RU2156751C2 - Addition to concrete mixture - Google Patents

Addition to concrete mixture Download PDF

Info

Publication number
RU2156751C2
RU2156751C2 RU98114766A RU98114766A RU2156751C2 RU 2156751 C2 RU2156751 C2 RU 2156751C2 RU 98114766 A RU98114766 A RU 98114766A RU 98114766 A RU98114766 A RU 98114766A RU 2156751 C2 RU2156751 C2 RU 2156751C2
Authority
RU
Russia
Prior art keywords
concrete
addition
amount
additive
weight
Prior art date
Application number
RU98114766A
Other languages
Russian (ru)
Other versions
RU98114766A (en
Inventor
Л.Б. Сватовская
В.Я. Соловьева
В.П. Овчинникова
В.Е. Иванова
А.М. Сычева
С.П. Павлович
В.М. Мартышко
Г.Н. Федотова
И.А. Радиевский
С.И. Седов
Original Assignee
Сватовская Лариса Борисовна
Соловьева Валентина Яковлевна
Овчинникова Вера Павловна
Иванова Вера Ефимовна
Сычева Анастасия Максимовна
Павлович Светлана Павловна
Мартышко Владимир Михайлович
Федотова Галина Николаевна
Радиевский Иван Аркадьевич
Седов Сергей Иванович
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Сватовская Лариса Борисовна, Соловьева Валентина Яковлевна, Овчинникова Вера Павловна, Иванова Вера Ефимовна, Сычева Анастасия Максимовна, Павлович Светлана Павловна, Мартышко Владимир Михайлович, Федотова Галина Николаевна, Радиевский Иван Аркадьевич, Седов Сергей Иванович filed Critical Сватовская Лариса Борисовна
Priority to RU98114766A priority Critical patent/RU2156751C2/en
Publication of RU98114766A publication Critical patent/RU98114766A/en
Application granted granted Critical
Publication of RU2156751C2 publication Critical patent/RU2156751C2/en

Abstract

FIELD: building materials. SUBSTANCE: invention relates to production of any concrete sort (heavy-weight, lighten-weight, light-weight) and solutions with addition and can be used in production of concrete and reinforced concrete articles at negative temperatures. Addition for concrete mixture has postyeast mash and modifying agent. Addition has granulated material with density 1.1 g/cm2 as modifying agent taken in the amount 4.5 ± 0.5 wt. -% in the form of calcium-magnesium alumosilicates taken in the amount 90 wt. -%, not less, and electrolyte NaNO2 taken in the amount 1.0 ± 0.2 wt.-%. The new addition for concrete mixture provides working at lower temperature (-25 C). EFFECT: increased strength of concrete in early and rated age, enhanced resistance to cold. 3 cl, 1 tbl

Description

Изобретение относится к области производства любого вида бетона (тяжелого, облегченного, легкого) и растворов и может быть использовано при изготовлении бетонных и железобетонных изделий при отрицательных температурах. The invention relates to the production of any type of concrete (heavy, lightweight, light) and mortars and can be used in the manufacture of concrete and reinforced concrete products at low temperatures.

Известна комплексная добавка для бетонной смеси на основе цемента, которая включает сульфитно-дрожжевую бражку и смолу, нейтрализованную, воздухововлекающую, соответственно в количествах 0,15...0,25% и 0,01...0,03% от веса цемента [1]. A well-known complex additive for cement-based concrete mix, which includes sulphite-yeast mash and resin, neutralized, air-entraining, respectively, in amounts of 0.15 ... 0.25% and 0.01 ... 0.03% of the weight of cement [1].

Известна также комплексная добавка для цементно-бетонной смеси, включающая смолу, нейтрализованную, воздухововлекающую (СНВ), натриевую соль сополимера солициловой кислоты и формальдегида (ВРП), соответственно, в количествах 0,01% и 0,05...0,1 % от веса цемента [2]. Also known is a complex additive for cement-concrete mixture, including resin, neutralized, air entraining (START), sodium salt of a copolymer of solicylic acid and formaldehyde (GRP), respectively, in amounts of 0.01% and 0.05 ... 0.1% by weight of cement [2].

Наиболее близкой к изобретению по совокупности существенных признаков является комплексная добавка для цементной смеси [3]. Добавка включает смолу? нейтрализованную воздухововлекающую и пластификатор. Closest to the invention in terms of essential features is a comprehensive additive for a cement mixture [3]. Does the additive include resin? neutralized air entrainment and plasticizer.

В качестве пластификатора она содержит упаренную последрожжевую барду при следующем соотношении компонентов, мас.%:
Смола нейтрализованная воздухововлекающая - 16,25 - 16,7
Упаренная последрожжевая барда - 83,3 - 93,65
Задачей, на решение которой направлено заявляемое изобретение, является создание новой добавки для бетонной смеси, работающей при более низкой температуре (-25oC), при использовании которой был бы получен технический результат, состоящий в повышении прочности в раннем и проектном возрасте, а так же увеличении морозостойкости бетона.
As a plasticizer, it contains one stripped post-yeast stillage in the following ratio of components, wt.%:
Neutralized air-entraining resin - 16.25 - 16.7
One-off post-yeast bard - 83.3 - 93.65
The problem to which the invention is directed, is to create a new additive for concrete mix, operating at a lower temperature (-25 o C), using which would be obtained a technical result, consisting in increasing strength at an early and design age, and same increase in frost resistance of concrete.

Заявляемая новая добавка для бетонной смеси включает последрожжевую барду, модификатор. Новым является то, что она содержит в качестве модификатора гранулированный материал с плотностью 1,1 г/см3 в количестве мас.% 4,5±0,5, представленной кальций-магниевыми алюмосиликатами, количество которых должно быть не менее, 90 мас. %, и электролит NaNO2 в количестве 1,0±0,2 мас.%.The inventive new additive for concrete mix includes post-yeast bard, modifier. What is new is that it contains, as a modifier, granular material with a density of 1.1 g / cm 3 in an amount of wt.% 4.5 ± 0.5, represented by calcium-magnesium aluminosilicates, the amount of which should be at least 90 wt. %, and NaNO 2 electrolyte in an amount of 1.0 ± 0.2 wt.%.

Размер зерен модификатора выбран от 0,5 - 3,0 мм. The grain size of the modifier is selected from 0.5 - 3.0 mm.

Содержание сухих веществ в последрожжевой барде составляет 2,8...4,5 мас.%. The solids content in the post-yeast stillage is 2.8 ... 4.5 wt.%.

Использование модификатора в виде указанного гранулированного материла с плотностью 1,1 г/см3 в указанном количестве в сочетании с указанными компонентами добавки и при отрицательных температурах обеспечивает повышение гидратационной активности цемента и образование гелевой структуры твердеющего камня. При этом, образующиеся гелевые поры способствуют повышению морозостойкости затвердевшего камня. Использование NaNO2 в добавках, работающих при отрицательных температурах известно [4].The use of a modifier in the form of the specified granular material with a density of 1.1 g / cm 3 in the specified amount in combination with the indicated components of the additive and at low temperatures provides an increase in the hydration activity of cement and the formation of a gel structure of a hardening stone. At the same time, the gel pores formed contribute to the increase in frost resistance of the hardened stone. The use of NaNO 2 in additives operating at low temperatures is known [4].

Но эффект действия NaNO2 в основном обусловлен понижением температуры замерзания воды, находящейся в бетонной массе. Заявляемая новая добавка для бетона проявляет новое свойство в новой совокупности существенных признаков, которое причинно следственной связью связано с указанным техническим результатом. Этот технический результат обусловлен большим понижением температуры замерзания воды и за счет использования электролитов, представленных NaNO2 и последрожжевой бардой, состоящей из комплекса органических и неорганических соединений, а так же за счет дополнительного выделения тепла в теле бетона, в следствии усиленных гидратационных процессов цемента, а так же уменьшенным количеством воды за счет пластифицирующего действия добавки, что приводит к возможности проведения бетонных работ при более низкой температуре (-25o) и повышению морозостойкости бетона.But the effect of NaNO 2 is mainly due to a decrease in the freezing temperature of water in the concrete mass. The inventive new additive for concrete exhibits a new property in a new set of essential features, which is causally related to the specified technical result. This technical result is due to a large decrease in the freezing temperature of water and due to the use of electrolytes represented by NaNO 2 and post-yeast bard consisting of a complex of organic and inorganic compounds, as well as due to the additional heat generation in the concrete body, as a result of enhanced hydration processes of cement, and also a reduced amount of water due to the plasticizing effect of the additive, which leads to the possibility of concrete work at a lower temperature (-25 o ) and an increase in mor resistance to concrete.

Указанная совокупность существенных признаков на дату подачи заявки заявителю не известна, поэтому заявляемое изобретение, по мнению заявителя, соответствует критерию охраноспособности - "новизны". The specified set of essential features at the filing date of the application is not known to the applicant, therefore, the claimed invention, according to the applicant, meets the eligibility criterion - "novelty".

Изобретение явным образом не следует из уровня техники, заявляемая совокупность существенных признаков проявляет новое дополнительное свойство, связанное с достижением указанного технического результата. Следовательно изобретение соответствует, по мнению заявителя, критерию охраноспособности "изобретательский уровень"
ПРИМЕР КОНКРЕТНОГО ВЫПОЛНЕНИЯ.
The invention does not explicitly follow from the prior art, the claimed combination of essential features exhibits a new additional property associated with the achievement of the specified technical result. Therefore, the invention meets, according to the applicant, the eligibility criterion of "inventive step"
EXAMPLE OF SPECIFIC IMPLEMENTATION.

1. Последрожжевую барду, характеризуемую следующими параметрами:
pH 4,5...5,5;
содержание сухих веществ, мас.% - 2,8...4,5;
ρ - 1,014 г/см3;
дозируют и отправляют в вертикальную конусообразную емкость.
1. Post-yeast bard, characterized by the following parameters:
pH 4.5 ... 5.5;
solids content, wt.% - 2.8 ... 4.5;
ρ - 1.014 g / cm 3 ;
dosed and sent to a vertical cone-shaped container.

2. Твердый модификатор, являющийся гранулированным материалом с плотностью 1,1 г/см3, состоящим из кальциймагниевых алюмосиликатов, с размером зерна 0,5...3,0 мм, дозируют и транспортируют в вертикальную конусообразную емкость.2. The solid modifier, which is a granular material with a density of 1.1 g / cm 3 , consisting of calcium-magnesium aluminosilicates, with a grain size of 0.5 ... 3.0 mm, is metered and transported into a vertical cone-shaped container.

3. Электролит NaNO2 дозируют и отправляют в вертикальную конусообразную емкость.3. The NaNO 2 electrolyte is dosed and sent to a vertical cone-shaped container.

4. Отдозированную последрожжевую барду, модификатор и электролит NaNO2 перемешивают в течение 1 часа.4. The dosed post-yeast stillage, modifier and NaNO 2 electrolyte are mixed for 1 hour.

5. Готовый продукт хранят в вертикальных конусообразных емкостях, снабженных воздухом для осуществления периодического барботирования. 5. The finished product is stored in vertical conical containers equipped with air for periodic sparging.

Введение добавки в бетон осуществляется следующим образом:
готовую добавку дозируют в количестве 1 мас.% от массы цемента;
отдозированную добавку вливают в отдозированную воду для приготовления бетонной смеси;
далее бетонную смесь готовят по обычной технологии;
эффективность добавки оценивалась на бетоне состава: Ц:П:Щ = 1:0,71: 2,58;
результаты исследований представлены в табл. 1.
The introduction of additives in concrete is as follows:
the finished additive is dosed in an amount of 1 wt.% by weight of cement;
the dosed additive is poured into the dosed water to prepare the concrete mixture;
then the concrete mixture is prepared according to conventional technology;
the effectiveness of the additive was evaluated on concrete of the composition: C: P: SC = 1: 0.71: 2.58;
research results are presented in table. 1.

Анализ полученных результатов показывает, что предлагаемая добавка повышает прочность бетона в возрасте 28 суток на 21...60%, в возрасте 180 суток на 56...62%, морозостойкость бетона увеличивается на 50%. An analysis of the results shows that the proposed additive increases the strength of concrete at the age of 28 days by 21 ... 60%, at the age of 180 days by 56 ... 62%, the frost resistance of concrete increases by 50%.

Заявляемое изобретение соответствует критерию охраноспособности "промышленная применимость", так как пригодно для использования в области производства бетонных изделий и осуществимо, что подтверждается примерами конкретного выполнения. The claimed invention meets the eligibility criterion of "industrial applicability", as it is suitable for use in the field of production of concrete products and is feasible, which is confirmed by examples of specific performance.

Источники информации
1. Рекомендации по применению добавок в бетоне, М., СН, 1977, с. 3.
Sources of information
1. Recommendations for the use of additives in concrete, M., CH, 1977, p. 3.

2. Гладков B. C. и др. Сравнительные исследования бетонов с различными комплексными добавками "Бетон и железобетон", 1976, N 10, с. 13-14. 2. Gladkov B. C. et al. Comparative studies of concrete with various complex additives "Concrete and reinforced concrete", 1976, N 10, p. 13-14.

3. Авторское свидетельство N 814928, М. кл. C 04 B 13/24, Б. N 11, 1981 г.- прототип. 3. Copyright certificate N 814928, M. cl. C 04 B 13/24, B. N 11, 1981 - prototype.

4. "Бетоны, твердеющие на морозе", Миронов С.А., Лагойда А.В., М., Стройиздат, 1974.1 4. "Concrete hardening in the cold", Mironov SA, Lagoida AV, M., Stroyizdat, 1974.1

Claims (3)

1. Добавка для бетонной смеси, включающая последрожжевую барду, модификатор, отличающаяся тем, что она содержит в качестве модификатора гранулированный материал с плотностью 1,1 г/см3 в количестве 4,5 ± 0,5 мас.%, представленный кальций-магниевыми алюмосиликатами, количество которых не менее 90 мас.% и электролит NaNO2 в количестве 1,2 ± 0,2 мас.%.1. Additive for concrete mix, including post-yeast bard, modifier, characterized in that it contains as a modifier granular material with a density of 1.1 g / cm 3 in an amount of 4.5 ± 0.5 wt.%, Represented by calcium-magnesium aluminosilicates, the amount of which is not less than 90 wt.% and the NaNO 2 electrolyte in an amount of 1.2 ± 0.2 wt.%. 2. Добавка для бетонной смеси по п.1, отличающаяся тем, что размер зерен модификатора выбран от 0,5 - 3,0 мм. 2. The additive for concrete mix according to claim 1, characterized in that the grain size of the modifier is selected from 0.5 - 3.0 mm 3. Добавка для бетонной смеси по п.1, отличающаяся тем, что содержание сухих веществ в последрожжевой барже составляет 2,8 - 4,5 мас.%. 3. The additive for concrete mixture according to claim 1, characterized in that the solids content in the post-yeast barge is 2.8 to 4.5 wt.%.
RU98114766A 1998-07-24 1998-07-24 Addition to concrete mixture RU2156751C2 (en)