Abstract
Description
Изобретение относится к технологии силикатов, в частности к составам фритты эмали для покрытия изделий из углеродистой стали.The invention relates to silicates technology, in particular to enamel frit compositions for coating carbon steel products.
Известна фритта эмали, включающая, мас.%: В2О3 13,5-40,0; СоО 0-1,0; RO+R2O (RO - CaO, MgO, BaO, ZnO, SrO; R2O - Na2O, K2O, Li2O) 15,0-40,0; TiO2 - 0-23,0; SiO2 4,5-34,0 [1].Known enamel frit, including, wt.%: In 2 About 3 13.5-40.0; CoO 0-1.0; RO + R 2 O (RO — CaO, MgO, BaO, ZnO, SrO; R 2 O — Na 2 O, K 2 O, Li 2 O) 15.0-40.0; TiO 2 0-23.0; SiO 2 4.5-34.0 [1].
Задачей изобретения является повышение термостойкости эмали.The objective of the invention is to increase the heat resistance of enamel.
Технический результат достигается тем, что во фритте эмали, включающей В2O3, СоО, Na2O, CaO, Al2О3, TiO2, Li2O, SiO2, компоненты находятся при следующем соотношении, мас.%: В2O3 40,6-42,0; СоО 0,3-0,7; Na2O 6,0-6,5; CaO 6,0-6,5; Al2О3 16,0-18,0; TiO2 23,2-24,0; Li2O 0,3-0,7; SiO2 5,0-6,0.The technical result is achieved in that in the frit of enamel, including B 2 O 3 , CoO, Na 2 O, CaO, Al 2 O 3 , TiO 2 , Li 2 O, SiO 2 , the components are in the following ratio, wt.%: B 2 O 3 40.6-42.0; CoO 0.3-0.7; Na 2 O 6.0-6.5; CaO 6.0-6.5; Al 2 O 3 16.0-18.0; TiO 2 23.2-24.0; Li 2 O 0.3-0.7; SiO 2 5.0-6.0.
В таблице приведены составы фритты эмали.The table shows the composition of the enamel frit.
Фритту эмали варят в электропечи при температуре 1350°С. Расплав гранулируют в воду. Подготавливают эмалевый шликер, содержащий, мас.ч: фритта 100; глина 0,5; бура 0,1; вода 46. Эмалевый шликер наносят на поверхность стальных изделий и закрепляют обжигом при температуре 800°С.Enamel frit is cooked in an electric furnace at a temperature of 1350 ° C. The melt is granulated into water. Prepare an enamel slip containing, parts by weight: frit 100; clay 0.5; borax 0.1; water 46. An enamel slip is applied to the surface of steel products and fixed by firing at a temperature of 800 ° C.
Источник информацииThe source of information
1. JP 55020256 A, 1980.1. JP 55020256 A, 1980.
Claims (1)
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
RU2007118282/03A RU2350574C2 (en) | 2007-05-16 | 2007-05-16 | Enamel frit |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
RU2007118282/03A RU2350574C2 (en) | 2007-05-16 | 2007-05-16 | Enamel frit |
Publications (2)
Publication Number | Publication Date |
---|---|
RU2007118282A RU2007118282A (en) | 2008-11-27 |
RU2350574C2 true RU2350574C2 (en) | 2009-03-27 |
Family
ID=40543099
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
RU2007118282/03A RU2350574C2 (en) | 2007-05-16 | 2007-05-16 | Enamel frit |
Country Status (1)
Country | Link |
---|---|
RU (1) | RU2350574C2 (en) |
-
2007
- 2007-05-16 RU RU2007118282/03A patent/RU2350574C2/en active
Also Published As
Publication number | Publication date |
---|---|
RU2007118282A (en) | 2008-11-27 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
RU2008119422A (en) | GLASS COMPOSITIONS | |
DE602007008823D1 (en) | GLASS COMPOSITIONS | |
RU2350574C2 (en) | Enamel frit | |
RU2302400C1 (en) | Composition of the glaze blend | |
RU2405742C1 (en) | Enamel frit | |
RU2435739C1 (en) | Glass | |
RU2375318C1 (en) | Glase charge | |
RU2315011C1 (en) | Glaze | |
RU2446114C1 (en) | Enamel frit | |
RU2320580C1 (en) | Enamel | |
RU2320587C1 (en) | Enamel | |
RU2465229C1 (en) | Enamel slip | |
RU2455268C1 (en) | Non-fritted glaze | |
RU2332369C1 (en) | Enamel | |
RU2326830C1 (en) | Glass coating | |
RU2332368C1 (en) | Enamel | |
RU2333167C1 (en) | Non-fritted glaze | |
RU2329978C1 (en) | Glaze | |
RU2315013C1 (en) | Glaze | |
RU2343123C2 (en) | Enamel | |
RU2315731C1 (en) | Glaze | |
RU2459770C1 (en) | Enamel | |
RU2311370C1 (en) | Enamel | |
RU2329215C2 (en) | Enamel | |
RU2526445C2 (en) | Electroinsulating glass enamel for stainless steel products |