NZ735767B2 - Setting accelerator for a tile adhesive blend - Google Patents
Setting accelerator for a tile adhesive blendInfo
- Publication number
- NZ735767B2 NZ735767B2 NZ735767A NZ73576716A NZ735767B2 NZ 735767 B2 NZ735767 B2 NZ 735767B2 NZ 735767 A NZ735767 A NZ 735767A NZ 73576716 A NZ73576716 A NZ 73576716A NZ 735767 B2 NZ735767 B2 NZ 735767B2
- Authority
- NZ
- New Zealand
- Prior art keywords
- powder
- nitrate
- weight
- setting accelerator
- use according
- Prior art date
Abstract
The application relates to the use of a powder comprising calcium nitrate as a setting accelerator for a tile adhesive blend, wherein a powder comprising calcium nitrate, and optionally also comprising a nitrate salt different than the calcium nitrate, specifically potassium or ammonium nitrate, with at least 70 wt% of the powder having a particle size of between 0.01 mm and 1 mm, is used as the setting accelerator. The application furthermore relates to a process for producing such a setting accelerator comprising, in one possible embodiment, the step of cutting or grinding prills and/or granules comprising the calcium nitrate and optionally the different nitrate salt, and in another embodiment, a spray drying process, resulting into the setting accelerator. The application also relates to a tile adhesive blend comprising at least a cement, sand and a such setting accelerator.
Claims (9)
1. Use of a powder sing calcium nitrate as a g accelerator in a tile adhesive blend, wherein at least 70 weight% of the powder has a particle size of between 0.01 mm and 1 mm wherein the powder comprises at least 70 weight% calcium nitrate and wherein the powder comprises a further nitrate salt different from calcium e.
2. Use according to claim 1 wherein the further nitrate salt is potassium nitrate or ammonium nitrate.
3. Use according to claim 1 or 2 wherein at least 70 wt.% of the powder has a particle size between 0.1 mm and 1 mm.
4. Use according to any one of claims 1 to 3, wherein the powder comprises 75 weight% to 80 % of calcium e and 7 weight% to 11 weight% of potassium nitrate or ammonium nitrate.
5. Use according to any one of claims 1 to 4, wherein the powder has a water content between 0.1 weight% and 20 weight%.
6. Use according to any one of claims 1 to 5, wherein at least 80 weight% of the powder has a le size of between 0.01 mm and 1 mm.
7. Use according to claim 6, wherein at least 90 weight% of the powder has a particle size of between 0.01 mm and 1 mm.
8. Use according to claim 6, wherein at least 90 weight% of the powder has a particle size between 0.1 mm and 1.0 mm. gN -|> Jpn-r - - - ‘ ”?J l ...... :- u I. . . I. . 23 .....s 3 _ :. 4" -. .t' "t
9. “WT.................WW...“ __ .. g — l— 21 mmww-«m 20 "MW—T‘?mm?—T?mmmm?mwmrme—WWWTWWU"""""""""""1 6 9 12 15 18 21 24 Time(hours) VVVVVVVVVVVVVVVVVVVVVVVVVVVV A 22 , ...... U ' 3 —-Reference h - - >2mm E ....... 1_2mm '— 20 —O,5-1mm 0,1—O,5mm 19 ----<0,1mm — -Salt grinder 13 .............. ‘ 7 0 5 10 15 20 25 Time (hours)