NZ201908A - Gallium and/or indium-containing zeolites and use as olefin producing catalysts - Google Patents
Gallium and/or indium-containing zeolites and use as olefin producing catalystsInfo
- Publication number
- NZ201908A NZ201908A NZ201908A NZ20190882A NZ201908A NZ 201908 A NZ201908 A NZ 201908A NZ 201908 A NZ201908 A NZ 201908A NZ 20190882 A NZ20190882 A NZ 20190882A NZ 201908 A NZ201908 A NZ 201908A
- Authority
- NZ
- New Zealand
- Prior art keywords
- indium
- gallium
- strong
- weak
- oxides
- Prior art date
Description
New Zealand Paient Spedficaiion for Paient Number £01 908
2 019 0 8
Priority Dau^}: . J k.~. ?.......... I
Complete Specification FiJed: I
Class: £?.XPM I?-&•,.
PubSicsticrv Data: ... J) ?■. JUL J995...
PJX Wo:
N!
ill
N.Z. No.
NEW ZEALAND
Patents Act 1953
COMPLETE SPECIFICATION
"GALLIUM-CONTAINING AND/OR INDIUM-CONTAINING ZEOLITES, A PROCESS FOR THEIR PREPARATION, AND THEIR USE."
We, HOECHST AKTIENGESELLSCHAFT, a corporation,;
:| 415 "JCf/yig organized under the laws of the Federal Republic of Germany,of D-6230 Frankfurt/Main 80, Federal Republic of Germany,
do hereby declare the invention, for which we pray that a Patent may be granted to us, and the ;method by which it is to be performed,to be particularly described in and by the following statement
, 201908
Zeolites are crystalline aluminosiIicates in which, as a result of threedimensionaI linking of SiO^- and AlO^-tetrahedra, regular structures having cavities and pores are formed. In the hydrated state, these pores and cavi-5 ties are filled with water. This may be removed or replaced by other molecules without affecting the crystal structure. The negative charges of the AlO^ tetrahedra are compensated by cations. These can be replaced by other positively charged ions. The properties described 10 make it possible to use zeolites as ion exchangers, adsorbents and catalysts (D.W. Breck: Zeolite Molecular Si eves, 1974).
Zeolites of the X, Y, mordenite, erionite and offretite type, for example, are of considerable intei— 15 est industrially as catalysts for conversion reactions of hydrocarbons, such as cracking, hydrocracking or isomer i zat i ons . Zeolites of the pentasil type (for example Zeolite ZSM-5) are becoming increasingly important as catalysts for converting methanol to hydrocarbons. 20 Because of the large number of possible uses as catalysts, there is considerable interest in novel zeolites with specific catalytic properties.
For example, very interesting zeolites are obtained when, instead of aluminum and/or silicon, other elements 25 are incorporated into the zeolite structure. Thus, inter alia, zeolites of the pentasil series which contain boron
201908
iron, arsenic antimony, vanadium, chromium or galiium in tetrahedral sites have been disclosed.
The invention relates to gallium-containing and/or indium-containing zeolites which a) have the following composition:
Si02 : (0,09 i 0,07) £~M-203 + M203_7 :
(0,12 - 0,10) I bJa20 + K20J ; (0,12 ~ 0,10) R00
expressed as molar ratios of oxides, wherein R is choline
C(CH3)3NCH2CH2CHD+ and M is gallium and/or indium,
and
b) exhibit, in the X-ray diffraction diagram, the characteristic signals listed in Table 1:
Table 1
Interlayer spacing d c)b
Relative intensity I/I0
11.5 ♦ 0.2
very strong
9.2 + 0.2
weak
7.6 + 0.2
weak to medi urn
6.6 + 0.1
medi um to strong
.7 + 0.1
weak to medium
.35 + 0.1
weak
4.98 + 0.1
weak
4.56 + 0.1
nedi um to strong y, W T
|s. *. v ;10 ;15 ;20 ;4 ;- 4 - ;Interlayer spacing d c h ;Relative intensity ino ;4.32 + 0.1 ;strong ;4.16 + 0.1 ;weak ;3.81 + 0.1 ;strong to very strong ;3.75 + 0.1 ;strong to very strong ;3.59 + 0.1 ;strong to very strong ;3.30 + 0.1 ;medium ;3.15 + 0.1 ;medium ;2.92 + 0.1 ;weak ;2.86 + 0.1 ;strong to very strong ;2.80 + 0.1 ;weak ;2.67 + 0.1 ;weak ;2.49+0.1 ;weak ;In the above table, IQ denotes the intensity of the strongest signal. ;The following applies to the intensity data in ;Table 1: ;Relative intensity ;100 ;X/Io very strong ;80 - ;100 ;strong ;50 ■ ;- 80 ;medium ;20 - ;50 ;weak ;0 ■ ;• 20 ;The following applies in general to the zeolites 25 according to the invention: ;Al2°3 ;Al2°3 + M2°3 ;= 0,01 - 0.99, ;preferab ly ;- 5 - ;201908 ;Al^O^ ;= 0.40 - 0.99, ;A12°3 + M2°3 ;in parti cular ;A12°3 ;A12°3 + M2°3 ;= 0.60 - 0.99, ;expressed as molar ratios of the oxides, wherein M is 5 gallium and/or indium. ;The novel zeolites according to the invention have a structure similar to those of the zeolites T (U.S. Patent 2,950,952). and ZSM-34,-_ - ' ;but differ from these in composition, 10 in particular in the gallium or indium content. ;The zeolites according to the invention can be prepared by mixing gallium compounds and/or indium compounds with aluminum compounds, silicon compounds, sodium compounds, potassium compounds, choline compounds and 15 water, and heating the mixture in a closed vessel. ;The starting compounds are employed in general in the following ratio, expressed as molar ratios of the oxides: ;Si-O- : (0.06 - 0.058) Al-O,. : (0,06 - 0.058) : ;2 0 . 2 3 ;(0,2 - 0.15) Na20 : (0.12 - 0.10) K20 ;(0,22 i 0.2) R20 : (50 ± 40) H20 ;preferably in the ratio: ;1908 ;- 6 - ;Si02 : (0.05 - 0.04) Al2C>3 : (0.05 - 0.048) M2C>3 : (0.2 i 0.1) N^O : (0.09 ~ 0.05) K20 : ;(0.22 - 0.10) R20 : (20 - 10) H20 ;wherein R is choline and M is gallium and/or indigm. ;5 The following are examples of compounds which may be employed: silica gel, potassium silicate, sodium silicate, aluminum hydroxide, aluminum sulfate, sodium alu-minate, potassium aluminate, aluminum halides, aluminum metahydroxide, gallium(III) oxide, gallium(III) nitrate, 10 gal lium (III) sulfate, gallium(III) halides, gallium(III) hydroxide, indium(III) oxide, indium(III) nitrate, indium(III) sulfate, indium(III) halides, indium(III) hydroxide, sodium hydroxide, sodium sulfate, sodium halides, potassium hydroxide, potassium sulfate, potassium 15 halides, choline hydroxide and choline chloride. However, other silicon, aluminum, gallium, indium, potassium, sodium and choline compounds are also suitable for the preparation of the zeolites according to the invention. ;The mixture, with water, of the compounds selec-20 ted in each case is heated in a closed vessel in general for from 48 to 2,000 hours, preferably from 48 to 1,000 hours, at a temperature between 80 and 160°C, preferably between 90 and 150°C. ;The zeolites formed are isolated in a conventional 25 manner, for example by filtration, and are washed and dried. They can be converted into the cata lytica 11 y ;9 08 ;- 7 - ;active forms by known methods, for example by calcination and/or ion exchange (D.W. Breck, Zeolite Molecular Sieves, 1974). ;After their conversion to the cata lytica I ly active 5 form, the zeolites according to the invention are distinguished in particular by high selectivity and by low coke formation in the conversion of methanol to lower olefins. This reaction is carried out, for example, at temperatures between 350 and 430°C using methanol with a water content of 10 0 to 80% by weight or raw methanol. ;The examples which follow are intended to illustrate the invention, but are not intended to be restrictive in any way. All X-ray diffraction data given were recorded with a computer-controlled D-500 powder diffracto-15 meter from Siemens. Copper Kcc radiation was used. ;Example 1 ;11.2 g of sodium alurninate (54% by weight of AI2O3, 41% by weight of Na20>/ 11.15 g of gallium trioxide, 5.9 g of sodium hydroxide, 5.3 g of potassium hydroxide 20 and 45.6 g of choline chloride were dissolved in 150 g of water. 117 g of 40% strength by weight colloidal silica gel were introduced into this solution. The mixture formed was homogenized, and heated at 150°C for 8 days in a closed vessel. The product formed was filtered 25 off, washed with water and dried at 120°C. ;Chemical analysis gave the following composition, ;expressed as molar ratios of oxides: Si02 : 0.0 ;0.051 R20, ;Si02 : 0.098 A12C>3 : 0.031 Ga203 : 0.050 Na20 : 0.046 K20 ;8 - ;wherein R is choline. ;The result of the X-ray diffraction analysis is reproduced in Table 2. ;Table 2 ;10 ;15 ;20 ;25 ;Interlayer spacing d ifo ;Relative intensity 100 I/IQ ;11.50 ;100 ;9.16 ;5 ;7.58 ;18 ;6.62 ;49 ;6.33 ;8 ;5.74 ;16 ;5.35 ;3 ;4.98 ;2 ;4.56 ;37 ;4.33 ;60 ;4.16 ;6 ;3.81 ;92 ;3.76 ;91 ;3.59 ;80 ;3.30 ;33 ;3.16 ;41 ;2.92 ;10 ;2.85 ;88 ;2.80 ;6 ;2.67 ;7 ;2.49 ;8 ;Examp le 2 ;2.23 g of gallium trioxide, 7.41 g of aluminum ;?, 9 1 9 0 8 ;- 9 - ;hydroxide, 10.6 g of sodium hydroxide, 5.30 g of potassium hydroxide and 45.6 g of choline chloride were dissolved in 150 g of water. 117 g of 40% strength by weight colloidal silica gel were introduced into this solution. 5 The mixture formed was homogenized, and heated at 105°C for 720 hours in a closed vessel. After the mixture had been worked up as described in Example 1, a crystalline product of the following composition, expressed as molar ratios of oxides, was obtained: ;10 : 0-0*71 Al2C>3 • 0.014 Ga^O^ : 0.040 Na„0 : 0.031 K~0
^ 2
0.020 R20,
wherein R = choline.
The X-ray data correspond to those given in
T a b I e 1.
Example 3
As in Example 2, a mixture was prepared from 5.6 g of sodium aluminate, 11.0 g of gallium trioxide, 7.2 g of sodium hydroxide, 5.3 g of potassium hydroxide, 45.6 g of choline chloride, 117 g of 40% strength by weight col-20 loidal silica gel and 150 g of water. This mixture was heated at 100°C for 1,200 hours in a closed vessel.
After the mixture had been worked up as in Example 1, a crystalline product with the following composition, expressed as molar ratios of oxides, was obtained:
Si02 : 0.040 Al2°3 : 0.044 Ga2C>3 : 0.024 Na20 : 0.033 K20 0.051 R2Of wherein R = choline.
The product exhibited the X-ray signals given in
Table 1.
Claims (7)
1. A gallium-containing and/or indium-containing zeolite which a) has the following composition: Si02 : (0.09 - 0.07) /~A12C>3 + M203_7 : * (0.12 ~ 0.10) /~Na20 + K20J : (0.12 - 0.10) B20 expressed as molar ratios of oxides, wherein R is choline and M is gallium and/or indium, and b) exhibits, in the X-ray diffraction diagram, the characteristic signals listed in Table 1: Table 1 Interlayer spacing d :5b 11.5 + 0.2 9.2 + 0.2 7.6 + 0.2 6.6 + 0.1 5.7 + 0.1 5.35 + 0.1 4.98 + 0.1 4.56 + 0.1 4.32 + 0.1 4.16 + 0.1 3.81 + 0.1 3.75 + 0.1 3.59 + 0.1 3.30 + 0.1 3.15 + 0.1 Relative intensity I/I„ very strong weak weak to medium medium to strong weak to medium weak weak medi um to strong strong weak strong to very strong strong to very strong strong to very strong medium medi um 9 - 12 - ^01908 Interlayer spacing d ill Relative intensity I/In 2.92 +_ 0.1 weak 2.86 + 0.1 strong to very strong 2.80 + 0.1 weak 2.67 + 0.1 weak 2.A 9 + 0.1 weak of the strongest signal.
2. A gaI Iium-containing and/or indium-containing zeolite as claimed in claim 1, wherein the following a ppIi es: A12°3 = 0.01 - 0.99, A12°3 + M2°3 expressed as molar ratios of the oxides, wherein M is gallium and/or indium.
3. A gallium-containing and/or indium-containing zeolite as claimed in claim 1 or 2, wherein the following applies: — = 0.40 - 0.99, Al2°3 + M203 expressed as molar ratios of the oxides, wherein M is gallium and/or indium.
4. A gallium-containing and/or indium-containing zeolite as claimed in any one of claims 1 to 3, wherein the following applies: = 0.60 - 0.99, Al2°3 A12°3 + M2°3 expressed as molar ratios of the oxides, wherein, M i E •. gallium and/or indium. * L 201908 - 13 -
5. A process for the preparation of a gallium- containing and/or indium-containing zeolite as claimed in any one of claims 1 to 4, wherein a mixture of silicon compounds, aluminum compounds, sodium compounds, potassium compounds and choline compounds, water and gallium compounds and/or indium compounds is prepared, the mixture having the following composition, expressed as molar ratios of the oxides: Si02 : (0.06 i 0.058) A12C>3 : (0.06 ^ 0.058) : (0.2 - 0.15) Na20 : (0.12 - 0.10) K20 : (0.22 i 0.2) R20 : (50 - 40) H20 wherein R is choline and M is gallium and/or indium, and this mixture is heated in a closed vessel.
6. A process as claimed in claim 5, wherein the mix ture to be heated has the following composition, expressed as molar ratios of the oxides: Si02 : (0.05 - 0.04) A1203 : (0.05 i 0.048) M2C>3 : c ^ T (0.2 i 0.1) Na20 : (0.09 - 0.05) K20 : (0.22 - 0.10) R2C : (20 ~ 10) h'O V2 5®l%5 K'7/--1 >!,?-• wherein R is choline and M is gallium and/or indium. -14- 201908
7. Use, as catalysts, in the production of C2-C4- olefins from methanol, of gallium-containing and/or indium containing zeolites as claimed in any one of claims* 1 to 4 HOECHST AKTIENGESELLSCHAFT By Their Attorneys HENRY HUGHES LIMITED