RU128614U1 - Blast furnace air lance - Google Patents
Blast furnace air lance Download PDFInfo
- Publication number
- RU128614U1 RU128614U1 RU2013100964/02U RU2013100964U RU128614U1 RU 128614 U1 RU128614 U1 RU 128614U1 RU 2013100964/02 U RU2013100964/02 U RU 2013100964/02U RU 2013100964 U RU2013100964 U RU 2013100964U RU 128614 U1 RU128614 U1 RU 128614U1
- Authority
- RU
- Russia
- Prior art keywords
- coating
- blast furnace
- heat
- containing gas
- working surface
- Prior art date
Abstract
Воздушная фурма доменной печи, содержащая термообработанное алюмосодержащее газотермическое покрытие на рабочей поверхности, отличающаяся тем, что на термообработанное алюмосодержащее газотермическое покрытие нанесен слой абразивостойкой огнеупорной обмазки на основе карбида бора.An air tuyere of a blast furnace containing a heat-treated aluminum-containing gas-thermal coating on the working surface, characterized in that a layer of abrasion-resistant refractory coating based on boron carbide is applied to the heat-treated aluminum-containing gas-thermal coating.
Description
Полезная модель относится к области металлургии и может быть использована при подготовке к работе воздушных фурм доменных печей.The utility model relates to the field of metallurgy and can be used in preparation for operation of air tuyeres of blast furnaces.
Наиболее близким к предлагаемой по технической сущности является воздушная фурма доменной печи с термообработанным алюмосодержащим газотермическим покрытием на рабочей поверхности (патент №2465333, С21В 7/16, 04.02.11).Closest to the proposed technical essence is the air lance of a blast furnace with heat-treated aluminum-containing gas-thermal coating on the working surface (patent No. 2465333, C21B 7/16, 02/02/11).
Однако фурма с таким покрытием имеет не достаточно высокую стойкость при эксплуатации.However, a lance with such a coating does not have a sufficiently high resistance during operation.
Техническим результатом является повышение стойкости фурмы при эксплуатации.The technical result is to increase the resistance of the lance during operation.
Технический результат достигается тем, что в воздушной фурме доменной печи с термообработанным алюмосодержащим газотермическим покрытием на рабочей поверхности сверху покрытия нанесен слой абразивостойкой огнеупорной обмазки на основе карбида бора.The technical result is achieved by the fact that in the air tuyere of a blast furnace with heat-treated aluminum-containing gas-thermal coating, a layer of abrasion-resistant refractory coating based on boron carbide is applied on top of the coating on the working surface.
Слой абразивостойкой огнеупорной обмазки на основе карбида бора, нанесенный на рабочую поверхность фурмы сверху газотермического покрытия, защищает фурму от абразивного износа шихтовыми материалами и от прогара продуктами плавки, т.е. обеспечивает достижение технического результата.A layer of abrasion-resistant refractory coating based on boron carbide, deposited on the lance working surface on top of the gas-thermal coating, protects the lance from abrasive wear by charge materials and from burnout by smelting products, i.e. ensures the achievement of a technical result.
На рисунке представлено сечение воздушной фурмы доменной печи с термообработанным алюмосодержащим газотермическим покрытием (1) на рабочей поверхности, сверху которого нанесен слой абразивостойкой огнеупорной обмазки (2) на основе карбида бора.The figure shows a cross section of an air lance of a blast furnace with a heat-treated aluminum-containing gas-thermal coating (1) on the working surface, on top of which a layer of abrasion-resistant refractory coating (2) based on boron carbide is applied.
На рабочую поверхность воздушной фурмы доменной печи напыляют алюмосодержащее газотермическое покрытие и проводят термообработку фурмы. Далее на термообработанное покрытие наносят слой абразивостойкой огнеупорной обмазки на основе карбида бора при помощи кисти. После высыхания обмазки фурму устанавливают в доменную печь.An aluminum-containing gas-thermal coating is sprayed onto the working surface of the air tuyere of the blast furnace and heat treatment of the tuyere is carried out. Next, a layer of abrasion-resistant refractory coating based on boron carbide is applied to the heat-treated coating with a brush. After drying the coating, the tuyere is installed in a blast furnace.
Пример.Example.
На рабочую поверхность пяти воздушных фурм доменной печи напыляли алюминиевое газотермическое покрытие и провели термообработку фурм. Далее на термообработанное покрытие нанесли слой абразивостойкой огнеупорной обмазки на основе карбида бора при помощи кисти. После высыхания обмазки фурмы установили в доменную печь. Средняя стойкость опытных фурм оказалась на 20% выше серийных фурм с термообработаннымалюминиевым покрытием на рабочей поверхности без слоя обмазки на основе карбида бора, выведенных из эксплуатации за период работы опытных фурм.An aluminum gas-thermal coating was sprayed on the working surface of five air tuyeres of the blast furnace and heat treatment of the tuyeres was carried out. Next, a layer of abrasion-resistant refractory coating based on boron carbide was applied to the heat-treated coating with a brush. After drying, the lining was installed in a blast furnace. The average resistance of the experimental tuyeres was 20% higher than the serial tuyeres with heat-treated aluminum coating on the working surface without a coating layer based on boron carbide decommissioned during the period of operation of the experimental tuyeres.
Следовательно, слой абразивостойкой огнеупорной обмазки на основе карбида бора, нанесенный на рабочую поверхность воздушной фурмы сверху термообработанного алюмосодержащего газотермического покрытия, повышает стойкость фурмы.Therefore, a layer of abrasion-resistant refractory coating based on boron carbide deposited on the working surface of the air lance on top of the heat-treated aluminum-containing gas-thermal coating increases the resistance of the lance.
Кроме того, слой абразивостойкой огнеупорной обмазки на основе карбида бора, нанесенный на рабочую поверхность воздушной фурмы сверху термообработанного алюмосодержащего газотермического покрытия, способствует снижению тепловых потерь через поверхность фурмы.In addition, a layer of abrasion-resistant refractory coating based on boron carbide deposited on the working surface of the air lance on top of the heat-treated aluminum-containing gas-thermal coating helps to reduce heat loss through the surface of the lance.
Claims (1)