Abstract

FIELD: external appearance of glass bottles, cans with paper or bright metallized labels and aluminum foil. SUBSTANCE: invention makes it possible to prepare adhesive composition with stable properties up to 180 days or longer. Effect is attained due to using adhesive based on 16-24 wt % of casein, 8-15 wt % of urea, 3-5 wt % of borax, 0.26-0.4 wt % of n-butyl alcohol and 0.06-0.3 wt % of zinc stearate and 3.8-5 wt % of oxidized potato or oxidized corn starch as viscosity modifier. EFFECT: improved properties of the adhesive starch.

Description

Изобретение относится к водорастворимым клеям на основе казеина. Основное применение: для наклеивания бумажных, металлизированных этикеток, алюминиевой фольги к стеклянной, металлической таре, может применяться на эффективных скоростных автоматах в процессе розлива вино-водочных изделий и безалкогольных прохладительных напитков в пищевой промышленности. The invention relates to casein-based water-soluble adhesives. The main application: for gluing paper, metallized labels, aluminum foil to glass, metal containers, can be used on efficient high-speed machines in the process of bottling wine and vodka products and soft drinks in the food industry.

Целью изобретения является повышение стабильности клея и эффективности склеивания в более сложных случаях. The aim of the invention is to increase the stability of the adhesive and the bonding efficiency in more complex cases.

Известно достаточно много водорастворимых клеев на основе казеина, предназначенных для этикетирования. Основными недостатками известных клеев является возрастание вязкости клея в условиях хранения и эксплуатации при температуре ниже 291 К, что усложняет обслуживание оборудования, а также зависимость свойств клея от качества казеина. Последний эффект способствует увеличению продолжительности процесса изготовления клея, что приводит к дополнительным энергетическим и другим производственным затратам (см. Клеи водорастворимые для пищевой промышленности.- Пищевая промышленность, N 11, 1995, c. 20; Cпособ изготовления казеиновых клеев для этикетирования металлизированных и жирных сосудов. А. c. ЧССР N 268047, кл. C 09 J 3/24, 1990). Quite a few water-soluble casein-based adhesives for labeling are known. The main disadvantages of the known adhesives are an increase in the viscosity of the adhesive during storage and use at temperatures below 291 K, which complicates the maintenance of the equipment, as well as the dependence of the properties of the adhesive on the quality of casein. The latter effect helps to increase the duration of the glue manufacturing process, which leads to additional energy and other production costs (see Water-soluble adhesives for the food industry. - Food industry, N 11, 1995, p. 20; Method for the manufacture of casein adhesives for labeling metallized and greasy vessels A. A. c. Czechoslovakia N 268047, class C 09 J 3/24, 1990).

В качестве прототипа наиболее близким к предлагаемому изобретению является состав, свойства которого в меньшей степени зависят от качества казеина за счет введения в рецептуру клея небольшого количества окиси цинка в качестве структурирующей добавки (см. Клей казеиновый и способ получения. Патент Польши N 157390, кл. C 09 J 189/00, 1992). Способ получения казеинового клея, описанного в прототипе, заключается в последовательной гомогенизации смеси 44-46 вес. % воды, 2,4-4,8 вес.% картофельной муки, 8-15 вес.% мочевины, 2,5-5 вес.% буры, 0,2-0,4 вес.% консерванта, 0,2-0,4 вес.% н-бутилового спирта, 16-24 вес.% казеина, и при достижении температуры 323 K следует дозировка окиси цинка в количестве 0,04-0,2 вес.%, выдержка смеси при температуре, не превышающей 345 K. As a prototype, the closest to the present invention is a composition whose properties are less dependent on the quality of casein due to the introduction of a small amount of zinc oxide into the adhesive formulation as a structuring additive (see Casein adhesive and preparation method. Polish Patent No. 157390, cl. C 09 J 189/00, 1992). The method of obtaining casein glue described in the prototype, consists in sequential homogenization of a mixture of 44-46 weight. % water, 2.4-4.8 wt.% potato flour, 8-15 wt.% urea, 2.5-5 wt.% borax, 0.2-0.4 wt.% preservative, 0.2- 0.4 wt.% N-butyl alcohol, 16-24 wt.% Casein, and when a temperature of 323 K is reached, a dosage of zinc oxide in the amount of 0.04-0.2 wt.%, The mixture is kept at a temperature not exceeding 345 K.

Основными недостатками клея, описанного в прототипе, является отсутствие в рецептуре пеногасителя, доступных активных наполнителей, а также относительно узкая область применения. The main disadvantages of the adhesive described in the prototype is the lack of antifoam in the formulation, available active fillers, as well as the relatively narrow scope.

Целью изобретения является повышение стабильности клея и эффективности наклеивания бумажных, металлизированных этикеток, алюминиевой фольги к стеклянной, металлической таре на скоростном автомате. The aim of the invention is to increase the stability of the adhesive and the efficiency of gluing paper, metallized labels, aluminum foil to glass, metal containers on a speed machine.

Предлагаемый способ получения клея на основе казеина и активных наполнителей в виде окисленного картофельного крахмала или окисленного кукурузного крахмала позволяет исключить пенообразование и получить композицию, отличающуюся стабильными свойствами в процессе хранения при температуре ниже 291 К за счет введения в состав небольшого количества модификатора вязкости - цинка стеариновокислого. The proposed method for producing glue based on casein and active fillers in the form of oxidized potato starch or oxidized corn starch eliminates foaming and obtains a composition characterized by stable properties during storage at temperatures below 291 K due to the introduction of a small amount of viscosity modifier zinc stearic acid.

Способ получения клея заключается в том, что в реактор с лопастными мешалками загружается смесь, состоящая из 52,3-68,8 вес.% воды, 3,8-5,0 вес.% окисленного картофельного крахмала или окисленного кукурузного крахмала, 8-15 вес. % мочевины, 0,26-0,4 вес.% н-бутилового спирта, 3-5 вес.% буры, 16-24 вес.% казеина, 0,06-0,3 вес.% цинка стеариновокислого и 0,3-0,4 вес.% консерванта. The method of producing glue consists in loading a mixture consisting of 52.3-68.8 wt.% Water, 3.8-5.0 wt.% Oxidized potato starch or oxidized corn starch, into the reactor with paddle mixers, 8- 15 weight % urea, 0.26-0.4 wt.% n-butyl alcohol, 3-5 wt.% borax, 16-24 wt.% casein, 0.06-0.3 wt.% zinc stearic acid and 0.3 -0.4 wt.% Preservative.

Изобретение позволяет получать клеевую композицию, отличающуюся стабильными потребительскими свойствами до 180 суток и выше, характеризующуюся условной вязкостью на BЗ3-246 при 293 К в пределах 50-400 с в зависимости от содержания массовой доли сухого остатка в клее. Образец клея, полученный без модификатора вязкости, характеризуется величиной условной вязкости на 1 порядок большей величиной после хранения клея в течение 60 суток при 293 К. EFFECT: invention makes it possible to obtain an adhesive composition characterized by stable consumer properties up to 180 days and higher, characterized by a conditional viscosity of BZ3-246 at 293 K in the range of 50-400 s, depending on the content of the mass fraction of solids in the adhesive. An adhesive sample obtained without a viscosity modifier is characterized by a conditional viscosity value of 1 order of magnitude greater after storing the adhesive for 60 days at 293 K.

Claims

An adhesive composition, which is a homogeneous liquid mass, containing casein, urea, n-butyl alcohol, a preservative, characterized in that it further comprises zinc stearic acid and oxidized potato starch or oxidized corn starch in the following ratio, wt.%:
Casein - 16 - 24.0
Oxidized potato starch or oxidized corn starch - 3.8 - 5.0
Urea - 8 - 15
Borax - 3 - 5.0
N-butyl alcohol 0.26-0.4
Stearic Zinc - 0.06 - 0.3
Preservative - 0.3 - 0.4
Water - Else