RU2011124562A - METHOD FOR PRODUCING MULTI-FUNCTIONAL COATING ON ORGANIC GLASS - Google Patents

METHOD FOR PRODUCING MULTI-FUNCTIONAL COATING ON ORGANIC GLASS Download PDF

Info

Publication number
RU2011124562A
RU2011124562A RU2011124562/05A RU2011124562A RU2011124562A RU 2011124562 A RU2011124562 A RU 2011124562A RU 2011124562/05 A RU2011124562/05 A RU 2011124562/05A RU 2011124562 A RU2011124562 A RU 2011124562A RU 2011124562 A RU2011124562 A RU 2011124562A
Authority
RU
Russia
Prior art keywords
solution
filler
polymer binder
indium
colloidal
Prior art date
Application number
RU2011124562/05A
Other languages
Russian (ru)
Other versions
RU2485063C2 (en
Inventor
Владимир Васильевич Викулин
Вячеслав Иванович Самсонов
Александр Викторович Агафонов
Ольга Ивановна Давыдова
Вячеслав Николаевич Тростин
Original Assignee
Федеральное государственное унитарное предприятие "Обнинское научно-производственное предприятие "Технология"
Российская Федерация, от имени которой выступает Министерство промышленности и торговли Российской Федерации (Минпромторг России)
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Федеральное государственное унитарное предприятие "Обнинское научно-производственное предприятие "Технология", Российская Федерация, от имени которой выступает Министерство промышленности и торговли Российской Федерации (Минпромторг России) filed Critical Федеральное государственное унитарное предприятие "Обнинское научно-производственное предприятие "Технология"
Priority to RU2011124562/05A priority Critical patent/RU2485063C2/en
Publication of RU2011124562A publication Critical patent/RU2011124562A/en
Application granted granted Critical
Publication of RU2485063C2 publication Critical patent/RU2485063C2/en

Abstract

1. Способ получения многофункционального покрытия на органическом стекле, включающий нанесение пленкообразующих полимерных растворов с последующей термообработкой, отличающийся тем, что в качестве полимерных растворов используют тетрагидрофурановые растворы полимерного связующего и наноразмерного неорганического наполнителя в виде растворов оксидов индия и олова, коллоидного золота или коллоидной меди, которые поочередно наносят на органическое стекло, при этом вначале наносят слой раствора полимерного связующего с наполнителем в виде раствора оксидов индия и олова, затем слой раствора полимерного связующего с наполнителем в виде раствора коллоидного золота или коллоидной меди, затем еще слой полимерного связующего с наполнителем в виде раствора оксидов индия и олова, причем концентрация наполнителя в виде раствора оксидов индия и олова, взятых в соотношении 9:1 по массе, составляет 1,0-2,0% от массы всего раствора покрытия, концентрация наполнителя в виде раствора коллоидного золота составляет 0,1-0,2% от массы всего раствора покрытия, а концентрация наполнителя в виде раствора коллоидной меди составляет 0,2-0,5% от массы всего раствора покрытия.2. Способ по п.1, отличающийся тем, что в качестве полимерного связующего используют раствор метилметакрилата и сополимера 3-меркаптопропилтриметоксисилана.1. A method of obtaining a multifunctional coating on organic glass, including applying a film-forming polymer solutions followed by heat treatment, characterized in that tetrahydrofuran solutions of a polymer binder and nanoscale inorganic filler in the form of solutions of indium and tin oxides, colloidal gold or colloidal copper are used as polymer solutions which are alternately applied to organic glass, while first applying a layer of a polymer binder solution with a filler in the form of a solution of indium and tin oxides, then a layer of a polymer binder solution with a filler in the form of a solution of colloidal gold or colloidal copper, then another layer of a polymer binder with a filler in the form of a solution of indium and tin oxides, and the concentration of the filler in the form of a solution of indium and tin oxides, taken in a ratio of 9: 1 by weight, is 1.0-2.0% by weight of the total coating solution, the filler concentration in the form of a colloidal gold solution is 0.1-0.2% by weight of the total coating solution, and the filler concentration in view colloidal solution of copper is 0.2-0.5% by weight of the total solution pokrytiya.2. The method according to claim 1, characterized in that a solution of methyl methacrylate and a copolymer of 3-mercaptopropyltrimethoxysilane is used as the polymer binder.

Claims (2)

1. Способ получения многофункционального покрытия на органическом стекле, включающий нанесение пленкообразующих полимерных растворов с последующей термообработкой, отличающийся тем, что в качестве полимерных растворов используют тетрагидрофурановые растворы полимерного связующего и наноразмерного неорганического наполнителя в виде растворов оксидов индия и олова, коллоидного золота или коллоидной меди, которые поочередно наносят на органическое стекло, при этом вначале наносят слой раствора полимерного связующего с наполнителем в виде раствора оксидов индия и олова, затем слой раствора полимерного связующего с наполнителем в виде раствора коллоидного золота или коллоидной меди, затем еще слой полимерного связующего с наполнителем в виде раствора оксидов индия и олова, причем концентрация наполнителя в виде раствора оксидов индия и олова, взятых в соотношении 9:1 по массе, составляет 1,0-2,0% от массы всего раствора покрытия, концентрация наполнителя в виде раствора коллоидного золота составляет 0,1-0,2% от массы всего раствора покрытия, а концентрация наполнителя в виде раствора коллоидной меди составляет 0,2-0,5% от массы всего раствора покрытия.1. A method of obtaining a multifunctional coating on organic glass, including applying a film-forming polymer solutions followed by heat treatment, characterized in that tetrahydrofuran solutions of a polymer binder and nanoscale inorganic filler in the form of solutions of indium and tin oxides, colloidal gold or colloidal copper are used as polymer solutions which are alternately applied to organic glass, while first applying a layer of a polymer binder solution with a filler in the form of a solution of indium and tin oxides, then a layer of a polymer binder solution with a filler in the form of a solution of colloidal gold or colloidal copper, then another layer of a polymer binder with a filler in the form of a solution of indium and tin oxides, and the concentration of the filler in the form of a solution of indium and tin oxides, taken in a ratio of 9: 1 by weight, is 1.0-2.0% by weight of the total coating solution, the filler concentration in the form of a colloidal gold solution is 0.1-0.2% by weight of the total coating solution, and the filler concentration in view colloidal solution of copper is 0.2-0.5% by weight of the total coating solution. 2. Способ по п.1, отличающийся тем, что в качестве полимерного связующего используют раствор метилметакрилата и сополимера 3-меркаптопропилтриметоксисилана. 2. The method according to claim 1, characterized in that a solution of methyl methacrylate and a copolymer of 3-mercaptopropyltrimethoxysilane is used as the polymer binder.
RU2011124562/05A 2011-06-16 2011-06-16 Method of producing multifunctional coating on organic glass RU2485063C2 (en)