RU2212474C2 - Compositions for inhibiting salt formation, corrosion and washing of equipment in recycled water supply systems

Info

Publication number: RU2212474C2
Application number: RU2001132538A
Authority: RU
Inventors: В.А. Ильин; Н.Е. Жаворонкова; В.М. Курятникова; О.В. Кузнецова; Н.Н. Груздев
Original assignee: ОАО "Череповецкий "Азот"
Priority date: 2001-12-03
Filing date: 2001-12-03
Publication date: 2003-09-20

Abstract

FIELD: compositions for inhibiting carbonate, sulfate and iron oxide depositions in recycled water supply systems and for washing heat-exchanging equipment from salt deposits. SUBSTANCE: composition comprises following components used in the following ratio, wt%: oxyethylidenediphosphonic acid 5-12; commercial sodium polyphosphate 5-12; sodium lignosulfonate 5-12; alkyl dimethylamine oxide 8-16; and water the balance. EFFECT: increased efficiency in removing depositions from surfaces of heat-exchanging equipment and preventing salt and other substances from depositing on said surfaces and improved operation of water supplying systems. 1 tbl

Description

Изобретение относится к составам для предотвращения карбонатных, сульфатных и железооксидных отложений в системах оборотного водоснабжения и промывки теплообменного оборудования от железооксидных отложений и накипи на предприятиях химической и нефтехимической промышленности. The invention relates to compositions for preventing carbonate, sulfate and iron oxide deposits in water recycling systems and flushing heat exchange equipment from iron oxide deposits and scale at chemical and petrochemical enterprises.

Известен состав для ингибирования солеотложения в системах оборотного водоснабжения на основе оксиэтилидендифосфоновой кислоты (ОЭДФ), соединений цинка, лигносульфоната натрия (ЛСТ) и воды (патент RU 2146232, С 02 F 5/14, опубл. 10.03.2000);
Известен также состав на основе оксиэтилидендифосфоновой кислоты (ОЭДФ), соединений цинка, лигносульфоната натрия (ЛСТ), сульфонат порошка и воды (патент RU 2158714, С 02 F 5/14, опубл. 10.11.2000).A known composition for inhibiting scaling in water recycling systems based on hydroxyethylidene diphosphonic acid (HEDP), zinc compounds, sodium lignosulfonate (LST) and water (patent RU 2146232, C 02 F 5/14, publ. 10.03.2000);
Also known is a composition based on hydroxyethylidene diphosphonic acid (HEDP), zinc compounds, sodium lignosulfonate (LST), powder and water sulfonate (patent RU 2158714, С 02 F 5/14, publ. 10.11.2000).

Недостатками вышеназванных составов являются высокий расход ОЭДФ и содержание соединений цинка, отнесенных к категории санитарно-токсикологического действия. The disadvantages of the above formulations are the high consumption of OEDP and the content of zinc compounds classified as sanitary-toxicological action.

Задачей настоящего изобретения является получение состава, предотвращающего карбонатные, сульфатные, железооксидные отложения на теплообменных поверхностях и не содержащего соединений цинка, отнесенного к категории санитарно-токсикологического действия. The objective of the present invention is to obtain a composition that prevents carbonate, sulfate, iron oxide deposits on heat exchange surfaces and does not contain zinc compounds, classified as a sanitary-toxicological action.

Состав, содержащий оксиэтилендифосфоновую кислоту (ОЭДФ) и лигносульфонат натрия (ЛСТ), дополнительно содержит ингибитор коррозии натрия - полифосфат технический (НПФ) и диспергатор шлама - окись алкилдиметиламина (ОА) при следующем соотношении компонентов, мас.%:
ОЭДФ - 5 - 12
НПФ - 5 - 12
ЛСТ - 5 - 12
ОА - 8 - 16
Вода - Остальное
Оксиэтилидендифосфоновая кислота (ОЭДФ) предотвращает рост кристаллов нерастворимых солей в воде, натрия полифосфат технический (НПФ) предотвращает коррозию и солеотложения, окись алкилдиметиламина (ОА) и лигносульфонат натрия (ЛСТ) как поверхностно-активные вещества диспергируют мельчайшие кристаллы солей, предотвращая тем самым образование конгломератов, их слипание и нарастание на поверхности теплообменной аппаратуры.The composition containing oxyethylene diphosphonic acid (HEDP) and sodium lignosulfonate (LST), additionally contains sodium corrosion inhibitor - technical polyphosphate (NPF) and sludge dispersant - alkyldimethylamine oxide (OA) in the following ratio, wt.%:
OEDF - 5 - 12
NPF - 5 - 12
LST - 5 - 12
OA - 8 - 16
Water - Else
Hydroxyethylidene diphosphonic acid (HEDP) prevents the growth of crystals of insoluble salts in water, sodium polyphosphate technical (NPF) prevents corrosion and scaling, alkyldimethylamine oxide (OA) and sodium lignosulfonate (LST) as surface-active substances disperse the smallest crystals of conger salt, thereby , their adhesion and growth on the surface of heat exchange equipment.

Преимуществом этого состава является оптимальное соотношение компонентов, позволяющих получить устойчивую композицию, эффективно работающую при достаточно низких концентрациях и не содержащую цинк. The advantage of this composition is the optimal ratio of components that allows you to get a stable composition that works effectively at fairly low concentrations and does not contain zinc.

В качестве исходного сырья состава используется: 1-гидроксиэтилидендифосфоновая кислота ТУ 6-09-713-85; натрия полифосфат технический ГОСТ 20291-80; лигносульфонат натрия марки "А", ТУ 13-0281036-029-94 и окись алкилдиметиламина (водный раствор) ТУ 2413-016-13164401-95. As the starting material of the composition is used: 1-hydroxyethylidene diphosphonic acid TU 6-09-713-85; sodium polyphosphate technical GOST 20291-80; sodium lignosulfonate grade "A", TU 13-0281036-029-94 and alkyldimethylamine oxide (aqueous solution) TU 2413-016-13164401-95.

Практика эксплуатации состава показала, что наиболее оптимальной является композиция при следующем соотношении компонентов, мас.%:
ОЭДФ - 8
НПФ - 8
ОА - 9
ЛСТ - 8
Вода - 67
Изобретение позволяет эффективно проводить очистку и промывку теплообменного оборудования и в дальнейшем предотвратить образование солевых и железооксидных отложений на теплопередающих поверхностях и тем самым увеличить эффективность работы систем оборотного водоснабжения.The practice of operating the composition showed that the most optimal is the composition in the following ratio of components, wt.%:
OEDF - 8
NPF - 8
OA - 9
LST - 8
Water - 67
EFFECT: invention makes it possible to efficiently carry out cleaning and washing of heat-exchange equipment and in the future to prevent the formation of salt and iron oxide deposits on heat transfer surfaces and thereby increase the efficiency of circulating water supply systems.

Физико-химические показатели полученного состава приведены в таблице. Physico-chemical parameters of the obtained composition are given in the table.

Claims

Composition for inhibiting scaling, corrosion and washing equipment in water recycling systems, containing hydroxyethylidene diphosphonic acid (HEDP) and sodium lignosulfonate (LST), characterized in that it additionally contains a sodium corrosion inhibitor polyphosphate technical (NPF) and a sludge dispersant alkyldimethylamine oxide (OA) in the following ratio of components wt. %:
OEDF - 5-12
NPF - 5-12
LST - 5-12
OA - 8-16
Water - Else