RU2205898C2 - Solution for removing dross from steel surface - Google Patents

Solution for removing dross from steel surface Download PDF

Info

Publication number
RU2205898C2
RU2205898C2 RU2001119195/02A RU2001119195A RU2205898C2 RU 2205898 C2 RU2205898 C2 RU 2205898C2 RU 2001119195/02 A RU2001119195/02 A RU 2001119195/02A RU 2001119195 A RU2001119195 A RU 2001119195A RU 2205898 C2 RU2205898 C2 RU 2205898C2
Authority
RU
Russia
Prior art keywords
solution
scale
ethylene glycol
steel
etching
Prior art date
Application number
RU2001119195/02A
Other languages
Russian (ru)
Other versions
RU2001119195A (en
Inventor
Б.Е. Зайцев
А.И. Горичев
И.Г. Горичев
А.Д. Изотов
Е.Ю. Невска
Е.Ю. Невская
Original Assignee
Российский Университет Дружбы Народов
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Российский Университет Дружбы Народов filed Critical Российский Университет Дружбы Народов
Priority to RU2001119195/02A priority Critical patent/RU2205898C2/en
Publication of RU2001119195A publication Critical patent/RU2001119195A/en
Application granted granted Critical
Publication of RU2205898C2 publication Critical patent/RU2205898C2/en

Abstract

FIELD: chemical metal treatment. SUBSTANCE: water-based solution contains 24.0-8.0 wt % hydrogen chloride and 10.0-92.0 ethylene glycol. EFFECT: improved treatment quality and enabled treatment at high temperatures (up to 200 C). 2 ex

Description

Изобретение относится к химической обработке металлов, а именно к очистке поверхности стали от окалины. The invention relates to the chemical treatment of metals, namely to clean the surface of steel from scale.

В настоящее время исследователями для этих целей предлагаются составы, включающие в себя HF (патенты РФ 2072397, 2126460), обладающий повышенной коррозионной активностью, Н2О2 (патенты РФ 2110618, 2085616), источник свободных радикалов и вещество, обладающее окислительными свойствами, фосфатсодержащие компоненты (патент РФ 2162487), присутствие которых в сливных водах отрицательно сказывается на экологии водоемов, а также органические вещества (патент РФ 2061793), синтез которых требует значительных усилий.Currently, for these purposes, researchers are proposing compositions that include HF (RF patents 2072397, 2126460), which has increased corrosivity, H 2 O 2 (RF patents 2110618, 2085616), a source of free radicals and a substance with oxidizing properties, phosphate-containing components (RF patent 2162487), the presence of which in drainage waters adversely affects the ecology of water bodies, as well as organic substances (RF patent 2061793), the synthesis of which requires considerable effort.

Наиболее близким техническим решением является раствор для удаления окалины с поверхности стали, содержащий ацетон (авторское свидетельство СССР 1382875). Основным недостатком этого способа является нестабильность таких растворов во времени. В присутствии ионов Fe2+, Fe3+ в процессе травления происходит осмоление ацетона. Образующиеся полимерные продукты осаждаются на травящей поверхности, что препятствует дальнейшему избавлению от окалины. Другим важным недостатком является летучесть ацетона, препятствующая проведению процесса при высоких температурах, что ограничивает скорость травления.The closest technical solution is a solution for removing scale from the surface of steel containing acetone (USSR copyright certificate 1382875). The main disadvantage of this method is the instability of such solutions over time. In the presence of Fe 2+ and Fe 3+ ions , acetone is ground during etching. The resulting polymer products are deposited on the etching surface, which prevents further disposal of scale. Another important disadvantage is the volatility of acetone, which impedes the process at high temperatures, which limits the etching rate.

В основу изобретения поставлена задача создания раствора, позволяющего повысить качество очистки поверхности стали и проводить травление при более высоких температурах. The basis of the invention is the task of creating a solution that improves the quality of surface cleaning of steel and etching at higher temperatures.

Сущность изобретения заключается в том, что раствор для удаления окалины с поверхности стали содержит следующие компоненты, маc.%:
Хлороводород - 8,0-24,0
Этиленгликоль - 92,0-10,0
Вода - Остальное
В результате повышается качество очистки поверхности стали. Предлагаемый метод более технологичен, т.к. этиленгликоль имеет более высокую температуру кипения и позволяет проводить обработку стали при более высоких температурах (до ~200oС).
The essence of the invention lies in the fact that the solution for removing scale from the surface of the steel contains the following components, wt.%:
Hydrogen chloride - 8.0-24.0
Ethylene glycol - 92.0-10.0
Water - Else
As a result, the quality of steel surface cleaning is improved. The proposed method is more technological, because ethylene glycol has a higher boiling point and allows the processing of steel at higher temperatures (up to ~ 200 o C).

Состав травильного раствора железной окалины готовят смешиванием соляной кислоты I= 1130 кг/м3, этиленгликоля и воды или насыщением этиленгликоля хлороводородом при комнатной температуре до полного насыщения (появление паров HCL). Полученный насыщенный безводный раствор хлороводорода в этиленгликоле при необходимости разбавляют этиленгликолем, водой и соляной кислотой. Травление окалины с поверхности стальных образцов (сталь 20) проводилось в термостатированных стеклянных сосудах с обратным холодильником при Т= 295 К. Образец, представляющий собой полоску из стали 20, покрытую окалиной, подвешивался в сосуде на стеклянном крючке. Для снятия диффузионных затруднений растворение проводили при интенсивном перемешивании (500 <ω< 800 об/мин). В травильных растворах образцы с окалиной выдерживали до полного ее удаления. Момент полного стравливания окалины устанавливали визуально или по величине потенциала образца относительно хлорсеребряного электрода. Величина потенциала изменялась с положительных значений до (-0,2) - (-0,4) В. Коррозионные потери металла определялись взвешиванием на аналитических весах после промывания и высушивания образца. О степени наводораживания протравленных образцов судили по изменению их пластичности. Потери пластичности определяли на установке МП-1 и выражали числом перегибов на 180 градусов до полного разрушения образца. Контролем служили образцы, не подвергнутые травлению. Присутствие этиленгликоля в травильном растворе стимулирует процесс стравливания окалины с поверхности стальных образцов, способствует снижению наводораживания и коррозионных потерь металла под окалиной. Резкое уменьшение коррозионных потерь основного металла связано с сокращением времени удаления окалины. Растворы этиленгликоля и хлороводородной кислоты проявляют более низкую летучесть, что позволяет поднимать температуру травления до 200oС.The composition of the etching solution of iron oxide is prepared by mixing hydrochloric acid I = 1130 kg / m 3 , ethylene glycol and water, or by saturating the ethylene glycol with hydrogen chloride at room temperature until completely saturated (appearance of HCL vapors). The resulting saturated anhydrous solution of hydrogen chloride in ethylene glycol is, if necessary, diluted with ethylene glycol, water and hydrochloric acid. Etching of the scale from the surface of steel samples (steel 20) was carried out in temperature-controlled glass vessels with a reflux condenser at T = 295 K. The sample, which was a strip of steel 20 coated with scale, was suspended in a vessel on a glass hook. To remove diffusion difficulties, dissolution was carried out with vigorous stirring (500 <ω <800 rpm). In etching solutions, samples with scale were kept until it was completely removed. The moment of complete etching of the scale was established visually or by the magnitude of the potential of the sample relative to the silver chloride electrode. The potential value changed from positive values to (-0.2) - (-0.4) V. Corrosion losses of the metal were determined by weighing on an analytical balance after washing and drying the sample. The degree of hydrogenation of the etched samples was judged by the change in their ductility. Losses of ductility were determined on the MP-1 apparatus and expressed by the number of bends by 180 degrees until the complete destruction of the sample. The control was samples not subjected to etching. The presence of ethylene glycol in the etching solution stimulates the process of etching scale from the surface of steel samples, and helps to reduce the hydrogen disturbance and corrosion losses of the metal under the scale. A sharp decrease in corrosion losses of the base metal is associated with a reduction in the time of descaling. Solutions of ethylene glycol and hydrochloric acid exhibit lower volatility, which allows to raise the etching temperature to 200 o C.

ПРИМЕР 1. EXAMPLE 1

В раствор, содержащий хлороводород 8,0 мас.% и этиленгликоль 92,0 мас.%, опускали образцы стали 20 с окалиной и оставляли в растворе до полного удаления окалины. Через 3 минуты поверхность образца полностью очищалась. Поверхность протравленного образца стали после промывания и просушки гладкая без остатков окалины. Samples of steel 20 with scale were lowered into a solution containing 8.0 wt.% Hydrogen chloride and ethylene glycol 92.0 wt.% And left in solution until the scale was completely removed. After 3 minutes, the surface of the sample was completely cleaned. The surface of the pickled steel sample after washing and drying is smooth without residual scale.

ПРИМЕР 2. EXAMPLE 2

В раствор, содержащий хлороводород 24,0 мас.%, этиленгликоль 10,0 мас.% и воду 66,0 мас. %, опускали образцы стали 20 с окалиной и оставляли в растворе до полного удаления окалины. Через 8 минут поверхность образца полностью очищалась от окалины. После промывания образца и просушки его поверхность выглядела гладкой без остатков окалины. In a solution containing hydrogen chloride 24.0 wt.%, Ethylene glycol 10.0 wt.% And water 66.0 wt. %, samples of steel 20 with scale were lowered and left in solution until the scale was completely removed. After 8 minutes, the surface of the sample was completely cleaned of scale. After washing the sample and drying, its surface looked smooth without any residual scale.

Claims (1)

Раствор для удаления окалины с поверхности стали, содержащий хлороводород и воду, отличающийся тем, что раствор дополнительно содержит этиленгликоль при следующем соотношении компонентов, мас.%:
Хлороводород - 24,0-8,0
Этиленгликоль - 10,0-92,0
Вода - Остальноер
A solution for removing scale from the surface of a steel containing hydrogen chloride and water, characterized in that the solution additionally contains ethylene glycol in the following ratio, wt.%:
Hydrogen chloride - 24.0-8.0
Ethylene glycol - 10.0-92.0
Water - Rest
RU2001119195/02A 2001-07-12 2001-07-12 Solution for removing dross from steel surface RU2205898C2 (en)