RU2189999C2

RU2189999C2 - Water-diluting composition for bactericidal covers

Info

Publication number: RU2189999C2
Application number: RU98109097A
Authority: RU
Inventors: В.Г. Липович; Е.В. Лифанов; М.Е. Сарылова; Татьяна Владимировна Липович
Original assignee: Липович Владимир Григорьевич; Татьяна Владимировна Липович; Полянов Олег Мстиславович; Петроченко Александр Анатольевич
Priority date: 1998-05-14
Filing date: 1998-05-14
Publication date: 2002-09-27

Abstract

FIELD: paint and varnish industry. SUBSTANCE: invention relates to preparing a bactericidal cover that involves the use a bactericidal component on the base, for example, water-emulsion dyes, water glass or slaked lime. Invention relates to a water-diluting composition for bactericidal covers of articles made of ceramics, concrete, brick, stucco and other materials in air medium comprising a water-diluting dye and derivatives of polyhexamethyleneguanidine as a bactericidal component. A water-diluting composition comprises derivatives of polyhexamethyleneguanidine as a bactericidal component of the general formula:

Description

Изобретение относится к химической отрасли, в частности к составам, обладающим бактерицидными свойствами, используемым для предотвращения биообрастания различных материалов в среде, а также в качестве бактерицидного, вирулицидного, фунгицидного и спороцидного покрытия для промышленных, складских, общественных, медицинских, жилых помещений и зданий, в сельском хозяйстве и различных отраслях пищевой промышленности. The invention relates to the chemical industry, in particular to compositions having bactericidal properties used to prevent biofouling of various materials in the environment, as well as bactericidal, virucidal, fungicidal and sporicidal coatings for industrial, warehouse, public, medical, residential premises and buildings, in agriculture and various sectors of the food industry.

Известен водоразбавляемый состав введением бактерицидной добавки в краску на основе ПВА, где в качестве бактерицидной добавки используют смесь 5-50% цинковой соли N-окиси 2-меркаптопиридина и 95-50% бромсалициланилида [патент Франции 2114127, кл. МПК С 09 D 5/00, С 08 F 45/00, опубл. 30.06.1972]. A water-borne formulation is known by introducing a bactericidal additive into a PVA-based paint, where a mixture of 5-50% zinc salt of 2-mercaptopopyridine N-oxide and 95-50% bromosalicylanilide is used as a bactericidal additive [French patent 2114127, cl. IPC C 09 D 5/00, C 08 F 45/00, publ. 06/30/1972].

Указанная добавка далеко небезопасна для окружающей среды и неактивна по отношению ко многим микроорганизмам (например, к вирусам). The specified additive is far unsafe for the environment and inactive against many microorganisms (for example, viruses).

Известен также водоразбавляемый состав для бактерицидных покрытий, где в качестве антисептического компонента в краски вводят бензилбромацетат в количестве 0,025-1% [патент США 3896136, кл. МПК С 08 F 45/24, опубл. 22.07.1975]. Also known is a water-borne composition for bactericidal coatings, where benzyl bromoacetate is added to the paint as an antiseptic component in an amount of 0.025-1% [US patent 3896136, cl. IPC C 08 F 45/24, publ. 07/22/1975].

Недостатком этого известного состава является неустойчивость биоцидных свойств во времени, высокая токсичность биоцида и узкий круг его бактерицидной активности (только фунгицидное действие). The disadvantage of this known composition is the instability of the biocidal properties over time, the high toxicity of the biocide and the narrow circle of its bactericidal activity (only fungicidal effect).

Наиболее близкими из известных являются водоразбавляемые краски, где в качестве антисептических, бактерицидных и фунгицидных добавок используют смесь (тиоцианометилтио)бензтиазола и 1,2-бензизотиазолин-3-она при соотношении 1: 0,3-3 соответственно [заявка Японии 56-71009, кл. МПК А 01 N 43/80, опубл. 13.06.1981]. The closest known ones are water-borne paints, where a mixture of (thiocyanomethylthio) benzthiazole and 1,2-benzisothiazolin-3-one is used as antiseptic, bactericidal and fungicidal additives at a ratio of 1: 0.3-3, respectively [Japanese application 56-71009, class IPC A 01 N 43/80, publ. 06/13/1981].

Указанный состав не обладает вирулицидными и спороцидными свойствами и, кроме того, далеко небезопасен для окружающей среды. The specified composition does not have virucidal and sporocidal properties and, in addition, is far unsafe for the environment.

Технической задачей изобретения является создание водоразбавляемого состава с устойчивыми бактерицидными свойствами, обладающего широким спектром биоцидных свойств, и, кроме того, безопасного для человека. An object of the invention is the creation of a water-borne composition with stable bactericidal properties, with a wide range of biocidal properties, and, in addition, safe for humans.

Это достигается тем, что в состав водоразбавляемых красок дополнительно вводят бактерицидный компонент, представляющий собой производные полигексаметиленгуанидина (далее по тексту - ПГМГ) общей формулы:

где R - основание, хлорид, фосфат,
n - 2-60, при следующем соотношении компонентов, маc.ч.:
Производные ПГМГ - 0,5-9
Водоразбавляемая краска - 91-99,5
В качестве производного ПГМГ используют его основание, хлорид или фосфат.This is achieved by the fact that a bactericidal component, which is a derivative of polyhexamethylene guanidine (hereinafter referred to as PGMG) of the general formula, is additionally introduced into the composition of water-borne paints:

where R is the base, chloride, phosphate,
n - 2-60, in the following ratio of components, wt.h .:
Derivatives of PHMG - 0.5-9
Water-borne paint - 91-99.5
As a derivative of PHMG, its base, chloride or phosphate is used.

В качестве водоразбавляемой краски используют известь, водоэмульсионную краску, краску на основе жидкого стекла или гашеную известь. As a water-borne paint, lime, water-based paint, liquid glass paint or slaked lime are used.

Состав и свойства предлагаемых красок приведены в таблице 1. По примерам 1-4 используют водоэмульсионную краску, имеющую акриловую или поливинилацетатную основу по ГОСТ 28196-89. The composition and properties of the proposed paints are shown in table 1. In examples 1-4 use a water-based paint having an acrylic or polyvinyl acetate base in accordance with GOST 28196-89.

В примерах 6-10 используют известь гашеную по ГОСТ 9262-77. In examples 6-10 use slaked lime according to GOST 9262-77.

В примере 5 - жидкое стекло по ГОСТ 13-078-81. In example 5, liquid glass according to GOST 13-078-81.

Применяемые производные ПГМГ выпускаются в промышленности, например, марка "метацид" - по ТУ 10-09-41-90, марка "фогуцид" - по ТУ 4392-001-49362022-99. Производные ПГМГ вводят в водоразбавляемую краску в виде 0,3-30% водного эмульсионного раствора. Полученный водоразбавляемый состав затем наносят обычным способом на поверхность изделий из керамики, бетона, кирпича, штукатурки и других материалов кистью, валиком, напылением или поливом, а затем сушат. The used PGMG derivatives are produced in industry, for example, the metacid brand according to TU 10-09-41-90, the Fogucid brand according to TU 4392-001-49362022-99. Derivatives of PHMG are introduced into a water-borne paint in the form of a 0.3-30% aqueous emulsion solution. The resulting water-borne composition is then applied in the usual manner on the surface of ceramic, concrete, brick, plaster and other materials by brush, roller, spraying or watering, and then dried.

Изучение биоцидных свойств предлагаемых составов в воздушной среде проводят при контакте образцов с крупнодисперсными бактериальными аэрозолями (частицы - 10 мк. ) в аэрозольных камерах (методика НИИЭЧ и ГОС им. А.Н. Сысина РАМН - 1996 г.). В качестве биотестов используют бактерии (Е. Coli), вирусы (колифаг MS - 2), плесневые грибы (Penicillium ehrysogtnum), споры (Вас. cereus). The study of the biocidal properties of the proposed compounds in the air is carried out by contact of the samples with coarse-grained bacterial aerosols (particles - 10 microns) in aerosol chambers (methodology of the Scientific Research Institute of Electrochemical Physics and the SOSIN RAMS RAMS - 1996). Bacteria (E. Coli), viruses (Colophagus MS-2), mold fungi (Penicillium ehrysogtnum), spores (Vas. Cereus) are used as biotests.

Эксперименты с образцами покрытий на указанных выше керамических материалах показывают, что бактерицидные свойства покрытий сохраняются в течение 1 года. Experiments with coating samples on the above ceramic materials show that the bactericidal properties of the coatings are maintained for 1 year.

Результаты проведенных испытаний бактерицидных свойств разработанного состава приведены в таблицах 2 и 3. The results of the tests of the bactericidal properties of the developed composition are shown in tables 2 and 3.

Как видно из данных таблиц, предлагаемый состав уже при низких содержаниях производных ПГМГ обладает устойчивыми биоцидными свойствами, как минимум, в течение 1 года. As can be seen from these tables, the proposed composition already at low concentrations of derivatives of PHMG has stable biocidal properties for at least 1 year.

Предлагаемый состав может быть использован при решении многих экологических проблем (борьба с грибковым поражением конструкций, уничтожение болезнетворных микроорганизмов на поверхности стен, очистка воздуха от микробного загрязнения в медицинских, жилых, складских и др. помещений). The proposed composition can be used to solve many environmental problems (the fight against fungal damage to structures, the destruction of pathogens on the surface of the walls, air purification from microbial contamination in medical, residential, warehouse and other premises).

При этом предлагаемый состав обладает широким спектром действия, проявляя биоцидное, фунгицидное, бактерицидное, вирулицидное и спороцидное действие (см. таблицу 3). Moreover, the proposed composition has a wide spectrum of action, exhibiting biocidal, fungicidal, bactericidal, virucidal and sporocidal action (see table 3).

Предлагаемые водоразбавляемые составы промышленно применимы, их получение предусматривает применение исходных продуктов, производимых в промышленности, и стандартного оборудования. The proposed water-borne formulations are industrially applicable; their preparation involves the use of starting products manufactured in industry and standard equipment.

Claims

A water-borne composition for bactericidal coatings of ceramics, concrete, brick, plaster and other materials in air, including a water-borne paint and a bactericidal component - derivatives of polyhexamethylene guanidine, characterized in that the water-borne composition contains polyhexamethylene guanidine derivatives of the general formula

where R is the base, chloride, phosphate;
n is 2-60,
in the following ratio of components, wt. hours:
Polyhexamethylene guanidine derivatives - 0.5 - 9
Water-borne paint - 91 - 99.5