NO893437D0 - VERY SILICON DISPERSION. - Google Patents

VERY SILICON DISPERSION.

Info

Publication number
NO893437D0
NO893437D0 NO893437A NO893437A NO893437D0 NO 893437 D0 NO893437 D0 NO 893437D0 NO 893437 A NO893437 A NO 893437A NO 893437 A NO893437 A NO 893437A NO 893437 D0 NO893437 D0 NO 893437D0
Authority
NO
Norway
Prior art keywords
parts
emulsion
elastomer
silicone
water
Prior art date
Application number
NO893437A
Other languages
Norwegian (no)
Other versions
NO893437L (en
Inventor
Michel Feder
Jean Ulrich
Original Assignee
Rhone Poulenc Chimie
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Rhone Poulenc Chimie filed Critical Rhone Poulenc Chimie
Publication of NO893437D0 publication Critical patent/NO893437D0/en
Publication of NO893437L publication Critical patent/NO893437L/en

Abstract

The present invention relates to an aqueous silicone dispersion which crosslinks to give an elastomer by elimination of water and which comprises: 100 parts of an emulsion (A) of the oil-in-water type, of an alpha , omega -(dihydroxy)polydiorganosiloxane stabilised with an anionic and/or nonionic surfactant, 1 to 100 parts of a hydroxylic silicone resin which, per molecule, exhibits at least 2 different units chosen from among those of the formulae R3SiO0.5, R2SiO, RSiO1.5 and SiO2 and having a content of hydroxyl groups of between 0.1 and 10% by weight, 0 to 250 parts of a non-siliceous inorganic filler and 0.01 to 3 parts of a metal compound which acts as a hardening catalyst, the said emulsion having a pH which is generally between 4 and 13 and a solids content of at least 40%. Use of the emulsions for the production of silicone elastomer joints, especially in the building industry.
NO89893437A 1988-08-31 1989-08-28 VERY SILICON DISPERSION. NO893437L (en)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
FR8811609A FR2638166B1 (en) 1988-08-31 1988-08-31 AQUEOUS DISPERSION BASED ON SILICONE RESIN WHICH CAN CROSSLINK TO AN ELASTOMER BY REMOVING WATER

Publications (2)

Publication Number Publication Date
NO893437D0 true NO893437D0 (en) 1989-08-28
NO893437L NO893437L (en) 1990-03-01

Family

ID=9369732

Family Applications (1)

Application Number Title Priority Date Filing Date
NO89893437A NO893437L (en) 1988-08-31 1989-08-28 VERY SILICON DISPERSION.

Country Status (19)

Country Link
EP (1) EP0359676B1 (en)
JP (1) JPH0645756B2 (en)
KR (1) KR930003699B1 (en)
CN (1) CN1030460C (en)
AT (1) ATE96824T1 (en)
AU (1) AU627217B2 (en)
BR (1) BR8904277A (en)
CA (1) CA1326097C (en)
DE (1) DE68910449T2 (en)
DK (1) DK175833B1 (en)
ES (1) ES2047700T3 (en)
FI (1) FI894073A (en)
FR (1) FR2638166B1 (en)
HU (1) HUT53140A (en)
IE (1) IE63399B1 (en)
NO (1) NO893437L (en)
NZ (1) NZ230469A (en)
PT (1) PT91587A (en)
ZA (1) ZA896630B (en)

Families Citing this family (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2637606B1 (en) * 1988-10-11 1990-12-14 Rhone Poulenc Chimie AQUEOUS SILICONE DISPERSION BASED ON ALCENYLOXYSILANE CROSSLINKING TO AN ELASTOMER BY REMOVAL OF WATER
DE4026029A1 (en) * 1989-09-07 1992-02-20 Sandoz Ag AQUEOUS AMINOPOLYSILOXAN MICROEMULSIONS, THEIR PRODUCTION AND USE
DE4217561A1 (en) * 1992-05-27 1993-12-02 Wacker Chemie Gmbh Aqueous dispersions of organopolysiloxanes
US5449712A (en) * 1993-01-13 1995-09-12 Thoro System Products, Inc. Organosilicon emulsions for rendering porous substrates water repellent
US5895794A (en) * 1993-08-30 1999-04-20 Dow Corning Corporation Shelf stable cross-linked emulsions with optimum consistency and handling without the use of thickeners
FR2746052B1 (en) * 1996-03-15 1998-07-03 PROCESS FOR MOLDING AND WATERPROOFING MOLDED ELEMENTS IN CONCRETE, MORTAR, CEMENT, WITH A SILICONE RESIN
DE19934438B4 (en) * 1999-07-22 2008-01-17 Wacker Chemie Ag Process for the preparation of a 1-component aqueous silicone composition
ATE453677T1 (en) * 2003-10-08 2010-01-15 Dow Corning EMULSIONS CONTAINING MQ SILICONE RESIN REINFORCED SILICONE ELASTOMER
JP4678402B2 (en) * 2007-11-02 2011-04-27 信越化学工業株式会社 Film-forming organopolysiloxane emulsion composition and fiber texture improving agent
EP2231754B1 (en) 2007-12-14 2011-07-20 Henkel AG & Co. KGaA Curable compositions containing aqueous dispersions of organopolysiloxanes
DE102007060919A1 (en) 2007-12-14 2009-06-18 Henkel Ag & Co. Kgaa Aqueous dispersion of silicone oil, used e.g. as sealant, comprises hydroxyl/hydrolyzable group containing organopolysiloxane, organopolysiloxane, crosslinking agent, emulsifier, crosslinking catalyst, polymer dispersion, filler and water
DE102008003155A1 (en) 2008-01-03 2009-07-09 Henkel Ag & Co. Kgaa Curable composition, useful e.g. as sealants, coatings and curable adhesives, comprises organopolysiloxanes, crosslinking agent, emulsifier, crosslinking catalyst, aqueous silicon-free polymer dispersion, filler and optionally water
JP4678411B2 (en) * 2008-02-22 2011-04-27 信越化学工業株式会社 Film-forming organopolysiloxane emulsion composition
JP5608909B2 (en) * 2010-01-08 2014-10-22 モメンティブ・パフォーマンス・マテリアルズ・ジャパン合同会社 Room temperature curable polyorganosiloxane composition
JP2016027069A (en) * 2014-06-26 2016-02-18 日東電工株式会社 Flame-retardant material and its application

Family Cites Families (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3070560A (en) * 1959-01-19 1962-12-25 Dow Corning Composition comprising a polysiloxane resin, silica filler, a hydroxylated siloxane, and a boron compound
US4257932A (en) * 1978-06-27 1981-03-24 General Electric Company Curable compositions and process
DE3323909A1 (en) * 1983-07-02 1985-01-10 Bayer Ag, 5090 Leverkusen STABLE SILICONE EMULSIONS
FR2565593B1 (en) * 1984-06-12 1986-12-12 Rhone Poulenc Spec Chim AQUEOUS EMULSION COMPOSITIONS FOR NON-STICK AND WATER REPELLENT TREATMENT OF CELLULOSIC MATERIALS
JPH0639568B2 (en) * 1985-04-24 1994-05-25 東レ・ダウコーニング・シリコーン株式会社 Process for producing silicone aqueous emulsion composition
DE3637836A1 (en) * 1986-11-06 1988-05-19 Wacker Chemie Gmbh AQUEOUS SILICONE DISPERSIONS
DE3727180A1 (en) * 1987-08-14 1989-02-23 Wacker Chemie Gmbh AQUEOUS SILICONE DISPERSIONS
GB8806145D0 (en) * 1988-03-15 1988-04-13 Unilever Plc Electrical sensor & method

Also Published As

Publication number Publication date
KR900003306A (en) 1990-03-26
NO893437L (en) 1990-03-01
BR8904277A (en) 1990-04-17
CN1040997A (en) 1990-04-04
FI894073A (en) 1990-03-01
NZ230469A (en) 1991-09-25
AU627217B2 (en) 1992-08-20
KR930003699B1 (en) 1993-05-08
EP0359676A1 (en) 1990-03-21
CA1326097C (en) 1994-01-11
EP0359676B1 (en) 1993-11-03
DK426689A (en) 1990-03-01
JPH02105859A (en) 1990-04-18
AU4086889A (en) 1990-03-08
ES2047700T3 (en) 1994-03-01
FR2638166B1 (en) 1991-01-11
HUT53140A (en) 1990-09-28
DE68910449D1 (en) 1993-12-09
DK426689D0 (en) 1989-08-30
PT91587A (en) 1990-03-30
IE63399B1 (en) 1995-04-19
DE68910449T2 (en) 1994-05-11
ATE96824T1 (en) 1993-11-15
JPH0645756B2 (en) 1994-06-15
FI894073A0 (en) 1989-08-30
ZA896630B (en) 1990-05-30
IE892793L (en) 1990-02-28
DK175833B1 (en) 2005-03-21
CN1030460C (en) 1995-12-06
FR2638166A1 (en) 1990-04-27

Similar Documents

Publication Publication Date Title
NO893437D0 (en) VERY SILICON DISPERSION.
DE69020450T2 (en) Aqueous dispersion containing silicone oil and organic (co) polymer that hardens to an elastomer after removal of the water.
ES2056422T3 (en) AQUEOUS DISPERSION OF SILICONE BASED ON AMINOSILANE AND / OR AMIDOSILANE THAT RETICULATES IN AN ELASTOMER BY WATER DISPOSAL.
FR2565593B1 (en) AQUEOUS EMULSION COMPOSITIONS FOR NON-STICK AND WATER REPELLENT TREATMENT OF CELLULOSIC MATERIALS
ATE43621T1 (en) SILICONE RESIN EMULSION.
PT606671E (en) ORGANOSILICUM EMULSES TO BECOME POROUS SUBSTRATES
BR8805424A (en) SILICON EMULSION, PROCESS FOR THE PREPARATION OF THE SAME AND ELASTOMER
ATE138961T1 (en) AQUEOUS SILICONE OIL DISPERSION CURED BY WATER ELIMINATION TO A FLAME-RESISTANT ELASTOMER
DK0904321T3 (en) Aqueous dispersion based on silicones and organic (co) polymer latex to produce adjustable silicone elastomer
HU9600893D0 (en) Two steps method for impregnation of moisty plasers
KR960029412A (en) Organopolysiloxane composition which can be stabilized by heat and crosslinked to obtain an elastomer
KR910006562A (en) Microemulsions of Aminopolysiloxanes