PL171623B1 - Method of making blown glass christmas-tree ornaments

Info

Publication number: PL171623B1
Application number: PL30346494A
Authority: PL
Inventors: Robert Mostowski
Original assignee: Robert Mostowski
Priority date: 1994-05-12
Filing date: 1994-05-12
Publication date: 1997-05-30

Abstract

The method of producing glass bulb Christmas-tree ornaments consists in shaping glass half-product into a bulb with the main and supporting outlets. A heated bulb is placed in a mould and blow-moulded. Then, the supporting outlet is relaxed, singed and sealed by melting. When placed in a holder, the main outlet is singed and the entire bulb is relaxed. Characterized in that: During the blowing process, the glass bulb is equipped with an additional shape element in the form of a venting protrusion, located at one of the longer walls of the bulb. Once the bulb is relaxed, the protrusion is opened by a burner flame, while the main outlet is sealed by melting.

Description

Przedmiotem wynalazku jest sposób wytwarzania szklanych wydmuszek ozdób choinkowych, służących do przystrajania.The subject of the invention is a method of producing glass blown Christmas decorations for embellishments.

Znany jest sposób produkcji szklanych ozdób choinkowych, na przykład z opisu zgłoszeniowego nr 227033, opublikowanego w BUP 8/82, który polega na tym. że do produkcji baniek do ozdób choinkowych jako produkt wyjściowy stosuje się półfabrykat w postaci balonika do żarówki, który poddaje się operacji nagrzewania, kształtowania i wyciągania szyjki Szyjkębańki kształtuje się przez wytworzenie w niej podciśnienia poprzez rurkę umocowaną w głowicy, której koniec wchodzi do wnętrza bańki i która stanowi rdzeń dla wewnętrznej średnicy bańki.A method of producing glass Christmas tree ornaments is known, for example, from application description No. 227033, published in BUP 8/82, which is based on this. that for the production of bubbles for Christmas decorations, as a starting product, a semi-finished product in the form of a bulb for a bulb is used, which is subjected to the operation of heating, shaping and pulling the neck of the neck of the bulb by creating a negative pressure in it through a tube fixed in the head, the end of which goes inside the bubble and which is the core of the inner diameter of the bulb.

Inny znany sposób polega na tym, że odpowiednią porcję półproduktu, w postaci rury szklanej, nagrzewa się do stanu plastyczności, a następnie wykonuje odciąg główny ze grubionym przewężeniem oraz odciąg podtrzymujący, po czym tak uformowaną porcję upala się od rury Przygotowaną w ten sposób, tak zwaną oliwkę ogrzewa się do stanu plastyczności, następnie wkłada do formy i rozdmuchuje ustnie poprzez odciąg główny, przy czym, po wyjęciu wydmuszki z formy poddaje się ją odprężeniu, dla wyrównania temperatur. W następnej operacji upala i zatapia się odciąg podtrzymujący, po czym umieszcza się wydmuszkę w uchwycie, od strony odciągu podtrzymującego i upala odciąg główny W ostatniej operacji wydmuszkę odpręża się. Występ odciągu głównego służy do zamocowania zawieszki.Another known method consists in heating the appropriate portion of the semi-finished product, in the form of a glass tube, to the state of plasticity, and then making the main draft with a thick throat and supporting draft, and then the portion thus formed is heated from the pipe. the so-called olive is heated to a plastic state, then put into a mold and blown orally through the main extractor, whereby, after removing the shell from the mold, it is relaxed in order to equalize the temperatures. In the next operation, the supporting lashings are heated and submerged, then the shell is placed in the holder, from the side of the supporting lashings, and the main exhaust is heated. In the last operation, the shell is relaxed. The protrusion of the main lashing is used to attach the pendant.

Sposobem tym wykonywane są ozdoby choinkowe w znanych firmach na świecie, jak na przykład w firmie niemiecko-amerykańskiej Old World Christmas czy amerykańskiej Christopher Radko, przy czym sposobem tym wykonywane są zwłaszcza ozdoby kuliste oraz takie, których wymiary poprzeczne - po zawieszeniu są mniejsze od ich wysokości.This method is used to make Christmas tree decorations in well-known companies in the world, such as the German-American company Old World Christmas or the American Christopher Radko, and this method is used to make especially spherical decorations and those whose lateral dimensions - after hanging - are smaller than their heights.

Dla takich kształtów ozdób, które dla prawidłowego efektu estetycznego powinny być tak zawieszane, aby ich wymiary poprzeczne były większe od wysokości, należało wprowadzać dodatkową operację, to jest dolutowywanie zawieszek szklanych.For such shapes of ornaments, which for the proper aesthetic effect should be hung in such a way that their transverse dimensions are greater than their height, an additional operation had to be introduced, i.e. soldering glass hangers.

W celu wyeliminowania powyższej niedogodności opracowano sposób polegający na tym, ze podczas operacji rozdmuchiwania, nadaje się bance dodatkowy element kształtu, w postaci występu odpowietrzającego, usytuowanego na jednej z dłuzszych jej ścianek, który po odprężeniu wydmuszki zostaje otwarty płomieniem palnika, natomiast otwór odciągu głównego zatapia się.In order to eliminate the above inconvenience, a method has been developed whereby, during the blowing operation, an additional shape element is provided to the bend, in the form of a venting protrusion located on one of its longer walls, which, after the bladder is relaxed, is opened with the flame of the burner, while the opening of the main extractor is sealed out.

Sposób według wynalazku pozwala wyeliminować operację dolutowywama zawieszek szklanych dla wydmuszek ozdób choinkowych, których wymiary poprzeczne po zawieszeniu, są większe od wysokościThe method according to the invention makes it possible to eliminate the operation of soldering glass pendants for blown Christmas decorations, the lateral dimensions of which after hanging are greater than the height.

Przykład. Półprodukt szklany w postaci rury o średnicy zewnętrznej 45 mm ogrzano na odcinku 150 mm do stanu plastyczności i wykonano odciąg główny oraz pogrubioneExample. The glass semi-finished product in the form of a pipe with an outer diameter of 45 mm was heated on a 150 mm section to the state of plasticity, and the main and thickened stays were made

171 623 przewężenie, po czym na końcu wydzielonej porcji półproduktu wykonano cienki odciąg podtrzymujący. Otrzymaną w ten sposób tak zwaną oliwkę, podtrzymując z obu stron i obracając, podgrzano do temperatury plastyczności, po czym włożono do formy w celu nadania jej kształtu samochodu, a następnie ustnie poprzez odciąg główny rozdmuchano. Forma posiadała dodatkowy element kształtu w postaci kanału, usytuowanego na dłuzszej ściance - odpowiadającej dachowi samochodu, dzięki czemu wydmuszka samochodu zaopatrzona została w występ odpowietrzający, umieszczony na dachu. Po wyjęciu wydmuszki z formy poddano ją odprężaniu, a następnie upalono i zatopiono odciąg podtrzymujący. W kolejnej opeiacji. płomieniem palnika, otwarto występ odpowietrzający w celu wyrównania ciśnień, a następnie umieszczono wydmuszkę, od strony odciągu podtrzymującego, w podgrzanym uchwycie (dla zmniejszenia różnicy temperatur) i upalono oraz zatopiono odciąg główny. Ostatnią operacją było odprężenie wydmuszki.171 623 throat, and then a thin supporting haul-off was made at the end of the separated portion of intermediate. The so-called olive obtained in this way, supporting it on both sides and turning it, was heated to the temperature of plasticity, after which it was put into a mold to give it the shape of a car, and then orally blown through the main extractor. The mold had an additional element of shape in the form of a channel, situated on a longer wall - corresponding to the car roof, thanks to which the car's shell was provided with a venting protrusion placed on the roof. After removing the blown from the mold, it was stressed, then fired and the supporting haulage was submerged. In another opeiation. flame of the burner, the venting tab was opened to equalize the pressures, and then the blow-out, from the supporting hood side, was placed in the heated handle (to reduce the temperature difference) and the main hood was burned and flooded. The last operation was to relax the shell.

W ten sposób otrzymano wydmuszkę w postaci samochodu, posiadającą zawieszkę na dachu - bez potrzeby dolutowywania szklanego ucha.In this way, a car shell was obtained, with a pendant on the roof - without the need to solder a glass ear.

171 623171 623

Departament Wydawnictw UP RP. Nakład 90 egz. Cena 2,00 złPublishing Department of the UP RP. Circulation of 90 copies. Price PLN 2.00

Claims

Patent claim

A method of producing glass blown Christmas decorations, which consists in shaping a glass blank with a main and supporting extractor, which, after heating, is placed in the mold and blown, and then relaxes, fires and submerges the supporting extractor, and after placing it in the holder, the main extractor becomes hot, and the whole is relaxed, characterized in that during blowing, the bulb is provided with an additional shape element in the form of a venting protrusion, located on one of its longer walls, which, after the bladder is relaxed, is opened by the flame of the burner, while the main exhaust opening is flooded