antimicrobial coating is applied to both sides of the paper: front and bottom sides.
По меньшей мере согласно некоторым вариантам реализации изобретения противомикробная композиция содержит полимеризованный силоксан и фунгицид. В составе противомикробного покрытия можно использовать различные фунгициды. Особенно предпочтительными являются фунгициды, нерастворимые в воде или только плохо растворимые в воде. В описании настоящего изобретения термин «нерастворимый фунгицид» применяется широко и включает фунгициды, которые являются гидрофобными и плохо растворяются в воде. Согласно некоторым вариантам реализации изобретения растворимость в воде нерастворимых фунгицидов составляет всего лишь не более 35 частей на миллион (ppm). Фунгициды, растворимые в воде, не являются предпочтительными.In at least some embodiments, the antimicrobial composition comprises polymerized siloxane and a fungicide. In the composition of the antimicrobial coating, various fungicides can be used. Particularly preferred are fungicides insoluble in water or only poorly soluble in water. In the description of the present invention, the term "insoluble fungicide" is used broadly and includes fungicides that are hydrophobic and poorly soluble in water. According to some embodiments of the invention, the solubility in water of insoluble fungicides is only not more than 35 parts per million (ppm). Water soluble fungicides are not preferred.
На фиг. 1 приведены неожиданные результаты, показывающие, что стойкость к образованию плесени гипсовой панели зависит от того, применяют ли водонерастворимый или водорастворимый фунгицид в композиции для покрытия бумаги. Неплесневеющую бумагу получали с применением различных композиций для покрытия, в которых использовали водонерастворимый фунгицид и силоксан, как описано в настоящем документе. Затем изготавливали гипсовые панели с применением бумаги с покрытием или контрольной бумаги без покрытия или бумаги, покрытой комбинацией силоксана и водорастворимого фунгицида. Далее все гипсовые панели подвергали испытанию согласно стандартному испытанию на стойкость к образованию плесени D3273-12. Как показано на фиг. 1, контрольная гипсовая панель, которая была изготовлена с применением бумаги без фунгицида, не является стойкой к образованию плесени и получила оценку 0 (от 91 до 100% порчи) в испытании на стойкость к образованию плесени. См. фиг. 1, контроль. Гипсовая панель, изготовленная с применением бумаги, которая была покрыта комбинацией силоксана и водорастворимого фунгицида, проявляла только несколько улучшенную стойкость к образованию плесени, при этом большинство образцов получило оценку от 2 (от 71 до 80% порчи) до 6 (от 31 до 40% порчи). См. фиг. 1, растворимый фунгицид.In FIG. Figure 1 shows unexpected results showing that the resistance to mold of a gypsum board depends on whether a water-insoluble or water-soluble fungicide is used in the paper coating composition. Moldless paper was prepared using various coating compositions in which water-insoluble fungicide and siloxane were used, as described herein. Then gypsum panels were made using coated paper or uncoated control paper or paper coated with a combination of siloxane and a water-soluble fungicide. Next, all gypsum panels were tested according to the standard mold resistance test D3273-12. As shown in FIG. 1, the control gypsum board, which was made using paper without fungicide, is not resistant to mold and was rated 0 (91 to 100% spoilage) in the mold resistance test. See FIG. 1, control. A gypsum board made using paper that was coated with a combination of siloxane and a water-soluble fungicide showed only slightly improved mold resistance, with most of the samples rated between 2 (71 to 80% spoilage) to 6 (31 to 40% damage). See FIG. 1, soluble fungicide.
Кроме того, испытывали гипсовые панели, изготовленные с применением бумаги, которая была покрыта с применением комбинации силоксана и водонерастворимого фунгицида, как описано в настоящем описании изобретения. См. фиг. 1, нерастворимый фунгицид. Неожиданно было обнаружено, что указанные гипсовые панели имели значительно улучшенную стойкость к образованию плесени, при этом много образцов получило оценку по меньшей мере 8 (от 11 до 20% порчи) и выше. У некоторых образцов с водонерастворимым фунгицидом порча отсутствовала вовсе и они получили оценку 10. См. фиг. 1, нерастворимый фунгицид.In addition, gypsum panels made using paper that was coated using a combination of siloxane and a water-insoluble fungicide, as described herein, were tested. See FIG. 1, insoluble fungicide. It was unexpectedly found that these gypsum panels had significantly improved resistance to mold formation, with many samples having a rating of at least 8 (11 to 20% spoilage) and higher. In some samples with a water-insoluble fungicide, spoilage was completely absent and they received a rating of 10. See FIG. 1, insoluble fungicide.
Кроме того, неожиданно было установлено, что размер частиц фунгицида в противомикробном покрытии влияет на активность неплесневеющей бумаги при полном или частичном подавлении, замедлении или предотвращении микробного роста. Подходящие составы противомикробного покрытия включают составы с размерами частиц фунгицида в диапазоне от примерно 1 микрона до примерно 30 микрон. Согласно некоторым вариантам реализации изобретения состав покрытия изготавливают с применением фунгицида, частицы которого больше 1 микрона, но меньше 15 микрон. Согласно дополнительным вариантам реализации изобретения противомикробное покрытие получают с применением частиц фунгицида таким образом, чтобы по меньшей мере 90% частиц имели размеры больше 1 микрона, но меньше 15 микрон. Согласно другим вариантам реализации изобретения противомикробное покрытие получают с применением частиц фунгицида таким образом, чтобы по меньшей мере 90% частиц имели размеры в диапазоне от 8 до 15 микрон. По меньшей мере согласно некоторым вариантам реализации изобретения противомикробное покрытие получают с применением частиц фунгицида таким образом, чтобы по меньшей мере 90% частиц имели размеры в диапазоне от 10 до 26 микрон. Фунгицид, большинство частиц которого меньше 1 микрона или больше 30 микрон, не являются предпочтительным.In addition, it was unexpectedly found that the particle size of the fungicide in the antimicrobial coating affects the activity of non-moldy paper with the complete or partial suppression, retardation or prevention of microbial growth. Suitable antimicrobial coating compositions include those with fungicide particle sizes in the range of from about 1 micron to about 30 microns. According to some embodiments of the invention, the coating composition is made using a fungicide whose particles are greater than 1 micron but less than 15 microns. According to additional embodiments of the invention, an antimicrobial coating is prepared using fungicide particles so that at least 90% of the particles are larger than 1 micron, but less than 15 microns. In other embodiments, an antimicrobial coating is prepared using fungicide particles so that at least 90% of the particles have sizes in the range of 8 to 15 microns. In at least some embodiments, an antimicrobial coating is prepared using fungicide particles such that at least 90% of the particles have sizes in the range of 10 to 26 microns. A fungicide whose majority of particles is less than 1 micron or more than 30 microns is not preferred.
На фиг. 2 приведены удивительные результаты, показывающие, что стойкость к образованию плесени гипсовой панели зависит от размера частиц в водонерастворимом фунгициде, применяемом в композиции для покрытия бумаги. Неплесневеющую бумагу получали с применением различных композиций для покрытия, в которых использовали водонерастворимый фунгицид и силоксан, как описано в настоящем документе. Далее изготавливали гипсовые панели с применением бумаги с покрытием или контрольной бумаги без покрытия или бумаги, покрытой комбинацией силоксана и водорастворимого фунгицида. Затем все гипсовые панели подвергали испытанию согласно стандартному испытанию на стойкость к образованию плесени D3273-12.In FIG. 2 shows surprising results showing that the resistance to mold of a gypsum board depends on the particle size of the water-insoluble fungicide used in the paper coating composition. Moldless paper was prepared using various coating compositions in which water-insoluble fungicide and siloxane were used, as described herein. Next, gypsum panels were made using coated paper or control paper without coating or paper coated with a combination of siloxane and a water-soluble fungicide. Then all gypsum panels were tested according to the standard mold resistance test D3273-12.
На фиг. 2, подвергали испытанию один и тот же водонерастворимый фунгицид с двумя разными размерами частиц. В первом составе 95% частиц фунгицида имели размеры меньше 1 микрона и во втором составе 95% частиц фунгицида имели размеры больше 1 микрона, но меньше 5 микрон. Второй состав обеспечивал лучшую стойкость к образованию плесени, как показано на фиг. 2, D (95% <5 мкм) относительно D (95% <1 мкм). Кроме того, состав с другим водонерастворимым фунгицидом, в котором 95% частиц имели размеры примерно 13 микрон, обеспечивал отличную стойкость к образованию плесени и получил оценку 10 (0% порчи). См. фиг. 2, D (95% <13 мкм). Такой результат представлял собой значительное улучшение по сравнению с гипсовыми панелями, изготовленными с применением бумаги без неплесневеющего покрытия, и гипсовыми панелями, изготовленными с применением бумаги с неплесневеющим покрытием, в котором применяли водорастворимый фунгицид.In FIG. 2, tested the same water-insoluble fungicide with two different particle sizes. In the first composition, 95% of the fungicide particles were smaller than 1 micron and in the second composition, 95% of the fungicide particles were larger than 1 micron, but less than 5 microns. The second composition provided better mold resistance, as shown in FIG. 2, D (95% <5 μm) relative to D (95% <1 μm). In addition, a composition with another water-insoluble fungicide in which 95% of the particles were approximately 13 microns in size provided excellent mold resistance and was rated 10 (0% spoilage). See FIG. 2, D (95% <13 μm). This result was a significant improvement over gypsum panels made using paper without a moldy coating and gypsum panels made using paper with a moldless coating in which water-soluble fungicide was used.
Для получения противомикробного покрытия подходят различные фунгициды, в том числе, но не ограничиваясь ими, 3-йод-2-пропинилбутилкарбамат, пиритион цинка, оксид цинка, азоксистробин, тиабендазол, октилизотиазолин, дихлороктилизотиазолин, диметилдитиокарбамат цинка, бензимидазол и 3-(3,4-дихлорфенил)-1,1-диметилмочевина. Указанные фунгициды можно использовать либо по отдельности, либо в комбинации друг с другом. По меньшей мере согласно некоторым вариантам реализации изобретения пиритион цинка можно использовать в комбинации с оксидом цинка. Согласно другим вариантам реализации изобретения азоксистробин можно использовать в комбинации с тиабендазолом. Один из особенно предпочтительных составов противомикробного покрытия содержит фунгицид, в котором от 15 до 25% тиабендазола смешано с от 10 до 20% азоксистробина. По меньшей мере согласно некоторым вариантам реализации изобретения предпочтительный фунгицид представляет собой дисперсию из приблизительно 19,5% тиабендазола и приблизительно 15% азоксистробина. Согласно другим вариантам реализации изобретения комбинацию азоксистробина и тиабендазола применяют в качестве первого фунгицида и по меньшей мере одно другое соединение применяют в качестве второго фунгицида. Согласно некоторым вариантам реализации изобретения такой второй фунгицид может представлять собой пиритион цинка, оксид цинка или комбинацию двух указанных соединений.Various fungicides are suitable for antimicrobial coatings, including, but not limited to, 3-iodine-2-propynylbutylcarbamate, zinc pyrithione, zinc oxide, azoxystrobin, thiabendazole, octylisothiazoline, dichloroctyl isothiazoline, dimethyl dithiocarbimobenzoate -dichlorophenyl) -1,1-dimethylurea. These fungicides can be used either individually or in combination with each other. In at least some embodiments, zinc pyrithione can be used in combination with zinc oxide. In other embodiments, azoxystrobin can be used in combination with thiabendazole. One particularly preferred antimicrobial coating composition comprises a fungicide in which 15 to 25% of thiabendazole is mixed with 10 to 20% azoxystrobin. In at least some embodiments, a preferred fungicide is a dispersion of about 19.5% thiabendazole and about 15% azoxystrobin. In other embodiments, a combination of azoxystrobin and thiabendazole is used as the first fungicide and at least one other compound is used as the second fungicide. In some embodiments, such a second fungicide may be zinc pyrithione, zinc oxide, or a combination of the two.
Согласно некоторым вариантам реализации изобретения противомикробное покрытие содержит от 1,0 до 10% по массе фунгицида. Согласно другим вариантам реализации изобретения противомикробное покрытие содержит от 1 до 6% по массе фунгицида. Согласно другим вариантам реализации изобретения противомикробное покрытие содержит от 1 до 4% по массе фунгицида.According to some variants of the invention, the antimicrobial coating contains from 1.0 to 10% by weight of fungicide. According to other variants of the invention, the antimicrobial coating contains from 1 to 6% by weight of fungicide. According to other variants of the invention, the antimicrobial coating contains from 1 to 4% by weight of fungicide.
В составе противомикробного покрытия можно использовать различные полимеризованные силоксаны. Термин «полимеризованный силоксан» применяется широко и включает соединение с химической формулой [R2SiO]n, где «n» обозначает, сколько раз в полимере повторяется звено R2SiO. Каждая из двух групп R может представлять собой другую группу или одну и ту же группу. Каждую из двух групп R выбирают из группы, состоящей из водорода, галогена и органической группы. Подходящие органические группы включают, но не ограничиваются ими, метил, этил и фенил. Согласно некоторым вариантам реализации изобретения предпочтительным является неионный полимеризованный силоксан. По меньшей мере согласно некоторым вариантам реализации изобретения полимеризованный силоксан представляет собой полидиметилсилоксан.As part of the antimicrobial coating, various polymerized siloxanes can be used. The term "polymerized siloxane" is used broadly and includes a compound with the chemical formula [R 2 SiO] n , where "n" indicates how many times the R 2 SiO unit is repeated in the polymer. Each of the two R groups may be a different group or the same group. Each of the two R groups is selected from the group consisting of hydrogen, halogen and an organic group. Suitable organic groups include, but are not limited to, methyl, ethyl, and phenyl. In some embodiments, non-ionic polymerized siloxane is preferred. In at least some embodiments, the polymerized siloxane is polydimethylsiloxane.
Согласно некоторым вариантам реализации изобретения противомикробное покрытие содержит от 1 до 10% по массе полимеризованного силоксана. Согласно другим вариантам реализации изобретения используют от 1 до 6% по массе полимеризованного силоксана. Согласно дополнительным вариантам реализации изобретения используют от 1 до 4% по массе полимеризованного силоксана.According to some embodiments of the invention, the antimicrobial coating contains from 1 to 10% by weight of the polymerized siloxane. In other embodiments, 1 to 6% by weight of polymerized siloxane is used. According to additional embodiments of the invention, 1 to 4% by weight of polymerized siloxane is used.
По меньшей мере согласно некоторым вариантам реализации изобретения композицию для нанесения противомикробного покрытия изготавливают путем смешивания от 1 до 10 частей по меньшей мере одного фунгицида с от 1 до 10 частями полимеризованного силоксана и от 98 до 80 частями воды. Согласно дополнительным вариантам реализации изобретения примерно 10 частей по меньшей мере одного фунгицида смешивают с примерно 4 частями полимеризованного силоксана и примерно 86 частями воды. Согласно дополнительным вариантам реализации изобретения примерно 3 части по меньшей мере одного фунгицида смешивают с примерно 4 частями полимеризованного силоксана и примерно 97 частями воды.In at least some embodiments, an antimicrobial coating composition is prepared by mixing from 1 to 10 parts of at least one fungicide with 1 to 10 parts of polymerized siloxane and 98 to 80 parts of water. According to additional embodiments of the invention, about 10 parts of at least one fungicide are mixed with about 4 parts of polymerized siloxane and about 86 parts of water. According to additional embodiments of the invention, about 3 parts of at least one fungicide are mixed with about 4 parts of polymerized siloxane and about 97 parts of water.
Согласно некоторым вариантам реализации изобретения композиция для нанесения противомикробного покрытия дополнительно включает связующее вещество. Неожиданно было установлено, что связующие вещества улучшают прилипание частиц фунгицида к бумажному листу. Кроме того, неожиданно было установлено, что связующие вещества являются особенно предпочтительными в составах с более крупными частицами фунгицида. Согласно некоторым вариантам реализации изобретения предпочтительно, что композиция для нанесения противомикробного покрытия содержит связующее вещество, если ее получают с применением частиц фунгицида, размеры которых больше 5 микрон.In some embodiments, the antimicrobial coating composition further comprises a binder. Surprisingly, binders have been found to enhance the adhesion of fungicide particles to a paper sheet. In addition, it was unexpectedly found that binders are particularly preferred in formulations with larger fungicide particles. In some embodiments, it is preferred that the antimicrobial coating composition contains a binder if it is prepared using fungicide particles larger than 5 microns in size.
Для приготовления композиции для нанесения противомикробного покрытия подходят различные связующие вещества. Такие связующие вещества включают, но не ограничиваются ими, карбоксиметилцеллюлозу (CMC), поливиниловый спирт (PVOH), стирольные акриловые латексы, стирол-бутадиеновый полимер, казеин и крахмалы. По меньшей мере согласно некоторым вариантам реализации изобретения композиция для нанесения противомикробного покрытия содержит от примерно 0,01% до примерно 0,05% связующего вещества. Согласно некоторым другим вариантам реализации изобретения используют примерно 0,03% связующего вещества.Various binders are suitable for preparing an antimicrobial coating composition. Such binders include, but are not limited to, carboxymethyl cellulose (CMC), polyvinyl alcohol (PVOH), styrene acrylic latexes, styrene-butadiene polymer, casein and starches. In at least some embodiments, the antimicrobial coating composition comprises from about 0.01% to about 0.05% of a binder. In some other embodiments, approximately 0.03% of the binder is used.
По меньшей мере согласно некоторым вариантам реализации изобретения подходящая карбоксиметилцеллюлоза представляет собой низкомолекулярный полимер. Подходящее карбоксиметилцеллюлозное связующее вещество можно приобрести в компании Ashland Hercules, Inc. под названием AQUALON™ CMC-7LT со степенью замещения приблизительно 0,7 и низкой вязкостью. Согласно некоторым вариантам реализации изобретения карбоксиметилцеллюлозу можно использовать в составе противомикробного покрытия в количестве от примерно 2 (примерно 0,91 кг/т) до примерно 10 фунт/т (примерно 4,5 кг/т). По меньшей мере согласно некоторым предпочтительным вариантам реализации изобретения карбоксиметилцеллюлозу применяют в количестве примерно 6 фунт/т (примерно 2,7 кг/т).In at least some embodiments, a suitable carboxymethyl cellulose is a low molecular weight polymer. A suitable carboxymethyl cellulose binder is available from Ashland Hercules, Inc. called AQUALON ™ CMC-7LT with a degree of substitution of approximately 0.7 and low viscosity. In some embodiments, carboxymethyl cellulose can be used in the antimicrobial coating in an amount of from about 2 (about 0.91 kg / t) to about 10 lb / t (about 4.5 kg / t). In at least some preferred embodiments of the invention, carboxymethyl cellulose is used in an amount of about 6 lb / t (about 2.7 kg / t).
Другие подходящие связующие вещества включают продукты, представляющие собой частично гидролизованный PVOH, с вязкостью в диапазоне от низкой до средней. Такие связующие вещества можно приобрести в компании DuPont под названиями ELVANOL™ 51-05, 52-22 и 50-42. Указанные связующие вещества можно использовать в количестве от примерно 2 (примерно 0,91 кг/т) до примерно 10 фунт/т (примерно 4,5 кг/т) и предпочтительно примерно 6 фунт/т (примерно 2,7 кг/т).Other suitable binders include products that are partially hydrolyzed PVOH, with a viscosity in the range from low to medium. Such binders are available from DuPont under the names ELVANOL ™ 51-05, 52-22, and 50-42. These binders can be used in an amount of from about 2 (about 0.91 kg / t) to about 10 lb / t (about 4.5 kg / t) and preferably about 6 lb / t (about 2.7 kg / t) .
Дополнительные варианты реализации противомикробного покрытия включают краситель. Подходящие красители включают, но не ограничиваются ими, фталоцианиновый зеленый краситель от компании Chromatech, Inc., пигмент USGRN от компании Michelman, Inc. и краситель Solar Р Blue 42L от компании BASF, Inc. В конечной противомикробной композиции можно использовать краситель в количестве от примерно 0,01% до примерно 2%.Additional embodiments of the antimicrobial coating include a colorant. Suitable dyes include, but are not limited to, phthalocyanine green dye from Chromatech, Inc., USGRN pigment from Michelman, Inc. and dye Solar P Blue 42L from BASF, Inc. In the final antimicrobial composition, dye may be used in an amount of from about 0.01% to about 2%.
Неплесневеющую бумагу получают во время стадии каландрования путем покрытия бумаги противомикробной композицией, которую можно предварительно приготовить в емкости для смешивания и затем загрузить в каландры из приемного резервуара с помощью насоса. Согласно некоторым вариантам реализации изобретения покрытие наносят в количестве от примерно 0,10 фунт/тыс.кв.футов (примерно 0,49 кг/тыс.кв.м) до примерно 2,50 фунт/тыс.кв.футов (примерно 12,2 кг/тыс.кв.м). По меньшей мере согласно некоторым вариантам реализации изобретения композицию для покрытия можно нанести только на одну сторону бумаги. Согласно дополнительным вариантам реализации изобретения композицию для покрытия наносят на обе стороны. По меньшей мере согласно некоторым вариантам реализации изобретения композицию для покрытия наносят только на лицевую сторону бумаги. Согласно другим вариантам реализации изобретения композицию для покрытия наносят только на нижнюю сторону бумаги.Mold-free paper is obtained during the calendering step by coating the paper with an antimicrobial composition that can be pre-prepared in mixing containers and then loaded into calendars from a receiving tank using a pump. According to some embodiments of the invention, the coating is applied in an amount of from about 0.10 pound / thousand square feet (about 0.49 kg / thousand square meters) to about 2.50 pound / thousand square feet (about 12, 2 kg / thousand sq. M). In at least some embodiments, the coating composition can be applied to only one side of the paper. According to further embodiments of the invention, the coating composition is applied on both sides. In at least some embodiments, the coating composition is applied only to the front of the paper. According to other embodiments of the invention, the coating composition is applied only to the underside of the paper.
Скорость нанесения или налипания покрытия на каландре зависит от типа волокна, бумажных отходов, применяемых для получения слоя и/или слоев лайнера, пористости листа, влаги в листе, поступающей в каландры, водостойкости листа, плотности листа, содержащихся в покрытии твердых веществ, содержащейся в покрытии пены, температуры покрытия, скорости бумагоделательной машины и конструкции или механизма каландра. Скорость налипания покрытия в каландрах определяется некоторыми из перечисленных выше факторов и является аналогичной для конкретного сорта бумаги на конкретной бумагоделательной машине. Состав покрытия регулируют согласно дополнительным вариантам реализации изобретения с тем, чтобы фунгицид был нанесен в количестве от 300 ppm до примерно 4500 ppm.The speed of applying or sticking the coating on the calender depends on the type of fiber, paper waste used to obtain the liner and / or layers of the liner, the porosity of the sheet, the moisture in the sheet entering the calendars, the water resistance of the sheet, the density of the sheet contained in the coating of solids contained in foam coating, coating temperature, paper machine speed, and calender structure or mechanism. The calender sticking rate is determined by some of the factors listed above and is similar for a particular paper grade on a particular paper machine. The coating composition is controlled according to additional embodiments of the invention so that the fungicide is applied in an amount of from 300 ppm to about 4500 ppm.
По меньшей мере согласно некоторым вариантам реализации изобретения перед применением композицию для нанесения противомикробного покрытия предварительно нагревают от примерно 110°F (примерно 43°С) до примерно 160°F (примерно 71°С). Согласно дополнительным вариантам реализации изобретения предпочтительно, что композицию для покрытия предварительно нагревают от примерно 120°F (примерно 49°С) до примерно 140°F (примерно 60°С).At least in some embodiments, the antimicrobial coating composition is preheated from about 110 ° F (about 43 ° C) to about 160 ° F (about 71 ° C) before use. According to additional embodiments of the invention, it is preferable that the coating composition is preheated from about 120 ° F (about 49 ° C) to about 140 ° F (about 60 ° C).
Для определения количества активного фунгицида, удерживаемого в бумаге, можно проводить различные испытания. Такие способы включают, но не ограничиваются ими, испытания с применением УФ спектрофотометрии, аналитической жидкостной хроматографии при высоких давлениях (ЖХВД) и рентгеновской флуоресценции.Various tests can be performed to determine the amount of active fungicide held in paper. Such methods include, but are not limited to, tests using UV spectrophotometry, high pressure analytical liquid chromatography (HPLC), and X-ray fluorescence.
Дополнительные испытания включают испытание на водостойкость, которое позволяет определить количество воды, абсорбированное бумагой в течение определенного периода времени. Результаты такого испытания регистрируют как поверхностную впитываемость воды по Коббу в граммах воды, абсорбированной 100 см2 бумаги. Неожиданно было установлено, что подходящая неплесневеющая бумага включает бумагу с поверхностной впитываемостью воды по Коббу от 0,4 г на 100 см2 бумаги до 1,6 г на 100 см2.Additional tests include a water resistance test that measures the amount of water absorbed by the paper over a period of time. The results of such a test are recorded as Cobb surface water absorption in grams of water absorbed in 100 cm 2 of paper. Unexpectedly, it was found that a suitable non-moldable paper includes paper with a surface absorption of water according to Cobb from 0.4 g per 100 cm 2 of paper to 1.6 g per 100 cm 2 .
Различные сорта бумаги можно сделать неплесневеющими, в том числе манильскую бумагу и бумагу сорта Newslined. Манильская бумага представляет прочно склеенный лист. Обычно на верхние два слоя лайнера наносят от 8 (примерно 3,6 кг/т) до 10 фунт/т (примерно 4,5 кг/т) клея, представляющего собой алкенилянтарный ангидрид (ASA), но можно ввести ASA в количестве только от 4 (примерно 1,8 кг/т) до 5 фунт/т (примерно 2,3 кг/т). Слои наполнителя содержат клей ASA в количестве от 3 (примерно 1,4 кг/т) до 7 фунт/т (примерно 3,2 кг/т). В слои лайнера и наполнителя вводят квасцы в количестве от 3 (примерно 1,4 кг/т) до 7 фунт/т (примерно 3,2 кг/т), но обычно 5 фунт/т (примерно 2,3 кг/т). Волокнистый материал лайнера представляет собой «газетные обрезки», которые включают термомеханическую древесную массу или древесное волокно, представляющее собой волокнистый материал с высоким выходом, но с низким содержанием минеральных веществ. Такой лист необходимо высушить подходящим способом с тем, чтобы клей ASA образовал ковалентные связи с целлюлозой. Для получения правильно сформированного листа используют стандартные применяемые при производстве бумаги химические реагенты (вещества для повышения удерживаемости, коагулянты) и процедуры. Средняя плотность манильской бумаги составляет 44 фунт/тыс.кв.футов (примерно 215 кг/тыс.кв.м) и масса рулона обычно составляет 5530 фунтов (примерно 2508 кг) и содержит 125 тыс.кв. футов/рулон (примерно 12 тыс.кв.м/рулон).Various types of paper can be made non-moldy, including manila paper and Newslined paper. Manila paper is a firmly glued sheet. Usually, from the top two layers of the liner, from 8 (about 3.6 kg / t) to 10 lb / t (about 4.5 kg / t) glue, which is alkenyl succinic anhydride (ASA), is applied, but ASA can be added in an amount of only 4 (about 1.8 kg / t) to 5 lb / t (about 2.3 kg / t). The filler layers contain ASA glue in an amount of 3 (about 1.4 kg / t) to 7 lb / t (about 3.2 kg / t). Alum is added to the liner and filler layers in an amount of 3 (about 1.4 kg / t) to 7 lb / t (about 3.2 kg / t), but usually 5 lb / t (about 2.3 kg / t) . The fiber material of the liner is “newspaper clippings,” which include thermomechanical pulp or wood fiber, which is a fibrous material with a high yield but low mineral content. Such a sheet must be dried in a suitable way so that the ASA adhesive forms covalent bonds with the cellulose. To obtain a properly formed sheet using standard chemicals used in the manufacture of paper chemicals (substances to increase retention, coagulants) and procedures. The average density of manila paper is 44 pounds / thousand square feet (approximately 215 kg / thousand square meters) and the weight of the roll is usually 5530 pounds (approximately 2508 kg) and contains 125 thousand square meters. ft / roll (approximately 12 thousand sq. m / roll).
Согласно некоторым вариантам реализации изобретения манильскую бумагу можно сделать неплесневеющей путем покрытия бумаги композицией для нанесения противомикробного покрытия, содержащей от примерно 1,5% до примерно 7% полимеризованного силоксана и от примерно 1 до примерно 7% по меньшей мере одного фунгицида. Покрытие наносят влажным способом с применением каландра, используя от примерно 300 ppm до примерно 4500 ppm активного фунгицида. Согласно некоторым вариантам реализации изобретения покрытие наносят влажным способом с применением каландра, используя от примерно 300 ppm до примерно 1500 ppm активного фунгицида. Согласно другим вариантам реализации изобретения покрытие наносят влажным способом с применением каландра, используя от примерно 300 ppm до примерно 1500 ppm активного полимеризованного силоксана.In some embodiments, manila paper can be made non-moldy by coating the paper with an antimicrobial coating composition containing from about 1.5% to about 7% polymerized siloxane and from about 1 to about 7% of at least one fungicide. The coating is applied wet using a calender using from about 300 ppm to about 4,500 ppm of active fungicide. In some embodiments, the coating is applied wet using a calender using about 300 ppm to about 1500 ppm active fungicide. In other embodiments, the coating is applied wet using a calender using from about 300 ppm to about 1500 ppm of active polymerized siloxane.
Бумага Newslined представляет прочно склеенный лист. Обычно на верхние два слоя лайнера наносят клей ASA в количестве от 8 (примерно 3,6 кг/т) до 10 фунт/т (примерно 4,5 кг/т), но можно ввести клей ASA в количестве только от 4 (примерно 1,8 кг/т) до 5 фунт/т (примерно 2,3 кг/т). Слои наполнителя будут содержать клей ASA в количестве от 3 (примерно 1,4 кг/т) до 7 фунт/т (примерно 3,2 кг/т). В слои лайнера и наполнителя вводят квасцы в количестве от 3 (примерно 1,4 кг/т) до 7 фунт/т (примерно 3,2 кг/т), но обычно 5 фунт/т (примерно 2,3 кг/т). Волокнистый материал представляет собой макулатуру в виде «старого гофрированного картона» или «двухслойной крафт-бумаги». Эти же сорта бумажных отходов использовали в качестве слоев наполнителя для получения манильской бумаги. Концентрацию клея можно понизить для обеспечения поверхностной впитываемости воды по Коббу со стороны соединения. Лист необходимо высушить подходящим способом с тем, чтобы клей ASA образовал ковалентные связи с целлюлозой. Для получения правильно сформированного листа используют стандартные применяемые при производстве бумаги химические реагенты (вещества для повышения удерживаемости, коагулянты) и процедуры. Средняя плотность бумаги составляет 42 фунт/тыс.кв.футов (примерно 202 кг/тыс.кв.м) и масса рулона обычно составляет 5585 фунтов (примерно 2533 кг) и содержит 133,5 тыс.кв.футов/рулон (примерно 12,4 тыс.кв.м/рулон).Newslined paper presents a firmly glued sheet. Usually on the upper two layers of the liner, ASA glue is applied in an amount of from 8 (about 3.6 kg / t) to 10 lb / t (about 4.5 kg / t), but ASA glue can be added in an amount of only 4 (about 1 8 kg / t) to 5 lb / t (approximately 2.3 kg / t). The filler layers will contain ASA glue in an amount of 3 (about 1.4 kg / t) to 7 lb / t (about 3.2 kg / t). Alum is added to the liner and filler layers in an amount of 3 (about 1.4 kg / t) to 7 lb / t (about 3.2 kg / t), but usually 5 lb / t (about 2.3 kg / t) . The fibrous material is waste paper in the form of “old corrugated cardboard” or “two-layer kraft paper”. The same types of paper waste were used as filler layers to produce manila paper. The concentration of the adhesive can be lowered to ensure surface absorption of water on the Cobb side of the connection. The sheet must be dried in a suitable way so that ASA glue forms covalent bonds with cellulose. To obtain a properly formed sheet using standard chemicals used in the manufacture of paper chemicals (substances to increase retention, coagulants) and procedures. The average paper density is 42 lb / thousand square feet (approximately 202 kg / thousand square meters) and the weight of the roll is usually 5585 pounds (approximately 2533 kg) and contains 133.5 thousand square feet / roll (approximately 12 , 4 thousand square meters / roll).
Бумагу сорта Newslined можно сделать неплесневеющей путем покрытия бумаги композицией для нанесения противомикробного покрытия, содержащей от примерно 1,5% до примерно 7% полимеризованного силоксана и от примерно 1 до примерно 7% по меньшей мере одного фунгицида. Покрытие наносят влажным способом с применением каландра таким образом, чтобы концентрация активного фунгицида составляла от примерно 300 ppm до примерно 4500 ppm.Newslined paper can be made non-moldy by coating the paper with an antimicrobial coating composition containing from about 1.5% to about 7% polymerized siloxane and from about 1 to about 7% of at least one fungicide. The coating is applied wet using a calender so that the concentration of active fungicide is from about 300 ppm to about 4500 ppm.
Гипсовую панель с улучшенной стойкостью к образованию плесени можно получить путем применения неплесневеющей бумаги в качестве облицовочных материалов. Согласно некоторым вариантам реализации изобретения неплесневеющие бумажные листы манильской бумаги и бумаги сорта Newslined получают, как описано выше. Затем приготавливают гипсовый строительный раствор и помещают его между листом неплесневеющей манильской бумаги с одной стороны и листом неплесневеющей бумаги Newslined с другой стороны.A gypsum board with improved resistance to mold formation can be obtained by using non-moldy paper as facing materials. In some embodiments, non-moldy manila and Newslined paper sheets are prepared as described above. A gypsum mortar is then prepared and placed between a sheet of non-moldy manila paper on one side and a sheet of Newslined non-mold paper on the other.
ПРИМЕР 1EXAMPLE 1
Композиция для нанесения противомикробного покрытияAntimicrobial Coating Composition
Покрытие получали в соответствии с составом, приведенным в таблице 1, в котором все части были рассчитаны по массе.The coating was obtained in accordance with the composition shown in table 1, in which all parts were calculated by weight.
ПРИМЕР 2 EXAMPLE 2
Неплесневеющая манильская бумагаMoldless manila paper
Манильскую бумагу получали согласно техническим требованиям к данному сорту. Композицию для нанесения противомикробного покрытия получали, как описано в таблице 1. Затем композицию для нанесения противомикробного покрытия подавали в водяную приемную камеру и наносили на бумагу влажным способом с применением каландра, используя примерно 500 ppm пиритиона цинка, 950 ppm тиабендазола и 750 ppm азоксистробина.Manila paper was obtained according to the technical requirements for this grade. The antimicrobial coating composition was prepared as described in Table 1. Then, the antimicrobial coating composition was applied to the water receiving chamber and wet applied using calender using approximately 500 ppm zinc pyrithione, 950 ppm thiabendazole and 750 ppm azoxystrobin.
ПРИМЕР 3 EXAMPLE 3
Неплесневеющая газетная бумагаMoldless Newsprint
Бумагу Newslined получали с применением лайнера, в котором 30% форзацной бумаги смешано с 70% газетной бумаги. Противомикробное покрытие получали путем приготовления 6,5% раствора полимеризованного диметилсилоксана в воде и смешивания его с 3-йод-2-пропинилбутилкарбаматом (IPBC) с получением 2% раствора IPBC. Затем такую композицию для нанесения противомикробного покрытия подавали в водяную камеру и наносили на бумагу Newslined влажным способом с помощью каландра при количестве активного фунгицида примерно 500 ppm. Для улучшения водостойкости и связывания фунгицида с листом наносили акриловый латекс.Newslined paper was obtained using a liner in which 30% flyleaf was mixed with 70% newsprint. An antimicrobial coating was obtained by preparing a 6.5% solution of polymerized dimethylsiloxane in water and mixing it with 3-iodine-2-propynylbutylcarbamate (IPBC) to obtain a 2% IPBC solution. Then, such an antimicrobial coating composition was applied to a water chamber and wetly applied to Newslined paper using a calender with an active fungicide amount of about 500 ppm. To improve the water resistance and the binding of the fungicide to the sheet, acrylic latex was applied.
Хотя были показаны и описаны конкретные варианты реализации изобретения, специалистам в данной области техники будет понятно, что указанные варианты можно подвергнуть изменениям и модификациям без отклонения от изобретения в его более широких аспектах и как изложено в приведенной ниже формуле изобретения.Although specific embodiments of the invention have been shown and described, it will be understood by those skilled in the art that these options can be modified and modified without departing from the invention in its broader aspects and as set forth in the claims below.
Claims (13)