FIELD: metallurgy.

SUBSTANCE: rail is exposed to thermal treatment, including pre-heating, additional heating, cooling. Rail is heated continuously or discretely with control according to the program-specified mode. Pre-heating is carried out to the temperature of austenitisation start (point Ac₁), not exceeding temperature of austenitisation end (point Ac₃). Additional heating is carried out by thermocycling in the field of phase α-γ transformations. In intervals between separate heating devices, soaking is carried out to balance temperatures in each cross section. The rail is first cooled down to temperature providing for fine-grained perlite structure for each cross section of a rail, then cooled under natural conditions, at the same time cooling speeds are changed at various stages of the cooling mode. The method is carried out at an installation comprising zones of pre-heating, thermocycling, homogenisation with separate heating devices and intervals arranged between them and/or devices of temperature balancing along the cross section, a cooling zone, including cooling modules with a unit of control and adjustment of cooling parameters.

EFFECT: increased level of physical and mechanical properties and increased operating resistance.

8 cl, 2 tbl, 6 dwg

Description

The invention relates to the field of ferrous metallurgy, in particular to methods for heat treatment of rails, including railway rails.

A known method of heat treatment of a rail (patent RU 2266966 C21D 9/04, C21D 11/00, C21D 1/02), comprising passing a heated rail through a cooling section with inlet and outlet regions and cooling to convert the rail microstructure to a pearlite or ferrite-pearlite microstructure, characterized in that the rail is passed through a cooling section, consisting of separate, independent, sequentially located along the length of the cooling section cooling modules with independently adjustable cooling parameters and with intermediate regions, aspolozhennymi between the cooling modules for removing the structural stresses, with means for determining the actual temperature of the rail head. Depending on the corresponding value of the actual temperature of the part in the intermediate region, the cooling intensity parameters of at least the next cooling module are adjusted to provide a predetermined temperature of the rail head during the entire passage of the cooling section, exceeding the critical temperature of formation of the bainitic structure.

The disadvantage of this method can be attributed to the limited range of adjustment of cooling rates during the cooling mode. In addition, the temperature drop on the surface of the head during the first 4-5 s of the cooling mode reaches 350-450 ° C, which can lead to the formation of bainitic structures in the microstructure of the surface layers of the rail. Thus, the main disadvantage of this method is the significant temperature fluctuations on the surface of the rail head (from 350 ° C to 100 ° C), which can lead to heterogeneity of the macrostructure.

A known method of heat treatment of the rail (patent UA 61059 C21D 9/04), including heating the rail head along the entire length of high-frequency currents, while continuously moving the entire rail through the heating section. At the first stage, the heating of the head is carried out to a temperature of 1050-1100 ° C, after which a short-term intermediate natural quenching is performed to a temperature of 860-820 ° C for 10-25 seconds. At the second stage, heating is carried out to a temperature of 920-980 ° C with its stabilization, after which primary cooling is performed to 480-380 ° C, while cooling in the temperature range,

from 980 ° C to 800 ° C is carried out at a speed of 2-8 ° C / s,

from 800 ° C to 600 ° C is carried out at a speed of 6-14 ° C / s,

from 600 ° C to 380 ° C is carried out at a speed of 4-12 ° C / s,

Self-vacation is carried out in the temperature range 520-400 ° C for 55-90 seconds. After that, secondary cooling is carried out, while the rail is bent along a curve with maximum curvature to the sole in the heating and cooling zone by an amount that balances the residual stresses in the rail head that occur during heat treatment.

The disadvantage of this method can be attributed to the fact that heating and cooling is carried out only by the head, and not the entire rail profile, which entails the need to move the rails through the quenching machine in an elastic-bent state and the appearance of large residual stresses after heat treatment and, as a result, the need for final editing of the rail.

Another disadvantage is that at the junction of the neck to the rail head, a transition zone forms from heated to unheated material, where, after heat treatment, a transition layer with reduced physical and mechanical characteristics is formed.

A known method of heat treatment (RU 2162486 IPC C21D 9/04), selected for the prototype.

A method of heat treatment of a rail, comprising preheating each rail cross section made of steel and having a head, neck and sole, sequential or simultaneous additional heating or overheating of the rail head and cooling of each rail cross section. Preliminary heating of each rail cross section is carried out sequentially or simultaneously to a temperature exceeding the temperature of the end of the austenitic transformation of steel to obtain the same and uniform austenitic structure in series or simultaneously in each rail cross section; additional heating or overheating of the rail head is carried out to a temperature not exceeding 1050 ° C, preferably to a temperature not exceeding 1000 ° C, and is carried out in such a way that the average temperature of each cross section of the rail head exceeds at least 40 ° C the average temperature of the cross section of the sole, the cooling of each rail cross section is carried out sequentially or simultaneously first to a temperature that provides a fine-grained pearlite structure for each cross y cross section of the rail, and then, if necessary, is carried out sequential or simultaneous cooling of in vivo cross-section of each of the rail to ambient temperature.

The disadvantage of this method should be attributed to the fact that this method does not provide for regulation of the heating rate and overheating, carried out to a temperature not exceeding 1050 ° C, leads to a sharp increase in austenite grain and, as a result, to a decrease in physical and mechanical properties after quenching. In addition, the lack of regulation of the cooling ability of the medium does not allow to obtain high hardness at a depth of 22 mm from the rolling surface of the head. As a result, a sufficient operational stability of the rails is not provided.

The disadvantage of this method is that the preheating is carried out to a temperature exceeding the temperature of the end of the austenitic transformation, which entails a sharp change in the volume of material heated from the surface due to phase transformation, this can lead to warping and the appearance of thermal microcracks.

The disadvantages of the method include the fact that the diagram shown in Fig. 1 implies the presence of guide rollers located on the surface of the heated rail head, which can lead to damage to the rolling surface.

Known heat treatment installation described in the journal Industrial Heating - October, 1992, which is taken as a prototype. The installation consists of an induction preheating device for rail austenization, a rail heating device, a cooling device with a system of air chambers having independent control of rail blowing from above, from the side and from below.

This device allows the heat treatment of rails only from alloy steels. The disadvantage of this device is the narrow range of regulation of cooling rates, providing heat treatment of rails with speeds up to 4.5 ° C / s, since the cooling medium is air, which does not allow heat treatment of rails made of carbon unalloyed steel, since cooling rates are essential for this, substantially higher (12 ° C / s or more).

The objectives of the proposed method and device are:

Increasing the level of physical and mechanical properties and increasing the operational stability of the rail.

Obtaining the necessary straightness of the rail after heat treatment, which allows to exclude editing in the roller straightening machine.

Expanding the range of adjustment of cooling rates.

Stabilization of the rail speed through the installation and the necessary range of its regulation, depending on the steel grade.

Possibility of heat treatment of rails from various grades of rail steels.

The technical result is the creation of a method and installation, allowing:

- control individual heating devices in each zone according to the programmed mode, both continuously and discretely, depending on the chemical composition of the steel.

- to control the heating modes of the rails in a continuous mode with alternating heating zones with zones of temperature equalization.

- carry out pre-heating to the temperature of the onset of austenization (point Ac ₁ ).

- additional heating is carried out by thermal cycling in the temperature range of the phase α-γ transformation to complete austenization of the entire volume of each cross section;

- carry out the heat treatment of rails from carbon unalloyed and alloyed steels.

- smoothly or abruptly change the cooling rate during the heat treatment at various stages of cooling.

- to obtain a homogeneous finely dispersed lamellar pearlite structure to a depth of more than 22 mm from the surface of the head, due to the intensification of the cooling ability of the gaseous medium during the cooling process.

- to obtain hardness on the rolling surface to HB415, to increase the plastic and strength properties of heat-treated steel, by increasing the dispersion of perlite.

- change the cooling rate of each section of the rail, affecting the depth of calcination, the dispersion of the structure and physical and mechanical properties, due to the fact that each cooling module is equipped with a control unit and control the parameters of the cooling medium.

- to provide a stable speed of rail movement through the installation and the necessary range of its regulation, depending on the grade of steel.

The technical result is achieved by the method of heat treatment of a steel rail, including preheating the head, neck and sole of the rail and additional heating using separate heating devices, cooling each rail cross section sequentially first to a temperature that provides a fine-grained pearlite structure for each rail cross section, in the case of if necessary, consecutive cooling in vivo of each rail cross section to Environmental temperature, according to the invention, heating is carried out continuously or discontinuously with programmable control by means of separate induction heating devices with the possibility of holding intervals between them to equalize the temperatures of the surface and internal volumes of each rail cross-section, while the preliminary heating is carried out to a temperature austenitizing the beginning, the _Ac1 point without exceeding the austenitizing temperature end point _Ac3, and additional - by thermo iklirovaniya in phase α-γ transformation.

In addition, in the inventive method, after thermal cycling, the rail is homogenized by heating to a temperature above Ac ₃ .

In addition, in the inventive method, the cooling ability of the cooling gas medium is regulated depending on the temperature and humidity of the air, as well as depending on the chemical composition of the steel and the temperature of the rail at the entrance to the cooling zone.

The technical result of the method of heat treatment of steel rail is carried out on the installation for heat treatment of steel rail containing induction heating devices with zones of preliminary and additional heating, cooling modules, according to the invention, induction heating devices are located at intervals between each other, while in the zone of additional heating they are made with the possibility of thermal cycling of the rail in the region of phase α-γ transformations and equipped with spaced troystvami intermediate cooling, each cooling module comprises a device for creating a cooling gas medium with the control unit and the cooling control parameters. In addition, in the inventive installation, each heating device has an independent regulation.

In addition, in the inventive installation, each cooling module contains a control unit for controlling the parameters of the cooling gas medium supplied to various rail surfaces, depending on the cooling mode set for each rail cooling module, providing a change in the rail cooling rate at various stages of the cooling mode.

In addition, in the inventive installation, the mechanisms for moving and / or centering the rail are located outside the heating devices, and are also additionally built into the cooling modules, while in the mechanism for moving the rail head is pressed with a non-drive roller with an adjustable force, preloaded.

In addition, in the inventive installation, the movement mechanisms stabilize the speed of movement of the rail through the installation and provide the necessary range of its regulation, depending on the grade of steel.

The implementation of the invention

Figure 1 shows a diagram of the installation of heat treatment of rails that implements the inventive method for the heat treatment mode, presented in the form of a graph in figa.

The installation of figure 1 contains:

1. Rail;

2. Transportation device;

3. The device for feeding and moving the rail;

4. Heating devices pre-heating;

5. Heating devices of the thermal cycling zone;

6. Plots of cooling in the thermal cycling zone;

7. Heating devices of the homogenization zone;

8. Quench zone cooling modules;

9. The mechanism of centering the rail;

I - preheating zone;

II - thermal cycling zone;

III - homogenization zone;

IV - temperature equalization zone;

V - cooling zone.

The heat treatment schedule of the rails according to the claimed method in Fig. 1a is a graph of the surface temperature and the center of the rail head during its passage through the I-zone of preheating, II-zone of thermal cycling, III-zone of homogenization, IV-zone of temperature equalization, V-zone cooling.

Figure 2 shows the location of the heating elements in the heating devices of zone I and zone II, where:

1 - rail;

10 - heating element of the rail head;

11 - heating element of the neck of the rail;

12 - heating element of the sole of the rail.

Figure 3 shows the location of the heating elements in the heating devices of zone III, where:

1 - rail;

10 - heating element of the rail head;

12 - heating element of the sole of the rail.

Figure 4 shows a diagram of the cooling zone, where:

1 - rail;

8 - cooling modules;

13 - device for forming a cooling gas medium with a control unit and regulation of cooling parameters.

14 - control unit for parameters of air and water;

15 - air and water supply system;

16 - automated control system (ACS).

Figure 5 schematically shows a device for feeding and moving the rail (end view), where:

1 - rail;

17 - the mechanism for setting the upper roller;

18 - lower drive roller with drive;

19 - the drive mechanism of the lower drive roller;

20 - top roller.

A description of the operation of the claimed installation explains the implementation of the proposed method.

The rail 1 (figure 1) by means of a transportation device 2, which can be performed, for example, in the form of a roller table, is transported to a feeding and moving device 3. The feeding and moving device 3 moves the rail at a speed set in accordance with the heat treatment mode to the zones heating without damaging the surface of the rail. The movement mechanisms 3 stabilize the speed of movement of the rail through the installation and provide the necessary range of its regulation, depending on the grade of steel.

As a heating method, induction heating with high frequency currents is used. Heating is carried out at different speeds depending on the grade of steel, moreover, continuously or discontinuously according to the programmed mode in order to obtain more uniform heating of each rail cross section and equalize the temperature along the cross section not only of the rail head, but also along the neck and sole section to ensure minimum thermal stresses and deformations of the rail during heating. The head and sole have different masses and configurations; therefore, they are heated at different speeds, and the sole is heated according to a certain law in accordance with the mode of head heating in order to avoid curvature of the rail.

In the preheating zone I with separate heating devices 4 having independent control (not shown in Fig. 1), the rail is heated to the temperature of the beginning of austenization (point Ac ₁ ), not exceeding the temperature of the end of austenization (point Ac ₃ ), so that during heating, starting from the surface layers, to provide phase transformations with small volumes of material as the heating front moves deeper into the rail, which reduces internal stresses, eliminates the possibility of thermal microcracks and reduces the curvature of the relay sa

Heating in the preheating zone I is as follows.

When moving the rail 1 through the installation (Fig. 1), each cross section passes through the first preheater 4, the surface layers of the rail head are heated by the heating elements 10 (Fig. 2) to a predetermined temperature T ₁ , according to the program-defined mode, in time τ ₁ . During the same time τ _{1, the} center of the rail head warms up due to thermal conductivity to a temperature t ₁ (Fig. 1a).

The heating of other elements of the rail profile (neck and sole) is carried out by their independent heating elements 11 and 12 (figure 2). Moreover, the heating of the sole and neck is carried out according to a certain law in accordance with the mode of heating of the head, in order to avoid curvature of the rail.

Further, this cross section resembles through the first zone of temperature gradient equalization in depth and rail section (not marked in Fig. 1). In this zone, in the absence of heating devices 4, the surface of all elements of the rail profile 1 is podstuzhivanie. And at time τ _{2 the} exit of the given cross section of the rail from this zone of alignment of the temperature gradient in depth and section of the rail, the temperature of the surface of the rail head is T ₂ and center t ₂ , and T ₁ ≥T ₂ , at ₁ ≤t ₂ and, accordingly, the temperature gradient Δ _{2 of the} surface and center of the rail head at time τ ₂ , equal to Δ ₂ = T ₂ -t ₂ , will be less than the temperature gradient Δ _{1 of the} surface and center re heads bca at time τ ₁ equal to Δ ₁ = T ₁ -t _1. Similar actions occur with a temperature gradient in other elements of the rail profile.

Further, this cross section of the rail 1 enters the next heating device 4 and, passing through it, the head surface is heated to a temperature of T ₃ , and the center to t ₃ and then, falling into the next zone of alignment of the temperature gradient in depth and rail section, the difference decreases temperature of the surface and center of the rail head, and so on. By setting the heating modes for the heating elements 10, 11, 12 (FIG. 2) in the preheating zone I, a minimum temperature gradient can be achieved along the depth and cross section of the rail.

Then the rail is fed into zone II with separate heating devices 5 and intermediate cooling sections 6, where thermal cycling in the temperature range of phase α-γ transformations is carried out. Independent control of heating devices 5 in zone II (not shown in Fig. 1) allows you to set the necessary law of thermal cycling of each rail cross section depending on the chemical composition of steel, in order to ensure high physical and mechanical properties and reduce internal stresses that cause rail curvature. This gives a uniform and uniform fine-grained structure of austenite in the entire volume of each rail cross section.

The location of the independent heating elements in the heating devices of zone I and zone II is shown in figure 2. Where the rail - 1, differentially uniformly heated over the cross section by heating elements - 10, 11, 12, with independent control (not shown in figure 2). Independent control of heating elements allows you to set the heating mode of each element of the rail profile according to a certain law, and change it depending on the chemical composition of the steel.

Next, the rail is fed into zone III for homogenization of austenite, heated by individual heating devices 7 to a temperature above austenitization (i.e., Ac ₃ ) and maintained at this temperature to homogenize austenite. The location of the heating elements in the heating devices of zone III is shown in FIG. 3, where the head and sole of the rail - 1 are heated separately by adjustable heating elements 10 and 12, respectively.

In the heating zones I, II, III, the heating of the rail is carried out by heating the surface layers of the rail, and the internal volumes of the rail are heated due to thermal conductivity. Therefore, the heating mode of the rail, for each steel grade, in each zone is set at such a speed that provides a slight difference in surface temperature and inner layers. In addition, between the individual heating devices 4, 5, 7 there are zones (not shown in FIG. 1) of alignment of the temperature gradient in depth and rail section.

Then, the rail is fed into zone IV of the final leveling and temperature control, where the surface of the rail is cooled under natural conditions to a temperature not lower than Ar ₁ .

Next, the rail enters the cooling zone V with separate cooling modules 8, where they are controlled cooling at various speeds, depending on the steel grade, continuously and / or discretely according to the programmed mode in order to obtain highly dispersed perlite and high physical and mechanical properties in the structure become.

The cooling mode of both the head and other elements of the rail profile consists of several stages.

At the first stage, with intensive cooling, such a speed of cooling of the head surface is provided that the temperature of the surface of the rail head decreases from the heating temperature to the temperature of minimum austenite stability, for a time not exceeding the duration of the incubation period of pearlite transformation.

In the second cooling stage, the cooling rate is reduced to such a value as to ensure complete pearlite transformation in the surface layers.

Further, the cooling rate is gradually increased to ensure the formation of finely dispersed perlite as phase transformations move deeper into the head.

The programmed cooling mode is selected from the database according to the actual (measured) temperature of the rail surface and steel grade. Functional diagram of the cooling zone V is presented in figure 4. ACS 16 with a database of heat treatment modes, according to a predetermined rail cooling mode, transmits a signal to the air and water supply system 15, which through the control units 14 supplies a predetermined amount of air and water to form a cooling gas medium supplied by cooling modules 8 to rail 1. Each the device 13 by means of a control unit and regulation of the cooling parameters forms a predetermined composition of the cooling gas medium for its cooling module 8, which allows to provide the necessary cooling rate Ia rail 1 while passing through the cooling unit 8 in accordance with a predetermined program-cooling mode in this cooling step. This allows you to obtain the required cooling rate in accordance with the specified cooling mode of the rail when it is advanced in the cooling zone V. A sufficiently wide range of regulation of the cooling speeds (2 ÷ 14.5 ° C / s) allows heat treatment of rails made of carbon unalloyed and alloyed steels.

In the heating zones I, II, III, temperature equalization zone IV and cooling zone V between the individual heating devices and the cooling modules, rail centering mechanisms 9 are arranged to prevent damage to the rolling surface of the rail head. When moving the rail through the installation, the centering mechanisms 9 prevent its possible curvature at high temperatures (especially at the moments of phase transformations) under the action of gravity.

At the exit of zone V there is a feeding and moving device 3 (Fig. 5), which moves the rail at a speed set in accordance with the heat treatment mode, without damaging the rolling surface of the rail, to the transportation device 2, which can be performed, for example, in the form live rolls. The movement mechanisms 3 stabilize the speed of movement of the rail through the installation and provide the necessary range of its regulation, depending on the grade of steel.

The proposed method of heat treatment is implemented on full-profile samples 1200 mm long, taken from steel rails, the chemical composition of which is shown in table 1 (Fig.6).

The heat treatment of the rail samples was carried out on the installation, the diagram of which is shown in Fig. 1 according to the program-defined mode shown in Fig. 1a.

To assess the quality of heat treatment of the rails, the head microstructure, strength and plastic properties, hardness, and impact strength were determined. The results are presented in table 2 (Fig.7).

Measurements of the curvilinearity of the rail samples after heat treatment showed an increase in the initial curvature of 0.02 mm over a length of 1 meter.

Claims (8)

1. The method of heat treatment of a steel rail, including preheating the head, neck and sole of the rail and additional heating using separate heating devices, cooling each rail cross section sequentially first to a temperature that provides a fine-grained pearlite structure for each rail cross section, if necessary sequential cooling in vivo of each rail cross section to ambient temperature, excellent the fact that the heating is carried out continuously or discontinuously with control according to the programmed set mode by means of separate induction heating devices with the possibility of holding in the intervals between them to equalize the temperatures of the surface and internal volumes of each rail cross section, while the preliminary heating is carried out to the temperature of the beginning of austenization (point Ac ₁ ), not exceeding the temperature of the end of austenization (point Ac ₃ ), and additional heating is carried out by thermal cycling in the region of phase α-γ transformations. 2. The method according to claim 1, characterized in that after thermocycling the rail is homogenized by heating to a temperature above Ac ₃ . 3. The method according to claim 1, characterized in that the cooling ability of the cooling gas medium is regulated depending on the temperature and humidity of the air, as well as depending on the chemical composition of the steel and the temperature of the rail at the entrance to the cooling zone. 4. Installation for heat treatment of steel rail, comprising induction heating devices with zones of preliminary and additional heating, cooling modules, characterized in that the induction heating devices are spaced apart, while in the zone of additional heating they are made with the possibility of thermal cycling of the rail in the region phase α-γ transformations and are equipped with intermediate cooling devices located in the intervals, with each cooling module containing the formation of a cooling gas medium with a control unit and regulation of cooling parameters. 5. Installation according to claim 4, characterized in that each heating device has independent regulation. 6. Installation according to claim 4, characterized in that each cooling module contains a control unit and control the parameters of the cooling gas medium supplied to different rail surfaces, depending on the cooling mode specified for each individual rail cooling module, providing a change in the rail cooling rate at various stages of the cooling mode. 7. The installation according to claim 4, characterized in that the mechanisms for moving and / or centering the rail are located outside the heating devices and are additionally built into the cooling modules, while the rail head is pressed with a non-drive roller with an adjustable compression force. 8. The installation according to claim 4, characterized in that the movement mechanisms stabilize the speed of movement of the rail through the installation and provide the necessary range of its regulation depending on the steel grade.