RU2489404C1 - Raw mix for haydite production - Google Patents
Raw mix for haydite production Download PDFInfo
- Publication number
- RU2489404C1 RU2489404C1 RU2012113522/03A RU2012113522A RU2489404C1 RU 2489404 C1 RU2489404 C1 RU 2489404C1 RU 2012113522/03 A RU2012113522/03 A RU 2012113522/03A RU 2012113522 A RU2012113522 A RU 2012113522A RU 2489404 C1 RU2489404 C1 RU 2489404C1
- Authority
- RU
- Russia
- Prior art keywords
- waste
- zircon
- water
- clay
- production
- Prior art date
Abstract
Description
Изобретение относится к промышленности строительных материалов и касается производства керамзита.The invention relates to the building materials industry and for the production of expanded clay.
Известна сырьевая смесь для производства керамзита, содержащая, мас.%: глинистое сырье 75,5-76,8; волокнистые отходы первичной переработки шерсти 0,9-1,4; вода - остальное [1].Known raw mix for the production of expanded clay, containing, wt.%: Clay raw materials 75.5-76.8; fibrous waste from primary wool processing 0.9-1.4; water - the rest [1].
Задачей изобретения является повышение прочности керамзита, полученного из сырьевой смеси.The objective of the invention is to increase the strength of expanded clay obtained from a raw mix.
Технический результат достигается тем, что сырьевая смесь для производства керамзита, содержащая глинистое сырье, волокнистые отходы первичной переработки шерсти, воду, дополнительно содержит гравитационные отходы обогащения циркон-ильменитовой руды и пегматит при следующем соотношении компонентов, мас.%: глинистое сырье 43,4-44,5; волокнистые отходы первичной переработки шерсти 0,5-0,7; вода 22,0-26,0; гравитационные отходы обогащения циркон-ильменитовой руды 22,0-26,0; пегматит 6,0-8,0.The technical result is achieved by the fact that the raw material mixture for the production of expanded clay, containing clay raw materials, fibrous waste from the primary processing of wool, water, additionally contains gravity waste from the concentration of zircon-ilmenite ore and pegmatite in the following ratio of components, wt.%: Clay raw material 43.4- 44.5; fibrous waste from primary wool processing 0.5-0.7; water 22.0-26.0; Gravitational waste of zircon-ilmenite ore beneficiation 22.0-26.0; pegmatitis 6.0-8.0.
В таблице приведены составы сырьевой смеси для производства керамзита.The table shows the composition of the raw mix for the production of expanded clay.
В составе сырьевой смеси для производства керамзита используют глины монтмориллонитовые, включающие Al-монтмориллонит и Fe-монтмориллонит (нонтронит). Гравитационные отходы обогащения циркон-ильменитовой руды включают глину, до 3 мас.% циркона, до 2 мас.% ильменита.Montmorillonite clays, including Al-montmorillonite and Fe-montmorillonite (nontronite) are used in the composition of the raw material mixture for the production of expanded clay. Gravity wastes from the zircon-ilmenite ore beneficiation include clay, up to 3 wt.% Zircon, up to 2 wt.% Ilmenite.
Глинистое сырье смешивают с гравитационными отходами обогащения циркон-ильменитовой руды, молотым и просеянным через сетку 014 пегматитом, волокнистыми отходами первичной переработки шерсти, добавляют воду и готовят сырьевую смесь. Из сырьевой смеси формуют гранулы, например, фракции 20-40 мм, которые сушат при температуре 130°C и обжигают при температуре 1100-1150°C. Прочность керамзита на сжатие составит 3-3,5 МПа для всех приведенных в таблице составов.Clay raw materials are mixed with gravitational zircon-ilmenite ore dressing waste, ground and pegmatite sifted through mesh 014, fibrous waste from primary wool processing, water is added and the raw material mixture is prepared. Granules are formed from the raw mixture, for example, fractions of 20-40 mm, which are dried at a temperature of 130 ° C and fired at a temperature of 1100-1150 ° C. The expanded clay compressive strength will be 3-3.5 MPa for all the compositions listed in the table.
Источники информацииInformation sources
1. SU 628129, C04B 14/12, 1978.1. SU 628129, C04B 14/12, 1978.
Claims (1)