RU2015105523A - Раствор, улучшающий прозрачность диоксидциркониевой керамики - Google Patents

Раствор, улучшающий прозрачность диоксидциркониевой керамики Download PDF

Info

Publication number
RU2015105523A
RU2015105523A RU2015105523A RU2015105523A RU2015105523A RU 2015105523 A RU2015105523 A RU 2015105523A RU 2015105523 A RU2015105523 A RU 2015105523A RU 2015105523 A RU2015105523 A RU 2015105523A RU 2015105523 A RU2015105523 A RU 2015105523A
Authority
RU
Russia
Prior art keywords
solution
zirconia
product
mpa
mol
Prior art date
Application number
RU2015105523A
Other languages
English (en)
Inventor
Хольгер ГАУПТМАНН
Андреас ХЕРРМАНН
Брант Ю. КОЛБ
Original Assignee
3М Инновейтив Пропертиз Компани
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 3М Инновейтив Пропертиз Компани filed Critical 3М Инновейтив Пропертиз Компани
Publication of RU2015105523A publication Critical patent/RU2015105523A/ru

Abstract

1. Набор, содержащий:раствор,изделие из пористого диоксида циркония,необязательно принадлежности для нанесения,при этом раствор содержитпо меньшей мере один катион по меньшей мере одного агента, не придающего окраску, выбранный из ионов Y, Gd, La, Yb, Tm, Mg, Ca и их смесей,по меньшей мере один растворитель для по меньшей мере одного иона,необязательно по меньшей мере один комплексообразующий агент,необязательно по меньшей мере один загущающий агент,необязательно по меньшей мере одно органическое маркерное вещество,необязательно по меньшей мере одну добавку,причем изделие из пористого диоксида циркония характеризуется изотермой типа IV адсорбции и/или десорбции Nв соответствии с классификацией Международного союза теоретической и прикладной химии (IUPAC).2. Набор по п. 1, отличающийся тем, что изделие из пористого диоксида циркония характеризуется по меньшей мере одним из следующих признаков:петлей гистерезиса при анализе в отношении его поведения при адсорбции и десорбции азота;изотермой адсорбции и десорбции N, имеющей петлю гистерезиса типа H1 в соответствии с классификацией IUPAC;изотермой адсорбции и десорбции N, имеющей петлю гистерезиса в интервале p/p0,70-0,95;средним диаметром связанных пор от приблизительно 10 нм до приблизительно 100 нм, или от приблизительно 10 нм до приблизительно 80 нм, или от приблизительно 10 нм до приблизительно 50 нм;средним размером зерна менее приблизительно 100 нм;удельной поверхностью по методу БЭТ от приблизительно 10 м/г до приблизительно 200 м/г, или от приблизительно 15 м/г до приблизительно 100 м/г, или от приблизительно 16 м/г до приблизительно 60 м/г;прочностью на изгиб по двум осям от приблизительно 10 МПа до приблизительно 40 МПа или от приблизительно 15 МПа до

Claims (15)

1. Набор, содержащий:
раствор,
изделие из пористого диоксида циркония,
необязательно принадлежности для нанесения,
при этом раствор содержит
по меньшей мере один катион по меньшей мере одного агента, не придающего окраску, выбранный из ионов Y, Gd, La, Yb, Tm, Mg, Ca и их смесей,
по меньшей мере один растворитель для по меньшей мере одного иона,
необязательно по меньшей мере один комплексообразующий агент,
необязательно по меньшей мере один загущающий агент,
необязательно по меньшей мере одно органическое маркерное вещество,
необязательно по меньшей мере одну добавку,
причем изделие из пористого диоксида циркония характеризуется изотермой типа IV адсорбции и/или десорбции N2 в соответствии с классификацией Международного союза теоретической и прикладной химии (IUPAC).
2. Набор по п. 1, отличающийся тем, что изделие из пористого диоксида циркония характеризуется по меньшей мере одним из следующих признаков:
петлей гистерезиса при анализе в отношении его поведения при адсорбции и десорбции азота;
изотермой адсорбции и десорбции N2, имеющей петлю гистерезиса типа H1 в соответствии с классификацией IUPAC;
изотермой адсорбции и десорбции N2, имеющей петлю гистерезиса в интервале p/p0 0,70-0,95;
средним диаметром связанных пор от приблизительно 10 нм до приблизительно 100 нм, или от приблизительно 10 нм до приблизительно 80 нм, или от приблизительно 10 нм до приблизительно 50 нм;
средним размером зерна менее приблизительно 100 нм;
удельной поверхностью по методу БЭТ от приблизительно 10 м2/г до приблизительно 200 м2/г, или от приблизительно 15 м2/г до приблизительно 100 м2/г, или от приблизительно 16 м2/г до приблизительно 60 м2/г;
прочностью на изгиб по двум осям от приблизительно 10 МПа до приблизительно 40 МПа или от приблизительно 15 МПа до приблизительно 30 МПа;
геометрическим размером в направлениях x, y, z по меньшей мере приблизительно 5 мм, или по меньшей мере приблизительно 10 мм, или по меньшей мере приблизительно 20 мм;
твердостью по Виккерсу от приблизительно 25 до приблизительно 150.
3. Набор по п. 1, отличающийся тем, что изделие из пористого диоксида циркония характеризуется по меньшей мере одним из следующих признаков:
содержанием ZrO2 от приблизительно 70 мол.% до приблизительно 98 мол.%;
содержанием HfO2 от приблизительно 0 мол.% до приблизительно 2 мол.%;
содержанием Y2O3 от приблизительно 1 мол.% до приблизительно 15 мол.%;
содержанием Al2O3 от приблизительно 0 мол.% до приблизительно 1 мол.%.
4. Набор п. 1, отличающийся тем, что изделие из пористого диоксида циркония получено посредством термообработки аэрогеля диоксида циркония.
5. Набор по п. 1, отличающийся тем, что раствор характеризуется по меньшей мере одним из следующих признаков:
по меньшей мере один катион по меньшей мере одного агента, не придающего окраску, присутствует в количестве от приблизительно 0,3 моль на л растворителя до приблизительно 5 моль на л растворителя,
по меньшей мере один загущающий агент присутствует в количестве от приблизительно 0 вес.% до приблизительно 0,1 вес.%,
по меньшей мере один комплексообразующий агент присутствует в количестве от приблизительно 0 моль на л растворителя до приблизительно 3 моль на л растворителя,
по меньшей мере одно органическое маркерное вещество присутствует в количестве от приблизительно 0 вес.% до приблизительно 5 вес.%,
по меньшей мере одна добавка присутствует в количестве от приблизительно 0 вес. % до приблизительно 5 вес.%,
при этом вес.% указаны по отношению к весу всего состава.
6. Набор по п. 1, отличающийся тем, что раствор характеризуется по меньшей мере одним из следующих признаков:
по меньшей мере один растворитель выбран из воды, спиртов, кетонов и их смесей;
по меньшей мере один комплексообразующий агент, если он присутствует, выбран из ацетилацетоната, краун-эфиров, криптандов, этилендиаминтриацетата и его солей, этилендиаминтетраацетата и его солей, нитрилотриацетата и его солей, лимонной кислоты и ее солей, триэтилентетрамина, порфина, полиакрилата, полиаспартата, кислотных пептидов, фталоцианина, салицилата, глицината, лактата, пропилендиамина, аскорбата, щавелевой кислоты и ее солей и их смесей;
по меньшей мере один загущающий агент, если он присутствует, выбран из по меньшей мере одного полиола, по меньшей мере одного гликолевого эфира, по меньшей мере одного ди- и полиспирта, простого эфира глицерина, по меньшей мере одного полисахарида, ксантановой камеди, метилцеллюлозы и их смесей;
по меньшей мере одно органическое маркерное вещество, если оно присутствует, выбрано из пищевых красителей и их смесей;
по меньшей мере одна добавка, если она присутствует, выбрана из по меньшей мере одного буферного раствора, по меньшей мере одного консерванта, по меньшей мере одного стабилизатора и их смесей.
7. Набор по п. 1, отличающийся тем, что раствор характеризуется по меньшей мере одним из следующих признаков:
значением pH в интервале 0-9;
вязкостью от приблизительно 1 мПа·с до приблизительно 10000 мПа·с;
по существу не поглощает свет в диапазоне от приблизительно 380 нм до приблизительно 740 нм;
характеризуется контрастом пропускания света более приблизительно 80%;
является неокрашенным;
является устойчивым при хранении.
8. Набор по п. 1, отличающийся тем, что раствор не содержит по меньшей мере один из следующих компонентов:
придающие окраску ионы, выбранные из Fe, Mn, Er, Pr, V, Cr, Co, Mo и их смесей, в количестве более приблизительно 2 вес.% по отношению к весу раствора,
твердые частицы, оседающие из раствора при хранении в течение более приблизительно 2 часов.
9. Способ улучшения прозрачности диоксидциркониевого изделия, включающий этапы, на которых:
обеспечивают изделие из пористого диоксида циркония по п. 1 и раствор по п. 1,
наносят раствор по меньшей мере на часть наружной поверхности изделия из пористого диоксида циркония,
необязательно высушивают изделие из пористого диоксида циркония с предыдущего этапа,
спекают изделие из пористого диоксида циркония с получением диоксидциркониевого керамического изделия.
10. Диоксидциркониевое керамическое изделие, полученное способом по п. 1.
11. Диоксидциркониевое керамическое изделие по п. 10, отличающееся тем, что диоксидциркониевое керамическое изделие имеет форму стоматологического керамического изделия.
12. Диоксидциркониевое керамическое изделие по п. 10, отличающееся тем, что стоматологическое керамическое изделие имеет форму коронки, моста, вкладки, накладки, винира, фасетки, колпачка, каркаса коронок и мостов, имплантата, опорной коронки, ортодонтических аппаратов и их деталей.
13. Диоксидциркониевое керамическое изделие по п. 10, отличающееся тем, что стоматологическое керамическое изделие содержит по меньшей мере два участка А и В, причем участок А обработан раствором, охарактеризованным в п. 1, а участок В не обработан раствором, охарактеризованным в п. 1.
14. Применение раствора, охарактеризованного в п. 1, для улучшения прозрачности диоксидциркониевого изделия, в частности стоматологического керамического изделия по п. 12.
15. Применение по п. 14, отличающееся тем, что диоксидциркониевое изделие перед спеканием характеризуется следующими признаками:
изотермой типа IV адсорбции N2 в соответствии с классификацией IUPAC,
изотермой адсорбции и десорбции N2, имеющей петлю гистерезиса типа H1 в соответствии с классификацией IUPAC, в частности в интервале p/p0 0,70-0,95;
средним диаметром связанных пор от приблизительно 10 нм до приблизительно 100 нм,
средним размером зерна менее приблизительно 100 нм,
удельной поверхностью по методу БЭТ от приблизительно 10 м2/г до приблизительно 200 м2/г, или от приблизительно 15 м2/г до приблизительно 100 м2/г, или от приблизительно 16 м2/г до приблизительно 60 м2/г,
прочностью на изгиб по двум осям от приблизительно 10 МПа до приблизительно 40 МПа,
геометрическим размером в направлениях x, y, z по меньшей мере приблизительно 5 мм,
твердостью по Виккерсу от приблизительно 25 до приблизительно 150,
плотностью от приблизительно 40% до приблизительно 60% от теоретической плотности.
RU2015105523A 2012-08-03 2013-03-08 Раствор, улучшающий прозрачность диоксидциркониевой керамики RU2015105523A (ru)