RU2446117C1 - Method of decorating foamed glass - Google Patents

Method of decorating foamed glass Download PDF

Info

Publication number
RU2446117C1
RU2446117C1 RU2010140306/03A RU2010140306A RU2446117C1 RU 2446117 C1 RU2446117 C1 RU 2446117C1 RU 2010140306/03 A RU2010140306/03 A RU 2010140306/03A RU 2010140306 A RU2010140306 A RU 2010140306A RU 2446117 C1 RU2446117 C1 RU 2446117C1
Authority
RU
Russia
Prior art keywords
decorating
foamed glass
amber
pores
temperature
Prior art date
Application number
RU2010140306/03A
Other languages
Russian (ru)
Inventor
Юлия Алексеевна Щепочкина (RU)
Юлия Алексеевна Щепочкина
Original Assignee
Юлия Алексеевна Щепочкина
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Юлия Алексеевна Щепочкина filed Critical Юлия Алексеевна Щепочкина
Priority to RU2010140306/03A priority Critical patent/RU2446117C1/en
Application granted granted Critical
Publication of RU2446117C1 publication Critical patent/RU2446117C1/en

Abstract

FIELD: chemistry.
SUBSTANCE: invention relates to production of decorated foamed glass. Pores on the surface of foamed glass are filled with molten amber. The molten amber is obtained through dry distillation at temperature of approximately 420°C.
EFFECT: reduced susceptibility to cracking of articles made from foamed glass during decoration.

Description

Изобретение относится к производству декорированных изделий, преимущественно, плит, настенных панно из пеностекла.The invention relates to the production of decorated products, mainly plates, wall panels made of foam glass.

Известен способ декорирования пеностекла, предусматривающий заполнение пор на его поверхности расплавом декорирующего материала (стекла) с последующим его охлаждением [1]. При осуществлении декорирования таким способом пеностекло подвергается значительному термоудару, при этом возможно деформирование и частичное разрушение изделий из пеностекла.A known method of decorating foam glass, providing for the filling of pores on its surface with a melt of decorating material (glass) with its subsequent cooling [1]. When decorating in this way, the foamglass is subjected to significant thermal shock, with the possible deformation and partial destruction of products made of foamglass.

Задачей изобретения является обеспечение сохранности изделии из пеностекла при декорировании.The objective of the invention is to ensure the safety of the product of foam glass during decoration.

Технический результат достигается тем, что по способу декорирования пеностекла, предусматривающему заполнение пор на его поверхности расплавом декорирующего материала с последующим его охлаждением, в качестве декорирующего материала используют расплав янтаря. В качестве декорирующего материала используют расплав янтаря, полученного сухой возгонкой при температуре около 420°С.The technical result is achieved by the fact that according to the method of decorating foam glass, which provides for the filling of pores on its surface with a melt of a decorating material with its subsequent cooling, amber melt is used as a decorating material. Amber melt obtained by dry sublimation at a temperature of about 420 ° C is used as a decorating material.

Способ поясняется примерами.The method is illustrated by examples.

1. Янтарь (отходи обработки) расплавляют при температуре 250-300°С. Полученным расплавом заполняют поры на поверхности изделия и пеностекла. Декорированное изделие охлаждают до комнатной температуры.1. Amber (processing waste) is melted at a temperature of 250-300 ° C. The obtained melt fills the pores on the surface of the product and foam glass. The decorated item is cooled to room temperature.

2. Отходы обработки плавленного янтаря (легкоплавкой массы, предварительно полученной сухой возгонкой при температуре около 420°С) расплавляют при температуре 180°С. Расплавом заполняют поры на поверхности изделия из пеностекла. Декорированное изделие охлаждают до комнатной температуры. Способ несложен, позволяет получать оригинальные изделия из пеностекла.2. Wastes from the processing of fused amber (fusible mass previously obtained by dry sublimation at a temperature of about 420 ° C) are melted at a temperature of 180 ° C. The pores on the surface of the foam glass product are filled with melt. The decorated item is cooled to room temperature. The method is simple, allows you to get original products from foam glass.

Источник информацииThe source of information

1. JP №3218934, 1991.1. JP No. 3218934, 1991.

Claims (1)

Способ декорирования пеностекла, предусматривающий заполнение пор на его поверхности расплавом декорирующего материала с последующим его охлаждением, отличающийся тем, что в качестве декорирующего материала используют расплав янтаря, полученного сухой возгонкой при температуре около 420°С. A method of decorating foam glass, comprising filling the pores on its surface with a melt of a decorating material and then cooling it, characterized in that the amber melt obtained by dry sublimation at a temperature of about 420 ° C is used as a decorating material.
RU2010140306/03A 2010-10-01 2010-10-01 Method of decorating foamed glass RU2446117C1 (en)