RU2155834C1 - Wood-pulp bleaching process - Google Patents
Wood-pulp bleaching process Download PDFInfo
- Publication number
- RU2155834C1 RU2155834C1 RU2000104294A RU2000104294A RU2155834C1 RU 2155834 C1 RU2155834 C1 RU 2155834C1 RU 2000104294 A RU2000104294 A RU 2000104294A RU 2000104294 A RU2000104294 A RU 2000104294A RU 2155834 C1 RU2155834 C1 RU 2155834C1
- Authority
- RU
- Russia
- Prior art keywords
- sodium
- bleaching
- treatment
- carried out
- mixture
- Prior art date
Abstract
Description
Изобретение относится к целлюлозно-бумажной промышленности и может найти применение в производстве беленой древесной массы из лиственной или хвойной древесины. The invention relates to the pulp and paper industry and may find application in the production of bleached pulp from deciduous or coniferous wood.
Известен способ отбелки древесной массы, когда отрицательное действие ионов металлов переменной валентности на процесс отбелки устраняют за счет использования комплексообразователя - триполифосфата натрия. Триполифосфат натрия относятся к группе соединений так называемых конденсированных фосфатов, содержащих в молекуле более одного атома фосфора и имеющих P-O-P-связи. Водные растворы триполифосфата натрия имеют щелочную реакцию и, хотя не обладают сильными комплексующими свойствами, находят применение при осуществлении отбелки древесной массы гидросульфитом натрия. Применение триполифосфата натрия при отбелке древесной массы пероксидом водорода находит применение, но не в значительной мере, поскольку по своей эффективности как индивидуальный комплексообразователь он уступает многим известным реагентам (Лебедева И. А. , Кречетова С.П. Отбелка древесной массы. Лесная промышленность, 1975, с. 43-45). A known method of bleaching wood pulp, when the negative effect of metal ions of variable valency on the bleaching process is eliminated through the use of a complexing agent - sodium tripolyphosphate. Sodium tripolyphosphate belong to the group of compounds of the so-called condensed phosphates containing more than one phosphorus atom in the molecule and having P-O-P bonds. Aqueous solutions of sodium tripolyphosphate have an alkaline reaction and, although they do not have strong complexing properties, are used in the bleaching of wood pulp with sodium hydrosulfite. The use of sodium tripolyphosphate in the bleaching of wood pulp with hydrogen peroxide is used, but not to a large extent, since it is inferior to many known reagents as an individual complexing agent (I. Lebedeva, S.P. Krechetova, Pulp bleaching. Timber industry, 1975 , p. 43-45).
Известен способ отбелки древесной массы пероксидом водорода, согласно которому в качестве стабилизатора используют производные алкиламинметиленфосфонита, например этилендиаминтетраметиленфосфонат натрия (см. JP 53-44563, кл. D 21 C 9/16, опубл. 30.11.1978). A known method of bleaching wood pulp with hydrogen peroxide, according to which derivatives of alkylaminomethylene phosphonite, for example sodium ethylene diamine tetramethylene phosphonate are used as stabilizer (see JP 53-44563, class D 21 C 9/16, publ. 30.11.1978).
Данный способ позволяет вести отбелку пероксидом водорода полуфабрикатов высокого выхода, таких как дефибрерная, термомеханическая и химико-термомеханическая масса. Данный стабилизатор используется взамен силиката натрия, что сопряжено с повышенным расходом дорогостоящего химиката. Кроме того, использование производных алкиламинметиленфосфонатов в качестве стабилизаторов пероксида водорода сопряжено со снижением интенсивности процесса и, следовательно, с увеличением его продолжительности, поскольку они не выполняют роль активизаторов пероксида водорода. This method allows the bleaching of hydrogen peroxide semi-finished products of high yield, such as defibrera, thermomechanical and chemical-thermomechanical mass. This stabilizer is used instead of sodium silicate, which is associated with an increased consumption of an expensive chemical. In addition, the use of derivatives of alkylaminomethylene phosphonates as stabilizers of hydrogen peroxide is associated with a decrease in the intensity of the process and, consequently, with an increase in its duration, since they do not play the role of activators of hydrogen peroxide.
Наиболее близким к предлагаемому является способ отбелки древесной массы путем обработки ее водной суспензии отбеливающий реагентом и комплексообразователем на основе этиленаминметиленфосфоновой кислоты (см. DE 3308298 A1, кл. D 21 C 9/10, опубл. 13.09.1984). Closest to the proposed is a method of bleaching wood pulp by treating its aqueous suspension with a bleaching agent and a complexing agent based on ethyleneamine methylene phosphonic acid (see DE 3308298 A1, CL D 21 C 9/10, publ. 13.09.1984).
Сущность данного способа состоит в том, что отбелку древесной массы отбеливающим реагентом, например гидросульфитом натрия, осуществляют в присутствии одного из производных этиленаминметиленфосфоновой кислоты, например, диэтилентриаминпентаметиленфосфоновой или этилендиаминтетраметиленфосфоновой кислот. Процесс ведут в следующей последовательности: предварительно в водную суспензию древесной массы добавляют один из производных этиленаминметиленфосфоновой кислоты в количестве 0,2% от массы абсолютно сухого волокна и при перемешивании обрабатывают в течение 30 мин. В этом случае вышеуказанная кислота выполняет роль комплексообразователя, то есть имеет место инактивация ионов металлов переменной валентности. По окончании времени инактивации в волокнистую суспензию добавляют гидросульфит натрия и отбелку продолжают в течение 60 мин. Положительный результат данного способа состоит в том, что использование производных этиленаминметиленфосфонатов в качестве комплексообразователей обеспечивает повышение степени белизны по сравнению с контрольный образцом. The essence of this method is that the bleaching of wood pulp with a bleaching reagent, for example sodium hydrosulfite, is carried out in the presence of one of the derivatives of ethyleneamine methylenephosphonic acid, for example, diethylene triamine pentamethylene phosphonic or ethylenediamine tetramethylene phosphonic acid. The process is carried out in the following sequence: first, one of the derivatives of ethyleneaminemethylenephosphonic acid is added to an aqueous suspension of wood pulp in an amount of 0.2% by weight of absolutely dry fiber and is treated for 30 minutes with stirring. In this case, the above acid plays the role of a complexing agent, that is, there is an inactivation of metal ions of variable valency. At the end of the inactivation time, sodium hydrosulfite is added to the fiber suspension and bleaching is continued for 60 minutes. A positive result of this method is that the use of derivatives of ethyleneamine methylene phosphonates as complexing agents provides an increase in the degree of whiteness in comparison with a control sample.
Катализаторами разложения отбеливающих реагентов являются в основном ионы металлов переменной валентности, в частности железа, меди и марганца. Пока не известно комплексообразователя, который в равной степени мог бы инактивировать ионы вышеотмеченных металлов. Поэтому недостатком данного способа отбелки является то, что при использовании указанных химикатов как индивидуальных веществ в качестве комплексообразователя не решается проблема инактивации ионов всех металлов переменной валентности в равной степени, поскольку каждый из комплексообразователей может в большей степени воздействовать на ионы одного из металлов переменной валентности и в меньшей степени на ионы другого металла переменной валентности. При использовании другого комплексообразователя его действия на ионы металлов переменной валентности могут быть противоположными первому комплексообразователю. The catalysts for the decomposition of bleaching reagents are mainly metal ions of variable valency, in particular iron, copper and manganese. So far, no complexing agent is known that could equally inactivate the ions of the above metals. Therefore, the disadvantage of this bleaching method is that when using these chemicals as individual substances as a complexing agent, the problem of the inactivation of ions of all metals of variable valency is not solved equally, since each of the complexing agents can more strongly affect the ions of one of the metals of variable valency and a lesser degree on the ions of another metal of variable valency. When using another complexing agent, its action on metal ions of variable valency can be opposite to the first complexing agent.
Это в свою очередь отрицательно сказывается на белизне готовой древесной массы. This in turn adversely affects the whiteness of the finished wood pulp.
Новым техническим результатом предлагаемого технического решения является интенсификация процесса отбелки за счет снижения расхода отбеливающих реагентов и сокращения времени отбелки при одновременном повышении белизны древесной массы. A new technical result of the proposed technical solution is the intensification of the bleaching process by reducing the consumption of bleaching reagents and reducing the time of bleaching while increasing the brightness of the wood pulp.
Достигается технический результат тем, что в способе отбелки древесной массы путем обработки ее водной суспензии отбеливающим реагентом и комплексообразователем на основе этиленаминметиленфосфоновой кислоты согласно изобретению в качестве комплексообразователя используют смесь натриевых солей этилендиаминтетраметиленфосфоновой, диэтилентриаминпентаметиленфосфоновой и триэтилентетраамингексамэтиленфосфоновой кислоты при их массовом соотношении в смеси соответственно (0,8-1,2) : (0,8-1,2) : (0,8-1,2), при этом указанную обработку проводят в присутствии дополнительного комплексообразователя - триполифосфата натрия при соотношении соли указанной смеси кислот и триполифосфата натрия от 5:1 до 10:1 и общем расходе комплексообразователей 0,1-0,2% от массы абсолютно сухого волокна. The technical result is achieved by the fact that in the method of bleaching wood pulp by treating its aqueous suspension with a bleaching reagent and a complexing agent based on ethyleneamine methylenephosphonic acid according to the invention, a mixture of sodium salts of ethylene diamine tetramethylene phosphonic, diethylene triamine pentamethylene phosphonate and triethylenetomethene -1.2): (0.8-1.2): (0.8-1.2), while the specified processing is carried out in the presence of an additional complexing agent, sodium tripolyphosphate, with a salt ratio of the mixture of acids and sodium tripolyphosphate from 5: 1 to 10: 1 and a total consumption of complexing agents of 0.1-0.2% by weight of absolutely dry fiber.
В качестве отбеливающего реагента используют пероксид водорода или гидросульфит натрия. As a bleaching agent, hydrogen peroxide or sodium hydrosulfite is used.
Обработку проводят при температуре 40-80oC в течение 80-120 мин.The treatment is carried out at a temperature of 40-80 o C for 80-120 minutes
Обработку водной суспензии древесной массы можно проводить либо в одну стадию, либо сначала проводить смесью натриевых солей этилендиаминтетраметиленфосфоновой, диэтилентриаминпентаметиленфосфоновой и триэтилентетраамингексаметиленфосфоновой кислоты в присутствии триполифосфата натрия в течение 40-60 мин, а затем добавлять отбеливающий реагент и продолжать обработку в течение 40-60 мин. The processing of an aqueous suspension of wood pulp can be carried out either in one stage, or first with a mixture of sodium salts of ethylene diamine tetramethylene phosphonic, diethylene triamine pentamethylene phosphonic and triethylenetetraamine hexamethylene phosphonic acid in the presence of sodium tripolyphosphate for 40-60 minutes, and then add a bleaching agent for 40-60 minutes.
Ионы металлов переменной валентности - железа, меди, марганца и других, присутствующие в воде и самой древесной массе, являются инициаторами и катализаторами разложения отбеливающих реагентов - гидросульфита натрия и пероксида водорода, что приводит к повышенному их расходу. Химические вещества хелатного ряда, связывая ионы металлов в комплексы, инактивируют их. Химическое сродство и прочность образованных комплексов определяется условиями при их взаимодействии, а также химической природой и структурой самого хелатного вещества - комплексообразователя. Использование для инaктивации инициаторов разложения отбеливающих реагентов смеси комплексообразователей различного химического строения обеспечивает условия для равномерной и более полной инактивации практически всех ионов металлов переменной валентности. Условно можно принять этилендиаминтетраметиленфосфонат натрия в более полной мере инактивирует ионы железа и в меньшей степени ионы меди и марганца, диэтилентриаминпентаметиленфосфонат натрия в большей степени инактивирует ионы меди и в меньшей степени ионы железа и марганца, а триэтилентетраамингексаметиленфосфонат натрия в большей степени инактивирует ионы марганца и в меньшей ионы железа и меди. Суммарно смесь комплексообразователей устраняет вредное влияние практически всех ионов металлов. Ions of metals of variable valency - iron, copper, manganese and others, present in water and wood pulp itself, are the initiators and catalysts for the decomposition of bleaching reagents - sodium hydrosulfite and hydrogen peroxide, which leads to their increased consumption. Chelating chemicals, binding metal ions to complexes, inactivate them. The chemical affinity and strength of the formed complexes is determined by the conditions during their interaction, as well as by the chemical nature and structure of the chelating substance itself, the complexing agent. The use of a mixture of complexing agents of various chemical structures to inactivate the initiators of the decomposition of bleaching reagents provides the conditions for the uniform and more complete inactivation of almost all metal ions of variable valency. Conventionally, it is possible to take sodium ethylene diamine tetramethylene phosphonate to more fully inactivate iron ions and, to a lesser extent, copper and manganese ions, sodium diethylene triamine pentamethylene phosphonate to a greater extent inactivate copper ions and to a lesser extent iron and manganese ions, and sodium triethylenetetraamine hexamethylene phosphonate to a greater extent and to a greater extent iron and copper ions. The total mixture of complexing agents eliminates the harmful effects of almost all metal ions.
Роль триполифосфата натрия сводится к следующему: как комплексообразователь он также участвует в инактивации ионов металлов, однако его присутствие необходимо для обеспечения оптимальных условий работы основных комплексообразователей, поскольку, являясь щелочным реагентом, он создает буферные условия для поддержания определенной щелочной среды. Таким образом, совместное действие всех компонентов смеси обеспечивает синергетический эффект при осуществлении отбелки древесной массы гидросульфитом натрия или пероксидом водорода. The role of sodium tripolyphosphate is as follows: as a complexing agent, it also participates in the inactivation of metal ions, however, its presence is necessary to ensure optimal working conditions of the main complexing agents, since, being an alkaline reagent, it creates buffer conditions to maintain a certain alkaline environment. Thus, the combined action of all components of the mixture provides a synergistic effect when performing bleaching of wood pulp with sodium hydrosulfite or hydrogen peroxide.
Предложенный способ отбелки древесной массы осуществляют следующим образом: волокнистую массу, полученную термомеханическим или химико-термомеханическим путем, разбавляют горячей водой до концентрации 2-3%, при этом устанавливают заданную температуру волокнистой суспензии 40-80oC. Затем в суспензию при перемешивании вводят комплексообразователь, который получают из смеси натриевых солей этилендиаминтетраметиленфосфоновой, диэтилентриаминпентаметиленфосфоновой и триэтилентетраамингексаметиленфосфоновой кислот, взятых в соотношении (0,8-1,2) : (0,8-1,2) : (0,8-1,2), и в эту смесь солей добавляют триполифосфат натрия в количестве, обеспечивающем соотношение указанных солей и триполифосфата натрия от 5:1 до 10:1, соответственно.The proposed method of bleaching wood pulp is carried out as follows: the pulp obtained by thermomechanical or chemical-thermomechanical means is diluted with hot water to a concentration of 2-3%, while setting the desired temperature of the fiber suspension 40-80 o C. Then, a complexing agent is introduced into the suspension with stirring , which is obtained from a mixture of sodium salts of ethylene diamine tetramethylene phosphonic, diethylene triamine pentamethylene phosphonic and triethylene tetraamine hexamethylene phosphonic acids, taken in the ratio and (0.8-1.2): (0.8-1.2): (0.8-1.2), and sodium tripolyphosphate is added to this mixture of salts in an amount that ensures the ratio of these salts to sodium tripolyphosphate from 5: 1 to 10: 1, respectively.
Комплексообразователь сложного состава задают на обработку древесной массы в количестве от 0,1 до 0,2% от массы абсолютно сухого волокна. Обработку волокнистой массы комплексообразователей заканчивают через 40-60 мин. Затем массу сгущают до концентрации 5-15% и смешивают с предварительно приготовленным раствором отбеливающего реагента. Раствор гидросульфита натрия готовят посредством растворения порошка гидросульфита натрия в слабощелочном растворе воды, а рабочий раствор пероксида водорода готовят посредством последовательного введения в воду гидроксида натрия, силиката натрия и пероксида водорода. Расход гидросульфита натрия составляет 5-9,0 кг/т, а пероксида водорода 10-30 кг/т от массы абсолютно сухого волокна. Обработку древесной массы отбеливающими реагентами проводят при температуре 60-80oC в течение 40-60 мин. Возможны варианты, когда комплексообразователь используют не на стадии предобработки волокнистой суспензии, а вводят в массу совместно с отбеливающим реагентом. По истечении времени обработки древесной массы отбеливающим реагентом из беленой массы изготавливают бумажные листы и определяют степень белизны.Complexing agents of complex composition are asked to process wood pulp in an amount of from 0.1 to 0.2% by weight of absolutely dry fiber. The treatment of the pulp of the complexing agents is completed in 40-60 minutes. Then the mass is concentrated to a concentration of 5-15% and mixed with a pre-prepared solution of a bleaching reagent. A sodium hydrosulfite solution is prepared by dissolving sodium hydrosulfite powder in a slightly alkaline water solution, and a working solution of hydrogen peroxide is prepared by sequentially introducing sodium hydroxide, sodium silicate and hydrogen peroxide into the water. The consumption of sodium hydrosulfite is 5-9.0 kg / t, and hydrogen peroxide 10-30 kg / t by weight of absolutely dry fiber. The processing of wood pulp with bleaching reagents is carried out at a temperature of 60-80 o C for 40-60 minutes Variants are possible when the complexing agent is not used at the stage of pretreatment of the fibrous suspension, but is introduced into the mass together with the bleaching reagent. After the processing time of the pulp with a bleaching agent, paper sheets are made from the bleached pulp and the degree of whiteness is determined.
Изобретение иллюстрируется следующими примерами его осуществления. The invention is illustrated by the following examples of its implementation.
Пример 1. Способ отбелки древесной массы осуществляют следующим образом. Древесную массу, полученную термомеханическим методом, исходной концентрацией 22% помещает в емкость, куда приливают предварительно нагретую воду в количестве, обеспечивающем концентрацию массы 2,5%, при этом температуру волокнистой суспензии устанавливают равной 50oC. При перемешивании в волокнистую суспензию вносят раствор комплексообразователя в количестве 0,15% от массы абсолютно сухого волокна. Комплексообразователь готовят из смеси натриевых солей этилендиаминтетраметиленфосфоновой, диэтилентриаминпентаметиленфосфоновой и триэтилентетраамингексаметиленфосфоновой кислот, взятых в соотношении 0,8:1,0:1,2 соответственно, и в эту смесь солей добавляют триполифосфат натрия в количестве, обеспечивающем соотношение указанной выше смеси солей и триполифосфата натрия 8:1. Обработку волокнистой суспензии древесной массы осуществляют в течение 50 мин. По истечении указанного промежутка времени массу обезвоживают до концентрации 5% и при интенсивном перемешивании в массу вводят раствор гидросульфата натрия, что обеспечивает рабочую концентрацию 4%. Расход гидросульфита натрия 8 кг/т, температура обработки 60oC, а продолжительность 40 мин. По окончании обработки массу разбавляют водой, кислуют до pH 5, изготовляют листы бумаги и анализируют.Example 1. The method of bleaching wood pulp is as follows. The wood pulp obtained by the thermomechanical method, with an initial concentration of 22%, is placed in a container where pre-heated water is poured in an amount providing a mass concentration of 2.5%, while the temperature of the fibrous suspension is set to 50 o C. With stirring, a complexing agent solution is introduced into the fibrous suspension in the amount of 0.15% by weight of absolutely dry fiber. The complexing agent is prepared from a mixture of sodium salts of ethylene diamine tetramethylene phosphonic, diethylene triamine pentamethylene phosphonic and triethylenetetraamine hexamethylene phosphonic acids taken in a ratio of 0.8: 1.0: 1.2, respectively, and sodium tripolyphosphate is added to this mixture of salts in an amount providing sodium triphosphate of the above mixture :1. The processing of the fibrous suspension of wood pulp is carried out for 50 minutes After the specified period of time, the mass is dehydrated to a concentration of 5% and, with vigorous stirring, a solution of sodium hydrogen sulfate is introduced into the mass, which ensures a working concentration of 4%. The consumption of
Показатели беленой термомеханической массы приведены в таблице. The indicators of bleached thermomechanical mass are given in the table.
Пример 2. Способ отбелки древесной массы осуществляют аналогично примеру 1. Отличия состоят в том, что температура обработки волокнистой суспензии комплексообразователем 40oC, а продолжительность обработки 60 мин. Смесь натриевых солей органических кислот берут в соотношении 1,0:1,2:0,8, а соотношение смеси указанных солей и триполифосфата натрия 5:1, при общем расходе комплексообразователя 0,2% от массы абсолютно сухого волокна. Обработку ведут при расходе гидросульфита натрия 9,0 кг/т при температуре 70oC в течение 40 мин.Example 2. The method of bleaching wood pulp is carried out analogously to example 1. The differences are that the processing temperature of the fibrous suspension with complexing agent 40 o C, and the processing time of 60 minutes A mixture of sodium salts of organic acids is taken in a ratio of 1.0: 1.2: 0.8, and the ratio of the mixture of these salts and sodium tripolyphosphate is 5: 1, with a total complexing agent consumption of 0.2% by weight of absolutely dry fiber. Processing is carried out at a flow rate of sodium hydrosulfite 9.0 kg / t at a temperature of 70 o C for 40 minutes
Показатели беленой термомеханической массы приведены в таблице. The indicators of bleached thermomechanical mass are given in the table.
Пример 3. Способ отбелки древесной массы осуществляют аналогично примеру 1. Отличия состоят в том, что температура обработки волокнистой суспензии комплексообразователем 80oC, а продолжительность обработки 40 мин. Смесь натриевых солей органических кислот берут в соотношении 1,2:0,8:1,0, а соотношение смеси указанных солей и триполифосфата натрия 10:1, при общем расходе комплексообразователя 0,1% от массы абсолютно сухого волокна. Обезвоживание массы проводят до концентрации 15%, а отбелку проводят пероксидом водорода при его расходе 25 кг/т массы. Кроме того, в отбеливающий раствор добавляют гидроксид натрия 15 кг/т и силикат натрия в количестве 30 кг/т. После смешения отбеливающего раствора и массы обработку ведут при температуре 80oC в течение 60 мин при рабочей концентрации массы 10%.Example 3. The method of bleaching wood pulp is carried out analogously to example 1. The differences are that the processing temperature of the fibrous suspension with a complexing agent is 80 o C, and the processing time is 40 minutes The mixture of sodium salts of organic acids is taken in a ratio of 1.2: 0.8: 1.0, and the ratio of the mixture of these salts and sodium tripolyphosphate is 10: 1, with a total complexing agent consumption of 0.1% by weight of absolutely dry fiber. Dehydration of the mass is carried out to a concentration of 15%, and bleaching is carried out with hydrogen peroxide at a flow rate of 25 kg / t of mass. In addition, sodium hydroxide 15 kg / t and sodium silicate in an amount of 30 kg / t are added to the bleaching solution. After mixing the bleaching solution and the mass, the treatment is carried out at a temperature of 80 o C for 60 minutes at a working concentration of the mass of 10%.
Показатели беленой термомеханической массы приведены в таблице. The indicators of bleached thermomechanical mass are given in the table.
Пример 4. Способ отбелки древесной массы осуществляют следующим образом. Древесную массу, полученную химико-термомеханическим методом, с исходной концентрацией 25% помещают в емкость и заливают предварительно нагретой водой в количестве, обеспечивающем концентрацию массы 2,5%, при этом устанавливают температуру волокнистой суспензии 80oC и проводят водную обработку массы при перемешивании в течение 40 мин. Затем массу обезвоживают до концентрации 5% и смешивают ее с раствором гидросульфита натрия, содержащим в своем составе комплексообразователь. Расход гидросульфита натрия 9,0 кг/т, а комплексообразователя 0,15% от массы абсолютно сухого волокна. В состав комплексообразователя входят смесь натриевых солей этилендиаминтетраметиленфосфоновой, диэтилентриаминпентаметиленфосфоновой и триатилентетраамингексаметиленфосфоновой кислот, взятых в соотношении 1:1:1, и триполифосфат натрия в количестве, обеспечивающем соотношение указанных солей органических кислот и триполифосфата натрия 8:1. Обработку отбеливателем проводят при температуре 60oC в течение 40 мин. По истечении времени обработки массу разбавляют водой, кислуют до pH 5, изготовляют листы бумаги и анализируют.Example 4. The method of bleaching wood pulp is as follows. The wood pulp obtained by the chemical-thermomechanical method, with an initial concentration of 25%, is placed in a container and poured with pre-heated water in an amount providing a mass concentration of 2.5%, while the temperature of the fiber suspension is set to 80 o C and the mass is water treated with stirring in for 40 minutes Then the mass is dehydrated to a concentration of 5% and mixed with a solution of sodium hydrosulfite containing a complexing agent. The consumption of sodium hydrosulfite is 9.0 kg / t, and the complexing agent is 0.15% by weight of absolutely dry fiber. The complexing agent includes a mixture of sodium salts of ethylene diamine tetramethylene phosphonic, diethylene triamine pentamethylene phosphonic and triatylene tetraamine hexamethylene phosphonic acids taken in a ratio of 1: 1: 1, and sodium tripolyphosphate in an amount providing a ratio of the indicated salts of organic acids and sodium tripol: 1. The bleaching treatment is carried out at a temperature of 60 o C for 40 minutes After the processing time, the mass is diluted with water, acidified to
Показатели беленой химико-термомеханической массы приведены в таблице. The indicators of bleached chemical-thermomechanical mass are given in the table.
Пример 5. Способ отбелки древесной массы осуществляют аналогично примеру 4. Отличия состоят в том, что отбелку химико-термомеханической массы проводят щелочным раствором пероксида водорода. Концентрация массы при отбелке 10%, расход отбеливающих реагентов следующий, кг/т: пероксид водорода - 25, гидроксид натрия - 15, силикат натрия - 30. Example 5. The method of bleaching wood pulp is carried out analogously to example 4. The differences are that the bleaching of the chemical-thermomechanical pulp is carried out with an alkaline solution of hydrogen peroxide. The mass concentration during bleaching is 10%, the consumption of bleaching reagents is as follows, kg / t: hydrogen peroxide - 25, sodium hydroxide - 15, sodium silicate - 30.
Показатели беленой химико-термомеханической массы приведены в таблице. The indicators of bleached chemical-thermomechanical mass are given in the table.
Пример 6 (прототип). Способ отбелки древесной массы осуществляют следующим образом. Термомеханическую массу исходной концентрации 22% помещают в емкость, куда приливают предварительно нагретую воду в количестве, обеспечивающем концентрацию массы 2,5% и температуру 60oC. При перемешивании в волокнистую суспензию добавляют натриевую соль этилендиаминтетраметиленфосфоновой кислоты в количестве 0,2% от массы абсолютно сухого волокна. Перемешивание заканчивает через 60 мин и массу обезвоживают до концентрации 5%, после чего в волокнистую суспензию добавляют раствор гидросульфита натрия с расходом его 10 кг/т абсолютно сухого волокна, а отбелку при концентрации массы 4% ведут при температуре 60oC в течение 60 мин. По окончании обработки массу кислуют при разбавлении, изготавливают листы бумаги и анализируют.Example 6 (prototype). The method of bleaching wood pulp is as follows. The thermomechanical mass of the initial concentration of 22% is placed in a container where preheated water is poured in an amount providing a mass concentration of 2.5% and a temperature of 60 o C. With stirring, the sodium salt of ethylene diamine tetramethylene phosphonic acid in an amount of 0.2% by weight is absolutely dry fiber. Mixing ends after 60 minutes and the mass is dehydrated to a concentration of 5%, after which a solution of sodium hydrosulfite is added to the fiber suspension with a flow rate of 10 kg / t of absolutely dry fiber, and bleaching at a concentration of 4% is carried out at a temperature of 60 o C for 60 minutes . At the end of the treatment, the mass is acidified upon dilution, sheets of paper are made and analyzed.
Показатели беленой термомеханической массы приведены в таблице. The indicators of bleached thermomechanical mass are given in the table.
Пример 7 (прототип). Способ отбелки древесной массы осуществляют следующим образом. Химико-термомеханическую массу исходной концентрации 25% помещают в емкость, заливают предварительно нагретой водой в количестве, обеспечивающем концентрацию массы 2,5% и температуру 80oC. Волокнистую суспензию выдерживают при перемешивании в течение 40 мин, затем обезвоживают до концентрации 15% и проводят обработку щелочным раствором пероксида водорода совместно с натриевой солью диэтилентриаминпентаметиленфосфоновой кислоты, расход которой составляет 0,2% от массы абсолютно сухого волокна, пероксида водорода 25 кг/т, гидроксида натрия 15 кг/т и силиката натрия 30 кг/т. Концентрация массы при обработке щелочным раствором пероксидом водорода 10%, температура 80oC, а обработку ведут в течение 60 мин. По истечении времени обработки массу кислуют при разбавлении водой и изготовляют листы бумаги и анализируют.Example 7 (prototype). The method of bleaching wood pulp is as follows. The chemical-thermomechanical mass of the initial concentration of 25% is placed in a container, filled with pre-heated water in an amount providing a mass concentration of 2.5% and a temperature of 80 o C. The fiber suspension is kept under stirring for 40 minutes, then dehydrated to a concentration of 15% and carried out treatment with an alkaline solution of hydrogen peroxide together with the sodium salt of diethylene triamine pentamethylene phosphonic acid, the consumption of which is 0.2% by weight of absolutely dry fiber, hydrogen peroxide 25 kg / t, sodium hydroxide 15 g / t sodium silicate and 30 kg / t. The mass concentration during treatment with an alkaline solution of
Показатели беленой химико-термомеханической массы приведены в таблице. The indicators of bleached chemical-thermomechanical mass are given in the table.
Анализ приведенных в таблице данных свидетельствует, что предлагаемый способ отбелки древесной массы позволяет достигнуть более высокой степени белизны целевого продукта при меньшем расходе комплексообразователя и отбеливающих химикатов. The analysis of the data in the table indicates that the proposed method of bleaching wood pulp allows you to achieve a higher degree of whiteness of the target product with less consumption of complexing agents and bleaching chemicals.
Claims (4)