RU2008118260A - METHOD FOR PRODUCING SHEETS FROM TITANIUM ALLOY Ti-6Al-4V - Google Patents

METHOD FOR PRODUCING SHEETS FROM TITANIUM ALLOY Ti-6Al-4V Download PDF

Info

Publication number
RU2008118260A
RU2008118260A RU2008118260/02A RU2008118260A RU2008118260A RU 2008118260 A RU2008118260 A RU 2008118260A RU 2008118260/02 A RU2008118260/02 A RU 2008118260/02A RU 2008118260 A RU2008118260 A RU 2008118260A RU 2008118260 A RU2008118260 A RU 2008118260A
Authority
RU
Russia
Prior art keywords
annealing
cold rolling
tpp
deformation
carried out
Prior art date
Application number
RU2008118260/02A
Other languages
Russian (ru)
Other versions
RU2381296C1 (en
Inventor
Александр Николаевич Козлов (RU)
Александр Николаевич Козлов
Андрей Владимирович Зайцев (RU)
Андрей Владимирович Зайцев
Виталий Анатольевич Михайлов (RU)
Виталий Анатольевич Михайлов
Original Assignee
Открытое Акционерное Общество "Корпорация ВСМПО-АВИСМА" (RU)
Открытое Акционерное Общество "Корпорация Всмпо-Ависма"
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Открытое Акционерное Общество "Корпорация ВСМПО-АВИСМА" (RU), Открытое Акционерное Общество "Корпорация Всмпо-Ависма" filed Critical Открытое Акционерное Общество "Корпорация ВСМПО-АВИСМА" (RU)
Priority to RU2008118260/02A priority Critical patent/RU2381296C1/en
Publication of RU2008118260A publication Critical patent/RU2008118260A/en
Application granted granted Critical
Publication of RU2381296C1 publication Critical patent/RU2381296C1/en

Abstract

Способ получения листов из титанового сплава Ti-6Al-4V, включающий предварительную обработку заготовки перед холодной прокаткой, холодную прокатку, отжиг, резку листов и отделочные операции, отличающийся тем, что предварительную заготовку получают последовательной ковкой или штамповкой слитка в β, α+β областях, полученный сляб прокатывают в черновой клети при температуре металла (Тпп+10)±10°C с суммарной степенью деформации 80-95% и в чистовой клети при температуре металла (Тпп+30)±10°C с суммарной степенью деформации 60-85% рулонным способом, с последующим травлением и отжигом, а холодную прокатку ведут рулонным методом за несколько циклов до получения полуфабриката заданной толщины и микроструктуры, при этом каждый цикл включает холодную прокатку с суммарной степенью деформации 10-25%, отжиг и травление, отжиг на всех переделах производят при температуре (Тпп-100…170)±10°C, кроме последнего цикла холодной прокатки, в котором отжиг осуществляют при температуре (Тпп-170…220)±10°C.A method of producing sheets of titanium alloy Ti-6Al-4V, including pre-treatment of the workpiece before cold rolling, cold rolling, annealing, sheet cutting and finishing operations, characterized in that the preliminary workpiece is obtained by sequential forging or stamping of the ingot in β, α + β areas , the resulting slab is rolled in a roughing stand at a metal temperature (TPP + 10) ± 10 ° C with a total degree of deformation of 80-95% and in a finishing stand at a metal temperature (TPP + 30) ± 10 ° C with a total degree of deformation of 60-85 % roll method, with after by etching and annealing, and cold rolling is carried out by the roll method for several cycles until a semi-finished product of a given thickness and microstructure is obtained, each cycle including cold rolling with a total degree of deformation of 10-25%, annealing and etching, annealing at all stages, is carried out at a temperature ( TPP-100 ... 170) ± 10 ° C, except for the last cold rolling cycle, in which annealing is carried out at a temperature of (TPP-170 ... 220) ± 10 ° C.

Claims (1)

Способ получения листов из титанового сплава Ti-6Al-4V, включающий предварительную обработку заготовки перед холодной прокаткой, холодную прокатку, отжиг, резку листов и отделочные операции, отличающийся тем, что предварительную заготовку получают последовательной ковкой или штамповкой слитка в β, α+β областях, полученный сляб прокатывают в черновой клети при температуре металла (Тпп+10)±10°C с суммарной степенью деформации 80-95% и в чистовой клети при температуре металла (Тпп+30)±10°C с суммарной степенью деформации 60-85% рулонным способом, с последующим травлением и отжигом, а холодную прокатку ведут рулонным методом за несколько циклов до получения полуфабриката заданной толщины и микроструктуры, при этом каждый цикл включает холодную прокатку с суммарной степенью деформации 10-25%, отжиг и травление, отжиг на всех переделах производят при температуре (Тпп-100…170)±10°C, кроме последнего цикла холодной прокатки, в котором отжиг осуществляют при температуре (Тпп-170…220)±10°C.A method of producing sheets of titanium alloy Ti-6Al-4V, including pre-treatment of the workpiece before cold rolling, cold rolling, annealing, sheet cutting and finishing operations, characterized in that the preliminary workpiece is obtained by sequential forging or stamping of the ingot in β, α + β areas , the resulting slab is rolled in a roughing stand at a metal temperature (TPP + 10) ± 10 ° C with a total degree of deformation of 80-95% and in a finishing stand at a metal temperature (TPP + 30) ± 10 ° C with a total degree of deformation of 60-85 % roll method, with after by etching and annealing, and cold rolling is carried out by the roll method for several cycles until a semi-finished product of a given thickness and microstructure is obtained, each cycle including cold rolling with a total degree of deformation of 10-25%, annealing and etching, annealing at all stages, is carried out at a temperature ( TPP-100 ... 170) ± 10 ° C, except for the last cold rolling cycle, in which annealing is carried out at a temperature of (TPP-170 ... 220) ± 10 ° C.
RU2008118260/02A 2008-05-07 2008-05-07 METHOD OF RECEIVING OF SHEETS FROM TITANIUM ALLOY Ti-6Al-4V RU2381296C1 (en)