RU2661296C1 - Method of applying the wear-proof coatings based on titanium carbide, titanium and aluminum on stamp steel - Google Patents
Method of applying the wear-proof coatings based on titanium carbide, titanium and aluminum on stamp steel Download PDFInfo
- Publication number
- RU2661296C1 RU2661296C1 RU2017124846A RU2017124846A RU2661296C1 RU 2661296 C1 RU2661296 C1 RU 2661296C1 RU 2017124846 A RU2017124846 A RU 2017124846A RU 2017124846 A RU2017124846 A RU 2017124846A RU 2661296 C1 RU2661296 C1 RU 2661296C1
- Authority
- RU
- Russia
- Prior art keywords
- titanium
- mass
- coating
- aluminum
- shell
- Prior art date
Abstract
Description
Изобретение относится к технологии нанесения покрытий на металлические поверхности с использованием концентрированных потоков энергии, в частности к технологии получения на поверхности штамповых сталей, работающих в тяжелых условиях штамповки, покрытий на основе карбида титана, титана и алюминия, которые могут быть использованы в штамповом производстве для штамповки в холодном состоянии с целью формирования поверхностей с высокой твердостью и износостойкостью.The invention relates to a technology for coating metal surfaces using concentrated energy flows, in particular to a technology for producing stamped steels operating under severe conditions of stamping, coatings based on titanium carbide, titanium and aluminum, which can be used in stamping for stamping in the cold state in order to form surfaces with high hardness and wear resistance.
Известен способ [1] электровзрывного напыления композиционных износостойких покрытий системы TiC-Mo на поверхности трения, характеризующийся тем, что размещают порошковую навеску из карбида титана между двумя слоями молибденовой фольги, осуществляют электрический взрыв фольги с формированием импульсной многофазной плазменной струи, проводят оплавление ею поверхности трения при значении удельного потока энергии 3,5…4,5 ГВт/м2 и напыление на оплавленный слой компонентов плазменной струи с последующей самозакалкой и формированием композиционного покрытия, содержащего карбид титана и молибден.The known method [1] of electric explosive spraying of composite wear-resistant coatings of the TiC-Mo system on a friction surface, characterized in that a powder sample of titanium carbide is placed between two layers of molybdenum foil, an electric explosion of the foil is carried out with the formation of a pulsed multiphase plasma jet, it is melted by the friction surface at a value of specific energy flow of 3.5 ... 4.5 GW / m 2, and spraying the melted layer on components of the plasma jet, followed by self-hardening and the formation of composite ion coating comprising titanium carbide and molybdenum.
Недостатком способа является высокая шероховатость напыленных покрытий, а также низкая степень гомогенизации структуры, выраженная в неоднородности фазового и элементного состава покрытий. Это ограничивает возможность практического применения изделий с такими покрытиями. После электровзрывного напыления (ЭВН) на поверхности покрытий неравномерно распределены многочисленные деформированные закристаллизовавшиеся микрокапли меди. Это может стать причиной быстрого износа покрытия [2, 3].The disadvantage of this method is the high roughness of the sprayed coatings, as well as a low degree of homogenization of the structure, expressed in the heterogeneity of the phase and elemental composition of the coatings. This limits the possibility of practical use of products with such coatings. After electroexplosive deposition (EVN), numerous deformed crystallized microdroplets of copper are unevenly distributed on the surface of the coatings. This can cause rapid wear of the coating [2, 3].
Наиболее близким к заявляемому является способ [4] нанесения износостойких покрытий на основе диборида титана и молибдена на стальные поверхности, включающий электрический взрыв композиционного электрически взрываемого проводника, состоящего из двухслойной плоской молибденовой оболочки массой 60-530 мг и сердечника в виде порошка диборида титана массой, равной 0,5-2,0 массы оболочки, формирование из продуктов взрыва импульсной многофазной плазменной струи, оплавление ею стальной поверхности при поглощаемой плотности мощности 3,5-4,5 ГВт/м2, осаждение на поверхность продуктов взрыва с формированием на ней композиционного покрытия системы TiB2-Mo и последующую импульсно-периодическую электронно-пучковую обработку поверхности покрытия при поглощаемой плотности энергии 40-60 Дж/см2, длительности импульсов 150-200 мкс и количестве импульсов 10-30.Closest to the claimed is a method [4] applying wear-resistant coatings based on titanium diboride and molybdenum on steel surfaces, comprising an electric explosion of a composite electrically exploded conductor, consisting of a two-layer flat molybdenum shell weighing 60-530 mg and a core in the form of a powder of titanium diboride mass, equal to 0.5-2.0 mass of the shell, the formation of explosion products of a pulsed multiphase plasma jet, its fusion of a steel surface with an absorbed power density of 3.5-4.5 GW / m 2 , deposition of explosion products onto the surface with the formation of a composite coating of the TiB 2 -Mo system on it and subsequent pulse-periodic electron-beam treatment of the coating surface at an absorbed energy density of 40-60 J / cm 2 , pulse duration 150-200 μs and the number of pulses 10- thirty.
Недостатком способа является низкая адгезия покрытия системы TiB2-Мо со стальной подложкой. В случае применения этого покрытия для штамповки неизбежно произойдет отслаивание покрытия уже на первых циклах штамповки. Это может стать причиной быстрого выхода из строя штампов [2, 3].The disadvantage of this method is the low adhesion of the coating system TiB 2 -Mo with a steel substrate. If this coating is used for stamping, the coating will inevitably peel off already in the first stamping cycles. This can cause a quick failure of stamps [2, 3].
Задачей заявляемого изобретения является получение композиционных покрытий карбид титана - титан - алюминий с наполненной микрокристаллической структурой, обладающих высокой адгезией покрытия с подложкой из штамповой стали, а также высокой степенью гомогенизации структуры их поверхностного слоя, зеркальным блеском поверхности, высокой микротвердостью и износостойкостью.The objective of the invention is to obtain composite coatings of titanium carbide - titanium - aluminum with a filled microcrystalline structure, with a high adhesion of the coating to the stamped steel substrate, as well as a high degree of homogenization of the structure of their surface layer, mirror surface gloss, high microhardness and wear resistance.
Поставленная задача реализуется способом нанесения износостойких покрытий на основе карбида титана, титана и алюминия на штамповые стали.The task is realized by the method of applying wear-resistant coatings based on titanium carbide, titanium and aluminum to die steels.
Способ включает электрический взрыв композиционного электрически взрываемого проводника, состоящего из двухслойной плоской алюминиевой оболочки массой 60-530 мг и сердечника в виде смеси порошков карбида титана массой, равной 0,5-2,0 массы оболочки, и титана массой, равной 0,5-2,0 массы оболочки, формирование из продуктов взрыва импульсной многофазной плазменной струи, оплавление ею поверхности штамповой стали при поглощаемой плотности мощности 4,6-4,8 ГВт/м2, осаждение на поверхность продуктов взрыва и формирование на ней композиционного покрытия системы TiC-Ti-Al и последующую импульсно-периодическую электронно-пучковую обработку поверхности покрытия при поглощаемой плотности энергии 40-60 Дж/см2, длительности импульсов 150-200 мкс и количестве импульсов 10-30 имп.The method includes an electric explosion of a composite electrically exploded conductor, consisting of a two-layer flat aluminum shell weighing 60-530 mg and a core in the form of a mixture of titanium carbide powders with a mass equal to 0.5-2.0 shell masses and titanium with a mass equal to 0.5- 2.0 mass of the shell, the formation of the products of the explosion of a pulsed multiphase plasma jet, its fusion of the surface of die steel with an absorbed power density of 4.6-4.8 GW / m 2 , deposition on the surface of the products of the explosion and the formation of a composite coating on it tiya of the TiC-Ti-Al system and the subsequent pulse-periodic electron-beam treatment of the coating surface at an absorbed energy density of 40-60 J / cm 2 , pulse duration 150-200 μs and the number of pulses 10-30 imp.
Продукты разрушения композиционного электрически взрываемого проводника образуют плазменную струю, служащую инструментом формирования на поверхности штамповой стали композиционного покрытия с наполненной структурой [5], образованного включениями карбида титана в титан-алюминиевой матрице. Последующая импульсно-периодическая электронно-пучковая обработка (ЭПО) покрытия сопровождается переплавлением его поверхностного слоя толщиной 20-40 мкм. Дефекты в виде микропор и микротрещин, выявляемые после ЭВН [2, 3], в нем не наблюдаются. Импульсно-периодическая ЭПО приводит к формированию в покрытии высокодисперсной и однородной структуры. Размеры включений карбида титана в титан-алюминиевой матрице уменьшаются в 2-8 раза по сравнению с их размерами сразу после ЭВН. Поверхность покрытия приобретает зеркальный блеск. Преимущество заявляемого способа по сравнению с прототипом заключается в формировании поверхностного слоя с высокой адгезией покрытия с подложкой из штамповой стали, низкой шероховатостью и гомогенизированной структурой, что увеличивает срок службы деталей, работающих в условиях штамповки, и расширяет область практического применения.The destruction products of a composite electrically exploded conductor form a plasma jet, which serves as an instrument for forming a composite coating with a filled structure [5] on the surface of die steel [5] formed by inclusions of titanium carbide in a titanium-aluminum matrix. The subsequent pulse-periodic electron-beam processing (EPO) of the coating is accompanied by remelting of its surface layer with a thickness of 20-40 microns. Defects in the form of micropores and microcracks detected after EI [2, 3] are not observed in it. Pulse-periodic EPO leads to the formation of a finely dispersed and uniform structure in the coating. The dimensions of the inclusions of titanium carbide in the titanium-aluminum matrix are reduced by 2-8 times in comparison with their sizes immediately after the EVN. The surface of the coating acquires a mirror shine. The advantage of the proposed method compared with the prototype is the formation of a surface layer with high adhesion to the substrate with a stamped steel substrate, low roughness and a homogenized structure, which increases the service life of parts operating under stamping conditions and expands the field of practical application.
Способ поясняется чертежом, где на фиг. 1 представлена структура поперечного сечения поверхностного слоя электровзрывного композиционного покрытия системы TiC-Ti-Al без воздействия ЭПО, на фиг. 2 - структура поперечного сечения поверхностного слоя электровзрывного композиционного покрытия системы TiC-Ti-Al после воздействия ЭПО.The method is illustrated in the drawing, where in FIG. 1 shows the cross-sectional structure of the surface layer of an electro-explosive composite coating of a TiC-Ti-Al system without exposure to EPO, FIG. 2 is a cross-sectional structure of a surface layer of an electro-explosive composite coating of a TiC-Ti-Al system after exposure to EPO.
Исследования методом сканирующей электронной микроскопии показали, что при ЭВН на стальных поверхностях, работающих в условиях штамповки, путем электрического взрыва композиционного электрически взрываемого проводника при поглощаемой плотности мощности 4,6-4,8 ГВт/м2 происходит формирование покрытия с композиционной наполненной структурой, когда в титан-алюминиевой матрице располагаются включения карбида титана с размерами от 1,0 до 2,0 мкм (фиг. 2). Если же использовать режим напыления, указанный в прототипе 3,5-4,5 ГВт/м2, то на границе покрытия со штамповой сталью образуются дефекты в виде пор. В покрытии наблюдаются дефекты в виде микропор и микротрещин. Указанный режим, при котором поглощаемая плотность мощности составляет 4,6-4,8 ГВт/м2, установлен эмпирически и является оптимальным, поскольку при интенсивности воздействия ниже 4,6 ГВт/м2 не происходит образование рельефа между покрытием и подложкой из штамповой стали, вследствие чего возможно отслаивание покрытия, а выше 4,8 ГВт/м2 происходит формирование развитого рельефа поверхности напыляемого покрытия. При значении массы алюминиевой фольги менее 60 мг становится невозможным изготовление из нее композиционного электрически взрываемого проводника. При значении массы алюминиевой фольги более 530 мг покрытие с композиционной наполненной структурой на поверхностях из штамповых сталей, работающих в условиях холодной штамповки, обладает большим количеством дефектов. При значении массы сердечника, состоящего из смеси порошков карбида титана массой менее 0,5 или более 2,0 массы оболочки и титана массой менее 0,5 или более 2,0 массы оболочки покрытие с композиционной наполненной структурой на поверхностях штамповых сталей, работающих в условиях холодной штамповки, также обладает дефектной структурой. Граница электровзрывного покрытия с подложкой не является ровной, что позволяет увеличить адгезию покрытия с подложкой.Scanning electron microscopy studies have shown that in case of ESP on steel surfaces operating under stamping conditions, by electric explosion of a composite electrically exploded conductor with an absorbed power density of 4.6-4.8 GW / m 2 , a coating with a filled structure is formed when titanium carbide inclusions with sizes from 1.0 to 2.0 μm are located in the titanium-aluminum matrix (Fig. 2). If you use the spraying mode specified in the prototype 3,5-4,5 GW / m 2 , then at the border of the coating with die steel formed defects in the form of pores. Defects in the form of micropores and microcracks are observed in the coating. The specified mode, in which the absorbed power density is 4.6-4.8 GW / m 2 , is established empirically and is optimal, since at an intensity of exposure below 4.6 GW / m 2 there is no relief formation between the coating and the stamped steel substrate as a result of which peeling of the coating is possible, and above 4.8 GW / m 2 , a developed relief of the surface of the sprayed coating is formed. When the mass value of aluminum foil is less than 60 mg, it becomes impossible to make a composite electrically exploded conductor from it. When the mass value of aluminum foil is more than 530 mg, a coating with a composite filled structure on the surfaces of die steels operating in cold stamping has a large number of defects. With a core mass value consisting of a mixture of titanium carbide powders with a mass of less than 0.5 or more than 2.0 shell masses and titanium with a mass of less than 0.5 or more than 2.0 shell masses, a coating with a composite filled structure on the surfaces of die steels operating under conditions cold stamping also has a defective structure. The boundary of the electroexplosive coating with the substrate is not even, which allows to increase the adhesion of the coating to the substrate.
Импульсно-периодическая ЭПО поверхности электровзрывного покрытия с поверхностной плотностью поглощаемой энергии 40-60 Дж/см2, длительностью импульсов 150-200 мкс, количеством импульсов 10-30 приводит к выглаживанию рельефа поверхности до образования зеркального блеска. Толщина модифицированных слоев после ЭПО изменяется в пределах от 20 до 40 мкм и незначительно увеличивается с ростом плотности энергии пучка электронов. Электронно-пучковая обработка, сопровождающаяся переплавлением слоя покрытия, приводит к формированию композиционной наполненной [5] структуры (фиг. 2). Дефекты в виде микропор и микротрещин в нем не наблюдаются. Размеры включений карбида титана в титан-алюминиевой матрице изменяются в пределах от 0,1 до 0,4 мкм. Импульсно-периодическая ЭПО поверхностного слоя приводит к формированию в нем более дисперсной и однородной структуры. Указанный режим является оптимальным, поскольку при поверхностной плотности энергии меньше 40 Дж/см2, длительности импульсов короче 150 мкс, количестве импульсов менее 10 имп. не происходит образования однородной структуры на основе карбида титана, титана, алюминия и диспергирования титана, алюминия и карбида титана в покрытии. При поверхностной плотности энергии больше 60 Дж/см2, длительности импульсов длиннее 200 мкс, количестве импульсов более 30 имп. происходит формирование рельефа поверхности.Pulse-periodic EPO of the surface of an electric explosive coating with a surface density of absorbed energy of 40-60 J / cm 2 , a pulse duration of 150-200 μs, and a number of pulses of 10-30 leads to smoothing of the surface relief until a mirror shine is formed. The thickness of the modified layers after EPO varies from 20 to 40 microns and slightly increases with increasing electron beam energy density. Electron-beam processing, accompanied by remelting of the coating layer, leads to the formation of a composite filled [5] structure (Fig. 2). Defects in the form of micropores and microcracks are not observed in it. The dimensions of the inclusions of titanium carbide in the titanium-aluminum matrix vary from 0.1 to 0.4 microns. Pulse-periodic EPO of the surface layer leads to the formation of a more dispersed and uniform structure in it. The indicated mode is optimal, since at a surface energy density of less than 40 J / cm 2 , the pulse duration is shorter than 150 μs, the number of pulses is less than 10 pulses. there is no formation of a homogeneous structure based on titanium carbide, titanium, aluminum and dispersion of titanium, aluminum and titanium carbide in the coating. When the surface energy density is more than 60 J / cm 2 , the pulse duration is longer than 200 μs, the number of pulses is more than 30 pulses. surface relief is formed.
Трибологические свойства (износостойкость и коэффициент трения) покрытий изучали в геометрии диск-штифт с помощью трибометра (CSEM) при комнатной температуре и влажности. В качестве контртела использовался алмазную пирамидку, диаметр трека 3,9 мм, скорость вращения - 1,5 см/с, нагрузка - 8 Н, дистанция до остановки - 123 м. Критерием износостойкости являлся удельный объем трека износа материала, который определялся с помощью лазерного оптического профилометра MicroMeasure 3D Station и рассчитывался по формуле:The tribological properties (wear resistance and coefficient of friction) of coatings were studied in the geometry of a disk pin using a tribometer (CSEM) at room temperature and humidity. A diamond pyramid was used as a counterbody, the track diameter was 3.9 mm, the rotation speed was 1.5 cm / s, the load was 8 N, the distance to stop was 123 m. The wear resistance criterion was the specific volume of the material wear track, which was determined using a laser MicroMeasure 3D Station optical profiler and calculated by the formula:
где R - радиус трека, А - площадь поперечного сечения канавки износа, F - величина приложенной нагрузки, L - пройденная шариком дистанция.where R is the radius of the track, A is the cross-sectional area of the wear groove, F is the magnitude of the applied load, L is the distance traveled by the ball.
В результате проведенных испытаний установлено, что износостойкость покрытий на основе карбида титана, титана и алюминия повышается в 2 раза по сравнению с штамповыми сталями 5ХНМ и Х12МФ после изотермического отжига по режиму: нагрев 850-870°C, охлаждение со скоростью 40 град/ч до 700-720°C, выдержка 3-4 ч, охлаждение со скоростью 50 град/ч до 550°C, воздух. Значения коэффициента трения для покрытий на основе карбида титана, титана и алюминия составляют 0,5…0,6.As a result of the tests, it was found that the wear resistance of coatings based on titanium, titanium and aluminum carbide increases by 2 times compared to 5XHM and X12MF die steels after isothermal annealing according to the regime: heating 850-870 ° C, cooling at a speed of 40 deg / h to 700-720 ° C, holding 3-4 hours, cooling at a speed of 50 deg / h to 550 ° C, air. The values of the coefficient of friction for coatings based on titanium carbide, titanium and aluminum are 0.5 ... 0.6.
Микротвердость измеряли на микротвердомере HVS-1000A. Значения микротвердости сформированных покрытий находятся в интервале 24000-25000 МПа. Нанотвердость измеряли с использованием системы Agilent U9820A Nano Indenter G200. Значение нанотвердости сформированных покрытий составляет 24500 МПа.Microhardness was measured on an HVS-1000A microhardness meter. The microhardness values of the formed coatings are in the range of 24000-25000 MPa. Nanohardness was measured using an Agilent U9820A Nano Indenter G200 system. The nanohardness of the formed coatings is 24500 MPa.
Примеры конкретного осуществления способаExamples of specific implementation of the method
Пример 1Example 1
Обработке подвергали лист из штамповой стали 5ХНМ толщиной 25 мм площадью 4 см2. Использовали композиционный электрически взрываемый проводник, состоящий из оболочки и сердечника в виде порошков карбида титана и титана, при этом оболочка состояла из двух слоев электрически взрываемой плоской алюминиевой фольги массой 60 мг, а масса порошков карбида титана и титана в сердечнике составляла по 30 мг для каждого из порошков. Сформированной плазменной струей оплавляли поверхность листа штамповой стали 5ХНМ при поглощаемой плотности мощности 4,6 ГВт/м2 и формировали на ней композиционное электровзрывное покрытие системы TiC-Ti-Al. После самозакалки покрытия при теплоотводе в объем стального листа осуществляли импульсно-периодическую ЭПО поверхности электровзрывного покрытия при поверхностной плотности энергии 40 Дж/см2, длительности импульсов - 150 мкс, количестве импульсов - 10 имп.The processing was subjected to a sheet of die steel 5XHM 25 mm thick with an area of 4 cm 2 . A composite electrically exploded conductor was used, consisting of a shell and core in the form of titanium carbide and titanium carbide powders, while the shell consisted of two layers of 60 mg electrically exploded flat aluminum foil, and the mass of titanium carbide and titanium carbide powders in the core was 30 mg for each from powders. The formed plasma jet was used to melt the surface of a sheet of 5XHM die steel at an absorbed power density of 4.6 GW / m 2 and formed a composite electroexplosive coating of the TiC-Ti-Al system on it. After self-hardening of the coating with heat removal into the volume of the steel sheet, a pulse-periodic EPO of the surface of the electric explosive coating was carried out at a surface energy density of 40 J / cm 2 , the pulse duration was 150 μs, and the number of pulses was 10 pulses.
Получили износостойкое покрытие на основе карбида титана, титана и алюминия с высокой адгезией покрытия с подложкой на уровне когезии. На ОАО «Вест-2002» штампы из стали 5ХНМ, упрочненные заявляемым способом, показали увеличенный ресурс работы в 1,2 раза по сравнению со штампами без покрытия на основе карбида титана, титана и алюминия.Received a wear-resistant coating based on titanium carbide, titanium and aluminum with high adhesion to the substrate at the level of cohesion. At JSC "West-2002" dies made of steel 5XHM, hardened by the claimed method, showed an increased service life of 1.2 times compared with dies without coating based on titanium carbide, titanium and aluminum.
Пример 2Example 2
Обработке подвергали лист из штамповой стали Х12МФ толщиной 25 мм площадью 15 см2. Использовали композиционный электрически взрываемый проводник, состоящий из оболочки и сердечника в виде смеси порошков карбида титана и титана, при этом оболочка состояла из двух слоев электрически взрываемой плоской алюминиевой фольги массой 530 мг, а масса порошков карбида титана и титана в сердечнике составляла по 1060 мг для каждого из порошков. Сформированной плазменной струей оплавляли поверхность листа из штамповой стали Х12МФ при поглощаемой плотности мощности 4,8 ГВт/м2 и формировали на ней композиционное электровзрывное покрытие системы TiC-Ti-Al. После самозакалки покрытия при теплоотводе в объем основы стального листа осуществляли импульсно-периодическую ЭПО поверхности электровзрывного покрытия при поверхностной плотности энергии 60 Дж/см2, длительности импульсов - 200 мкс, количестве импульсов - 30 имп.The processing was subjected to a sheet of die steel X12MF with a thickness of 25 mm and an area of 15 cm 2 . A composite electrically exploded conductor was used, consisting of a shell and a core in the form of a mixture of powders of titanium and titanium carbide, while the shell consisted of two layers of electrically exploded flat aluminum foil weighing 530 mg, and the mass of powders of titanium and titanium carbide in the core was 1060 mg for each of the powders. The formed plasma jet was used to melt the surface of a sheet of X12MF die steel at an absorbed power density of 4.8 GW / m 2 and formed a composite electroexplosive coating of the TiC-Ti-Al system on it. After self-hardening of the coating with heat removal into the bulk of the steel sheet, a pulse-periodic EPO of the surface of the electric explosion coating was carried out at a surface energy density of 60 J / cm 2 , pulse duration 200 μs, and the number of pulses 30 imp.
Получили износостойкое покрытие на основе карбида титана, титана и алюминия с высокой адгезией покрытия с подложкой на уровне когезии. На ОАО «Вест-2002» штампы из стали Х12МФ, упрочненные заявляемым способом, показали увеличенный ресурс работы в 1,2 раза по сравнению со штампами без покрытия на основе карбида титана, титана и алюминия.Received a wear-resistant coating based on titanium carbide, titanium and aluminum with high adhesion to the substrate at the level of cohesion. At JSC "West-2002" dies made of steel X12MF, hardened by the claimed method, showed an increased service life of 1.2 times compared with dies without coating based on titanium carbide, titanium and aluminum.
Источники информацииInformation sources
1. Патент РФ №2518037 на изобретение «Способ электровзрывного напыления композиционных износостойких покрытий системы TiC-Al на поверхности трения» / Романов Д.А., Олесюк О.В., Будовских Е.А., Громов В.Е.; заявл. 25.03.2013; опубл. 10.06.2014, бюл. №16. 8 с.1. RF patent No. 2518037 for the invention “Method of electric explosive spraying of composite wear-resistant coatings of the TiC-Al system on the friction surface” / Romanov D.A., Olesyuk O.V., Budovskikh E.A., Gromov V.E .; declared 03/25/2013; publ. 06/10/2014, bull. No. 16. 8 sec
2. Романов Д.А., Будовских Е.А., Громов В.Е. Электровзрывное напыление электроэрозионностойких покрытий: формирование структуры, фазового состава и свойств электроэрозионностойких покрытий методом электровзрывного напыления. - Saarbrucken: LAP LAMBERT Academic Publishing GmbH & Co. KG, 2012. - 170 c.2. Romanov D.A., Budovsky E.A., Gromov V.E. Electro-explosive spraying of electroerosion-resistant coatings: the formation of the structure, phase composition and properties of electroerosion-resistant coatings by the method of electric explosive spraying. - Saarbrucken: LAP LAMBERT Academic Publishing GmbH & Co. KG, 2012 .-- 170 c.
3. Электровзрывное напыление износо- и электроэрозионностойких покрытий / Д.А. Романов, Е.А. Будовских, В.Е. Громов, Ю.Ф. Иванов. - Новокузнецк: Изд-во ООО «Полиграфист», 2014. - 203 с.3. Electroexplosive spraying of wear- and electroerosion-resistant coatings / D.A. Romanov, E.A. Budovsky, V.E. Gromov, Yu.F. Ivanov. - Novokuznetsk: Publishing house LLC "Polygraphist", 2014. - 203 p.
4. Патент РФ №2583227 на изобретение «Способ нанесения износостойких покрытий на основе диборида титана и алюминия на стальные поверхности» / Романов Д.А., Будовских Е.А., Гончарова Е.Н., Громов В.Е.; заявл. 15.12.2014; опубл. 10.05.2016, бюл. №13. 7 с.4. RF patent No. 2583227 for the invention "Method of applying wear-resistant coatings based on titanium and aluminum diboride on steel surfaces" / Romanov D.A., Budovskikh E.A., Goncharova E.N., Gromov V.E .; declared 12/15/2014; publ. 05/10/2016, bull. No. 13. 7 sec
5. Мэттьюз М., Ролингс Р. Композиционные материалы. Механика и технология. - М.: Техносфера, 2004. - 408 с.5. Matthews M., Rawlings R. Composite materials. Mechanics and technology. - M .: Technosphere, 2004 .-- 408 p.
Claims (1)