RU1709613C - Process for manufacture of collagen

Info

Publication number: RU1709613C
Authority: RU
Inventors: О.И. Левина; Л.З. Чернышева; Л.П. Истранов
Original assignee: Казанское производственное объединение "Татхимфармпрепараты"
Priority date: 1990-04-12
Filing date: 1990-04-12
Publication date: 1995-01-09

Abstract

FIELD: medicine and pharmaceutical industry. SUBSTANCE: essence of this method resides in comminuting catgut waste, treating it with 10-percent solution containing 2 % sodium chloride during 24 h, dissolving stock in sodium hydroxide saturated by sodium sulfate during 24 h, neutralizing resultant solution with boric acid, and finally pressing out and freezing thus produced collagen. EFFECT: desired collagen product possesses solubility 1.4 to 2.0 times as high as prior art and purity 1.2 times as high.

Description

Изобретение относится к области медицины и фармацевтической промышленности, а именно к технологии получения коллагена для изготовления лекарственных форм. The invention relates to the field of medicine and the pharmaceutical industry, in particular to a technology for producing collagen for the manufacture of dosage forms.

Цель предложенного способа - повышение чистоты целевого продукта и его растворимости. The purpose of the proposed method is to increase the purity of the target product and its solubility.

Способ осуществляют следующим образом. The method is as follows.

В качестве сырья для получения коллагена используют отходы производства кетгута, которые измельчают и обрабатывают раствором пероксида водорода с добавлением хлорида натрия, что интенсифицирует процесс растворения сухих отходов кетгута и позволяет получить отбеленную и пластичную коллагеновую массу. Catgut production waste is used as a raw material for collagen production, which is ground and treated with a solution of hydrogen peroxide with the addition of sodium chloride, which intensifies the process of dissolving dry catgut waste and allows to obtain a bleached and plastic collagen mass.

П р и м е р 1. Отходы производства кетгута измельчают до размеров длиной 10 мм и обрабатывают 10%-ным раствором пероксида водорода, содержащим 2% хлорида натрия, для отбеливания и набухания в течение 24 ч. Затем растворяют с помощью щелочного денатурирующего процесса в 10-12%-ном растворе гидроокиси натрия, насыщенном сульфатом натрия, в течение 24 ч при 20-25^оС. Нейтрализацию осуществляют с помощью 3% -ного раствора борной кислоты. Далее коллагеновую массу промывают проточной и дистиллированной водой до получения стекловидной прозрачной массы. Остатки воды механически отжимают и коллагеновую нейтральную массу с содержанием сухого вещества 7-10% по сухому остатку замораживают при температуре ниже 0^оС до дальнейшего использования.PRI me R 1. Catgut production wastes are ground to 10 mm length and treated with 10% hydrogen peroxide solution containing 2% sodium chloride for bleaching and swelling for 24 hours. Then, they are dissolved using an alkaline denaturing process in 10-12% solution of sodium hydroxide saturated with sodium sulfate for 24 hours at 20-25 ^C. The neutralization is carried out using a 3% boric acid solution. Next, the collagen mass is washed with running and distilled water until a glassy transparent mass is obtained. Residual water is mechanically squeezed and neutral collagen mass with a solids content of 7-10% on a dry residue is frozen at a temperature below 0 ° ^C until further use.

Полученная таким образом коллагеновая масса может быть использована как основа для приготовления различных лекарственных форм, например коллагеновых мазей и кремов, пленок и губок в сочетании с различными лекарственными формами. The collagen mass obtained in this way can be used as the basis for the preparation of various dosage forms, for example, collagen ointments and creams, films and sponges in combination with various dosage forms.

Использование предлагаемого способа получения коллагена обеспечивает по сравнению с прототипом следующие преимущества: повышает растворимость получаемого коллагена в 1,4-2,0 раза, в 1,2 раза повышается чистота препарата. Способ также позволяет расширить сырьевую базу, дает возможность утилизации отходов производства кетгута, интенсифицирует процесс извлечения коллагена. Using the proposed method for producing collagen provides the following advantages in comparison with the prototype: it increases the solubility of the resulting collagen in 1.4-2.0 times, the purity of the drug increases by 1.2 times. The method also allows to expand the raw material base, makes it possible to utilize catgut production wastes, intensifies the process of collagen extraction.

Claims

METHOD FOR PRODUCING COLLAGEN by extraction of raw materials with sodium hydroxide containing sodium sulfate, followed by neutralization and washing of the target product, characterized in that, in order to increase the solubility and purity of the target product, dry catgut is used as a raw material, which is crushed and treated with 10% before extraction solution of hydrogen peroxide containing 2% sodium chloride.