RU2622954C1 - Manufacturing method of fiberglass reinforcement - Google Patents
Manufacturing method of fiberglass reinforcement Download PDFInfo
- Publication number
- RU2622954C1 RU2622954C1 RU2016117325A RU2016117325A RU2622954C1 RU 2622954 C1 RU2622954 C1 RU 2622954C1 RU 2016117325 A RU2016117325 A RU 2016117325A RU 2016117325 A RU2016117325 A RU 2016117325A RU 2622954 C1 RU2622954 C1 RU 2622954C1
- Authority
- RU
- Russia
- Prior art keywords
- fiberglass
- binder
- ribbon
- preforms
- manufacturing
- Prior art date
Abstract
Description
Изобретение относится к производству стеклопластиковой арматуры для бетона.The invention relates to the production of fiberglass reinforcement for concrete.
Известен способ изготовления стеклопластиковой арматуры, предусматривающий формование из стекловолокна жгута, его пропитку раствором полимерного связующего, формование заготовок с приданием ей профиля до завершения процесса полимеризации связующего, отверждение связующего [1].A known method of manufacturing fiberglass reinforcement, comprising forming a fiberglass tow, impregnating it with a solution of a polymer binder, forming blanks to give it a profile until the completion of the polymerization of the binder, curing the binder [1].
Задача изобретения заключается в увеличении прочности сцепления стеклопластиковой арматуры с бетоном.The objective of the invention is to increase the adhesion strength of fiberglass reinforcement with concrete.
Технический результат достигается тем, что по способу изготовления стеклопластиковой арматуры, предусматривающему формование из стекловолокна жгута, его пропитку раствором полимерного связующего, формование заготовок с приданием им профиля до завершения процесса полимеризации связующего, отверждение связующего, до отверждения связующего между двумя заготовками полукруглого поперечного сечения, сложенными плоскостями, размещают пропитанную полимерным связующим ленту стеклохолста или ленту стеклоткани, края которой выступают из заготовок, после чего заготовки с лентой скручивают по винтовой линии.The technical result is achieved by the fact that according to the method of manufacturing fiberglass reinforcement, forming a fiberglass bundle, impregnating it with a polymer binder solution, forming the blanks to give them a profile until the binder is polymerized, curing the binder until the binder cures between the two semi-circular cross-section blanks folded planes, place the fiberglass tape impregnated with a polymer binder or a fiberglass tape, the edges of which protrude from preparations, after which blanks with tape are twisted along a helix.
На фиг. 1 изображены две заготовки полукруглого поперечного сечения, сложенные плоскостями, с размещенной между ними лентой: где 1 - верхняя заготовка прута; 2 - нижняя заготовка прута; 3 - лента стеклохолста; на фиг. 2 - фрагмент готовой арматуры.In FIG. 1 shows two billets of a semicircular cross section, folded by planes, with a tape placed between them: where 1 is the upper billet of the rod; 2 - the bottom blank of the rod; 3 - fiberglass tape; in FIG. 2 - a fragment of the finished reinforcement.
Способ поясняется примерами.The method is illustrated by examples.
1. Из стекловолокна (например, алюмоборосиликатного) формуют жгут, пропитывают его раствором полимерного связующего (например, смола эпоксидная), формуют заготовки прута с приданием им профиля полукруглого поперечного сечения. Между двумя заготовками (верхней и нижней) полукруглого поперечного сечения, сложенными плоскостями, размещают пропитанную полимерным связующим (смола эпоксидная) ленту стеклохолста (например, стеклохолста из рубленых стеклянных нитей), при этом края ленты выступают из заготовок. Затем заготовки с лентой скручивают по винтовой линии и осуществляют отверждение полимерного связующего (например, путем термообработки при температуре 90-180°С).1. A bundle is formed from fiberglass (for example, aluminoborosilicate), impregnated with a solution of a polymer binder (for example, epoxy resin), the rod blanks are formed to give them a semicircular cross-sectional profile. Between two preforms (upper and lower) of a semicircular cross section, folded by planes, a fiberglass tape impregnated with a polymer binder (epoxy resin) is placed (for example, fiberglass from chopped glass fibers), while the edges of the tape protrude from the blanks. Then the blanks with tape are twisted along a helix and the polymer binder is cured (for example, by heat treatment at a temperature of 90-180 ° C).
2. Из стекловолокна (например, алюмомагнезиального) формуют жгут, пропитывают его раствором полимерного связующего (например, смола полиэфирная ПН-3), формуют заготовки прута с приданием им профиля полукруглого поперечного сечения. Между двумя заготовками (верхней и нижней) полукруглого поперечного сечения, сложенными плоскостями, размещают пропитанную полимерным связующим (смола полиэфирная ПН-3) ленту стеклоткани, при этом края ленты выступают из заготовок. Затем заготовки с лентой скручивают по винтовой линии и осуществляют отверждение полимерного связующего (например, путем термообработки при температуре 90-180°С).2. A bundle is formed from fiberglass (for example, alumina-magnesian), impregnated with a solution of a polymer binder (for example, polyester resin PN-3), and rod blanks are formed to give them a semicircular cross-sectional profile. Between the two blanks (upper and lower) of a semicircular cross section, folded by planes, a fiberglass tape impregnated with a polymeric binder (polyester resin PN-3) is placed, with the edges of the tape protruding from the blanks. Then the blanks with tape are twisted along a helix and the polymer binder is cured (for example, by heat treatment at a temperature of 90-180 ° C).
Выступающие из скрученного прута стеклопластиковой арматуры участки ленты стеклохолста или ленты стеклоткани повышают прочность сцепления прута с бетоном.The protruding sections of the fiberglass reinforcement rod of the fiberglass tape or fiberglass tape increase the adhesion of the rod to concrete.
Источники информацииInformation sources
1. Фролов Н.П. Стеклопластиковая арматура и стеклопластбетонные конструкции / Н.П. Фролов. - М.: Стройиздат, 1980. - С. 20-24.1. Frolov N.P. Fiberglass reinforcement and fiberglass concrete structures / N.P. Frolov. - M .: Stroyizdat, 1980 .-- S. 20-24.
Claims (1)