RU2377195C1 - Fusion mixture for glass production - Google Patents
Fusion mixture for glass production Download PDFInfo
- Publication number
- RU2377195C1 RU2377195C1 RU2008140792/03A RU2008140792A RU2377195C1 RU 2377195 C1 RU2377195 C1 RU 2377195C1 RU 2008140792/03 A RU2008140792/03 A RU 2008140792/03A RU 2008140792 A RU2008140792 A RU 2008140792A RU 2377195 C1 RU2377195 C1 RU 2377195C1
- Authority
- RU
- Russia
- Prior art keywords
- rock
- glass production
- fusion mixture
- silica sand
- glass
- Prior art date
Abstract
Description
Изобретение относится к области технологии силикатов и касается производства стекла, которое может быть использовано для изготовления изделий декоративно-художественного назначения, посуды.The invention relates to the field of technology of silicates and for the production of glass, which can be used for the manufacture of decorative products, tableware.
Известна шихта для получения цветного стекла, включающая соду, кварцевый песок; диопсидовую породу 25,9-85,0 мас.% (с содержанием примесей не более 15,0 мас.%.Known mixture for producing colored glass, including soda, quartz sand; diopside rock of 25.9-85.0 wt.% (with an impurity content of not more than 15.0 wt.%.
Задачей изобретения является снижение температуры варки стекла.The objective of the invention is to reduce the temperature of glass melting.
Технический результат достигается тем, что шихта для получения стекла, включающая соду, кварцевый песок, диопсидовую породу, дополнительно содержит титаногипс, при следующем соотношении компонентов, мас.%: сода 10,0-12,0; кварцевый песок 36,0-38,0; диопсидовая порода 40,0-42,0; титаногипс 10,0-12,0.The technical result is achieved by the fact that the mixture for producing glass, including soda, quartz sand, diopside rock, additionally contains titanogypsum, in the following ratio of components, wt.%: Soda 10.0-12.0; silica sand 36.0-38.0; diopside rock 40.0-42.0; titanogypsum 10.0-12.0.
Титаногипс - отход, получаемый при разложении титановых руд серной кислотой, содержит, мас.%: SiO2 0,61; Fe2O3 13,12; Al2O3 0,68; СаО 30,17; SO3 40,11; TiO2 1,08.Titanogypsum - waste obtained by the decomposition of titanium ores with sulfuric acid, contains, wt.%: SiO 2 0,61; Fe 2 O 3 13.12; Al 2 O 3 0.68; CaO 30.17; SO 3 40.11; TiO 2 1.08.
В таблице приведены составы шихты.The table shows the composition of the charge.
Стекло может быть получено в стекловаренных печах любой конструкции.Glass can be obtained in glassmaking furnaces of any design.
Источник информацииThe source of information
1. SU 1530588, С03С 6/00, 1990.1. SU 1530588, C03C 6/00, 1990.
Claims (1)