RO119149B1

RO119149B1 - Adhesive composition based on polyvinyl acetate and process for preparing the same

Info

Publication number: RO119149B1
Application number: ROA200300220A
Authority: RO
Inventors: Ion Dobre
Original assignee: S.C. Vadova S.R.L.
Priority date: 2003-03-13
Filing date: 2003-03-13
Publication date: 2004-04-30

Abstract

According to the invention, the composition comprises an aqueous dispersion of polyvinyl acetate, softened water, hydroxyethylcellulose, sodium hexamethaphosphate, sodium polyacrylate, a dispersion of sodium silicate in mineral oil, methapropylene glycol, micronised calcium carbonate and possibly isothiazolinone mixture. The process for preparing the composition consists in producing, while stirring, an initial aqueous composition, wetting agents, increasing the viscosity, dispersing, preserving whereto the calcium carbonate and the aqueous dispersion of polyvinyl acetate are added.

Description

Invenția se referă la o compoziție adezivă pe bază de poliacetat de vinii și la un procedeu de obținere a acesteia, compoziția în două variante de realizare fiind utilizată fie în industria lemnului, la lipirea elementelor de mobilier și a furnirului, și în industria poligrafică, în operații de legătorie, fie în construcții pentru zugrăveli, lipirea faianței și gresiei, tapetului, parchetului și în industria textilă, la apretarea țesăturilor.The invention relates to an adhesive composition based on vinyl polyacetate and to a process for obtaining it, the composition in two embodiments being used either in the wood industry, the gluing of furniture and veneer, and in the polygraphic industry, in binding operations, either in constructions for paintings, bonding of tiles and tiles, wallpaper, parquet and in the textile industry, to the tightening of fabrics.

Sunt cunoscute compoziții adezive și procedee de obținere a lor, constituite din poliacetat de vinii în dispersie apoasă, carbonat de calciu, barită și/sau praf de marmură micronizat, dibutilftalat, acetat de butii, hidroxietilceluloză, mixtură de izotiazolinonă, ulei mineral neionic și apă distilată, obținute prin omogenizarea într-un vas de reacție prevăzut cu agitator și dispozitiv de control al temperaturii cu termostat (RO 116632,116633,116634).Adhesive compositions and processes for making them are known, consisting of vinyl polyacetate in aqueous dispersion, calcium carbonate, barite and / or micronized marble powder, dibutyl phthalate, butyl acetate, hydroxyethyl cellulose, isothiazolinone mixture, nonionic mineral oil and water. distillate, obtained by homogenization in a reaction vessel provided with a stirrer and a thermostat temperature control device (RO 116632,116633,116634).

Dezavantajele acestor compoziții și procedee constau în aceea că folosesc un procent ridicat de poliacetat de vinii în dispersie, folosit în compoziție, și necesită instalații complicate și consumatoare de energie termică, prin faptul că omogenizarea trebuie făcută la temperaturi controlate.The disadvantages of these compositions and processes are that they use a high percentage of dispersed vinyl polyacetate, used in the composition, and require complicated and consuming installations of thermal energy, by the fact that the homogenization must be done at controlled temperatures.

Problema tehnică pe care o rezolvă invenția constă în îmbunătățirea caracteristicilor de aderare la suporturi de diferite naturi și menținerea acestora în timp.The technical problem that the invention solves is to improve the characteristics of adhesion to supports of different natures and to maintain them over time.

Compoziția adezivă conform invenției înlătură dezavantajele de mai sus prin aceea că este constituită din: 20% apă dedurizată, 0,3% hexametafosfat de sodiu, 0,3% hidroxietilceluloză, 0,2% poliacrilat de sodiu, 0,2% dispersie 50% silicat de sodiu în ulei mineral, 0,2% metilpropilenglicol și eventual 0,2% mixtură de izotiazolinonă, 31,3% sau 55,1% carbonat de calciu micronizat și 47,5% sau 23,5% dispersie apoasă de poliacetat de vinii.The adhesive composition according to the invention removes the above disadvantages in that it consists of: 20% softened water, 0.3% sodium hexametaphosphate, 0.3% hydroxyethyl cellulose, 0.2% sodium polyacrylate, 0.2% dispersion 50% sodium silicate in mineral oil, 0.2% methylpropylene glycol and optionally 0.2% isothiazolinone mixture, 31.3% or 55.1% micronized calcium carbonate and 47.5% or 23.5% aqueous polyacetate dispersion. chloride.

Procedeul de preparare a compoziției conform invenției, constă în realizarea unei compoziții inițiale prin adăugarea succesivă sub agitare continuă, pe parcursul a 20...30 min, în apă la temperatura ambiantă, a ingredientelor de umectare, creșterea viscozității, dispersare și omogenizare, coalescență și eventual conservare, la care tot sub agitare continuă pe parcursul a 20...30 min, se adaugă carbonat de calciu micronizat și dispersia apoasă de poliacetat de vinii, apoi se continuă amestecarea încă 20 min și se toarnă în ambalaje.The process of preparing the composition according to the invention consists in achieving an initial composition by successively adding under continuous stirring, during 20 ... 30 min, in water at ambient temperature, the wetting ingredients, the viscosity increase, dispersion and homogenization, coalescence. and possibly preservation, which is continued under stirring for 20 to 30 minutes, adding micronized calcium carbonate and aqueous dispersion of vinyl polyacetate, then mixing for another 20 minutes and pour into packages.

Compoziția și procedeul conform invenției prezintă următoarele avantaje:The composition and process according to the invention have the following advantages:

- asigură o îmbunătățire a calităților adezive față de suporturi de natură diferită;- ensures an improvement of the adhesive qualities with respect to different media;

- conferă o bună rezistență și o bună stabilitate în timp;- gives good strength and stability over time;

- simplifică procedeul și instalațiile folosite.- simplifies the process and the installations used.

Se dau în continuare două exemple de realizare a invenției.Two examples of embodiments of the invention are given below.

Exemplul 1. într-un vas de reacție, prevăzut cu agitator la temperatura mediului ambiant de 18...20°C se introduc 20 kg apă dedurizată, în care se realizează o compoziție inițială, prin adăugare progresivă prin dispersare uniformă, pentru elemente sub formă de pulberi și prin curgere continuă constantă cu debit mic, pentru elementele lichide, sub agitare continuă pe parcursul a 20...30 min, în următoarea ordine: 0,3 kg hexametafosfat de sodiu cu rol de umectat al compoziției, 0,3 kg hidroxietilceluloză cu rol de creștere a viscozității, 0,2 kg poliacrilat de sodiu pentru dispersarea și omogenizarea elementelor, 0,2 kg dispersie 50% silicat de sodiu în ulei mineral ca antispumant, 0,2 kg metilpropilenglicol ca element de coalescență și eventual 0,2 kg mixtură de izotiazolinonă cu rolul de conservant. în această compoziție inițială se adaugă, de asemenea, prin amestecare continuă pe parcursul aExample 1. In a reaction vessel, provided with an agitator at ambient temperature of 18 ... 20 ° C, 20 kg softened water is introduced, in which an initial composition is achieved, by progressive addition by uniform dispersion, for elements below powder form and by constant continuous flow with low flow, for the liquid elements, under continuous stirring during 20 ... 30 min, in the following order: 0.3 kg sodium hexametaphosphate with a wetting role of the composition, 0.3 kg hydroxyethyl cellulose with increasing viscosity role, 0.2 kg sodium polyacrylate for dispersing and homogenizing elements, 0.2 kg dispersing 50% sodium silicate in mineral oil as a non-foaming agent, 0.2 kg methylpropylene glycol as a coalescing element and possibly 0 , 2 kg isothiazolinone mixture with the role of preservative. to this initial composition is also added by continuous mixing over a

20...30 min, 31,3 kg carbonat de calciu micronizat și 47,5 kg dispersie apoasă de poliacetat de vinii cu 46...50% conținut solid și se continuă amestecarea încă 20 min, apoi se toarnă în ambalaje.20 ... 30 min, 31.3 kg micronized calcium carbonate and 47.5 kg aqueous dispersion of vinyl polyacetate with 46 ... 50% solid content and continue mixing for another 20 min, then pour into packages.

Se obține astfel o compoziție care poate fi utilizată în industria lemnului și în industria tipografică.This gives a composition that can be used in the wood industry and in the printing industry.

Exemplul 2. Se procedează la fel ca la exemplul 1 și se obține compoziția inițială în care prin amestecare continuă pe parcursul a 20...30 min, se adaugă 55,1 kg carbonat de calciu micronizat și 23,5 kg dispersie apoasă de poliacetat de vinii cu 46...50% conținut solid și se continuă amestecarea încă 20 min, apoi se toarnă în ambalaje.Example 2. Proceed as in Example 1 and obtain the initial composition in which by continuous mixing for 20 ... 30 min, 55.1 kg of micronized calcium carbonate and 23.5 kg of aqueous polyacetate dispersion are added. of vinyl with 46 ... 50% solid content and continue mixing for another 20 minutes, then pour into packages.

Se obține astfel o compoziție care poate fi utilizată în industria textilă și în construcții.This results in a composition that can be used in the textile and construction industries.

RO 119149 Β1RO 119149 Β1

Claims

claims

1. Adhesive composition based on vinyl polyacetate, characterized in that 55 consists of: 20% softened water, 0.3% sodium hexametaphosphate, 0.3% hydroxyethyl cellulose, 0.2% sodium polyacrylate, 0.2% dispersion 50% sodium silicate in mineral oil, 0.2% methylpropylene glycol and possibly 0.2% isothiazolinone mixture, 31.3% or 55.1% micronized calcium carbonate and 47.5% or 23.5% aqueous dispersion vinyl polyacetate.

2. Process for obtaining the adhesive compositions according to claim 1, characterized in that, at ambient temperature, an initial composition is achieved by successively adding under continuous stirring for 20 to 30 minutes in water, the wetting ingredients, increasing the viscosity, dispersion and homogenization, coalescence and possibly preservation, to which, under continuous stirring, for 20 ... 30 min, micronized calcium carbonate and aqueous dispersion of vinyl polyacetate are added, then further stirring for another 65 20 min. and pour into packages.