RU2417175C1 - Crude mixture for making expanded clay - Google Patents

Crude mixture for making expanded clay Download PDF

Info

Publication number
RU2417175C1
RU2417175C1 RU2009143154/03A RU2009143154A RU2417175C1 RU 2417175 C1 RU2417175 C1 RU 2417175C1 RU 2009143154/03 A RU2009143154/03 A RU 2009143154/03A RU 2009143154 A RU2009143154 A RU 2009143154A RU 2417175 C1 RU2417175 C1 RU 2417175C1
Authority
RU
Russia
Prior art keywords
expanded clay
clay
crude mixture
water
gypsum
Prior art date
Application number
RU2009143154/03A
Other languages
Russian (ru)
Inventor
Юлия Алексеевна Щепочкина (RU)
Юлия Алексеевна Щепочкина
Original Assignee
Юлия Алексеевна Щепочкина
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Юлия Алексеевна Щепочкина filed Critical Юлия Алексеевна Щепочкина
Priority to RU2009143154/03A priority Critical patent/RU2417175C1/en
Application granted granted Critical
Publication of RU2417175C1 publication Critical patent/RU2417175C1/en

Abstract

FIELD: chemistry. ^ SUBSTANCE: invention relates to the industry of construction materials and making expanded clay. The crude mixture for preparing expanded clay contains the following in wt %: clay material 75.0-78.0; glass which is ground to specific surface area 2500-3500 cm2/g 2.0-3.0 and gypsum 0.5-1.0; water 19.0-21.0. ^ EFFECT: high water resistance of the expanded clay, which is characterised by softening coefficient of 0,75 and high strength of the expanded clay. ^ 1 cl, 1 tbl

Description

Изобретение относится к промышленности строительных материалов и касается производства керамзита.The invention relates to the building materials industry and for the production of expanded clay.

Известна сырьевая смесь для производства керамзита, содержащая, мас.%: глинистое сырье 75,5-76,8; волокнистые отходы первичной переработки шерсти 0,9-1,4; вода - остальное [1].Known raw mix for the production of expanded clay, containing, wt.%: Clay raw materials 75.5-76.8; fibrous waste from primary wool processing 0.9-1.4; water - the rest [1].

Задачей изобретения является повышение прочности керамзита, полученного из сырьевой смеси.The objective of the invention is to increase the strength of expanded clay obtained from a raw mix.

Технический результат достигается тем, что сырьевая смесь для производства керамзита, включающая глинистое сырье и воду, дополнительно содержит молотое стекло и гипс при следующем соотношении компонентов, мас.%: глинистое сырье 75,0-78,0; молотое стекло 2,0-3,0; гипс 0,5-1,0; вода 19,0-21,0.The technical result is achieved in that the raw mix for the production of expanded clay, including clay raw materials and water, further contains ground glass and gypsum in the following ratio of components, wt.%: Clay raw materials 75.0-78.0; ground glass 2.0-3.0; gypsum 0.5-1.0; water 19.0-21.0.

В таблице приведены составы сырьевой смеси для производства керамзита.The table shows the composition of the raw mix for the production of expanded clay.

Сос-
тав
№SOS-
tav
No. КомпонентыComponents Прочность керамзита (фракция 20-40 мм) при сжатии, МПаThe strength of expanded clay (fraction 20-40 mm) in compression, MPa Глинистое сырьеClay raw materials Молотое стеклоGround glass ГипсGypsum ВодаWater 1one 75,075.0 3,03.0 1,01,0 21,021.0 ~3~ 3 22 77,077.0 2,52.5 0,50.5 20,020,0 ~3~ 3 33 78,078.0 2,02.0 1,01,0 19,019.0 ~3~ 3

В составе сырьевой смеси может быть использовано глинистое сырье, характеризующееся следующим химическим составом, мас.%: SiO2 64,7-73,0; Al2O3 9,87-13,41; Fe2O3 1,92-2,72; CaO 0,98-1,6; MgO 2,13-2,99; SO3 0,51-0,81; п.п.п. 11,45-14,32. Используют размолотое до удельной поверхности 2500-3500 см2/г любое силикатное стекло (бой): листовое, тарное, сортовое, медицинское и др., в любых сочетаниях. Используют природный гипс размолотый до удельной поверхности 2500-3500 см2/г.In the composition of the raw material mixture can be used clay raw materials, characterized by the following chemical composition, wt.%: SiO 2 64,7-73,0; Al 2 O 3 9.87-13.41; Fe 2 O 3 1.92-2.72; CaO 0.98-1.6; MgO 2.13-2.99; SO 3 0.51-0.81; p.p.p. 11.45-14.32. Any silicate glass (battle) ground to a specific surface of 2500-3500 cm 2 / g is used: sheet, container, high-quality, medical, etc., in any combination. Use natural gypsum ground to a specific surface of 2500-3500 cm 2 / g.

Глинистое сырье смешивают с молотым стеклом и молотым гипсом, добавляют воду и готовят сырьевую смесь. Из сырьевой смеси формуют гранулы, которые сушат и обжигают при температуре 1000°С.Clay raw materials are mixed with ground glass and ground gypsum, water is added and the raw material mixture is prepared. Granules are formed from the raw mixture, which are dried and fired at a temperature of 1000 ° C.

Источники информацииInformation sources

1. SU 628129, С04В 14/12, 1978.1. SU 628129, C04B 14/12, 1978.

Claims (1)

Сырьевая смесь для производства керамзита, включающая глинистое сырье сульфат кальция и воду, отличающаяся тем, что в качестве сульфата кальция содержит природный гипс и дополнительно - стекло, размолотые до удельной поверхности 2500-3500 см2/г, причем компоненты находятся при следующем соотношении, мас.%:
глинистое сырье 75,0-78,0 указанный гипс 0,5-1,0 указанное стекло 2,0-3,0 вода 19,0-21,0
The raw material mixture for the production of expanded clay, including clay raw materials, calcium sulfate and water, characterized in that as calcium sulfate contains natural gypsum and additionally glass, ground to a specific surface of 2500-3500 cm 2 / g, and the components are in the following ratio, wt .%:
clay raw materials 75.0-78.0 specified gypsum 0.5-1.0 specified glass 2.0-3.0 water 19.0-21.0
RU2009143154/03A 2009-11-23 2009-11-23 Crude mixture for making expanded clay RU2417175C1 (en)