RU2013104502A - Биоразлагаемые пленки - Google Patents

Биоразлагаемые пленки Download PDF

Info

Publication number
RU2013104502A
RU2013104502A RU2013104502/05A RU2013104502A RU2013104502A RU 2013104502 A RU2013104502 A RU 2013104502A RU 2013104502/05 A RU2013104502/05 A RU 2013104502/05A RU 2013104502 A RU2013104502 A RU 2013104502A RU 2013104502 A RU2013104502 A RU 2013104502A
Authority
RU
Russia
Prior art keywords
film
biodegradable
weight
oxidized starch
polyester
Prior art date
Application number
RU2013104502/05A
Other languages
English (en)
Other versions
RU2575265C2 (ru
Inventor
Бо ШИ
Джеймс Х. ВАНГ
Original Assignee
Кимберли-Кларк Ворлдвайд, Инк.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Кимберли-Кларк Ворлдвайд, Инк. filed Critical Кимберли-Кларк Ворлдвайд, Инк.
Publication of RU2013104502A publication Critical patent/RU2013104502A/ru
Application granted granted Critical
Publication of RU2575265C2 publication Critical patent/RU2575265C2/ru

Abstract

1. Биоразлагаемая пленка, отличающаяся тем, что она содержит:от около 1 мас.% до около 49 мас.% от массы пленки матричной фазы, содержащей по меньшей мере один биоразлагаемый сложный полиэфир; иот около 46 мас.% до около 75 мас.% от массы пленки диспергированной фазы, содержащей по меньшей мере один окисленный крахмал и по меньшей мере один пластификатор;где диспергированная фаза диспергирована в матричной фазе, а также где мас.% матричной фазы от массы пленки меньше, чем мас.% диспергированной фазы от массы пленки.2. Биоразлагаемая пленка по п.1, отличающаяся тем, что биоразлагаемым сложным полиэфиром является алифатический сложный полиэфир, алифатический-ароматический сложный полиэфир или их сочетание.3. Биоразлагаемая пленка по п.1, где биоразлагаемый сложный полиэфир составляет от около 20 мас.% до около 43 мас.% от массы пленки.4. Биоразлагаемая пленка по п.1, где окисленный крахмал составляет от около 45 мас.% до около 75 мас.% от массы пленки.5. Биоразлагаемая пленка по п.1, где пластификатор составляет от около 5 мас.% до около 30 мас.% от массы пленки.6. Биоразлагаемая пленка по п.1, где окисленным крахмалом является модифицированный окисленный крахмал.7. Биоразлагаемая пленка по п.6, где модифицированным окисленным крахмалом является сложный эфир крахмала, простой эфир крахмала, гидролизованный крахмал или их сочетание.8. Биоразлагаемая пленка по п.1, где пластификатором является многоатомный спирт.9. Биоразлагаемая пленка по п.1, где пленка имеет толщину около 50 мкм или менее.10. Биоразлагаемая пленка по п.1, где пленка имеет коэффициент эластичности в сухом состоянии от около 50 до около 100 МПа в направлении обработки.11. Биоразлагаем�

Claims (20)

1. Биоразлагаемая пленка, отличающаяся тем, что она содержит:
от около 1 мас.% до около 49 мас.% от массы пленки матричной фазы, содержащей по меньшей мере один биоразлагаемый сложный полиэфир; и
от около 46 мас.% до около 75 мас.% от массы пленки диспергированной фазы, содержащей по меньшей мере один окисленный крахмал и по меньшей мере один пластификатор;
где диспергированная фаза диспергирована в матричной фазе, а также где мас.% матричной фазы от массы пленки меньше, чем мас.% диспергированной фазы от массы пленки.
2. Биоразлагаемая пленка по п.1, отличающаяся тем, что биоразлагаемым сложным полиэфиром является алифатический сложный полиэфир, алифатический-ароматический сложный полиэфир или их сочетание.
3. Биоразлагаемая пленка по п.1, где биоразлагаемый сложный полиэфир составляет от около 20 мас.% до около 43 мас.% от массы пленки.
4. Биоразлагаемая пленка по п.1, где окисленный крахмал составляет от около 45 мас.% до около 75 мас.% от массы пленки.
5. Биоразлагаемая пленка по п.1, где пластификатор составляет от около 5 мас.% до около 30 мас.% от массы пленки.
6. Биоразлагаемая пленка по п.1, где окисленным крахмалом является модифицированный окисленный крахмал.
7. Биоразлагаемая пленка по п.6, где модифицированным окисленным крахмалом является сложный эфир крахмала, простой эфир крахмала, гидролизованный крахмал или их сочетание.
8. Биоразлагаемая пленка по п.1, где пластификатором является многоатомный спирт.
9. Биоразлагаемая пленка по п.1, где пленка имеет толщину около 50 мкм или менее.
10. Биоразлагаемая пленка по п.1, где пленка имеет коэффициент эластичности в сухом состоянии от около 50 до около 100 МПа в направлении обработки.
11. Биоразлагаемая пленка по п.1, где пленка имеет удлинение при разрыве в направлении обработки более 500%.
12. Покровная пленка, содержащая биоразлагаемую пленку по п.1 и разделительный агент, нанесенный на ее поверхность.
13. Абсорбирующее изделие, содержащее биоразлагаемую пленку по п.1, где абсорбирующее изделие имеет прилегающую к телу часть, которая включает проницаемое для жидкости верхнее покрытие, в общем непроницаемое для жидкости нижнее покрытие и абсорбирующую середину, расположенную между нижним покрытием и верхним покрытием.
14. Абсорбирующее изделие по п.13, где нижнее покрытие включает биоразлагаемую пленку.
15. Абсорбирующее изделие по п.13, также содержащее покровную пленку, которая определяет первую поверхность и противоположную вторую поверхность, где первая поверхность расположена рядом с адгезивом, нанесенным на абсорбирующее изделие, где покровная пленка включает биоразлагаемую пленку.
16. Мешок, обертка или пакет, содержащий биоразлагаемую пленку по п.1.
17. Абсорбирующее изделие, имеющее прилегающую к телу часть, которая включает проницаемое для жидкости верхнее покрытие, в общем непроницаемое для жидкости нижнее покрытие и абсорбирующую середину, расположенную между нижним покрытием и верхним покрытием, где абсорбирующее изделие также включает покровную пленку, которая определяет первую поверхность и противоположную вторую поверхность, где первая поверхность расположена рядом с адгезивом, нанесенным на абсорбирующее изделие, где покровная пленка, нижнее покрытие или оба содержат от около 1 мас.% до около 49 мас.% матричной фазы, содержащей по меньшей мере один биоразлагаемый сложный полиэфир, и от около 46 мас.% до около 75 мас.% диспергированной фазы, содержащей по меньшей мере один окисленный крахмал и по меньшей мере один пластификатор, где диспергированная фаза диспергирована в матричной фазе, и где мас.% матричной фазы меньше, чем мас.% диспергированной фазы.
18. Абсорбирующее изделие по п.17, где окисленный крахмал составляет от около 45 мас.% до около 75 мас.% от массы пленки.
19. Абсорбирующее изделие по п.17, где пластификатор составляет от около 5 мас.% до около 30 мас.% от массы пленки.
20. Биоразлагаемая пленка, отличающаяся тем, что она содержит:
от около 1 мас.% до около 49 мас.% от массы пленки по меньшей мере одного биоразлагаемого сложного полиэфира; и
от около 46 мас.% до около 75 мас.% от массы пленки термопластичного окисленного крахмала, содержащего по меньшей мере один окисленный крахмал и по меньшей мере один пластификатор;
где мас.% биоразлагаемого сложного полиэфира от массы пленки меньше, чем мас.% термопластичного окисленного крахмала от массы пленки.
RU2013104502/05A 2010-07-19 2011-06-16 Биоразлагаемые пленки RU2575265C2 (ru)