RU2179986C2 - Composition (variants) - Google Patents
Composition (variants) Download PDFInfo
- Publication number
- RU2179986C2 RU2179986C2 RU99125753A RU99125753A RU2179986C2 RU 2179986 C2 RU2179986 C2 RU 2179986C2 RU 99125753 A RU99125753 A RU 99125753A RU 99125753 A RU99125753 A RU 99125753A RU 2179986 C2 RU2179986 C2 RU 2179986C2
- Authority
- RU
- Russia
- Prior art keywords
- bitumen
- composition
- hardener
- filler
- plasticizer
- Prior art date
Abstract
Description
Изобретение относится к битуминозным составам для производства кровельных и гидроизоляционных материалов, может быть использовано для гидроизоляции строительных конструкций и герметизации швов в автодорожном строительстве. The invention relates to bituminous compositions for the production of roofing and waterproofing materials, can be used for waterproofing building structures and sealing joints in road construction.
Известны композиции [1-3] для гидроизоляции на основе битумов, содержащие полимерные добавки - эластомеры, наполнители, обеспечивающие хорошие физико-механические характеристики, однако эти композиции имеют слабую стойкость к тепловому старению, узкий температурный диапазон эксплуатации, что сокращает эксплуатационные сроки материалов на их основе. Тепловое старение известных композиций вызвано, в основном, испарением из битума его легких фракций, особенно при повышении температуры окружающей среды, что делает битум хрупким, не отвечающим требованиям по деформативности, в частности эластичности, водостойкости. Неширокий температурный диапазон ограничивается плюсовыми температурами, когда композиция размягчается и становится текучей, а также минусовыми температурами, когда композиция становится хрупкой и не отвечает своему назначению, появляются микротрещины, пропускающие воду. Так, гидроизоляционное вяжущее [3], используемое для устройства кровель, герметизации стыков в дорожном строительстве, содержит битум, высокомолекулярный бутилкаучук, пентахлорфенол, олигомер бутилкаучука и наполнитель. Known compositions [1-3] for bitumen-based waterproofing containing polymer additives - elastomers, fillers, providing good physical and mechanical characteristics, however, these compositions have poor resistance to thermal aging, a narrow temperature range of operation, which reduces the operational life of materials on them basis. The thermal aging of the known compositions is mainly caused by the evaporation of its light fractions from bitumen, especially with increasing ambient temperature, which makes the bitumen brittle, not meeting the requirements for deformability, in particular elasticity, water resistance. The non-wide temperature range is limited by plus temperatures, when the composition softens and becomes fluid, as well as minus temperatures, when the composition becomes brittle and does not meet its intended purpose, microcracks appear that allow water to pass through. Thus, a waterproofing binder [3] used for roofing, sealing joints in road construction, contains bitumen, high molecular weight butyl rubber, pentachlorophenol, butyl rubber oligomer and filler.
Стойкость к тепловому старению материалов, их температурный диапазон эксплуатации характеризуют такие показатели, как температура размягчения, пенетрация, температура хрупкости, водопоглощение. Указанные характеристики в этом решении несколько улучшены за счет использования в гидроизоляционном вяжущем в качестве полимерной добавки олигомеров бутилкаучука [3], однако для резкоконтинентального климата с большим разбросом температур рабочий температурный диапазон вяжущего недостаточен. Другим недостатком известного вяжущего является сложность его приготовления, использование мощного, энергоемкого смесителя, необходимого для перемешивания вязкого бутилкаучука. Resistance to thermal aging of materials, their temperature range of operation is characterized by such indicators as softening temperature, penetration, brittleness temperature, water absorption. The indicated characteristics in this solution are somewhat improved due to the use of butyl rubber oligomers in the waterproofing binder as a polymer additive [3], however, for a sharply continental climate with a large temperature dispersion, the working temperature range of the binder is insufficient. Another disadvantage of the known binder is the complexity of its preparation, the use of a powerful, energy-intensive mixer, necessary for mixing viscous butyl rubber.
Наиболее близким аналогом является жидкая мастика - "битизол-1" по a.c. 382658 для гидроизоляционных работ [4], содержащая битум и наполнители при следующем соотношении компонентов, в вес. ч.:
Жидкий тиокол - 80-100
Эпоксидная смола - 4-6
Разжижитель - 15-25
Вулканизатор - 20-34
Битум - 24-40
Белая сажа - 10-15
Тальк - 18-22
Жидкая мастика после улетучивания растворителя образует однородную структурированную тонкую пленку, отличающуюся при различной температуре высокими показателями эластичности, прочности, трещиностойкости, воздухо- и паронепроницаемости, стойкости к ультрафиолетовому облучению и воздействию высококонцентрированных агрессивных сред.The closest analogue is liquid mastic - “bitizol-1” according to ac 382658 for waterproofing works [4], containing bitumen and fillers in the following ratio of components, in weight. hours:
Liquid thiokol - 80-100
Epoxy Resin - 4-6
Thinner - 15-25
Vulcanizer - 20-34
Bitumen - 24-40
White soot - 10-15
Talc - 18-22
Liquid solvent after volatilization of the solvent forms a homogeneous structured thin film, characterized at different temperatures by high indicators of elasticity, strength, crack resistance, air and vapor impermeability, resistance to ultraviolet radiation and exposure to highly concentrated aggressive media.
Основу мастики составляет тиокол, свойства которого и определяют свойства мастики. Во-первых, мастика - это жидкое вещество, которое наносится на обрабатываемую поверхность тонким слоем, при высыхании образующем пленку. При увеличении толщины покрытия мастики она пузырится, в результате чего ухудшаются характеристики покрытия (адгезия, водостойкость); при этом есть необходимость использовать мастику для заделки достаточно глубоких швов, поэтому мастика в этом случае неприменима. Многослойное нанесение мастики для увеличения толщины повышает трудоемкость ее использования, время обработки, при этом толщина все же остается небольшой. Кроме того, высокое содержание тиокола резко увеличивает стоимость такой мастики, что также ограничивает ее применение. The basis of mastic is thiocol, whose properties determine the properties of mastic. Firstly, mastic is a liquid substance that is applied to the surface to be treated with a thin layer, forming a film when dried. With an increase in the thickness of the coating of the mastic, it bubbles, as a result of which the characteristics of the coating deteriorate (adhesion, water resistance); at the same time, there is a need to use mastic to seal deep enough seams, so mastic is not applicable in this case. Multilayer application of mastic to increase the thickness increases the complexity of its use, processing time, while the thickness still remains small. In addition, the high content of thiocol sharply increases the cost of such a mastic, which also limits its use.
Задачей изобретения является расширение области применения композиции, улучшение характеристик покрытия, в частности адгезии, водостойкости, удешевление композиции. The objective of the invention is to expand the scope of the composition, improving the characteristics of the coating, in particular adhesion, water resistance, cheapening the composition.
Указанные задачи решаются в битумсодержащей композиции, включающей битум (его различные модификации, например, БН-70/30) с полисульфидным олигомером - тиоколом, отвердителем, пластификатором, наполнителем, в которой соотношение компонентов следующее, мас.%:
Битум - 46,14-85,0
Тиокол - 4,744-33,33
Отвердитель - 0,4-2,48
Пластификатор - 0,322-1,91
Наполнитель - 4,53-31,67
Указанные задачи решаются также в битумсодержащей композиции, включающей битум, полисульфидный олигомер, отвердитель, пластификатор, наполнитель, в которой в качестве полисульфидного олигомера используют ТПМ-2-полимер, при следующем соотношении компонентов, мас.%:
Битум - 46,14-85,0
ТПМ-2-полимер - 4,744-33,33
Отвердитель - 0,4-2,48
Пластификатор - 0,322-1,91
Наполнитель - 4,53-31,67
Полисульфидный олигомер должен отвечать ряду требований, а именно он должен быть веществом гибкоцепным, насыщенным, водостойким, растворимым в битуме, т.е. совместимым с битумами, быть способным создавать с ним гомогенную однородную структуру.These tasks are solved in a bitumen-containing composition, including bitumen (its various modifications, for example, BN-70/30) with a polysulfide oligomer — thiocol, hardener, plasticizer, filler, in which the ratio of components is as follows, wt.%:
Bitumen - 46.14-85.0
Thiokol - 4,744-33,33
Hardener - 0.4-2.48
Plasticizer - 0.322-1.91
Filler - 4.53-31.67
These problems are also solved in a bitumen-containing composition, including bitumen, polysulfide oligomer, hardener, plasticizer, filler, in which TPM-2 polymer is used as a polysulfide oligomer, in the following ratio, wt.%:
Bitumen - 46.14-85.0
TPM-2 polymer - 4.744-33.33
Hardener - 0.4-2.48
Plasticizer - 0.322-1.91
Filler - 4.53-31.67
The polysulfide oligomer must meet a number of requirements, namely, it must be a flexible chain substance, saturated, waterproof, soluble in bitumen, i.e. compatible with bitumen, be able to create a homogeneous homogeneous structure with it.
Водостойкость полисульфидного олигомера должна быть ограничена не менее 1% набухания в воде от общего объема добавки в течение 24 часов. Этим условиям отвечают тиокол, ТПМ-2-полимер и некоторые вещества из группы полисульфидных олигомеров. The water resistance of the polysulfide oligomer should be limited to at least 1% of the swelling in water of the total additive for 24 hours. Thiocol, TPM-2 polymer, and some substances from the group of polysulfide oligomers meet these conditions.
ТПМ-2-полимер известен, например, из статьи А.А.Идиятовой, Ю.Н.Хакимуллина, С.И.Вольфсона, С.А.Лиакумовича "Регулирование вязкостных и тиксотропных свойств герметиков на основе полисульфидных олигомеров". Журнал прикладной химии, 1999 г. , т. 72, вып. 5, стр. 849-852, подписано в печать 23.04.99 [5] и соответствует требованиям ТУ 38.103636-87 [6], имеет структурную формулу:
где N=20-24, и следующие характеристики
Массовая доля SH групп, % - 1,7-2,7
Динамическая вязкость при 25oС, Па•С - 1,0-4,0
Массовая доля Н20, %, не более - 0,4
Жизнеспособность, ч - 4-36
Условная прочность в момент разрыва, МПа - 0,3-1,0
Относительное удлинение в момент разрыва %, - не менее 350
В качестве отвердителя (вулканизатора) может быть использован сшивающий агент-окислитель, например оксиды, диоксиды металлов (диоксид марганца, окись цинка, бихромат натрия); в качестве пластификатора - пластификатор полярного типа, например дибутилфталат, стеариновая кислота и т.п.TPM-2 polymer is known, for example, from an article by A. A. Idiyatova, Yu. N. Khakimullin, S. I. Wolfson, S. A. Liakumovich "Regulation of the viscosity and thixotropic properties of sealants based on polysulfide oligomers". Journal of Applied Chemistry, 1999, v. 72, no. 5, p. 849-852, signed on April 23, 1999 [5] and meets the requirements of TU 38.103636-87 [6], has the structural formula:
where N = 20-24, and the following characteristics
Mass fraction of SH groups,% - 1.7-2.7
Dynamic viscosity at 25 o С, Pa • С - 1.0-4.0
Mass fraction of
Vitality, h - 4-36
Conditional strength at the time of rupture, MPa - 0.3-1.0
Elongation at break%, - not less than 350
As a hardener (vulcanizer), a crosslinking agent-oxidizing agent, for example, oxides, metal dioxides (manganese dioxide, zinc oxide, sodium dichromate) can be used; as a plasticizer, a polar type plasticizer, for example dibutyl phthalate, stearic acid, etc.
В состав отверждающей пасты может быть введен ускоритель вулканизации, например дифенилгуанидин, однако в ряде рецептур композиции, например, в случае применения композиции для дорожных покрытий, он не нужен. A vulcanization accelerator, for example diphenylguanidine, can be introduced into the composition of the curing paste, however, in a number of formulations of the composition, for example, in the case of using the composition for paving, it is not needed.
Жидкая полимерная добавка с отвердителем (вулканизатором), формируя устойчивую эластичную структуру в виде каркасной трехмерной сетки с молекулами битума, с распределенным отвердителем в полимерной добавке, препятствует расслоению композиции, делает композицию высокоэластичным материалом, стойким к термоокислительному старению, связывает молекулы битума, предотвращая испарение его легких фракций, эластифицируя его, сообщает композиции повышенную температуру размягчения, стойкость к деструкции при низких температурах, имеющей низкую температуру хрупкости, тем самым обеспечивает широкий рабочий температурный диапазон, высокую стабильность эксплуатационных свойств, большую долговечность службы гидроизоляционных материалов на основе композиции; расширяется область применения композиции, например, ее можно использовать для нанесения толстым слоем в широкие и глубокие швы дорожных покрытий, при этом сохраняются высокие характеристики по адгезии и водостойкости. По сравнению с прототипом стоимость композиции уменьшается за счет меньшего (примерно в три раза) содержания более дорогого тиокола. Получаемая композиция может наноситься любой толщиной, не ухудшая физико-механических свойств заделываемого шва. A liquid polymer additive with a hardener (vulcanizer), forming a stable elastic structure in the form of a three-dimensional wire mesh with bitumen molecules, with a distributed hardener in a polymer additive, prevents the composition from stratifying, makes the composition highly elastic material resistant to thermal oxidative aging, binds the bitumen molecules, preventing its evaporation light fractions, elasticizing it, gives the composition an increased softening temperature, resistance to degradation at low temperatures, which has a low low brittleness temperature, thereby ensuring a wide operating temperature range, high stability of operational properties, long service life of waterproofing materials based on the composition; the field of application of the composition is expanding, for example, it can be used for applying a thick layer in wide and deep seams of road surfaces, while maintaining high characteristics of adhesion and water resistance. Compared with the prototype, the cost of the composition is reduced due to the lower (about three times) content of a more expensive thiol. The resulting composition can be applied in any thickness, without compromising the physical and mechanical properties of the weld being closed.
В таблице 1 приведены составы композиции и разные качественные и количественные составы компонентов предлагаемой композиции и одного из аналогов, в таблице 2 - свойства композиции в зависимости от ее состава и свойства одного из аналогов. Table 1 shows the composition of the composition and various qualitative and quantitative compositions of the components of the proposed composition and one of the analogues, table 2 shows the properties of the composition depending on its composition and the properties of one of the analogues.
Способ получения композиции осуществляется следующим образом. A method of obtaining a composition is as follows.
В нагретый до 140-150oС битум вводится отвердитель, например двуокись марганца, и равномерно распределяется в битуме с помощью лопастного смесителя. В смесь может быть добавлен ускоритель вулканизации. Затем в полученную смесь вводится тиокол либо ТПМ-2-полимер и перемешивается до образования гомогенной массы в течение 15-30 минут при температуре 140oС. При этом состав композиции подобран таким образом, что введение вулканизатора не приведет к увеличению вязкости композиции непосредственно в процессе ее приготовления, что делает его технологичным. Наполнитель вводится либо в тиокол (ТПМ-2-полимер), либо непосредственно в битум. Пластификатор может быть введен непосредственно в битум перед отвердителем, либо смешан с отвердителем. При применении композиции в качестве покровного слоя рулонных материалов из смесителя готовая масса самотеком поступает в покровную ванну агрегата, где производят нанесение покровных слоев на основу. Готовый материал пропускают через зону холодильных цилиндров, магазин запаса готовой продукции и наматывают в рулоны. В случае модификации битумов гидроизоляционного назначения битумполимерную композицию используют в виде мастики.A hardener, for example manganese dioxide, is introduced into bitumen heated to 140-150 o С and is evenly distributed in bitumen using a paddle mixer. A vulcanization accelerator may be added to the mixture. Then, thiocol or TPM-2 polymer is introduced into the resulting mixture and mixed until a homogeneous mass is formed for 15-30 minutes at a temperature of 140 o C. The composition of the composition is selected so that the introduction of a vulcanizer will not increase the viscosity of the composition directly in the process its preparation, which makes it technological. The filler is introduced either into the thiocol (TPM-2 polymer), or directly into bitumen. The plasticizer can be introduced directly into the bitumen in front of the hardener, or mixed with a hardener. When using the composition as a coating layer of roll materials from the mixer, the finished mass flows by gravity into the coating bath of the unit, where coating layers are applied to the substrate. Finished material is passed through the zone of refrigeration cylinders, a store of stock of finished products and wound into rolls. In the case of modification of bitumen waterproofing purpose bitumen-polymer composition is used in the form of mastic.
Предлагаемая композиция в отличие от прототипа может использоваться для заделки широких и глубоких швов и трещин дорожного, аэродромного покрытия, т. е. имеет расширенный диапазон применения, при этом свойства композиции, такие как адгезия и водостойкость, имеют лучшие значения. Как показывают исследования, водопоглощение, характеризующее водостойкость, в предлагаемой композиции составляет от 0,049 до 0,12%, в то время как при нанесении мастики-прототипа слоем более 2 мм водопоглощение будет составлять не менее 2-3%. Снижение стоимости композиции по сравнению с прототипом обусловлено более низким процентным содержанием дорогого тиокола. В пересчете на мас.% содержание тиокола в прототипе составляет 43,4%, в то время как в предлагаемой композиции - в среднем 14,3%, что в три раза меньше. В пересчете на потребное количество композиции для ремонта дорожного покрытия выигрыш в стоимости будет существенным. The proposed composition, unlike the prototype, can be used to seal wide and deep seams and cracks in road and airfield coatings, that is, it has an extended range of applications, while the properties of the composition, such as adhesion and water resistance, have better values. Studies show that the water absorption characterizing the water resistance in the proposed composition is from 0.049 to 0.12%, while when applying the prototype mastic with a layer of more than 2 mm, the water absorption will be at least 2-3%. The decrease in the cost of the composition compared to the prototype is due to the lower percentage of expensive thiol. In terms of wt.% The content of thiol in the prototype is 43.4%, while in the proposed composition - on average 14.3%, which is three times less. In terms of the required amount of composition for repairing the road surface, the gain in cost will be substantial.
Источники информации
1. Авторское свидетельство 383724, С 08 L 95/11, 11.02.71.Sources of information
1. Copyright certificate 383724, C 08 L 95/11, 11.02.71.
2. Авторское свидетельство 398586, С 08 L 95/11, 27.03.72. 2. Copyright certificate 398586, C 08 L 95/11, 03/27/72.
3. Авторское свидетельство 761527, С 08 L 95/00, 07.09.90. 3. Copyright certificate 761527, C 08 L 95/00, 09/07/90.
4. Авторское свидетельство 382658, C 08 H 13/00, опубликовано 23.05.73, бюлл. 23 прототип. 4. Copyright certificate 382658, C 08 H 13/00, published May 23, 73, bull. 23 prototype.
5. А.А.Идиятова, Ю.Н.Хакимуллин, С.И.Вольфсон, С.А.Лиакумович "Регулирование вязкостных и тиксотропных свойств герметиков на основе полисульфидных олигомеров". Журнал прикладной химии, 1999 г., т. 72, вып. 5, стр. 849-852, подписано в печать 23.04.99. 5. A.A. Idiyatova, Yu.N. Khakimullin, S.I. Wolfson, S.A. Liakumovich "Regulation of the viscosity and thixotropic properties of sealants based on polysulfide oligomers". Journal of Applied Chemistry, 1999, v. 72, no. 5, pp. 849-852, signed on April 23, 1999.
6. ТУ 38.103636-87. 6. TU 38.103636-87.
Claims (8)
Битум - 46,14-85,0
Полисульфидный олигомер - тиокол - 4,744-33,33
Отвердитель из группы окислителей - 0,40-2,48
Пластификатор полярного типа - 0,322-1,91
Наполнитель - 4,53-31,67
2. Битумполимерная композиция по п. 1, отличающаяся тем, что в качестве отвердителя используют окислы металлов.1. Bitumen-polymer composition comprising bitumen, polysulfide oligomer — thiocol, hardener from the group of oxidizing agents, polar type plasticizer, filler, characterized in that the components of the composition are used in the following ratio of components, wt. %:
Bitumen - 46.14-85.0
Polysulfide oligomer - thiocol - 4,744-33,33
Hardener from the group of oxidizing agents - 0.40-2.48
Plasticizer of the polar type - 0.322-1.91
Filler - 4.53-31.67
2. The bitumen polymer composition according to claim 1, characterized in that metal oxides are used as a hardener.
Битум - 46,14-85,0
ТПМ-2 - 4,744-33,33
Отвердитель из группы окислителей - 0,40-2,48
Пластификатор полярного типа - 0,322-1,91
Наполнитель - 4,53-31,67
7. Битумполимерная композиция по п. 6, отличающаяся тем, что в качестве отвердителя используют окислы металлов.6. Bitumen-polymer composition comprising bitumen, a thiol-containing oligomer, a hardener from the group of oxidizing agents, a polar type plasticizer, a filler, characterized in that it contains a thiol-containing oligomer TPM-2 as a thiol-containing oligomer, and the composition components are used in the following ratio of components, wt. %:
Bitumen - 46.14-85.0
TPM-2 - 4.744-33.33
Hardener from the group of oxidizing agents - 0.40-2.48
Plasticizer of the polar type - 0.322-1.91
Filler - 4.53-31.67
7. Bitumen polymer composition according to claim 6, characterized in that metal oxides are used as a hardener.