Abstract
Description
Изобретение относится к области технологии силикатов и касается производства стекла, которое может быть использовано для изготовления посуды, изделий декоративно-художественного назначения.The invention relates to the field of technology of silicates and for the production of glass, which can be used for the manufacture of glassware, decorative and artistic products.
Известна шихта для получения цветного стекла, включающая, мас.%: сода 5,0-20,0; кварцевый песок 30,0-80,0; окрашивающая добавка 0,01-8,0 [1].Known mixture to obtain colored glass, including, wt.%: Soda 5,0-20,0; silica sand 30.0-80.0; coloring additive 0.01-8.0 [1].
Задачей изобретения является обеспечение термостойкости цветного стекла при снижении температуры его варки.The objective of the invention is to provide thermal stability of colored glass while lowering the temperature of its cooking.
Технический результат достигается тем, что шихта для получения цветного стекла, содержащая соду, кварцевый песок, окрашивающую добавку, дополнительно включает мел, а в качестве окрашивающей добавки - сухой гальваношлам, характеризующийся следующим средним химическим составом, мас.%: SiO2 10,78; Al2O3 2,73; Fe2O3 12,9; FeO 0,33; TiO2 0,21; Cr2O3 1,08; NiO 0,46, CuO 7,09; ZnO 1,42; CaO 27,85; MgO 2,12; SO3 1,75; K2O 0,88, Na2O 2,18; п.п.п. 28,21, при следующем соотношении компонентов, мас.%: сода 7,0-11,0; кварцевый песок 46,0-58,0; мел 3,0-5,0; указанный гальваношлам 30,0-40,0.The technical result is achieved in that the mixture to obtain colored glass containing soda, quartz sand, a coloring additive, further includes chalk, and as a coloring additive - dry galvanic sludge, characterized by the following average chemical composition, wt.%: SiO 2 10.78; Al 2 O 3 2.73; Fe 2 O 3 12.9; FeO 0.33; TiO 2 0.21; Cr 2 O 3 1.08; NiO 0.46; CuO 7.09; ZnO 1.42; CaO 27.85; MgO 2.12; SO 3 1.75; K 2 O 0.88; Na 2 O 2.18; p.p.p. 28.21, in the following ratio of components, wt.%: Soda 7.0-11.0; silica sand 46.0-58.0; chalk 3.0-5.0; the specified galvanic sludge 30,0-40,0.
Гальваношлам представляет собой продукт очистки и нейтрализации сточных вод гальваноцехов. Отход представляет собой микрогетерогенные коллоидные дисперсные и ультрадисперсные системы, в которых твердой фазой являются нерастворимые в воде аморфизированные гидроксиды металлов, тонко дисперсный гидроксид кальция, а дисперсионной средой - вода. Сухой гальваношлам в виде порошка бурого цвета, со средним размером частиц 0,38 мкм включает кальцит, кварц, гидроксиды тяжелых металлов, гематит, оксид хрома. Состав гальваношлама непостоянен и колеблется в достаточно широком интервале, что связано с особенностями технологического процесса.Galvanic sludge is a product of purification and neutralization of wastewater of galvanic shops. The waste is microheterogeneous colloidal dispersed and ultrafine systems in which the solid phase is water-insoluble amorphized metal hydroxides, finely dispersed calcium hydroxide, and dispersion medium is water. Dry galvanic sludge in the form of a brown powder with an average particle size of 0.38 microns includes calcite, quartz, heavy metal hydroxides, hematite, chromium oxide. The composition of galvanic sludge is unstable and varies in a fairly wide range, which is associated with the features of the process.
В таблице приведены составы шихты.The table shows the composition of the charge.
Стекло может быть получено в стекловаренных печах любой конструкции при температуре - 1400°C. Стекло имеет зеленоватую окраску.Glass can be obtained in glass melting furnaces of any design at a temperature of - 1400 ° C. Glass has a greenish tint.
Источник информацииThe source of information
1. CN 1131644 A, 1996.1. CN 1131644 A, 1996.
Claims (1)
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
RU2011117600/03A RU2465228C1 (en) | 2011-04-29 | 2011-04-29 | Mixture for producing coloured glass |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
RU2011117600/03A RU2465228C1 (en) | 2011-04-29 | 2011-04-29 | Mixture for producing coloured glass |
Publications (1)
Publication Number | Publication Date |
---|---|
RU2465228C1 true RU2465228C1 (en) | 2012-10-27 |
Family
ID=47147377
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
RU2011117600/03A RU2465228C1 (en) | 2011-04-29 | 2011-04-29 | Mixture for producing coloured glass |
Country Status (1)
Country | Link |
---|---|
RU (1) | RU2465228C1 (en) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
RU2525099C1 (en) * | 2013-07-08 | 2014-08-10 | Юлия Алексеевна Щепочкина | Charge to produce coloured glass |
Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
SU638550A1 (en) * | 1977-06-21 | 1978-12-25 | Научно-исследовательский и проектный институт по газоочистным сооружениям, технике безопасности и охране труда в промышленности строительных материалов | Method of obtaining glass mass |
CN1131644A (en) * | 1995-12-25 | 1996-09-25 | 许昌东方光色玻璃有限责任公司 | Production technology for colour decorative glass and its product |
EP1946858A2 (en) * | 2005-09-12 | 2008-07-23 | MARTINEZ MANENT, Salvador | Method of producing glass articles |
-
2011
- 2011-04-29 RU RU2011117600/03A patent/RU2465228C1/en active
Patent Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
SU638550A1 (en) * | 1977-06-21 | 1978-12-25 | Научно-исследовательский и проектный институт по газоочистным сооружениям, технике безопасности и охране труда в промышленности строительных материалов | Method of obtaining glass mass |
CN1131644A (en) * | 1995-12-25 | 1996-09-25 | 许昌东方光色玻璃有限责任公司 | Production technology for colour decorative glass and its product |
EP1946858A2 (en) * | 2005-09-12 | 2008-07-23 | MARTINEZ MANENT, Salvador | Method of producing glass articles |
Non-Patent Citations (1)
Title |
---|
ПАВЛУШКИН Н.М. Технология стекла и ситаллов. - М.: Стройиздат, 1983, с.80. * |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
RU2525099C1 (en) * | 2013-07-08 | 2014-08-10 | Юлия Алексеевна Щепочкина | Charge to produce coloured glass |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
CN100447111C (en) | Crystalline glaze of iron, zinc and augite and its material compounding process | |
RU2541703C1 (en) | Coloured glaze | |
CA3065070C (en) | High-modulus glass fiber composition based on basalt | |
CN105693200A (en) | Jingdezhen misty blue durable china and preparation method thereof | |
CN102659314A (en) | Barium oxide based crystal lead-free glass and preparation method thereof | |
CN105344317A (en) | Active carbon stain remover | |
CN106145676A (en) | A kind of pottery orchid glaze | |
RU2465228C1 (en) | Mixture for producing coloured glass | |
CN103172321B (en) | A kind of environment friendly silicon segasso sea bubble slime paint | |
CN101885581B (en) | Ultraviolet-resistant hard glass-bulb glass and preparation method thereof | |
RU2420462C1 (en) | Mixture for producing coloured glass | |
US3844796A (en) | Colored glass compositions | |
RU2427541C1 (en) | Mixture for producing coloured glass | |
RU2424992C1 (en) | Mixture for producing coloured glass | |
RU2525099C1 (en) | Charge to produce coloured glass | |
RU2462432C1 (en) | Ceramic mass for brick production | |
CN105777063A (en) | Natural energy Baijiu cup | |
RU2495837C1 (en) | Mixture for producing coloured glass | |
RU2495838C1 (en) | Mixture for producing coloured glass | |
CN106316120A (en) | Manufacturing technology of large-ball mud high-end art porcelain feldspar glaze | |
RU2606888C1 (en) | Ceramic pigment | |
RU2481279C1 (en) | Glaze composition | |
RU2646118C1 (en) | Mixture for producing coloured glass | |
CN104556707A (en) | Glass ball producing formula | |
RU2643827C1 (en) | Charge for producing of colored glass |