RU2655408C1 - Method for application of wear-resistant coatings based on titanium carbide, nickel and molybdenum on die steels - Google Patents
Method for application of wear-resistant coatings based on titanium carbide, nickel and molybdenum on die steels Download PDFInfo
- Publication number
- RU2655408C1 RU2655408C1 RU2017125425A RU2017125425A RU2655408C1 RU 2655408 C1 RU2655408 C1 RU 2655408C1 RU 2017125425 A RU2017125425 A RU 2017125425A RU 2017125425 A RU2017125425 A RU 2017125425A RU 2655408 C1 RU2655408 C1 RU 2655408C1
- Authority
- RU
- Russia
- Prior art keywords
- nickel
- coating
- mass
- molybdenum
- shell
- Prior art date
Abstract
Description
Изобретение относится к технологии нанесения покрытий на металлические поверхности с использованием концентрированных потоков энергии, в частности к технологии получения на поверхности штамповых сталей, работающих в тяжелых условиях штамповки, покрытий на основе карбида титана, никеля и молибдена, которые могут быть использованы в штамповом производстве для штамповки в холодном состоянии с целью формирования поверхностей с высокой твердостью и износостойкостью.The invention relates to a technology for coating metal surfaces using concentrated energy flows, in particular to a technology for producing stamped steels operating under severe stamping conditions, coatings based on titanium carbide, nickel and molybdenum, which can be used in stamping for stamping in the cold state in order to form surfaces with high hardness and wear resistance.
Известен способ [1] электровзрывного напыления композиционных износостойких покрытий системы TiC-Mo на поверхности трения, характеризующийся тем, что размещают порошковую навеску из карбида титана между двумя слоями молибденовой фольги, осуществляют электрический взрыв фольги с формированием импульсной многофазной плазменной струи, проводят оплавление ею поверхности трения при значении удельного потока энергии 3,5…4,5 ГВт/м2 и напыление на оплавленный слой компонентов плазменной струи с последующей самозакалкой и формированием композиционного покрытия, содержащего карбид титана и молибден.The known method [1] of electric explosive spraying of composite wear-resistant coatings of the TiC-Mo system on a friction surface, characterized in that a powder sample of titanium carbide is placed between two layers of molybdenum foil, an electric explosion of the foil is carried out with the formation of a pulsed multiphase plasma jet, it is melted by the friction surface at a value of specific energy flow of 3.5 ... 4.5 GW / m 2, and spraying the melted layer on components of the plasma jet, followed by self-hardening and the formation of composite ion coating comprising titanium carbide and molybdenum.
Недостатком способа является высокая шероховатость напыленных покрытий, а также низкая степень гомогенизации структуры, выраженная в неоднородности фазового и элементного состава покрытий. Это ограничивает возможность практического применения изделий с такими покрытиями. После электровзрывного напыления (ЭВН) на поверхности покрытий неравномерно распределены многочисленные деформированные закристаллизовавшиеся микрокапли меди. Это может стать причиной быстрого износа покрытия [2, 3].The disadvantage of this method is the high roughness of the sprayed coatings, as well as a low degree of homogenization of the structure, expressed in the heterogeneity of the phase and elemental composition of the coatings. This limits the possibility of practical use of products with such coatings. After electroexplosive deposition (EVN), numerous deformed crystallized microdroplets of copper are unevenly distributed on the surface of the coatings. This can cause rapid wear of the coating [2, 3].
Наиболее близким к заявляемому является способ [4] нанесения износостойких покрытий на основе диборида титана и молибдена на стальные поверхности, включающий электрический взрыв композиционного электрически взрываемого проводника, состоящего из двухслойной плоской молибденовой оболочки массой 60-530 мг и сердечника в виде порошка диборида титана массой, равной 0,5-2,0 массы оболочки, формирование из продуктов взрыва импульсной многофазной плазменной струи, оплавление ею стальной поверхности при поглощаемой плотности мощности 3,5-4,5 ГВт/м2, осаждение на поверхность продуктов взрыва с формированием на ней композиционного покрытия системы TiB2-Mo и последующую импульсно-периодическую электронно-пучковую обработку поверхности покрытия при поглощаемой плотности энергии 40-60 Дж/см2, длительности импульсов 150-200 мкс и количестве импульсов 10-30.Closest to the claimed is a method [4] applying wear-resistant coatings based on titanium diboride and molybdenum on steel surfaces, comprising an electric explosion of a composite electrically exploded conductor, consisting of a two-layer flat molybdenum shell weighing 60-530 mg and a core in the form of a powder of titanium diboride mass, equal to 0.5-2.0 mass of the shell, the formation of explosion products of a pulsed multiphase plasma jet, its fusion of a steel surface with an absorbed power density of 3.5-4.5 GW / m 2 , deposition of explosion products onto the surface with the formation of a composite coating of the TiB 2 -Mo system on it and subsequent pulse-periodic electron-beam treatment of the coating surface with an absorbed energy density of 40-60 J / cm 2 , pulse duration 150-200 μs and the number of pulses 10- thirty.
Недостатком способа является низкая адгезия покрытия системы TiB2-Мо со стальной подложкой. В случае применения этого покрытия для штамповки неизбежно произойдет отслаивание покрытия уже на первых циклах штамповки. Это может стать причиной быстрого выхода из строя штампов [2, 3].The disadvantage of this method is the low adhesion of the coating system TiB 2 -Mo with a steel substrate. If this coating is used for stamping, the coating will inevitably peel off already in the first stamping cycles. This can cause a quick failure of stamps [2, 3].
Задачей заявляемого изобретения является получение композиционных покрытий карбид титана - никель - молибден с наполненной микрокристаллической структурой, обладающих высокой адгезией покрытия с подложкой из штамповой стали, а также высокой степенью гомогенизации структуры их поверхностного слоя, зеркальным блеском поверхности, высокой микротвердостью и износостойкостью.The objective of the invention is to obtain composite coatings of titanium carbide - nickel - molybdenum with a filled microcrystalline structure, with high adhesion of the coating to the die steel substrate, as well as a high degree of homogenization of the structure of their surface layer, specular gloss of the surface, high microhardness and wear resistance.
Поставленная задача реализуется способом нанесения износостойких покрытий на основе карбида титана, никеля и молибдена на штамповые стали.The task is realized by the method of applying wear-resistant coatings based on titanium carbide, nickel and molybdenum to die steels.
Способ включает электрический взрыв композиционного электрически взрываемого проводника, состоящего из двухслойной плоской молибденовой оболочки массой 60-530 мг и сердечника в виде смеси порошков карбида титана массой, равной 0,5-2,0 массы оболочки, и никеля массой, равной 0,5-2,0 массы оболочки, формирование из продуктов взрыва импульсной многофазной плазменной струи, оплавление ею поверхности штамповой стали при поглощаемой плотности мощности 4,6-4,8 ГВт/м2, осаждение на поверхность продуктов взрыва и формирование на ней композиционного покрытия системы TiC-Ni-Mo и последующую импульсно-периодическую электронно-пучковую обработку поверхности покрытия при поглощаемой плотности энергии 40-60 Дж/см2, длительности импульсов 150-200 мкс и количестве импульсов 10-30.The method includes an electric explosion of a composite electrically exploded conductor, consisting of a two-layer flat molybdenum shell weighing 60-530 mg and a core in the form of a mixture of titanium carbide powders with a mass equal to 0.5-2.0 shell masses and nickel with a mass equal to 0.5- 2.0 mass of the shell, the formation of the products of the explosion of a pulsed multiphase plasma jet, its fusion of the surface of die steel with an absorbed power density of 4.6-4.8 GW / m 2 , deposition on the surface of the products of the explosion and the formation of composite coating on it The existence of the TiC-Ni-Mo system and the subsequent repetitively pulsed electron-beam treatment of the coating surface at an absorbed energy density of 40-60 J / cm 2 , pulse durations of 150-200 μs and the number of pulses of 10-30.
Продукты разрушения композиционного электрически взрываемого проводника образуют плазменную струю, служащую инструментом формирования на поверхности штамповой стали композиционного покрытия с наполненной структурой [5], образованного включениями карбида титана в никелево-молибденовой матрице. Последующая импульсно-периодическая электронно-пучковая обработка (ЭПО) покрытия сопровождается переплавлением его поверхностного слоя толщиной 20-40 мкм. Дефекты в виде микропор и микротрещин, выявляемые после ЭВН [2, 3], в нем не наблюдаются. Импульсно-периодическая ЭПО приводит к формированию в покрытии высокодисперсной и однородной структуры. Размеры включений карбида титана в никелево-молибденовой матрице уменьшаются в 2-4 раза по сравнению с их размерами сразу после ЭВН. Поверхность покрытия приобретает зеркальный блеск. Преимущество заявляемого способа по сравнению с прототипом заключается в формировании поверхностного слоя с высокой адгезией покрытия с подложкой из штамповой стали, низкой шероховатостью и гомогенизированной структурой, что увеличивает срок службы деталей, работающих в условиях штамповки, и расширяет область практического применения.The destruction products of a composite electrically exploded conductor form a plasma jet, which serves as an instrument for forming a composite coating with a filled structure [5] on the surface of die steel [5] formed by inclusions of titanium carbide in a nickel-molybdenum matrix. The subsequent pulse-periodic electron-beam processing (EPO) of the coating is accompanied by remelting of its surface layer with a thickness of 20-40 microns. Defects in the form of micropores and microcracks detected after EI [2, 3] are not observed in it. Pulse-periodic EPO leads to the formation of a finely dispersed and uniform structure in the coating. The sizes of inclusions of titanium carbide in the nickel-molybdenum matrix are reduced by 2-4 times in comparison with their sizes immediately after the EVN. The surface of the coating acquires a mirror shine. The advantage of the proposed method compared with the prototype is the formation of a surface layer with high adhesion to the substrate with a stamped steel substrate, low roughness and a homogenized structure, which increases the service life of parts operating under stamping conditions and expands the field of practical application.
Способ поясняется чертежом, где на фиг. 1 представлена структура поперечного сечения поверхностного слоя электровзрывного композиционного покрытия системы TiC-Ni-Mo без воздействия ЭПО, на фиг. 2 - структура поперечного сечения поверхностного слоя электровзрывного композиционного покрытия системы TiC-Ni-Mo после воздействия ЭПО.The method is illustrated in the drawing, where in FIG. 1 shows the cross-sectional structure of the surface layer of an electro-explosive composite coating of a TiC-Ni-Mo system without exposure to EPO, FIG. 2 is a cross-sectional structure of the surface layer of an electro-explosive composite coating of a TiC-Ni-Mo system after exposure to EPO.
Исследования методом сканирующей электронной микроскопии показали, что при ЭВН на стальных поверхностях, работающих в условиях штамповки, путем электрического взрыва композиционного электрически взрываемого проводника при поглощаемой плотности мощности 4,6-4,8 ГВт/м2 происходит формирование покрытия с композиционной наполненной структурой, когда в никелево-молибденовой матрице располагаются включения карбида титана с размерами от 1,0 до 2,0 мкм (фиг. 2). Если же использовать режим напыления, указанный в прототипе 3,5-4,5 ГВт/м2, то на границе покрытия со штамповой сталью образуются дефекты в виде пор. В покрытии наблюдаются дефекты в виде микропор и микротрещин. Указанный режим, при котором поглощаемая плотность мощности составляет 4,6-4,8 ГВт/м2, установлен эмпирически и является оптимальным, поскольку при интенсивности воздействия ниже 4,6 ГВт/м2 не происходит образование рельефа между покрытием и подложкой из штамповой стали, вследствие чего возможно отслаивание покрытия, а выше 4,8 ГВт/м2 происходит формирование развитого рельефа поверхности напыляемого покрытия. При значении массы молибденовой фольги менее 60 мг становится невозможным изготовление из нее композиционного электрически взрываемого проводника. При значении массы молибденовой фольги более 530 мг покрытие с композиционной наполненной структурой на поверхностях из штамповых сталей, работающих в условиях холодной штамповки, обладает большим количеством дефектов. При значении массы сердечника, состоящего из смеси порошков карбида титана массой менее 0,5 или более 2,0 массы оболочки и никеля массой менее 0,5 или более 2,0 массы оболочки покрытие с композиционной наполненной структурой на поверхностях штамповых сталей, работающих в условиях холодной штамповки, также обладает дефектной структурой. Граница электровзрывного покрытия с подложкой не является ровной, что позволяет увеличить адгезию покрытия с подложкой.Scanning electron microscopy studies have shown that in case of ESP on steel surfaces operating under stamping conditions, by electric explosion of a composite electrically exploded conductor with an absorbed power density of 4.6-4.8 GW / m 2 , a coating with a filled structure is formed when titanium carbide inclusions with sizes from 1.0 to 2.0 μm are located in the nickel-molybdenum matrix (Fig. 2). If you use the spraying mode specified in the prototype 3,5-4,5 GW / m 2 , then at the border of the coating with die steel formed defects in the form of pores. Defects in the form of micropores and microcracks are observed in the coating. The specified mode, in which the absorbed power density is 4.6-4.8 GW / m 2 , is established empirically and is optimal, since at an intensity of exposure below 4.6 GW / m 2 there is no relief formation between the coating and the stamped steel substrate as a result of which peeling of the coating is possible, and above 4.8 GW / m 2 , a developed relief of the surface of the sprayed coating is formed. When the mass value of the molybdenum foil is less than 60 mg, it becomes impossible to make a composite electrically exploded conductor from it. With a molybdenum foil weight of more than 530 mg, a coating with a composite filled structure on the surfaces of die steels operating in cold stamping has a large number of defects. With a core mass value consisting of a mixture of titanium carbide powders weighing less than 0.5 or more than 2.0 shell masses and nickel weighing less than 0.5 or more than 2.0 shell masses, a coating with a composite filled structure on the surfaces of die steels operating under conditions cold stamping also has a defective structure. The boundary of the electroexplosive coating with the substrate is not even, which allows to increase the adhesion of the coating to the substrate.
Импульсно-периодическая ЭПО поверхности электровзрывного покрытия с поверхностной плотностью поглощаемой энергии 40-60 Дж/см2, длительностью импульсов 150-200 мкс, количеством импульсов 10-30 приводит к выглаживанию рельефа поверхности до образования зеркального блеска. Толщина модифицированных слоев после ЭПО изменяется в пределах от 20 до 40 мкм и незначительно увеличивается с ростом плотности энергии пучка электронов. Электронно-пучковая обработка, сопровождающаяся переплавлением слоя покрытия, и приводит к формированию композиционной наполненной [5] структуры (фиг. 2). Дефекты в виде микропор и микротрещин в нем не наблюдаются. Размеры включений карбида титана в никелево-молибденовой матрице изменяются в пределах от 0,1 до 0,4 мкм. Импульсно-периодическая ЭПО поверхностного слоя приводит к формированию в нем более дисперсной и однородной структуры. Указанный режим является оптимальным, поскольку при поверхностной плотности энергии меньше 40 Дж/см2, длительности импульсов короче 150 мкс, количестве импульсов менее 10 не происходит образования однородной структуры на основе карбида титана, никеля, молибдена и диспергирования никеля, молибдена и карбида титана в покрытии. При поверхностной плотности энергии больше 60 Дж/см2, длительности импульсов длиннее 200 мкс, количестве импульсов более 30 происходит формирование рельефа поверхности.Pulse-periodic EPO of the surface of an electric explosive coating with a surface density of absorbed energy of 40-60 J / cm 2 , a pulse duration of 150-200 μs, and a number of pulses of 10-30 leads to smoothing of the surface relief until a mirror shine is formed. The thickness of the modified layers after EPO varies from 20 to 40 microns and slightly increases with increasing electron beam energy density. Electron-beam processing, accompanied by remelting of the coating layer, leads to the formation of a composite filled [5] structure (Fig. 2). Defects in the form of micropores and microcracks are not observed in it. The sizes of inclusions of titanium carbide in the nickel-molybdenum matrix vary from 0.1 to 0.4 microns. Pulse-periodic EPO of the surface layer leads to the formation of a more dispersed and uniform structure in it. This mode is optimal, since at a surface energy density of less than 40 J / cm 2 , the pulse duration is shorter than 150 μs, the number of pulses is less than 10, a uniform structure does not form on the basis of titanium carbide, nickel, molybdenum and dispersion of nickel, molybdenum and titanium carbide in the coating . When the surface energy density is more than 60 J / cm 2 , the pulse duration is longer than 200 μs, and the number of pulses is more than 30, a surface relief is formed.
Трибологические свойства (износостойкость и коэффициент трения) покрытий изучали в геометрии диск-штифт с помощью трибометра (CSEM) при комнатной температуре и влажности. В качестве контртела использовали алмазную пирамидку, диаметр трека 3,9 мм, скорость вращения - 1,5 см/с, нагрузка - 8 Н, дистанция до остановки - 123 м. Критерием износостойкости являлся удельный объем трека износа материала, который определялся с помощью лазерного оптического профилометра MicroMeasure 3D Station и рассчитывался по формуле:The tribological properties (wear resistance and coefficient of friction) of coatings were studied in the geometry of a disk pin using a tribometer (CSEM) at room temperature and humidity. A diamond pyramid was used as a counterbody, the track diameter was 3.9 mm, the rotation speed was 1.5 cm / s, the load was 8 N, the distance to stop was 123 m. The wear resistance criterion was the specific volume of the material wear track, which was determined using a laser MicroMeasure 3D Station optical profiler and calculated by the formula:
где R - радиус трека, А - площадь поперечного сечения канавки износа, F - величина приложенной нагрузки, L - пройденная шариком дистанция.where R is the radius of the track, A is the cross-sectional area of the wear groove, F is the magnitude of the applied load, L is the distance traveled by the ball.
В результате проведенных испытаний установлено, что износостойкость покрытий на основе карбида титана, никеля и молибдена повышается в 2 раза по сравнению с штамповыми сталями 5ХНМ и Х12МФ после изотермического отжига по режиму: нагрев 850-870°C, охлаждение со скоростью 40 град/ч до 700-720°C, выдержка 3-4 ч, охлаждение со скоростью 50 град/ч до 550°C, воздух. Значения коэффициента трения для покрытий на основе карбида титана, никеля и молибдена составляют 0,5…0,6.As a result of the tests, it was found that the wear resistance of coatings based on titanium carbide, nickel and molybdenum is 2 times higher than that of 5XHM and X12MF die steels after isothermal annealing according to the regime: heating 850-870 ° C, cooling at a speed of 40 deg / h to 700-720 ° C, holding 3-4 hours, cooling at a speed of 50 deg / h to 550 ° C, air. The values of the coefficient of friction for coatings based on titanium carbide, nickel and molybdenum are 0.5 ... 0.6.
Микротвердость измеряли на микротвердомере HVS-1000A. Значения микротвердости сформированных покрытий находятся в интервале 24000-25000 МПа. Нанотвердость измеряли с использованием системы Agilent U9820A Nano Indenter G200. Значения нанотвердости сформированных покрытий составляет 24 500 МПа.Microhardness was measured on an HVS-1000A microhardness meter. The microhardness values of the formed coatings are in the range of 24000-25000 MPa. Nanohardness was measured using an Agilent U9820A Nano Indenter G200 system. The values of the nanoc hardness of the formed coatings is 24 500 MPa.
Примеры конкретного осуществления способаExamples of specific implementation of the method
Пример 1.Example 1
Обработке подвергали лист из штамповой стали 5ХНМ толщиной 25 мм площадью 4 см2. Использовали композиционный электрически взрываемый проводник, состоящий из оболочки и сердечника в виде порошков карбида титана и никеля, при этом оболочка состояла из двух слоев электрически взрываемой плоской молибденовой фольги массой 60 мг, а масса порошков карбида титана и никеля в сердечнике составляла по 30 мг для каждого из порошков. Сформированной плазменной струей оплавляли поверхность листа штамповой стали 5ХНМ при поглощаемой плотности мощности 4,6 ГВт/м2 и формировали на ней композиционное электровзрывное покрытие системы TiC-Ni-Mo. После самозакалки покрытия при теплоотводе в объем стального листа осуществляли импульсно-периодическую ЭПО поверхности электровзрывного покрытия при поверхностной плотности энергии 40 Дж/см2, длительности импульсов - 150 мкс, количестве импульсов - 10.The processing was subjected to a sheet of die steel 5XHM 25 mm thick with an area of 4 cm 2 . A composite electrically exploded conductor was used, consisting of a shell and a core in the form of titanium and nickel carbide powders, while the shell consisted of two layers of 60 mg electrically exploded flat molybdenum foil, and the mass of titanium and nickel carbide powders in the core was 30 mg for each from powders. The formed plasma jet was used to melt the surface of a sheet of 5XHM die steel at an absorbed power density of 4.6 GW / m 2 and formed a composite electroexplosive coating of the TiC-Ni-Mo system on it. After self-hardening coating with the heat sink in the amount of steel sheet performed repetitively pulsed EPO electroexplosive surface coating when the surface energy density of 40 J / cm2, pulse duration - 150 microseconds, the number of pulses - 10.
Получили износостойкое покрытие на основе карбида титана, никеля и молибдена с высокой адгезией покрытия с подложкой на уровне когезии. На ОАО «Вест-2002» штампы из стали 5ХНМ, упрочненные заявляемым способом, показали увеличенный ресурс работы в 1,2 раза по сравнению со штампами без покрытия на основе карбида титана, никеля и молибдена.A wear-resistant coating based on titanium carbide, nickel and molybdenum was obtained with high adhesion of the coating to the substrate at the cohesion level. At JSC "West-2002" dies made of steel 5XHM, hardened by the claimed method, showed an increased service life of 1.2 times compared with dies without coating based on titanium carbide, nickel and molybdenum.
Пример 2.Example 2
Обработке подвергали лист из штамповой стали Х12МФ толщиной 25 мм площадью 15 см2. Использовали композиционный электрически взрываемый проводник, состоящий из оболочки и сердечника в виде смеси порошков карбида титана и никеля, при этом оболочка состояла из двух слоев электрически взрываемой плоской молибденовой фольги массой 530 мг, а масса порошков карбида титана и никеля в сердечнике составляла по 1060 мг для каждого из порошков. Сформированной плазменной струей оплавляли поверхность листа из штамповой стали Х12МФ при поглощаемой плотности мощности 4,8 ГВт/м2 и формировали на ней композиционное электровзрывное покрытие системы TiC-Ni-Mo. После самозакалки покрытия при теплоотводе в объем основы стального листа осуществляли импульсно-периодическую ЭПО поверхности электровзрывного покрытия при поверхностной плотности энергии 60 Дж/см2, длительности импульсов - 200 мкс, количестве импульсов - 30.The processing was subjected to a sheet of die steel X12MF with a thickness of 25 mm and an area of 15 cm 2 . A composite electrically exploded conductor was used, consisting of a shell and core in the form of a mixture of titanium carbide and nickel powders, while the shell consisted of two layers of 530 mg electrically exploded flat molybdenum foil, and the mass of titanium carbide and nickel powders in the core was 1060 mg for each of the powders. The formed plasma jet melted the surface of a sheet of X12MF die steel at an absorbed power density of 4.8 GW / m 2 and formed a composite electroexplosive coating of the TiC-Ni-Mo system on it. After self-hardening of the coating with heat removal into the bulk of the steel sheet base, a pulse-periodic EPO of the surface of the electric explosive coating was carried out at a surface energy density of 60 J / cm 2 , pulse duration 200 μs, and the number of pulses 30.
Получили износостойкое покрытие на основе карбида титана, никеля и молибдена с высокой адгезией покрытия с подложкой на уровне когезии. На ОАО «Вест-2002» штампы из стали Х12МФ, упрочненные заявляемым способом, показали увеличенный ресурс работы в 1,2 раза по сравнению со штампами без покрытия на основе карбида титана, никеля и молибдена.A wear-resistant coating based on titanium carbide, nickel and molybdenum was obtained with high adhesion of the coating to the substrate at the cohesion level. At JSC "West-2002" dies made of steel X12MF, hardened by the claimed method, showed an increased service life of 1.2 times compared with dies without coating based on titanium carbide, nickel and molybdenum.
Источники информацииInformation sources
1. Патент РФ №2518037 на изобретение «Способ электровзрывного напыления композиционных износостойких покрытий системы TiC-Mo на поверхности трения» / Романов Д.А., Олесюк О.В., Будовских Е.А., Громов В.Е.; заявл. 25.03.2013; опубл. 10.06.2014, Бюл. №16. 8 с.1. RF patent No. 2518037 for the invention “Method of electric explosive spraying of composite wear-resistant coatings of a TiC-Mo system on a friction surface” / Romanov D.A., Olesyuk O.V., Budovskikh E.A., Gromov V.E .; declared 03/25/2013; publ. 06/10/2014, Bull. No. 16. 8 sec
2. Романов Д.А., Будовских Е.А., Громов В.Е. Электровзрывное напыление электроэрозионностойких покрытий: формирование структуры, фазового состава и свойств электроэрозионностойких покрытий методом электровзрывного напыления. - Saarbrucken: LAP LAMBERT Academic Publishing GmbH & Co. KG, 2012.- 170 c.2. Romanov D.A., Budovsky E.A., Gromov V.E. Electro-explosive spraying of electroerosion-resistant coatings: the formation of the structure, phase composition and properties of electroerosion-resistant coatings by the method of electric explosive spraying. - Saarbrucken: LAP LAMBERT Academic Publishing GmbH & Co. KG, 2012.- 170 c.
3. Электровзрывное напыление износо- и электроэрозионностойких покрытий / Д.А. Романов, Е.А. Будовских, В.Е. Громов, Ю.Ф. Иванов. - Новокузнецк: Изд-во ООО «Полиграфист», 2014. - 203 с.3. Electroexplosive spraying of wear- and electroerosion-resistant coatings / D.A. Romanov, E.A. Budovsky, V.E. Gromov, Yu.F. Ivanov. - Novokuznetsk: Publishing house LLC "Polygraphist", 2014. - 203 p.
4. Патент РФ №2583227 изобретение «Способ нанесения износостойких покрытий на основе диборида титана и молибдена на стальные поверхности» / Романов Д.А., Будовских Е.А., Гончарова Е.Н., Громов В.Е.; заявл. 15.12.2014; опубл. 10.05.2016, Бюл. №13. 7 с.4. RF patent No. 2583227 invention "A method for applying wear-resistant coatings based on titanium diboride and molybdenum on steel surfaces" / Romanov D.A., Budovskikh E.A., Goncharova E.N., Gromov V.E .; declared 12/15/2014; publ. 05/10/2016, Bull. No. 13. 7 sec
5. Мэттьюз М., Ролингс Р. Композиционные материалы. Механика и технология. - М.: Техносфера, 2004. - 408 с.5. Matthews M., Rawlings R. Composite materials. Mechanics and technology. - M .: Technosphere, 2004 .-- 408 p.
Claims (1)