RU2354729C1 - Sintered alloy - Google Patents
Sintered alloy Download PDFInfo
- Publication number
- RU2354729C1 RU2354729C1 RU2007136562/02A RU2007136562A RU2354729C1 RU 2354729 C1 RU2354729 C1 RU 2354729C1 RU 2007136562/02 A RU2007136562/02 A RU 2007136562/02A RU 2007136562 A RU2007136562 A RU 2007136562A RU 2354729 C1 RU2354729 C1 RU 2354729C1
- Authority
- RU
- Russia
- Prior art keywords
- nickel
- indium
- alloy
- silver
- sintered alloy
- Prior art date
Abstract
Description
Изобретение относится к области металлургии и касается производства спеченных сплавов, которые могут быть использованы для изготовления бижутерии, наградных знаков, монет, изделий декоративно-прикладного искусства.The invention relates to the field of metallurgy and for the production of sintered alloys, which can be used for the manufacture of jewelry, award signs, coins, decorative and applied arts.
Известен сплав, содержащий алюминий, никель и другие компоненты [1].Known alloy containing aluminum, Nickel and other components [1].
Задачей изобретения является повышение коррозионной стойкости сплава.The objective of the invention is to increase the corrosion resistance of the alloy.
Технический результат достигается тем, что спеченный сплав, содержащий алюминий и никель, дополнительно содержит серебро и индий, при следующем соотношении компонентов, мас.%: алюминий 24,0-26,0; никель 24,0-26,0; серебро 24,0-26,0; индий 24,0-26,0.The technical result is achieved in that the sintered alloy containing aluminum and nickel additionally contains silver and indium, with the following ratio of components, wt.%: Aluminum 24.0-26.0; nickel 24.0-26.0; silver 24.0-26.0; indium 24.0-26.0.
В таблице приведены составы сплава.The table shows the alloy compositions.
Никель
Серебро
ИндийAluminum
Nickel
Silver
Indium
24,0
26,0
26,024.0
24.0
26.0
26.0
25,0
25,0
25,025.0
25.0
25.0
25.0
26,0
24,0
24,026.0
26.0
24.0
24.0
Скорость разрушения сплава в агрессивной среде (водный раствор 3% хлорида натрия и 0,1% перекиси водорода) составит 40-45 мг/м2·ч для всех приведенных в таблице составов.The destruction rate of the alloy in an aggressive environment (an aqueous solution of 3% sodium chloride and 0.1% hydrogen peroxide) will be 40-45 mg / m 2 · h for all the compositions listed in the table.
В составе компоненты проявляют себя следующим образом.In the composition, the components manifest themselves as follows.
Никель снижает пористость и повышает плотность сплава. Серебро в сочетании с алюминием и никелем повышает механические свойства сплава. Индий способствует “изоляции” очагов межкристаллитной коррозии.Nickel reduces porosity and increases the density of the alloy. Silver in combination with aluminum and nickel increases the mechanical properties of the alloy. Indium contributes to the "isolation" of foci of intergranular corrosion.
Порошки компонентов сплава смешивают в указанных соотношениях, смесь прессуют под давлением 2-2,5 т/см2 в изделия и спекают в электропечах при температуре 850-870°С в среде инертного газа.The powders of the alloy components are mixed in the indicated proportions, the mixture is pressed under pressure of 2-2.5 t / cm 2 into products and sintered in electric furnaces at a temperature of 850-870 ° C in an inert gas environment.
Источник информации:The source of information:
1. Иванов В.Н. Словарь-справочник по литейному производству. - М.: Машиностроение, 1990. - С.90.1. Ivanov V.N. Foundry Dictionary. - M .: Mechanical Engineering, 1990. - P.90.
Claims (1)