RU2375399C1 - Composition for bioprotective coating wood - Google Patents

Composition for bioprotective coating wood Download PDF

Info

Publication number
RU2375399C1
RU2375399C1 RU2008130232/04A RU2008130232A RU2375399C1 RU 2375399 C1 RU2375399 C1 RU 2375399C1 RU 2008130232/04 A RU2008130232/04 A RU 2008130232/04A RU 2008130232 A RU2008130232 A RU 2008130232A RU 2375399 C1 RU2375399 C1 RU 2375399C1
Authority
RU
Russia
Prior art keywords
composition
polymethylphenylsiloxane
wood
resin
terms
Prior art date
Application number
RU2008130232/04A
Other languages
Russian (ru)
Inventor
Анатолий Иванович Катанаев (RU)
Анатолий Иванович Катанаев
Ренфира Султангареевна Миргазитова (RU)
Ренфира Султангареевна Миргазитова
Original Assignee
Общество с ограниченной ответственностью "Элкон"
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Общество с ограниченной ответственностью "Элкон" filed Critical Общество с ограниченной ответственностью "Элкон"
Priority to RU2008130232/04A priority Critical patent/RU2375399C1/en
Application granted granted Critical
Publication of RU2375399C1 publication Critical patent/RU2375399C1/en

Abstract

FIELD: chemistry.
SUBSTANCE: composition is described for bioprotective coating wood, which contains organosilicon lacquer based on polymethylphenylsiloxane or polydimethylphenylsiloxane in amount of 1.5 to 10.0 wt % in terms of dry residue, polyphenylsiloxane or polymethylphenylsiloxane resin or tetraethoxysilane or ethylsilicate in amount of 3.0 to 24.0 wt % in terms of dry residue, a copolymer based on butylmethacrylate and methacrylic acid or its ether in amount of 5.0 to 10.0 wt % and organic solvent - the rest.
EFFECT: method increases water resistance and biostability of wood and wooden materials.
2 tbl

Description

Изобретение относится к области защиты древесины и материалов на ее основе от биоповреждений и может быть использовано в деревообрабатывающей промышленности, строительстве и других областях для получения материалов и конструкций, не подверженных гниению.The invention relates to the field of protection of wood and materials based on it from biodeterioration and can be used in the woodworking industry, construction and other fields to obtain materials and structures that are not susceptible to decay.

Основная причина малого срока службы древесины и древесных материалов, особенно в конструкциях зданий и сооружений - гниение, то есть разложение ее под влиянием жизнедеятельности дереворазрушающих грибов, которые проникли в ткани древесины, используя ее составные части для своего развития.The main reason for the short life of wood and wood materials, especially in the construction of buildings and structures, is rotting, that is, its decomposition under the influence of the activity of wood-destroying fungi that penetrated the wood tissues, using its components for their development.

Известны различные составы с биоцидными свойствами, которые применяются в строительстве и других областях техники, в композицию которых входят различные бактерицидные компоненты. В настоящее время используются фунгицидные и бактерицидные добавки, большинство из которых очень токсичны.There are various compositions with biocidal properties that are used in construction and other fields of technology, the composition of which includes various bactericidal components. Currently fungicidal and bactericidal additives are used, most of which are very toxic.

Известен атмосферостойкий состав "Синтекс" (ТУ 6-02-1-629-89), который содержит органические растворители, нитраты целлюлозы, а также кремнийорганический ингредиент (его аддукт с канифолью) в качестве модификатора. Состав имеет удовлетворительную атмосферостойкость, но не обладает антисептической активностью.Known weather-resistant composition "Syntex" (TU 6-02-1-629-89), which contains organic solvents, cellulose nitrates, as well as an organosilicon ingredient (its adduct with rosin) as a modifier. The composition has a satisfactory weather resistance, but does not have antiseptic activity.

Известен состав для защиты древесины, обладающий более высоким комплексом атмосферостойких свойств (влагостойкость, светойстойкость, тепломорозостойкость, антисептическая активность), который содержит глифталиевую смолу, фосфатный пластификатор, олеат меди, Этилсиликат-40, биоцидную добавку - бистрибутилоловооксид и смесь органических растворителей (RU №2091415, C07D 101/18, 1997).A known composition for protecting wood with a higher complex of weather-resistant properties (moisture resistance, light resistance, heat and cold resistance, antiseptic activity), which contains glyptal resin, phosphate plasticizer, copper oleate, Ethyl silicate-40, biocide additive - bistributyltin oxide and a mixture of organic solvents (RU No. 20914 C07D 101/18, 1997).

Известен состав для пропитки древесины, который, с целью придания ей формостабильности, грибо- и морозостойкости, включает смесь олигоэтоксисилоксанов с олигоэтоксисилоксановой жидкостью в массовом соотношении 5:(0,5-1,5) (SU №1826937, В27К 3/15, 1993). Данная композиция полимеризуется только при нагревании 50-55°С, имеет грибостойкость 2 балла.A known composition for wood impregnation, which, in order to give it form stability, mushroom and frost resistance, includes a mixture of oligoethoxysiloxanes with oligoethoxysiloxane liquid in a mass ratio of 5: (0.5-1.5) (SU No. 1826937, B27K 3/15, 1993 ) This composition polymerizes only when heated at 50-55 ° C, has a mushroom resistance of 2 points.

Известен состав для гидрофобизации целлюлозусодержащих материалов, включающий раствор силоксансодержащего алкоксипроизводного титана в органическом растворителе (RU №2021298, C08G 77/22, C08L 83/08, В27К 3/34, 1994). Состав обладает высокими водоотталкивающими свойствами, однако в описании изобретения ничего не сказано о биоцидных свойствах получаемых покрытий.A known composition for the hydrophobization of cellulose-containing materials, including a solution of a siloxane-containing alkoxy derivative of titanium in an organic solvent (RU No. 2021298, C08G 77/22, C08L 83/08, B27K 3/34, 1994). The composition has high water-repellent properties, however, the description of the invention does not say anything about the biocidal properties of the resulting coatings.

Основными признаками указанных аналогов, совпадающих с существенными признаками заявленной композиции, являются биостойкость и влагостойкость, а по содержанию компонентов наличие силоксансодержащего компонента и органических растворителей.The main features of these analogues, which coincide with the essential features of the claimed composition, are biostability and moisture resistance, and the content of components is the presence of a siloxane-containing component and organic solvents.

Наиболее близким по составу и достигаемому результату к предлагаемому изобретению является состав для модификации твердых поверхностей, в т.ч. дерева, включающий кремнийорганическое соединение, гидрофобный порошковый наполнитель, органический растворитель и полиакриловую смолу, в качестве адгезива (RU №2036213, C09D 183/04, С08К 9/04). В качестве кремнийорганического соединения состав может содержать диметилдихлорсилан, полиэтилсилоксановую жидкость, полиметилсилоксановую жидкость или полиметилдисилазан. Данный состав обеспечивает обрабатываемому материалу влагостойкость и биостойкость (грибостойкость).The closest in composition and the achieved result to the proposed invention is a composition for the modification of hard surfaces, including wood, including an organosilicon compound, a hydrophobic powder filler, an organic solvent and a polyacrylic resin, as an adhesive (RU No. 2036213, C09D 183/04, C08K 9/04). As the organosilicon compound, the composition may contain dimethyldichlorosilane, polyethylsiloxane liquid, polymethylsiloxane liquid or polymethyldisilazane. This composition provides the processed material with moisture resistance and biostability (mushroom resistance).

Задачей изобретения является создание нового защитного состава, обеспечивающего влагостойкость и высокую эффективность биозащиты материалов из древесины.The objective of the invention is the creation of a new protective composition that provides moisture resistance and high biosecurity of wood materials.

Указанная задача решается за счет того, что состав для биозащитного покрытия древесины, содержащий кремнийорганическое соединение, акриловый полимер и органический растворитель, согласно изобретению, в качестве кремнийорганического соединения содержит смесь кремнийорганического лака на основе полиметилфенилсилоксана или полидиметилфенилсилоксана с полифенилсилоксановой или полиметилфенилсилоксановой смолой или тетраэтоксисиланом или этилсиликатом, а в качестве акрилового полимера содержит сополимер на основе бутилметакрилата и метакриловой кислоты или ее эфира при следующем соотношении компонентов, мас.%:This problem is solved due to the fact that the composition for bioprotective coating of wood, containing an organosilicon compound, an acrylic polymer and an organic solvent, according to the invention, contains, as an organosilicon compound, a mixture of organosilicon varnish based on polymethylphenylsiloxane or polydimethylphenylsiloxane with polyphenylsiloxane or polymethylphenylsiloxane ethylene or tetra and as an acrylic polymer contains a butyl methacrylate-based copolymer methacrylic acid or an ester thereof in the following ratio, wt.%:

кремнийорганический лак на основе полиметилфенилсилоксанаpolymethylphenylsiloxane-based silicone varnish 1,5-10,01.5-10.0 или полидиметилфенилсилоксана or polydimethylphenylsiloxane   в пересчете на сухой остатокin terms of solids   полифенилсилоксановая или полиметилфенилсилоксановая смола,polyphenylsiloxane or polymethylphenylsiloxane resin, 3,0-24,03.0-24.0 или тетраэтоксисилан, или этилсиликатor tetraethoxysilane or ethyl silicate   в пересчете на сухой остатокin terms of solids   указанный акриловый полимерspecified acrylic polymer 5-105-10 органический растворительorganic solvent остальноеrest

Все компоненты, входящие в состав композиции, не дефицитны и выпускаются промышленностью.All components that make up the composition are not deficient and are produced by industry.

Каждый из названных признаков сам по себе известен, но их устойчивая взаимная связь в заявленном соотношении является необходимой и достаточной для достижения суммарного эффекта, неочевидного для специалиста, нового технического результата, не присущего данным признакам в их раздробленности. Поэтому, по мнению заявителя, заявленный состав соответствует критерию "изобретательский уровень".Each of these characteristics is known per se, but their stable mutual relationship in the stated ratio is necessary and sufficient to achieve a total effect that is not obvious to the specialist, a new technical result that is not inherent in these characteristics in their fragmentation. Therefore, according to the applicant, the claimed composition meets the criterion of "inventive step".

Предлагаемый состав обеспечивает одновременно био- и влагозащиту древесных материалов.The proposed composition provides both bio and moisture protection of wood materials.

В качестве полиорганосилоксана используют (но не ограничиваются ими) полиметилфенилсилоксановую смолу (ПМФСС), представляющую собой 50-60% раствор полиметилфенилизобутоксисилоксановой смолы в толуоле или ксилоле; кремнийорганическую смолу КО 134-276, представляющую собой 34-40% раствор полифенилсилоксановой смолы в толуоле или ксилоле; кремнийорганическую смолу 139-297, представляющую собой 60-70% раствор полифенилизобутоксисилоксановой смолы в толуоле или ксилоле; Этилсиликат-32 и Этилсиликат 40, представляющие собой сложную смесь тетраэтоксисилана (ТЭОС) и олигоэтоксисилоксанов, с разной степенью конденсации. Средний состав Этилсиликатов соответствует формуле олигомера: (RO)3Si[OSi(OR)2]4OSi(OR)3. Этилсиликат-32 и Этилсиликат-40 различаются содержанием SiO2 - соответственно 32% и 40 мас.%.As the polyorganosiloxane, use (but not limited to) polymethylphenylsiloxane resin (PMFSS), which is a 50-60% solution of polymethylphenylisobutoxysiloxane resin in toluene or xylene; organosilicon resin KO 134-276, which is a 34-40% solution of polyphenylsiloxane resin in toluene or xylene; organosilicon resin 139-297, which is a 60-70% solution of polyphenylisobutoxysiloxane resin in toluene or xylene; Ethyl silicate-32 and ethyl silicate 40, which are a complex mixture of tetraethoxysilane (TEOS) and oligoethoxysiloxanes, with varying degrees of condensation. The average composition of ethyl silicates corresponds to the oligomer formula: (RO) 3 Si [OSi (OR) 2 ] 4 OSi (OR) 3 . Ethyl silicate-32 and ethyl silicate-40 differ in the content of SiO 2 - respectively 32% and 40 wt.%.

В качестве кремнийорганических лаков на основе полиметилфенилсилоксана или полидиметилфенилсилоксана используют (но не ограничиваются ими) электроизоляционные кремнийорганические лаки: КО-921, представляющий собой 48-52% раствор полидиметилфенилсилоксановой смолы в толуоле, модифицированной полимером; КО-915, представляющий собой 63-67% раствор в толуоле полиметилфенилсилоксановой смолы, модифицированной полиэфиром; КО -916А, представляющие собой 58-62% раствор в толуоле полиметилфенилсилоксановой смолы, модифицированной полиэфиром; КО-916К, представляющий собой 64-68% раствор в ксилоле полиметилфенилсилоксановой смолы, модифицированной полиэфиром; лак КО-075, представляющий собой 34-40% раствор в толуоле, ксилоле или сольвенте полиметилфенилсилоксановой смолы, модифицированной пентафталиевым лаком.As organosilicon varnishes based on polymethylphenylsiloxane or polydimethylphenylsiloxane use (but are not limited to) insulating organosilicon varnishes: KO-921, which is a 48-52% solution of a polymer-modified polydimethylphenylsiloxane resin in toluene; KO-915, which is a 63-67% solution in toluene of polyester modified polymethylphenylsiloxane resin; KO-916A, which is a 58-62% solution in toluene of a polyester-modified polymethylphenylsiloxane resin; KO-916K, which is a 64-68% solution in xylene of a polyester modified polymethylphenylsiloxane resin; KO-075 varnish, which is a 34-40% solution in toluene, xylene or a solvent of a polymethylphenylsiloxane resin modified with pentaphthalic varnish.

В качестве акрилового полимера может быть использован сополимер БМК-5, представляющий собой сополимер бутилметакрилата и метакриловой кислоты, Дегалан LP 64/12 - бисерный полимер на основе метилметакрилата и н-бутилметакрилата, Дегалан LP 65/12 - бисерный полимер на основе метилметакрилата и н-бутилметакрилата, Дегалан LP 675 - бисерный полимер на основе изо-бутилметакрилата.As an acrylic polymer, a BMK-5 copolymer can be used, which is a copolymer of butyl methacrylate and methacrylic acid, Degalan LP 64/12 is a bead polymer based on methyl methacrylate and n-butyl methacrylate, Degalan LP 65/12 is a bead polymer based on methyl methacrylate and n- butyl methacrylate, Degalan LP 675 - isobutyl methacrylate-based bead polymer.

В качестве растворителя используют преимущественно ароматические растворители: толуол, ксилол, сольвент и т.п или их смесь.The solvent used is mainly aromatic solvents: toluene, xylene, solvent, etc., or a mixture thereof.

Состав готовят следующим образом: расчетное количество акрилового полимера растворяют в расчетном количестве органического растворителя, далее последовательно загружают остальные ингредиенты, смесь перемешивают до однородного состояния, выдерживают 2 часа и после анализа на соответствие ТУ разливают в тару.The composition is prepared as follows: the calculated amount of acrylic polymer is dissolved in the estimated amount of organic solvent, then the remaining ingredients are loaded sequentially, the mixture is stirred until it is homogeneous, kept for 2 hours and after analysis for compliance with the technical specifications, it is poured into containers.

При необходимости допускается введение в состав, в качестве пигмента, красителей органических серии Тиразоль (ТУ 6-36-5763445-40-91, ТУ 6-00-04691277-146-96, ТУ 6-00-5763441-86-93).If necessary, it is allowed to introduce into the composition, as a pigment, dyes of the Tirazol organic series (TU 6-36-5763445-40-91, TU 6-00-04691277-146-96, TU 6-00-5763441-86-93).

Варианты предложенного состава представлены в таблице 1.Options for the proposed composition are presented in table 1.

Полученные составы представляют собой однородную жидкость от светло-желтого до коричневого цвета без посторонних включений, массовая доля нелетучих веществ составляет 17-24%, условная вязкость при температуре (20±0,5)°С по вискозиметру типа В3-246 с диаметром сопла 4 мм 11-12 с, время высыхания до степени 3 при температуре (20±2)°С не более 0,5 ч.The resulting compositions are a homogeneous liquid from light yellow to brown in color without impurities, the mass fraction of non-volatiles is 17-24%, the nominal viscosity at a temperature of (20 ± 0.5) ° C according to a viscometer type B3-246 with a nozzle diameter of 4 mm 11-12 s, drying time to degree 3 at a temperature of (20 ± 2) ° С no more than 0.5 hours

Состав применяют для придания древесине грибостойкости, влагостойкости, атмосферостойкости и повышения прочности.The composition is used to give wood mushroom resistance, moisture resistance, weather resistance and increase strength.

Перед нанесением состава поверхность очищают от грязи и пыли. На обрабатываемую поверхность состав наносят краскораспылителем, кистью или валиком вдоль волокон древесины. После высыхания первого слоя (через 20-30 минут) наносят второй слой. Общий расход состава составляет 160-180 г/м2.Before applying the composition, the surface is cleaned of dirt and dust. On the surface to be treated, the composition is applied with a spray gun, brush or roller along the wood fibers. After the first layer has dried (after 20-30 minutes), a second layer is applied. The total consumption of the composition is 160-180 g / m 2 .

Для испытания на биостойкость (по ГОСТ 9.048-89, метод 1) на деревянные образцы кисточкой наносили состав в два слоя, затем высушивали сутки при комнатной температуре. После этого образцы заражали суспензией с концентрацией 1-2 млн/мл спор грибов Aspergillus niger van Tieghem, Aspergillus terreus Thom, Aureobasidium pullulans (de Bary) Arnaud, Paecilomyces variotii Bainier, Penicillium funiculosum Thom, Penicillium ochrochloron Biourge, Scopularipsis brevicaulis Bainier, Trichoderma viride Pers. ex S.F.Gray. Дополнительно в суспензию были введены споры дереворазрушающих грибов Serpula lacrimans BKM F - 465 и Antrodia sinuosa BKM F - 1741. Контролем служили деревянные образцы без пропитки.For biostability testing (according to GOST 9.048-89, method 1), two layers of the composition were applied to wooden samples with a brush, then dried for 24 hours at room temperature. After that, the samples were infected with a suspension with a concentration of 1-2 million / ml of spores of the fungi Aspergillus niger van Tieghem, Aspergillus terreus Thom, Aureobasidium pullulans (de Bary) Arnaud, Paecilomyces variotii Bainier, Penicillium funiculosum Thom, Penicillium ochrochloruliris beris biormema Pers. ex S.F. Gray. Additionally, spores of wood-destroying fungi Serpula lacrimans BKM F - 465 and Antrodia sinuosa BKM F - 1741 were introduced into the suspension. Wooden samples without impregnation were used as controls.

Образцы, зараженные суспензией грибов, помещали в открытой чашке Петри в эксикатор и выдерживали в условиях, оптимальных для роста грибов: температуре 27-28°С и влажности 98% в течение 28 суток. Промежуточные осмотры образцов проводили через каждые 14 суток.Samples infected with a suspension of mushrooms were placed in an open Petri dish in a desiccator and kept under conditions optimal for mushroom growth: temperature 27-28 ° С and 98% humidity for 28 days. Interim examinations of the samples were carried out every 14 days.

Результаты испытаний представлены в таблице 2, из которых видно, что покрытия, на основе предложенного состава придают древесине влагостойкость и биостойкость (грибостойкость)100%.The test results are presented in table 2, from which it can be seen that coatings, based on the proposed composition, give wood moisture resistance and biostability (mushroom resistance) of 100%.

ТаблицаTable Наименование компонентовName of components Содержание компонентов, мас.%The content of components, wt.% 1.one. 2.2. 3.3. 4.four. 5.5. 6.6. 7.7. 8.8. 9.9. 10.10. Кремнийорганическая смола 134-276 (ТУ 2228-463-05763441-2005)Organosilicon resin 134-276 (TU 2228-463-05763441-2005) 6,86.8   3,03.0     13,613.6 9,09.0       Кремнийорганическая смола 139-297 (ТУ 2228-440-05763441-2004)Organosilicon resin 139-297 (TU 2228-440-05763441-2004)               12,412,4     Полиметилфенилсилоксановая смола (ТУ 2228-277-05763441 -99)Polymethylphenylsiloxane resin (TU 2228-277-05763441 -99)   15,015.0   24,024.0             ТЭОС (ТУ 2435-419-05763441-2003)TEOS (TU 2435-419-05763441-2003)                 6,06.0   Этилсиликат-40 (ТУ 2435-427-05763441-2004)Ethyl silicate-40 (TU 2435-427-05763441-2004)         6,06.0           Этилсиликат-32 (ТУ 2435-397-05763441-2003)Ethylsilicate-32 (TU 2435-397-05763441-2003)                   7,57.5 Лак КО -921 (ГОСТ 16508-70)Varnish KO-921 (GOST 16508-70)         7,57.5           Лак КО-915Б (ТУ 2311-429-05763441-2004)Varnish KO-915B (TU 2311-429-05763441-2004) 6,36.3         3,23.2 4,64.6       Лак КО 916 А (ГОСТ 16508-70)Varnish KO 916 A (GOST 16508-70)   3,03.0             10,010.0   Лак КО-916К (ТУ 2311-396-05763441-2003)Varnish KO-916K (TU 2311-396-05763441-2003)     10,010.0               Лак КО 075 (ТУ 2311-462-05763441-2004)Varnish KO 075 (TU 2311-462-05763441-2004)       1,51,5       3,63.6   2,02.0 - БМК-5 (ТУ 2216-012-55856863-2002)- BMK-5 (TU 2216-012-55856863-2002)           6,06.0         Дегалан LP 64/12Degalan LP 64/12 5,05,0 5,05,0 8,08.0 6,06.0 10,010.0   6,06.0 7,07.0 5,05,0 9,09.0 Органический растворитель:Organic solvent:                     толуолtoluene Ост.Ost. Ост.Ost.     Ост.Ost. Ост.Ost. Ост.Ost.   Ост.Ost. Ост.Ost. ксилолxylene     Ост.Ost. Ост.Ost.       Ост.Ost.    

Таблица 2table 2   Шифр образцаSample Code Внешний вид после испытанийAppearance after testing БаллScore Биостойкость, %Biostability,% Образцы с пропиткойImpregnated Samples 1-11-1 Визуально и под микроскопом прорастания спор и конидий не обнаруженоVisually and under a microscope, germination of spores and conidia was not detected 00 100one hundred 1-21-2 00 100one hundred 1-31-3 00 100one hundred 1-41-4 00 100one hundred 1-51-5 00 100one hundred 1-61-6 00 100one hundred 1-71-7 00 100one hundred 1-81-8 00 100one hundred 1-91-9 00 100one hundred 1-101-10 00 100one hundred Образцы без пропиткиSamples without impregnation 2-12-1 Визуально отчетливо видно развитие грибов на 30% поверхностиThe development of mushrooms on 30% of the surface is visually clearly visible 4four 00 2-22-2 4four 00 2-3-2-3- 4four 00 2-42-4 4four 00 2-52-5 4four 00 2-62-6 4four 00 2-72-7 4four 00 2-82-8 4four 00 2-92-9 4four 00 2-102-10 4four 00

Claims (1)

Состав для биозащитного покрытия древесины, содержащий кремнийорганическое соединение, акриловый полимер и органический растворитель, отличающийся тем, что в качестве кремнийорганического соединения содержит смесь кремнийорганического лака на основе полиметилфенилсилоксана или полидиметилфенилсилоксана с полифенилсилоксановой или полиметилфенилсилоксановой смолой или тетраэтоксисиланом или этилсиликатом, а в качестве акрилового полимера содержит сополимер на основе бутилметакрилата и метакриловой кислоты или ее эфира при следующем соотношении компонентов, мас.%:
кремнийорганический лак на основе   полиметилфенилсилоксана или полидиметилфенилсилоксана   в пересчете на сухой остаток 1,5-10,0 полифенилсилоксановая или полиметилфенилсилоксановая смола   или тетраэтоксисилан или этилсиликат   в пересчете на сухой остаток 3,0-24,0 указанный акриловый полимер 5,0-10,0 органический растворитель остальное
Composition for bioprotective coating of wood, containing an organosilicon compound, an acrylic polymer and an organic solvent, characterized in that the organosilicon compound contains a mixture of organosilicon varnish based on polymethylphenylsiloxane or polydimethylphenylsiloxane with polyphenylsiloxane or polymethylphenylsiloxane resin or tetraethoxysilane polymer or ethyl ethylene polymer based on butyl methacrylate and methacrylic acid or its ester when the ratio of components, wt.%:
silicone based varnish polymethylphenylsiloxane or polydimethylphenylsiloxane in terms of solids 1.5-10.0 polyphenylsiloxane or polymethylphenylsiloxane resin or tetraethoxysilane or ethyl silicate in terms of solids 3.0-24.0 specified acrylic polymer 5.0-10.0 organic solvent rest
RU2008130232/04A 2008-07-21 2008-07-21 Composition for bioprotective coating wood RU2375399C1 (en)