RU2097355C1 - Composition for manufacturing of protective material - Google Patents
Composition for manufacturing of protective material Download PDFInfo
- Publication number
- RU2097355C1 RU2097355C1 RU94017485A RU94017485A RU2097355C1 RU 2097355 C1 RU2097355 C1 RU 2097355C1 RU 94017485 A RU94017485 A RU 94017485A RU 94017485 A RU94017485 A RU 94017485A RU 2097355 C1 RU2097355 C1 RU 2097355C1
- Authority
- RU
- Russia
- Prior art keywords
- composition
- glass
- irradiation
- articles
- optical glass
- Prior art date
Abstract
Description
Изобретение относится к строительным материалам для защиты от ионизирующих излучений и может быть использовано для изготовления строительных деталей и конструкций. The invention relates to building materials for protection against ionizing radiation and can be used for the manufacture of building parts and structures.
Известна композиция, включающая жидкое стекло, функциональную добавку, в том числе кремнефторид щелочного металла и оксиды титана, кобальта и железа, наполнитель, в том числе измельченное стекло и сложный отвердитель [1]
Наиболее близкой к предлагаемой по технической сущности и достигаемому результату является композиция, включающая жидкое стекло, кремнефтористый калий и наполнитель, например хромит [2]
Недостатками указанных композиций являются низкие плотность и коэффициент ослабления гамма-лучей.A known composition comprising liquid glass, a functional additive, including alkali metal silicofluoride and oxides of titanium, cobalt and iron, a filler, including ground glass and a complex hardener [1]
Closest to the proposed technical essence and the achieved result is a composition comprising water glass, potassium silicofluoride and a filler, such as chromite [2]
The disadvantages of these compositions are low density and attenuation coefficient of gamma rays.
Целью изобретения являются повышение плотности и коэффициента ослабления гамма-лучей. The aim of the invention is to increase the density and attenuation coefficient of gamma rays.
Поставленная цель достигается тем, что композиция, включающая жидкое стекло, кремнефтористый калий и наполнитель, в качестве наполнителя содержит смесь боя оптического стекла оксида свинца при следующем соотношении компонентов, мас. This goal is achieved in that the composition comprising liquid glass, potassium silicofluoride and a filler, as a filler, contains a mixture of a battle of optical glass of lead oxide in the following ratio of components, wt.
Жидкое стекло 7,9 8,6
Кремнефтористый калий 0,8 0,9
Оксид свинца 4,3 11,9
Бой оптического стекла 79,4 86,2
Для приготовления композиции используют жидкое натриевое стекло с силикатным модулем 3 и плотностью 1,475 г/см3 (ГОСТ 13078-81); оксид свинца с плотностью 8000 кг/м3; бой оптического стекла, химический состав которого характеризуется следующими данными: PbO 70,93; SiO2 27,00; As2O3 0,3; Na2O 0,5; K2O 1,27; плотность 5100 кг/м3.Liquid glass 7.9 8.6
Potassium silicofluoride 0.8 0.9
Lead oxide 4.3 11.9
Optical Glass Fight 79.4 86.2
To prepare the composition, liquid sodium glass with a
Бой оптического стекла (являющийся отходом производства оптического стекла) подвергают помолу и рассвету. Гранулометрический состав используемого боя оптического стекла представлен следующими фракциями, мас. The battle of optical glass (which is a waste of the production of optical glass) is subjected to grinding and dawn. The granulometric composition of the used optical glass battle is represented by the following fractions, wt.
Фракции 1,25 0,63 50
Фракции 0,63 0,313 мм 25
Фракции 0,315 0,14 мм 12,5
Фракции 0,14 мм 12,5
Композицию готовят следующим образом. В жидкое стекло вводят кремнефтористый калий, перемешивают, добавляют смесь боя оптического стекла и оксида свинца, после чего вновь перемешивают. Образцы цилиндры высотой 50 мм и диаметром 30 мм изготавливают прессованием при давлении 135 МПа. В табл. 1 приведены составы композиции, в табл. 2 физико-механические показатели изделий. Линейный коэффициент ослабления определялся при облучении источником Cs -137.Fractions 1.25 0.63 50
Fractions 0.63 0.313 mm 25
Fractions 0.315 0.14 mm 12.5
Fractions 0.14 mm 12.5
The composition is prepared as follows. Potassium silicofluoride is introduced into the liquid glass, mixed, a mixture of optical glass and lead oxide is added, and then mixed again. Samples of cylinders with a height of 50 mm and a diameter of 30 mm are made by pressing at a pressure of 135 MPa. In the table. 1 shows the composition, in table. 2 physical and mechanical properties of products. The linear attenuation coefficient was determined upon exposure to a Cs -137 source.
Claims (1)
Кремнефтористый калий 0,8 0,9
Бой оптического стекла 79,4 86,2
Оксид свинца 4,3 11,9мLiquid glass 7.9 8.6
Potassium silicofluoride 0.8 0.9
Optical Glass Fight 79.4 86.2
Lead oxide 4.3 11.9m