RU2022989C1

RU2022989C1 - Method for making protective coat

Info

Publication number: RU2022989C1
Authority: RU
Inventors: Л.Т. Смола; С.В. Гуренко
Original assignee: Смола Любовь Тимофеевна
Priority date: 1989-07-06
Filing date: 1989-07-06
Publication date: 1994-11-15

Abstract

FIELD: corrosion- protecting pipe treatment. SUBSTANCE: a metallic surface is coated with mastic composition comprising 1.0-1.5 parts by weight of benzoic acid and 5 parts by weight of mixture consisting of varnish " КОРПС " prepared from copolymerization product of styrene rectification still residue with maleic anhydride and chrysotile asbestos in varnish-asbestos ratio of 35:65 % by weight followed by drying the resulting coat at temperatures of 50-90 C for 15-20 min. until the full cure. EFFECT: increased corrosion-proof capacity. 2 tbl

Description

Изобретение относится к области эксплуатации трубопроводов, непосредственно к защите от коррозии металлических поверхностей. The invention relates to the field of operation of pipelines, directly to the protection against corrosion of metal surfaces.

Наиболее близким к заявляемому способу является способ получения покрытия, который включает в себя нанесение на трубы мастики, содержащей полистирольную смолу КОРС, асбест хризотиловый, органический растворитель, смолу СПП, и последующее отверждение мастики при 55-60^оС в течение 2-3 ч.The closest to the claimed method is a method of producing a coating, which comprises applying to the mastic tubes containing polystyrene resin Corso, chrysotile asbestos, an organic solvent, the resin CPR, and subsequent curing mastic at 55-60 ^{° C} for 2-3 hours.

По данному способу получают покрытие с недостаточной адгезией и низкой стойкостью к абразивному износу. According to this method, a coating with insufficient adhesion and low resistance to abrasion is obtained.

Технической задачей изобретения является повышение адгезии и стойкости покрытия к абразивному износу. An object of the invention is to increase the adhesion and resistance of the coating to abrasion.

Технический результат достигается тем, что в способе получения защитного покрытия путем нанесения на металлическую поверхность мастики на основе сополимера кубового остатка ректификации стирола и последующего отверждения покрытия, на поверхность наносят мастику, содержащую 1,0-1,5 мас.ч. бензойной кислоты на 5 мас.ч. смеси лака "Корс" на основе сополимера кубового остатка ректификации стирола с малеиновым ангидридом и асбеста хризотилового в массовом соотношении 35-65. Лак "КОРС" представляет собой раствор сополимера стирола с малеиновым ангидридом в ксилоле. ТУ 38.403200-87. The technical result is achieved by the fact that in the method of obtaining a protective coating by applying mastic on the metal surface based on a copolymer of distillation of styrene rectification and subsequent curing of the coating, a mastic containing 1.0-1.5 parts by weight is applied to the surface. benzoic acid to 5 parts by weight a mixture of varnish "Kors" based on a copolymer of distillation distillation residue of styrene with maleic anhydride and chrysotile asbestos in a mass ratio of 35-65. KORS varnish is a solution of a copolymer of styrene with maleic anhydride in xylene. TU 38.403200-87.

Асбест хризотиловый ГОСТ 12871-83. Asbestos chrysotile GOST 12871-83.

Способ осуществляют следующим образом. Лак "КОРС" смешивают с асбестом хризотиловым, тщательно перемешивают и вводят бензойную кислоту. The method is as follows. KORS varnish is mixed with chrysotile asbestos, mixed thoroughly and benzoic acid is added.

Состав наносят в 2 слоя, предварительного отверждения не происходит. Каждый слой выдерживают на воздухе около 15 мин до "отлипа", затем подвергают термообработке в течение 1 ч. Начальное отверждение мастики начинается с 20 мин выдержки, а полное отверждение происходит после 2 ч выдержки в термошкафу при 50-70^оС.The composition is applied in 2 layers, preliminary curing does not occur. Each layer is allowed to stand in air for about 15 minutes to "tack", is then subjected to heat treatment for 1 hour. The initial curing mastic begins with 20 minutes exposure, and full curing occurs after 2 hours exposure in an oven at 50-70 ° ^C.

При толщине покрытия 0,65 мм, его адгезия составляет 1 балл, химстойкость за 24 ч 0,07% , водопоглощение 0,08%, прочность на удар - 5 н.м., эластичность 1 мм, переходное сопротивление - 7 cdot<N>10⁶ cdot<N>Ом cdot<N>м². Покрытие стойкое к кислотам и абразивному износу.With a coating thickness of 0.65 mm, its adhesion is 1 point, chemical resistance in 24 hours is 0.07%, water absorption is 0.08%, impact strength is 5 nm, elasticity is 1 mm, and transition resistance is 7 cdot <N > 10 ⁶ cdot <N> Ohm cdot <N> m ² . The coating is resistant to acids and abrasion.

Химстойкость определяли в водном растворе 3%-ного NaCl. Chemical resistance was determined in an aqueous solution of 3% NaCl.

Кислотостойкость, контактный метод. Acid resistance, contact method.

Claims

METHOD FOR PRODUCING PROTECTIVE COATING by applying mastic on the metal surface based on copolymer of styrene rectification distillation residue and subsequent curing of the coating, characterized in that a mastic containing 1.0-1.5 parts by weight is applied to the surface. benzoic acid to 5 parts by weight a mixture of varnish "Kors" based on a copolymer of distillation distillation residue of styrene with maleic anhydride and chrysotile asbestos in a mass ratio of 35: 65.