RU2268139C2 - Method for working of wood products (modifications) - Google Patents
Method for working of wood products (modifications) Download PDFInfo
- Publication number
- RU2268139C2 RU2268139C2 RU2003136643/04A RU2003136643A RU2268139C2 RU 2268139 C2 RU2268139 C2 RU 2268139C2 RU 2003136643/04 A RU2003136643/04 A RU 2003136643/04A RU 2003136643 A RU2003136643 A RU 2003136643A RU 2268139 C2 RU2268139 C2 RU 2268139C2
- Authority
- RU
- Russia
- Prior art keywords
- products
- drying
- wood
- water
- glycerol
- Prior art date
Abstract
Description
Изобретение относится к области деревообработки, в частности касается способов защиты изделий из древесины, и может быть использовано в мебельной промышленности и в строительстве.The invention relates to the field of woodworking, in particular, to methods for protecting wood products, and can be used in the furniture industry and in construction.
Существует большое количество технологий, содержащих различные приемы, с использованием разнообразных составов растворов для защиты изделий из древесины с целью увеличения срока их службы и качества.There are a large number of technologies containing various techniques, using a variety of solutions for the protection of wood products in order to increase their service life and quality.
Известен способ обработки древесины, заключающийся в том, что древесину погружают в горячее масло, выдерживают в течение времени, достаточного для полного удаления влаги и последующего частичного заполнения освободившихся полостей древесины маслом (RU патент 2168408, В 27 К 3/02, 2001). Способ прост в техническом исполнении.A known method of processing wood, which consists in the fact that the wood is immersed in hot oil, is incubated for a time sufficient to completely remove moisture and subsequent partial filling of the freed cavities of wood with oil (RU patent 2168408, 27 K 3/02, 2001). The method is simple in technical execution.
Недостатком известного способа является неполное удаление влаги и недостаточная герметизация поверхностного слоя, что может привести к попаданию влаги в древесину, а затем к деформации древесины и сокращению ее срока службы.The disadvantage of this method is the incomplete removal of moisture and insufficient sealing of the surface layer, which can lead to moisture in the wood, and then to the deformation of the wood and reduce its service life.
Известен способ защиты отделочной плитки из модифицированной древесины, применяемой для отделки полов, облицовки стен и потолков (RU патент 2146610, В 27 К 3/02, 2000). Известный способ включает однократную пропитку отделочной плитки путем погружения ее в пропиточную жидкость и последующую сушку, при этом в качестве пропиточной жидкости используют раствор паркетного лака в уайт-спирите. Способ позволяет снизить влагопоглощение отделочной плитки и повысить ее атмосферостойкость.A known method of protecting tiles made of modified wood used for finishing floors, wall and ceiling cladding (RU patent 2146610, 27 K 3/02, 2000). The known method includes a single impregnation of the tiles by dipping it in an impregnating liquid and subsequent drying, while a solution of parquet varnish in white spirit is used as an impregnating liquid. The method allows to reduce the moisture absorption of the tiles and increase its weather resistance.
Недостатком известного способа является недолговечность защитного покрытия на поверхности обработанной плитки и, как следствие, снижение качества плитки.The disadvantage of this method is the fragility of the protective coating on the surface of the treated tile and, as a result, the decrease in the quality of the tile.
Наиболее близким техническим решением к заявленному изобретению является способ обработки древесины (SU авторское свидетельство 1328200, В 27 К 3/32, 1987). В известном способе обработку древесины ведут в несколько циклов (холодная - горячая ванна). В качестве раствора холодной ванны используют фенолоспирты, а для приготовления горячей ванны используют водные растворы глицерина и/или этиленгликоля с добавлением в этот раствор молочной кислоты до достижении кислотности рН 3,5 при температуре 103°С. Этот способ позволяет повысить прочность и стабильность размеров обрабатываемой древесины.The closest technical solution to the claimed invention is a method of processing wood (SU copyright certificate 1328200, 27 K 3/32, 1987). In the known method, wood processing is carried out in several cycles (cold - hot bath). Phenol alcohols are used as a cold bath solution, and aqueous solutions of glycerol and / or ethylene glycol are used to prepare a hot bath with the addition of lactic acid to this solution until the pH reaches pH 3.5 at a temperature of 103 ° C. This method improves the strength and dimensional stability of the processed wood.
Недостатком известного способа является его сложность, трудоемкость, длительность в технологическом исполнении, дороговизна, а также наличие больших энергозатрат при его выполнении.The disadvantage of this method is its complexity, complexity, duration in technological design, high cost, as well as the presence of large energy costs in its implementation.
Технической задачей, на которое направлено изобретение, является повышение качества изделий из древесины за счет увеличения их прочности, стабильности размеров.The technical problem to which the invention is directed is to improve the quality of wood products by increasing their strength, dimensional stability.
Техническим результатом изобретения является упрощение способа обработки изделий из древесины, повышение атмосферостойкости изделий и обеспечение биозащиты изделий от бактерий, грибов и воздействия насекомых.The technical result of the invention is to simplify the method of processing wood products, increase the weather resistance of products and provide biosecurity products from bacteria, fungi and insects.
Указанный технический результат достигается тем, что в способе обработки изделий из древесины по первому варианту, включающем обработку поверхности изделий пропиточным раствором, содержащим смесь глицерина с водой, с последующей сушкой, обработку поверхности изделий пропиточным раствором проводят однократно, а время сушки обработанной поверхности составляет 10-12 часов, при этом обработку и сушку осуществляют при температуре 15-30°С, причем для обработки поверхности изделия используют раствор, содержащий следующий состав компонентов, мас.%:The specified technical result is achieved by the fact that in the method of processing wood products according to the first embodiment, comprising treating the surface of the products with an impregnating solution containing a mixture of glycerol with water, followed by drying, treating the surface of the products with an impregnating solution is carried out once, and the drying time of the treated surface is 10- 12 hours, while processing and drying are carried out at a temperature of 15-30 ° C, and for processing the surface of the product using a solution containing the following composition of components, ma from.%:
Указанный технический результат в способе обработки изделий из древесины по второму варианту, включающем обработку поверхности изделий пропиточным раствором, содержащим смесь глицерина с водой, с последующей сушкой, достигается тем, что обработку поверхности изделий пропиточным раствором проводят однократно, а время сушки обработанной поверхности изделия составляет 10-12 часов, при этом обработку и сушку осуществляют при температуре 15-30°С, а для обработки поверхности изделия используют раствор, содержащий следующий состав компонентов, мас.%:The specified technical result in the method of processing wood products according to the second embodiment, including surface treatment of the products with an impregnating solution containing a mixture of glycerin with water, followed by drying, is achieved by treating the surface of the products with an impregnating solution once, and the drying time of the treated surface of the product is 10 -12 hours, while processing and drying is carried out at a temperature of 15-30 ° C, and for surface treatment of the product using a solution containing the following composition of components, wt.%:
Сущность изобретения.SUMMARY OF THE INVENTION
Способ обработки изделий из древесины по первому варианту исполнения применяют преимущественно для изделий, выполненных их хвойных пород древесины. В этом случае используют пропиточный раствор, содержащий 70-80 мас.% глицерина и 20-30 мас.% воды. Для обеспечения равномерного поступления пропиточного раствора вглубь изделия из древесины обработку (пропитку) поверхности изделия осуществляют при температуре 15-30°С при нормальном атмосферном давлении путем однократного механического нанесения на поверхность изделия пропиточного раствора кистью или валиком, или путем аэрозольного распыления пропиточного раствора, или погружением изделий из древесины в пропиточный раствор и выдержке в нем в течение 5-10 сек. После пропитки осуществляют сушку обработанного изделия, которую проводят в воздушной среде при той же температуре и нормальном атмосферном давлении. Для изделий, выполненных из разных пород древесины и имеющих разную толщину, время последующей сушки обработанного изделия будет разным и будет равно 10-12 часов. После обработки изделия пропиточным раствором глубина пропиточного слоя в нем может составлять до 4 мм.The method of processing wood products according to the first embodiment is used mainly for products made of their coniferous species. In this case, an impregnating solution containing 70-80 wt.% Glycerol and 20-30 wt.% Water is used. To ensure uniform penetration of the impregnating solution deep into the wood product, the surface treatment (impregnation) of the product is carried out at a temperature of 15-30 ° C at normal atmospheric pressure by a single mechanical application of the impregnating solution to the product surface with a brush or roller, or by aerosol spraying of the impregnating solution, or by immersion wood products in an impregnating solution and exposure in it for 5-10 seconds. After impregnation, the processed product is dried, which is carried out in air at the same temperature and normal atmospheric pressure. For products made from different types of wood and having different thicknesses, the time for subsequent drying of the processed product will be different and will be 10-12 hours. After processing the product with an impregnating solution, the depth of the impregnating layer in it can be up to 4 mm.
Способ обработки изделий из древесины по второму варианту применяют для изделий, выполненных из лиственных пород: дуб, ясень, береза, ольха. В этом случае для осуществления способа используют пропиточный раствор, состоящий из 70-80 мас.% глицерина, 5-10 мас.% медного купороса и 15-20 мас.% воды. Обработку (пропитку) поверхности изделия осуществляют путем однократного нанесения на поверхность изделия пропиточного раствора при температуре окружающей среды 15-30°С и нормальном атмосферном давлении. При этом нанесение пропиточного (защитного) раствора на поверхность изделия осуществляют кистью или валиком, или аэрозольным распылением, или методом погружения в пропиточный раствор на 5-10 сек. После пропитки изделия, его сушат в воздушной среде в течение 10-12 часов при температуре 15-30°С и нормальном атмосферном давлении.The method of processing wood products according to the second embodiment is used for products made from hardwood: oak, ash, birch, alder. In this case, for the implementation of the method using an impregnating solution consisting of 70-80 wt.% Glycerol, 5-10 wt.% Copper sulfate and 15-20 wt.% Water. Processing (impregnation) of the surface of the product is carried out by a single application on the surface of the product of an impregnating solution at an ambient temperature of 15-30 ° C and normal atmospheric pressure. In this case, the application of an impregnating (protective) solution to the surface of the product is carried out with a brush or roller, or by aerosol spraying, or by immersion in an impregnating solution for 5-10 seconds. After impregnation of the product, it is dried in air for 10-12 hours at a temperature of 15-30 ° C and normal atmospheric pressure.
Следует отметить, что для таких изделий, как, например, шпон с толщиной 0,8-1 мм после обработки указанным способом происходит полное насыщение изделия пропиточным раствором, а для изделий, толщина которых равна 3-4 мм и более, пропитка происходит частично с образованием пропиточного слоя. Пропиточный раствор проникает в поры древесины и формирует в течение указанного времени сушки защитный каркас, который не изменяет пластичность поверхностного пропитанного слоя и сохраняет влажность внутри изделия, предохраняя изделия от коробления и деформации.It should be noted that for products such as veneer with a thickness of 0.8-1 mm after processing in this way, the product is completely saturated with an impregnating solution, and for products whose thickness is 3-4 mm or more, the impregnation occurs partially with the formation of an impregnating layer. The impregnating solution penetrates into the pores of the wood and forms a protective frame during the specified drying time, which does not change the plasticity of the surface impregnated layer and retains moisture inside the product, protecting the product from warping and deformation.
В результате испытаний образцов из различных пород древесины было установлено, что при нанесении указанного раствора на изделия из древесины с влажностью, равной 6-8%, происходит повышение влажности поверхностного слоя до величины 10-12%. Контрольные испытания обработанных изделий согласно настоящему изобретению в течение 30 суток показали, что влажность изделий с толщиной, образованного пропиточного, слоя, равной 2-3 мм, не изменялась при колебаниях влажности окружающей среды в пределах 45-70%. Кроме того, влажность обработанных изделий не изменялась и после смачивания их поверхности водой.As a result of tests of samples from various wood species, it was found that when applying the specified solution to wood products with a moisture content of 6-8%, the moisture of the surface layer increases to 10-12%. Control tests of the processed products according to the present invention for 30 days showed that the humidity of the products with a thickness formed by the impregnating layer of 2-3 mm did not change with fluctuations in ambient humidity in the range of 45-70%. In addition, the humidity of the processed products did not change after wetting their surface with water.
Пример 1. Для обработки дверных блоков, выполненных из хвойных пород (ель или сосна) и влажностью 8-10% на поверхность изделия наносили с помощью кисти пропиточный раствор один раз при комнатной температуре, равной 24°С, и нормальном атмосферном давлении. Для пропитки в этом случае использовали пропиточный раствор, содержащий, мас.%: 80 глицерина и 20 воды. Затем осуществляли сушку изделия на воздухе при тех же условиях в течение 10 часов. Толщина образованного защитного слоя составляла 1,5-2 мм, при этом влажность его поднялась до 10-12%.Example 1. For processing door blocks made of coniferous species (spruce or pine) and with a moisture content of 8-10%, an impregnating solution was applied with a brush once at room temperature, equal to 24 ° С, and normal atmospheric pressure. For impregnation in this case, an impregnating solution was used, containing, wt.%: 80 glycerol and 20 water. Then the product was dried in air under the same conditions for 10 hours. The thickness of the formed protective layer was 1.5-2 mm, while its humidity rose to 10-12%.
Пример 2. Для обработки паркетной планки из дуба размером 420×70×18 мм и влажностью 6-8% при температуре 20°С и нормальном атмосферном давлении на поверхность изделия путем аэрозольного напыления наносили пропиточный раствор, содержащий, мас.%: 75 глицерина, 20 воды и 5 медного купороса. Пропиточный раствор наносили один раз, а затем осуществляли процесс сушки в воздушной среде изделия при той же температуре и нормальном атмосферном давлении в течение 12 часов. За это время произошла частичная пропитка поверхности изделия на глубину 3 мм, а влажность в пропиточном слое поднялась до 10-12%.Example 2. For processing parquet planks of oak with a size of 420 × 70 × 18 mm and a moisture content of 6-8% at a temperature of 20 ° C and normal atmospheric pressure, an impregnating solution was applied to the surface of the product by aerosol spraying, containing, wt.%: 75 glycerol, 20 water and 5 copper sulfate. The impregnating solution was applied once, and then the drying process was carried out in the air of the product at the same temperature and normal atmospheric pressure for 12 hours. During this time, a partial impregnation of the surface of the product to a depth of 3 mm occurred, and the humidity in the impregnating layer rose to 10-12%.
Способ обработки изделий из древесины применяют, как было указано выше, для изделий, выполненных из различных пород древесины, в мебельной промышленности, а также в строительстве и для защиты других товаров народного потребления.The method of processing wood products is used, as mentioned above, for products made from various types of wood, in the furniture industry, as well as in construction and for the protection of other consumer goods.
Способ согласно настоящему изобретению прост в техническом исполнении, повышает качество изделий из древесины, создавая влагозащитный и биозащитный слой, что увеличивает срок службы изделий из древесины.The method according to the present invention is simple in technical execution, improves the quality of wood products, creating a moisture-proof and bioprotective layer, which increases the service life of wood products.
Кроме того, поверхности изделий из древесины, прошедших обработку согласно изобретению по первому или второму варианту, обладают наилучшей адгезией к лакам и клеевым составам. Полученный пропитанный слой на поверхности изделий согласно настоящему изобретению обеспечивает более глубокое проникновение в него лака или клея. В ряде случаев, поверхность изделий из древесины, прошедшая обработку согласно изобретению, не требует дополнительной шлифовки.In addition, the surfaces of wood products that have been treated according to the invention in the first or second embodiment have the best adhesion to varnishes and adhesives. The obtained impregnated layer on the surface of the products according to the present invention provides a deeper penetration of varnish or glue into it. In some cases, the surface of wood products that has undergone processing according to the invention does not require additional grinding.
Claims (2)