RU2120514C1 - Reinforced elastomer support for engineering structures - Google Patents

Reinforced elastomer support for engineering structures Download PDF

Info

Publication number
RU2120514C1
RU2120514C1 RU97107142/03A RU97107142A RU2120514C1 RU 2120514 C1 RU2120514 C1 RU 2120514C1 RU 97107142/03 A RU97107142/03 A RU 97107142/03A RU 97107142 A RU97107142 A RU 97107142A RU 2120514 C1 RU2120514 C1 RU 2120514C1
Authority
RU
Russia
Prior art keywords
engineering structures
rubber
elastomeric
support
reinforced
Prior art date
Application number
RU97107142/03A
Other languages
Russian (ru)
Other versions
RU97107142A (en
Inventor
А.Р. Козлюк
М.И. Лебедев
С.В. Насонов
В.М. Поспелов
А.А. Снапковский
Original Assignee
Совместное российско-сербское предприятие "РОССЕРБМОСТ"
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Совместное российско-сербское предприятие "РОССЕРБМОСТ" filed Critical Совместное российско-сербское предприятие "РОССЕРБМОСТ"
Priority to RU97107142/03A priority Critical patent/RU2120514C1/en
Application granted granted Critical
Publication of RU2120514C1 publication Critical patent/RU2120514C1/en
Publication of RU97107142A publication Critical patent/RU97107142A/en

Abstract

FIELD: construction and repair of engineering structures, in particular, bridges. SUBSTANCE: support consists of reinforcement in the form of steel plates between which intermediate elastomer layers are located and outer elastomer layer. All layers are made of rubber based on combination of butyl rubber and ethylenepropylene-diene rubber in ratio of 40-80% : 20-60%, respectively. EFFECT: higher low-temperature operating characteristics of elastomer support for engineering structures. 1 dwg, 1 tbl

Description

Изобретение относится к строительству и ремонту инженерных сооружений, в частности для мостов. The invention relates to the construction and repair of engineering structures, in particular for bridges.

Известна армированная эластомерная опора для мостов, содержащая арматуру в виде стальных пластин, расположенных между ними промежуточных эластомерных слоев, выполненных из резин на основе комбинаций полихлоропренового и бутадиен-нитрильного каучуков, либо полиизопренового и бутадиенового каучуков, и наружнего эластомерного слоя, выполненного из резины на основе комбинаций полихлоропренового и бутадиен-нитрильного каучуков [1]. Known reinforced elastomeric support for bridges containing reinforcement in the form of steel plates located between them intermediate elastomeric layers made of rubbers based on combinations of polychloroprene and nitrile butadiene rubbers, or polyisoprene and butadiene rubbers, and an outer elastomeric layer made of rubber based combinations of polychloroprene and nitrile butadiene rubbers [1].

Недостатком данной армированной эластомерной опоры для мостов является быстрая потеря эксплуатационных характеристик изделия вследствие низкой стойкости резин эластомерных слоев к старению. The disadvantage of this reinforced elastomeric support for bridges is the rapid loss of product performance due to the low resistance of rubber elastomeric layers to aging.

Известна армированная эластомерная опора для инженерных сооружений, в частности для мостов, содержащая арматуру в виде стальных пластин, расположенных между ними промежуточных эластомерных слоев и наружнего эластомерного слоя, изготовленных из резины на основе полихлоропренового каучука [2]. Known reinforced elastomeric support for engineering structures, in particular for bridges, containing reinforcement in the form of steel plates located between them of intermediate elastomeric layers and the outer elastomeric layer made of rubber based on polychloroprene rubber [2].

Недостатками данной армированной эластомерной опоры для мостов являются плохие низкотемпературные эксплуатационные характеристики, которые оценивали согласно DIN 4141 часть 140 пункт 4.3.2. The disadvantages of this reinforced elastomeric support for bridges are poor low-temperature performance, which was evaluated according to DIN 4141 part 140 clause 4.3.2.

Целью изобретения является улучшение низкотемпературных эксплуатационных характеристик армированной эластомерной опоры для инженерных сооружений. The aim of the invention is to improve the low temperature performance of reinforced elastomeric bearings for engineering structures.

Указанная цель достигается тем, что армированная эластомерная опора для инженерных сооружений, содержащая арматуру в виде стальных пластин, расположенных между ними промежуточных эластомерных слоев и наружного эластомерного слоя, отличается тем, что промежуточные и наружный эластомерные слои выполнены из резины на основе комбинации бутилкаучука и этиленпропилендиенового каучука в соотношении 40-80% на 20-60% соответственно. This goal is achieved in that the reinforced elastomeric support for engineering structures, containing reinforcement in the form of steel plates, intermediate elastomeric layers located between them and the outer elastomeric layer, is characterized in that the intermediate and external elastomeric layers are made of rubber based on a combination of butyl rubber and ethylene propylene diene rubber in the ratio of 40-80% by 20-60%, respectively.

На чертеже изображена армированная эластомерная опора для инженерных сооружений. The drawing shows a reinforced elastomeric support for engineering structures.

Армированная эластомерная опора для инженерных сооружений содержит арматуру в виде стальных пластин 1, расположенных между ними промежуточных эластомерных слоев 2 и наружного эластомерного слоя 3, выполненных из резины на основе комбинации бутилкаучука (БК) и этиленпропилендиенового (ЭПДК) каучука в соотношении 40-80% на 20-60% соответственно. Стальные пластины перекладывают резиновыми листами, затем накладывают резиновые листы наружного эластомерного слоя. После подобной сборки полученную заготовку помещают в пресс-форму и вулканизируют в прессе под действием температуры и давления. По окончании процесса вулканизации готовую армированную эластомерную опору для инженерных сооружений извлекают из пресс-формы. Reinforced elastomeric support for engineering structures contains reinforcement in the form of steel plates 1, intermediate elastomeric layers 2 located between them and the outer elastomeric layer 3 made of rubber based on a combination of butyl rubber (EP) and ethylene propylene diene (EPDM) rubber in a ratio of 40-80% per 20-60% respectively. The steel plates are laid with rubber sheets, then rubber sheets of the outer elastomeric layer are applied. After such assembly, the resulting preform is placed in a mold and vulcanized in the press under the influence of temperature and pressure. At the end of the vulcanization process, the finished reinforced elastomeric support for engineering structures is removed from the mold.

Низкотемпературные эксплуатационные характеристики армированной эластомерной опоры для инженерных сооружений оценивали по показателю модуля упругости сдвига при комнатной температуре, -30oC и -40oC согласно DIN 4141 часть 140 пункт 4.3.2. результаты испытаний армированной эластомерной опоры для инженерных сооружений представлены в таблице, из которой можно сделать следующие выводы:
1. Армированные эластомерные опоры для инженерных сооружений (2-4), изготовленные согласно изобретению, обладают более низкими значениями модуля упругости сдвига при низких температурах по сравнению с армированными эластомерными опорами для инженерных сооружений, изготовленными по прототипу и контрольному примеру (6).The low-temperature performance of the reinforced elastomeric support for engineering structures was evaluated by the shear modulus at room temperature, -30 o C and -40 o C according to DIN 4141 part 140 clause 4.3.2. The test results of the reinforced elastomeric support for engineering structures are presented in the table, from which the following conclusions can be drawn:
1. Reinforced elastomeric supports for engineering structures (2-4) made according to the invention have lower shear modulus at low temperatures compared to reinforced elastomeric supports for engineering structures made according to the prototype and control example (6).

2. Армированная эластомерная опора для инженерных сооружений (5), изготовленная согласно контрольному примеру, обладает низкими значениями модуля упругости сдвига при комнатной температуре по сравнению с армированными эластомерными опорами для инженерных сооружений, изготовленными согласно изобретению и по прототипу. 2. Reinforced elastomeric support for engineering structures (5), made according to the control example, has low shear modulus values at room temperature compared to reinforced elastomeric supports for engineering structures made according to the invention and the prototype.

3. Поскольку состав резин эластомерных слоев армированных эластомерных опор для инженерных сооружений, содержащих комбинации бутилкаучука и этиленпропилендиенового каучука согласно изобретению (2-4) и контрольных примеров (5-6) одинаков, достигнутый положительный эффект обеспечен только за счет применяемой комбинации бутилкаучука и этиленпропилендиенового каучука в пропорциях согласно изобретению. 3. Since the rubber composition of the elastomeric layers of reinforced elastomeric supports for engineering structures containing a combination of butyl rubber and ethylene propylene diene rubber according to the invention (2-4) and control examples (5-6) is the same, the achieved positive effect is achieved only due to the combination of butyl rubber and ethylene propylene diene rubber in proportions according to the invention.

4. Высокие низкотемпературные эксплуатационные характеристики армированной эластомерной опоры для инженерных сооружений могут быть получены только с использованием технического решения согласно изобретению. 4. High low-temperature operational characteristics of a reinforced elastomeric support for engineering structures can only be obtained using the technical solution according to the invention.

Источники информации
1. Инструкция по проектированию и установке полимерных опорных частей мостов. ВСН 86-83. М., 1983 г., пункт 4.1.Sources of information
1. Instructions for the design and installation of polymer supporting parts of bridges. BCH 86-83. M., 1983, paragraph 4.1.

2. Германский стандарт DIN 4141 часть 140, 1991 г., пункты: 2.1.2., 3.2. - прототип. 2. German standard DIN 4141 part 140, 1991, clauses: 2.1.2., 3.2. - prototype.

Claims (1)

Армированная эластомерная опора для инженерных сооружений, содержащая арматуру в виде стальных пластин, расположенных между ними промежуточных эластомерных слоев и наружного эластомерного слоя, отличающаяся тем, что промежуточные и наружный эластомерные слои выполнены из резины на основе комбинации бутилкаучука и этиленпропилендиенового каучука в соотношении 40-80% на 20-60% соответственно. Reinforced elastomeric support for engineering structures, containing reinforcement in the form of steel plates, intermediate elastomeric layers located between them and an external elastomeric layer, characterized in that the intermediate and external elastomeric layers are made of rubber based on a combination of butyl rubber and ethylene propylene diene rubber in a ratio of 40-80% 20-60% respectively.
RU97107142/03A 1997-04-29 1997-04-29 Reinforced elastomer support for engineering structures RU2120514C1 (en)