RU2394863C2 - Wax composition for restoring surfaces of vehicles - Google Patents
Wax composition for restoring surfaces of vehicles Download PDFInfo
- Publication number
- RU2394863C2 RU2394863C2 RU2008137704/04A RU2008137704A RU2394863C2 RU 2394863 C2 RU2394863 C2 RU 2394863C2 RU 2008137704/04 A RU2008137704/04 A RU 2008137704/04A RU 2008137704 A RU2008137704 A RU 2008137704A RU 2394863 C2 RU2394863 C2 RU 2394863C2
- Authority
- RU
- Russia
- Prior art keywords
- composition
- wax
- vehicles
- ceresin
- pigment
- Prior art date
Abstract
Description
Изобретение относится к средствам защиты поверхностей транспортных средств от атмосферных явлений и одновременно является средством автокосметики, в частности для заделки различных дефектов поверхности транспортного средства.The invention relates to means for protecting vehicle surfaces from atmospheric phenomena and at the same time is a means of car care products, in particular for sealing various surface defects of a vehicle.
Известен состав для защитного покрытия с полирующими свойствами (патент РФ №2031917), содержащий монтановый воск, парафин нефтяной, шерстный жир, стеариновую кислоту, полиэтилсилоксановую жидкость, водный раствор аммиака, уайт-сприт, воду. Недостатком данного состава является невозможность длительного хранения состава, т.к. входящий в его состав жир животного происхождения не имеет длительного срока хранения.A known composition for a protective coating with polishing properties (RF patent No. 2031917) containing montan wax, petroleum paraffin, wool grease, stearic acid, polyethylsiloxane liquid, aqueous ammonia, white spray, water. The disadvantage of this composition is the impossibility of long-term storage of the composition, because its animal fat does not have a long shelf life.
Наиболее близким к изобретению по технической сущности и достигаемому результату является восковой состав, описанный в патенте США №5821291 «Карандаш для заполнения, маскирования и заделки царапин на окрашенной поверхности». Состав содержит вещество восковой структуры, пигмент, и жидкий силиконовый полимерный материал в следующих пропорциях: карнаубский воск 5%; монтановый воск 35%; парафин 35%; пигмент 13%; жидкий силиконовый полимерный материал 12%.Closest to the invention in technical essence and the achieved result is the wax composition described in US patent No. 5821291 "Pencil for filling, masking and sealing scratches on a painted surface." The composition contains a waxy substance, a pigment, and a liquid silicone polymer material in the following proportions: carnauba wax 5%; montan wax 35%; paraffin 35%; pigment 13%; liquid silicone polymer material 12%.
Данный состав обладает недостаточной пластичностью, что не обеспечивает качественного заполнения глубоких царапин и сколов, не обладает высокой адгезией с поверхностью кузова транспортного средства, а также не обеспечивает желаемого антикоррозионного действия препарата. Кроме того, в нем использованы дорогостоящие материалы. Цветовая гамма не отличается разнообразием, в частности отсутствуют цвета с металлическим блеском (металлик).This composition has insufficient plasticity, which does not provide high-quality filling of deep scratches and chips, does not have high adhesion to the surface of the vehicle body, and also does not provide the desired anticorrosive effect of the drug. In addition, it uses expensive materials. The color scheme does not differ in variety, in particular there are no colors with a metallic sheen (metallic).
Задачей настоящего изобретения является создание воскового состава для заделки различных дефектов на поверхности транспортного средства, простого в применении, имеющего длительный срок хранения, обладающего водоотталкивающими и антикоррозионными свойствами, а также, по сравнению с прототипом, более высокой пластичностью и адгезией.The objective of the present invention is to provide a wax composition for sealing various defects on the surface of a vehicle, easy to use, having a long shelf life, having water repellent and anticorrosion properties, and also, in comparison with the prototype, higher ductility and adhesion.
Это достигается тем, что создан состав, включающий вещество восковой структуры, пигмент и жидкий силиконовый полимерный материал, отличающийся тем, что в качестве воскового материала используется карнаубский воск и церезин, в качестве жидкого полимерного материала используется полиметилсилоксан, и, кроме того, в состав добавлены слюда и абиетиновая кислота со следующим соотношением компонентов, мас.%:This is achieved by creating a composition comprising a wax substance, a pigment and a liquid silicone polymer material, characterized in that carnauba wax and ceresin are used as a wax material, polymethylsiloxane is used as a liquid polymer material, and, in addition, mica and abietic acid with the following ratio of components, wt.%:
Входящий в состав карнаубский воск является самым твердым и устойчивым из природных восков. Материалы с использованием карнаубского воска становятся благодаря нему более теплостойкими и нерастекаемыми. Чрезмерная твердость этого воска снижается в заявляемом составе благодаря использованию церезина. Церезин благодаря мелкокристаллической структуре обладает хорошей вязкостью, поэтому придает более высокую пластичность конечному составу. Содержание этих веществ именно в пределах 30-40% оптимально, так как при содержании карнаубского воска больше 40% конечный продукт становится хрупким, что плохо сказывается при заполнении дефектов на реставрируемой поверхности. А при содержании карнаубского воска менее 30% конечный продукт становится более легкоплавким и мягким - это снижает качество восстановленной поверхности. При содержании церезина меньше 30% снижаются адгезионные свойства и пластичность заявленного состава, а при содержании церезина больше 40% - нанесение состава на реставрируемую поверхность будет затруднено вследствие мягкой структуры состава. Для придания металлического блеска и для равномерности нанесения состава на поверхность автомобиля в состав вводится слюда. В качестве слюды может быть использован мусковит или любой другой вид слюды, производимой для лакокрасочной промышленности. Нижний предел количественного состава слюды - 8,8%. Меньшее ее количество не окажет влияния на равномерность нанесения состава. Верхний предел содержания в составе слюды - 18,8%. В случае содержания слюды более чем 18,8%, нарушится адгезия конечного состава, он станет хрупким. В качестве технологической добавки вводится кремний - органический полимер - поли-метилсилоксан в количестве 0,2%. Он известен как вещество, улучающее структуру и взаимосовместимость различных ингредиентов, а также используется для придания водоотталкивающих свойств конечному составу. При меньшем количестве полиметилсилоксана была бы снижена антикоррозионная устойчивость заявляемого состава. Для улучшения адгезии состава с поверхностью транспортного средства вводится абиетиновая кислота. Ее процентное содержание 10% необходимо и достаточно для наилучшего «прилипания» состава к поверхности транспортного средства.The carnauba wax which is a part is the hardest and most stable of natural waxes. Materials using carnauba wax become more heat-resistant and non-flowable due to it. Excessive hardness of this wax is reduced in the claimed composition due to the use of ceresin. Due to the fine crystalline structure, ceresin has a good viscosity, therefore, it gives higher ductility to the final composition. The content of these substances in the range of 30-40% is optimal, since when the content of Carnauba wax is more than 40%, the final product becomes brittle, which is bad for filling defects on the restored surface. And when the content of Carnauba wax is less than 30%, the final product becomes more fusible and softer - this reduces the quality of the restored surface. When the ceresin content is less than 30%, the adhesive properties and ductility of the claimed composition are reduced, and when the ceresin content is more than 40%, applying the composition to the surface to be restored will be difficult due to the soft structure of the composition. To give a metallic shine and to evenly apply the composition to the surface of the car, mica is introduced into the composition. As mica, muscovite or any other type of mica produced for the paint and varnish industry can be used. The lower limit of the quantitative composition of mica is 8.8%. A smaller amount will not affect the uniformity of application of the composition. The upper limit of the content in the mica is 18.8%. In the case of a mica content of more than 18.8%, the adhesion of the final composition is broken, it will become brittle. As a technological additive, silicon is introduced - an organic polymer - polymethylsiloxane in an amount of 0.2%. It is known as a substance that improves the structure and interoperability of various ingredients, and is also used to impart water-repellent properties to the final composition. With less polymethylsiloxane, the anticorrosion resistance of the claimed composition would be reduced. To improve the adhesion of the composition to the vehicle surface, abietic acid is introduced. Its percentage of 10% is necessary and sufficient for the best "adhesion" of the composition to the surface of the vehicle.
Для того чтобы придать составу цвет, соответствующий цвету реставрируемой поверхности, в него добавляются различные пигменты как органического, так и неорганического или комплексного происхождения, а также их смеси. При этом свойства состава от использования различных пигментов не изменяются. Для придания составу, например, черного цвета используется такой пигмент, как технический углерод. От количества технического углерода в диапазоне от 1,0 до 11,0% зависит насыщенность черного цвета, а в комбинации его с белым пигментом (в том же диапазоне) цвет варьируется от светло-серого до черного. Таким же образом использование других пигментов или их комбинации придаст составу другой требуемый цвет.In order to give the composition a color corresponding to the color of the surface being restored, various pigments of both organic and inorganic or complex origin, as well as mixtures thereof, are added to it. Moreover, the properties of the composition from the use of various pigments do not change. To give the composition, for example, black, a pigment such as carbon black is used. The saturation of black depends on the amount of carbon black in the range from 1.0 to 11.0%, and in combination with white pigment (in the same range), the color varies from light gray to black. In the same way, the use of other pigments or a combination thereof will give the composition a different desired color.
Долговечность состава, его стойкость к вредным воздействиям окружающей среды - (влажность, низкая температура, соляной туман) обеспечивается содержанием в нем церезина.The durability of the composition, its resistance to harmful environmental influences - (humidity, low temperature, salt fog) is ensured by the content of ceresin in it.
Технология получения воскового состава состоит в следующем.The technology for producing the wax composition is as follows.
В диспергатор загружают все компоненты, кроме пигментов, расплавляют их и перемешивают при температуре t=100°С в течение 2 часов. Затем в расплав добавляют пигменты и продолжают помешивание еще в течение 20 минут для тщательного распределения всех компонентов в однородную жидкую массу. После этого ее разливают в цилиндрические металлические формы, охлаждают и выдавливают из формы. Готовые восковые карандаши оборачивают в фольгу или вставляют в специальные футляры.All components except the pigments are loaded into the dispersant, melted and mixed at a temperature of t = 100 ° C for 2 hours. Then pigments are added to the melt and stirring is continued for another 20 minutes to thoroughly distribute all components into a homogeneous liquid mass. After that, it is poured into cylindrical metal molds, cooled and squeezed out of the mold. Finished wax pencils are wrapped in foil or inserted into special cases.
Использование карандашей заявляемого состава происходит следующим образом.The use of pencils of the claimed composition is as follows.
Выбирается карандаш того цвета, который соответствует цвету обрабатываемой поверхности. Затем, прижимая карандаш, следует наносить состав на поверхность, производя движения карандашом вдоль царапины, или скола до тех пор, пока вся царапина или скол не будет заполнена составом карандаша. Излишек состава выше окрашенной поверхности можно стереть тканью.A pencil of the color that matches the color of the surface being machined is selected. Then, pressing the pencil, the composition should be applied to the surface, making movements with the pencil along the scratch, or chip, until the entire scratch or chip is filled with the composition of the pencil. Excess composition above the painted surface can be wiped off with a cloth.
Использование в заявляемом составе менее дорогостоящих и дефицитных компонентов - карнаубского воска и церезина - позволяет снизить цену на восковой состав, не снижая, а улучшая при этом те его свойства, которые особенно важны в климатических условиях Российской Федерации (использование состава при низких температурах воздуха, в условиях соляного тумана).The use of less expensive and scarce components — carnauba wax and ceresin — in the claimed composition allows one to lower the price of the wax composition without decreasing, but improving its properties that are especially important in the climatic conditions of the Russian Federation (using the composition at low air temperatures, salt fog conditions).
Для исследования свойств заявляемого состава и для подтверждения преимуществ заявленного состава перед прототипом, Заявитель обратился в ООО «Экспертное бюро» г.Ижевска».To study the properties of the claimed composition and to confirm the advantages of the claimed composition over the prototype, the Applicant applied to the Expert Bureau LLC of Izhevsk. ”
В ООО «Экспертное бюро г.Ижевска» экспертом Федоровой Т.В. были проведены исследования свойств состава, разработанного автором и Заявителем данного состава Шаповалом Сергеем Викторовичем. Для наглядности одновременно с исследованием свойств карандаша заявляемого состава были исследованы свойства автомобильного реставрационного воскового карандаша «Turtle wax», произведенного компанией «Concept Chemicals & Coating Ltd.» в Великобритании, состав которого соответствует составу нашего прототипа. Карандаш заявляемого состава, свойства которого исследовались ООО «Экспертное бюро» г.Ижевска», был следующим:In LLC "Expert Bureau of Izhevsk" expert Fedorova T.V. Studies were conducted on the properties of the composition developed by the author and applicant of this composition Shapoval Sergey Viktorovich. For clarity, simultaneously with the study of the properties of the pencil of the claimed composition, the properties of the Turtle wax automobile restoration pencil produced by Concept Chemicals & Coating Ltd. in the UK, the composition of which corresponds to the composition of our prototype, were investigated. The pencil of the claimed composition, the properties of which were examined by LLC "Expert Bureau" of Izhevsk ", was as follows:
Карнаубский воск - 30%Carnauba wax - 30%
Церезин - 40%Ceresin - 40%
Пигмент - 10,8%Pigment - 10.8%
Слюда - 9%Mica - 9%
Полиметилсилоксан - 0,2%;Polymethylsiloxane - 0.2%;
Абиетиновая кислота - 10%;Abietic acid - 10%;
В качестве церезина в данном составе был использован церезин по ГОСТ 2488-79. В качестве пигмента для придания составу черного цвета использовался технический углерод - продукт предприятия ОАО «Пигмент», г.Тамбов. Слюда мокрого помола по ГОСТ 19571-74 - продукт предприятия ООО «Батолит», г.Москва. Полиметилсилоксан - НПК ЗАО «Ермакхим», г.Москва по ГОСТ 13032-77. Абиетиновая кислота - ЗАО «Лабтех», г.Москва. Карнаубский воск - АО "МХК "ЕвроХим" г.Москва.As ceresin in this composition, ceresin was used in accordance with GOST 2488-79. As a pigment to give the composition a black color, carbon black was used - a product of the enterprise Pigment OJSC, Tambov. Wet mica according to GOST 19571-74 is a product of Batolit LLC, Moscow. Polymethylsiloxane - NPK ZAO Ermakkhim, Moscow, according to GOST 13032-77. Abietic acid - CJSC "Labtech", Moscow. Karnaubsky wax - JSC "MCC" EuroChem "Moscow.
Проведенные исследования качества подтвердили высокие адгезионные и антикоррозионные свойства заявляемого состава, а также его устойчивость к неблагоприятным воздействиям окружающей среды - влажность, низкая температура, соляной туман.The quality studies conducted have confirmed the high adhesive and anticorrosive properties of the claimed composition, as well as its resistance to adverse environmental influences - humidity, low temperature, salt fog.
Claims (1)