Abstract

FIELD: chemistry.

SUBSTANCE: invention relates to production of artificial materials which imitate natural materials. The crude mixture for making material which imitates natural stone contains, wt %: coal dust 20.0-25.0; mica which is ground and sieved through sieve No.5 5.0-7.0; blast-furnace slag which is ground and sieved through sieve No.5 5.0-7.0; water 25.0-30.0; scrap ceramic brick which is ground until complete passage through sieve No.014 13.0-18.0; portland-slag cement 20.0-25.0.

EFFECT: high water resistance of the material which imitates natural stone.

1 tbl

Description

Изобретение относится к области производства искусственных материалов, имитирующих природные.The invention relates to the production of artificial materials that mimic natural.

Известна сырьевая смесь для изготовления материала, имитирующего природный камень, включающая, мас.%: угольная пыль 23,0-27,0; измельченная слюда 23,0-27,0; измельченный доменный шлак 23,0-27,0; жидкое стекло 23,0-27,0 [1].Known raw mix for the manufacture of a material that simulates natural stone, including, wt.%: Coal dust 23,0-27,0; crushed mica 23.0-27.0; crushed blast furnace slag 23.0-27.0; water glass 23.0-27.0 [1].

Задача изобретения состоит в повышении водостойкости материала, имитирующего природный камень.The objective of the invention is to increase the water resistance of a material that simulates natural stone.

Технический результат достигается тем, что сырьевая смесь для изготовления материала, имитирующего природный камень, включающая угольную пыль, измельченную слюду, измельченный доменный шлак, дополнительно включает воду, измельченный бой керамического кирпича и шлакопортландцемент, при следующем соотношении компонентов, мас.%: угольная пыль 20,0-25,0; измельченная и просеянная через сетку №5 слюда 5,0-7,0; измельченный и просеянный через сетку №5 доменный шлак 5,0-7,0; вода 25,0-30,0; измельченный до полного прохождения через сетку №014 бой керамического кирпича 13,0-18,0; шлакопортландцемент 20,0-25,0.The technical result is achieved by the fact that the raw material mixture for the manufacture of a material that simulates natural stone, including coal dust, crushed mica, crushed blast furnace slag, further includes water, crushed ceramic bricks and slag Portland cement, in the following ratio, wt.%: Coal dust 20 0-25.0; crushed and sieved through a grid No. 5 of mica 5.0-7.0; crushed and sifted through a mesh No. 5 blast furnace slag 5.0-7.0; water 25.0-30.0; crushed to complete passage through the mesh No. 014 the battle of ceramic brick 13.0-18.0; slag Portland cement 20.0-25.0.

В таблице приведены составы смеси.The table shows the composition of the mixture.

ТаблицаTable КомпонентыComponents Состав, мас.%:Composition, wt.%: 1one 22 33 Угольная пыльCoal dust 25,025.0 23,023.0 20,020,0 Измельченная и просеянная через сетку №5 слюдаMica crushed and sifted through mesh No. 5 5,05,0 6,06.0 7,07.0 Измельченный и просеянный через сетку №5 доменный шлакCrushed and sifted through a mesh No. 5 blast furnace slag 7,07.0 6,06.0 5,05,0 ВодаWater 25,025.0 27,027.0 30,030,0 Измельченный до полного прохождения через сетку №014 бой керамического кирпичаCrushed to full passage through the mesh No. 014 the battle of ceramic brick 13,013.0 15,015.0 18,018.0 ШлакопортландцементSlag Portland Cement 25,025.0 23,023.0 20,020,0

Доменный шлак и слюду предварительно измельчают и просеивают через сетку №5. Бой керамического кирпича измельчают до полного прохождения через сетку №014. Компоненты смеси дозируют в требуемых количествах и смешивают. Из полученной смеси формуют материал (изделие), имитирующий природный камень желаемого размера и конфигурации. Затем оставляют изделие до полного отверждения на воздухе при комнатной температуре. Материал, имитирующий природный камень, водостоек (коэффициент размягчения не менее 0,8).Blast furnace slag and mica are pre-crushed and sieved through mesh No. 5. The ceramic brick fight is crushed until it passes completely through mesh No. 014. The components of the mixture are dosed in the required quantities and mixed. A material (product) is formed from the resulting mixture, imitating a natural stone of the desired size and configuration. Then leave the product until completely cured in air at room temperature. The material imitating natural stone is water resistant (softening coefficient not less than 0.8).

Источник информацииThe source of information

1. RU 2440944 C1, 2012.1. RU 2440944 C1, 2012.

Claims

The raw material mixture for the manufacture of a material that simulates natural stone, including coal dust, crushed mica, crushed blast furnace slag, characterized in that it further includes water, crushed ceramic bricks and slag Portland cement in the following ratio, wt.%: Coal dust 20,0- 25.0; crushed and sieved through a grid No. 5 of mica 5.0-7.0; crushed and sifted through a mesh No. 5 blast furnace slag 5.0-7.0; water 25.0-30.0; crushed to complete passage through the mesh No. 014 the battle of ceramic brick 13.0-18.0; slag Portland cement 20.0-25.0.